Telah dilakukan analisis pengaruh penambahan 0.5 mol berat Mn terhadap struktur kristal dan konstanta dielektrik barium titanat. Bahan percobaan terbaik yang didapat dari sintesis metalurgi serbuk dengan temperatur sintering maksimum 950°C dan perbandingan stoichiometrinya adalah 1 : 0.5 : 0.5 mol berat bahan asal BaCO3, MnO2 dan TiO2 yang merupakan reagen dari E-Merck. Difraktogram sinar-x dengan cacah kontinu dan panjang gelombang atau X (Co Ka) = 1.7889 A yang diperoleh pada suhu kamar, dianalisis menggunakan program Kristalografi GSAS. Analisis struktur memperlihatkan bahwa bahan terdiri dari 5 (lima) fasa, struktur kristal fasa utamanya adalah BaTi0.5Mno.5O3 dengan tipe struktur perovskite BaTiO3, grup ruang tetragonal P4mm, parameter kisi masing-masing, a = 3,998 A, c = 4,022 A, reduced x2 = 1,706 , I tp = '0,176, wRp = 0,230, dengan jumlah variabel 58 . Keempat fasa pengotor tersebut adalah BaCO3, MnO2, TiO2 dan Mn3Ti2 yang masing-masing mempunyai grup ruang Pnma, P42lmnm, 1411amd dan P 631mmc. Bahan uji mempunyai nilai konstanta dielektrik minimum adalah 265,23 pada temperatur ruang dan nilai konstanta dielektrik maksimum dicapai pada temperatur 110 °C.
The effect of 0.5 weight mole Mn on crystal structure and dielectric constant of barium titanate has been analyzed. The best sample in this study were synthesized using powder metallurgy with maximum sintering temperature at 950 °C and stoichiometric amounts of BaCO3, MnO2 and TiO2 that were reagents from E-Merck. The X-ray difractograms wich were obtained with continuous counts and X (Co Ka) = 1.7889 A at room temperature, were refined using the GSAS crystallographic soft ware package. Structural analysis shows that sample consist of 5 (five) phases where the parent phase is BaTio.5Mno.5G3 with the perovskite-type BaTiO3 structure, the space group is tetragonal P4mm, a = 3.999 A, c = 4.028 A, the goodness of fit x2 is of 1.864 with 56 refined variables and the residual parameters .Rp and wRp are of 18.8% and 24.2% respectively. The impurities phase are BaCO3, MnO2, TiO2 and Mn3Ti2 with the space group each are Prima, P 42lmnm, l 41/amd and P 63/mmc respectively. The sample has a minimum dielectric constant value is 265.23 at room temperature and maximum dielectric constant value is 519.32 at 110 °C temperature reached. |
T5187-Zulkarnain Nasution.pdf :: Unduh