Synthesis and magnetic characterization of mn-ti substituted sro.6fe2-xmnx/2tix/2o3 (x = 0.0–1.0) nanoparticles by combined destruction process

Mas Ayu Elita Hafizah, Azwar Manaf (Faculty of Engineering, Universitas Indonesia, 2017)

 Abstrak

Single phased SrO.6Fe2-xMnx/2Tix/2O3 (x = 0.0; 0.5; and 1.0) nanoparticles, whose mean size was comparable with the crystallite size, were successfully fabricated through mechanical alloying and a subsequent ultrasonic destruction processes. The ultrasonic destruction process employed a transducer operated under amplitudes of 35, 45, and 55 ?m. Results indicated that the mean particle size was not determined by the transducer amplitude, but the mechanical properties of the materials, as well as the initial size of the particles. After ultrasonic destruction, the mean sizes of the particles decreased to the range of 87–194 nm with a narrow distribution width. The mean particle sizes were about 1 to 3 times larger than the respective crystallite sizes. Such fine particles were aimed to decrease the coercivity, as was seen in the sample with x = 0, which showed a decrease in coercivity from 474 kA.m-1 to 24 kA.m-1 and 15 kA.m-1. A further reduction in the coercivity was observed in Mn-Ti substituted strontium hexaferrite.

 Metadata

No. Panggil : UI-IJTECH 8:4 (2017)
Entri utama-Nama orang :
Subjek :
Penerbitan : Depok: Faculty of Engineering, Universitas Indonesia, 2017
Sumber Pengatalogan : LibUI eng rda
ISSN : 20869614
Majalah/Jurnal : International Journal of Technology
Volume : Vol. 8, No. 4, July 2017: Hal. 644-650
Tipe Konten : text
Tipe Media : unmediated
Tipe Carrier : volume
Akses Elektronik : https://doi.org/10.14716/ijtech.v8i4.9484
Institusi Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 4 R. Koleksi Jurnal
  • Ketersediaan
  • Ulasan
No. Panggil No. Barkod Ketersediaan
UI-IJTECH 8:4 (2017) 08-23-33911704 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 9999920532881