Sintesis dan Karakterisasi Nanokomposit Pd/CuBi2O4 sebagai Fotokatalis pada Degradasi Zat Warna Metilen Biru di Bawah Iluminasi Cahaya Tampak = Synthesis and Characterization of Pd/CuBi2O4 Nanocomposite as a Photocatalyst for the Degradation Methylene Blue under Visible Light Illumination

Febby Widyasari; Aminah, supervisor; Ridla Bakri, supervisor; Yuni Krisyuningsih Krisnandi, examiner; Rahmat Wibowo, examiner (Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2023)

 Abstrak

Industri tekstil merupakan penyumbang terbesar limbah zat warna ke dalam air, contohnya zat warna metilen biru yang bersifat racun, karsinogenik, dan tidak dapat terurai secara alami. Salah satu teknik mengurangi kadar metilen biru adalah melalui degradasi secara fotokatalitik dengan menggunakan semikonduktor. CuBi2O4 merupakan semikonduktor tipe-p dengan celah pita yang sempit (1,5 – 1,8 eV) dapat digunakan sebagai fotokatalis untuk degradasi metilen biru karena memiliki respon cahaya tampak. Penambahan logam mulia Paladium (Pd) dapat meningkatkan kinerja aktivitas fotokatalitik CuBi2O4 karena dapat menekan rekombinasi pasangan e− dan h+. Penelitian ini, telah berhasil mensintesis CuBi2O4 melalui metode solvotermal, dan mensintesis nanokomposit Pd/CuBi2O4 dengan variasi perbandingan rasio mol Pd:CuBi2O4 (1:1, 1:2, dan 2:1) melalui metode presipitasi dan reduksi. CuBi2O4 dan Pd/CuBi2O4 hasil sintesis telah dibuktikan melalui karakterisasi dengan XRD, TEM, FTIR, dan UV-Vis DRS. Uji sifat katalis dilakukan pada larutan Metilen Biru dengan variasi penambahan massa katalis sebesar 5 mg, 10 mg, dan 15 mg, serta variasi kondisi (fotolisis dan adsorpsi). Persentase degradasi metilen biru paling optimum adalah pada katalis Pd/CuBi2O4 (2:1) 10 mg, yaitu sebesar 82,63% dengan laju degradasi 8,9 × 10-3 min-1.

Textile industry is the largest contributor of colorant waste into water, for instance, the toxic, carcinogenic, and non-biodegradable dye methylene blue. One of the techniques to reduce the concentration of methylene blue is through photocatalytic degradation using a semiconductor. CuBi2O4 is a p-type semiconductor with a narrow bandgap (1.5 - 1.8 eV) that can be utilized as a photocatalyst for methylene blue degradation due to its visible light response. The addition of the noble metal Palladium (Pd) can enhance the photocatalytic activity of CuBi2O4 by suppressing the recombination of electron-hole pairs (e− dan h+). In this research, CuBi2O4 has been successfully synthesized through the solvothermal method, and Pd/CuBi2O4 nanocomposites have been synthesized with various ratios of Pd:CuBi2O4 (1:1, 1:2, and 2:1) using the precipitation and reduction method. CuBi2O4 and Pd/CuBi2O4 synthesized products have been characterized using XRD, TEM, FTIR, and UV-Vis DRS. The catalytic properties test was performed on Methylene Blue solutions with varying catalyst masses of 5 mg, 10 mg, and 15 mg, as well as different conditions (photolysis and adsorption). The optimum percentage of methylene blue degradation was observed with the catalyst Pd/CuBi2O4 (2:1) 10 mg, which was 82.63%, with a degradation rate of 8,9 × 10-3 min-1.

 File Digital: 1

Shelf
 S-Febby Widyasari.pdf :: Unduh

LOGIN required

 Metadata

No. Panggil : S-pdf
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Subjek :
Penerbitan : Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2023
Program Studi :
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : computer
Tipe Carrier : online resource
Deskripsi Fisik : xvi, 64 pages : illustration + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI
  • Ketersediaan
  • Ulasan
No. Panggil No. Barkod Ketersediaan
S-pdf 14-24-50728031 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 9999920522482