Pengembangan Veneer dan Selulosa Bakteri Sebagai Material Komposit Penyerap Energi Balistik = Development of Veneer and Bacterial Cellulose as Ballistic Energy-absorbing Composite Materials
Ananto Nugroho;
Anne Zulfia Syahrial, promotor; Sandi Sufiandi, co-promotor; Mochammad Chalid, examiner; Asep Handaya Saputra, examiner; Nofrijon Sofyan, examiner; Donanta Dhaneswara, examiner; Wahyu Dwianto, examiner
(Fakultas Teknik Universitas Indonesia, 2022)
|
|
Komposit polimer berbasis lignoselulosa memiliki potensi untuk dikembangkansebagai lapis penyerap energi balistik di dalam sistem pelindung berlapis. Dalampenelitian ini, panel hibrid penyerap energi balistik dikembangkan dari bahan kayu veneeryang di modifikasi dengan selulosa bakteri (BC) dan proses pemadatan panas. Hasilpenelitian menunjukkan bahwa veneer-BC padatan dapat digunakan sebagai panelkomposit hibrid bersama serat aramid sebagai lapis tengah di dalam sistem pelindungberlapis. Pengujian balistik terhadap panel komposit hibrid sebagai lapis tengah di dalamsistem pelindung berlapis tidak dapat tertembus peluru kaliber 7,62 mm NATO. Dengannilai BFS 24,62 ± 5,78 mm lebih kecil dari 44 mm menjadikan struktur pelindung inimemenuhi kriteria pengujian level III menurut standar NIJ 0101.06. Laminasi kompositkayu veneer-BC padatan memiliki keunggulan dalam menghilangkan energi denganmenangkap fragmen pecahan keramik dan proyektil sehingga menghasilkan transferenergi trauma yang kecil. Polymer composites based on lignocellulosic materials have the potential to bedeveloped as a ballistic energy-absorbing layer in a multilayered armor system (MAS).In this research, a ballistic energy-absorbing hybrid panel was developed using a woodveneer modified with bacteria cellulose (BC) and a heat compression process. Theresearch found that densified veneer-BC could be applied as a hybrid composite panelwith aramid fiber in a MAS as the middle layer. Ballistic testing of hybrid compositepanels as the middle layer of a MAS impervious to 7,62 mm NATO bullets. This armordesign fulfills the requirements for level III testing according to NIJ 0101.06 based on thevalue BFS 24,62 ± 5,78 mm, which is less than 44 mm. The laminated compositedensified veneer-BC has a great capacity to disperse energy by capturing the ceramicfragment and the projectile, then transferring the small trauma energy. |
 D-Ananto Nugroho.pdf :: Unduh
|
| No. Panggil : | D-pdf |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Teknik Universitas Indonesia, 2022 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | computer |
| Tipe Carrier : | online resource |
| Deskripsi Fisik : | xviii, 152 pages : illustration ; appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| D-pdf | 07-23-86704186 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 9999920516527 |