Synthesis of tio2 nanotube in ti-10ta-10nb thin film by anodization
Deni Ferdian, Yudha Pratesa (Faculty of Engineering, Universitas Indonesia, 2012)
|
| The purpose of this research was to study the synthesis of TiO2 nanotubes on Ti-10Ta-10Nb thin film and the effect of applied potential on the tube size, length and morphology. The Ti-10Ta-10Nb thin film was deposited by dc magnetron sputtering on the CP Ti substrate. The anodization of this Ti-10Ta-10Nb thin film was performed in the solution containing 1M H3PO4 + 1.5wt.% HF at the potential readings of 4, 6, 8 and 10 V for 10 minutes. The results showed that there was a slight increase in the tube diameter from approximately 25 nm at 4 V to 50 nm at 8 V. The length of nanotube varied from 700-900 nm. Interestingly, at the potential of 10 V, the nanotube diameters were damaged with slight decreases in nanotube lengths (500 nm). |
| No. Panggil : | UI-IJTECH 3:2 (2012) |
| Entri utama-Nama orang : | |
| Subjek : | |
| Penerbitan : | Depok: Faculty of Engineering, Universitas Indonesia, 2012 |
| Sumber Pengatalogan : | LibUI eng rda |
| ISSN : | 20869614 |
| Majalah/Jurnal : | International Journal of Technology |
| Volume : | Vol. 3, No. 2, July 2012: Hal. 140-144 |
| Tipe Konten : | text |
| Tipe Media : | unmediated |
| Tipe Carrier : | volume |
| Akses Elektronik : | https://doi.org/10.14716/ijtech.v3i2.96 |
| Institusi Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 4 R. Koleksi Jurnal |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| UI-IJTECH 3:2 (2012) | 08-23-59121857 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 9999920535802 |