Effects of water quenching before hydrogenation, disproportionation, desorption, and recombination process on the magnetic properties of nd-fe-b powder
Yongjin Kim, Djoko Hadi Prajitno (Faculty of Engineering, Universitas Indonesia, 2016)
|
| In general, the Nd-Fe-B as-cast ingot is homogenized for a long time before the hydrogenation, disproportionation, desorption and recombination (HDDR) process, to produce good magnetic properties. Since the homogenizing process is expensive, this work examined the possibility of replacing it with a water quenching process for Nd-Fe-B magnetic powder. The magnetic powders were soaked at 1100oC for 4 hours, followed by water quenching prior to HDDR. The resulting powder had magnetic properties that were almost similar to magnetic powder that was homogenized prior to HDDR. The remanence values of the water-quenched alloy and the homogenized alloy were 7.8 KG and 8.9 KG, respectively, while the coercivity values were 12.6 KOe and 10.3 KOe, respectively. In general, the magnetic properties of both samples were not much different. The microstructure of Nd2Fe14B phase combined with a very slight Nd rich phase in micro grain boundary likely caused the coercivity enhancement. |
| No. Panggil : | UI-IJTECH 7:3 (2016) |
| Entri utama-Nama orang : | |
| Subjek : | |
| Penerbitan : | Depok: Faculty of Engineering, Universitas Indonesia, 2016 |
| Sumber Pengatalogan : | LibUI eng rda |
| ISSN : | 20869614 |
| Majalah/Jurnal : | International Journal of Technology |
| Volume : | Vol. 7, No. 3, April 2016: Hal. 471-478 |
| Tipe Konten : | text |
| Tipe Media : | unmediated |
| Tipe Carrier : | volume |
| Akses Elektronik : | https://doi.org/10.14716/ijtech.v7i3.2785 |
| Institusi Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 4 R. Koleksi Jurnal |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| UI-IJTECH 7:3 (2016) | 08-23-60550227 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 9999920521690 |