Karakterisasi Komposit Hidroksiapatit-Silk Fibroin-Gelatin dengan Metode Ex-Situ = Characterization of Hydroxyapatite-Silk Fibroin-Gelatin Composite by Ex-Situ Method
Diah Ayu Susilowati;
Djati Handoko, supervisor; Siti Julia, supervisor; Anawati, examiner; Ariadne Lakshmidevi Juwono, examiner
(Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2023)
|
|
Biomaterial pada rekayasa jaringan tulang harus memenuhi karakteristik yaitu biokompatibilitas, efektivitas, dan non-toksisitas. Penelitian ini bertujuan untuk mempelajari karakteristik komposit hidroksiapatit dan fibroin sutra dengan dan tanpa gelatin yang disiapkan dengan ex-situ berbantukan iradiasi gelombang mikro. Pengujian karakterisasi yang dilakukan pada penelitian ini adalah X-Ray Diffraction, Fourier Transform Infared, dan Scanning Electron Microscopy. Pengujian mekanik yang dilakukan pada penelitian ini adalah micro-Vickers. Hasil XRD menyatakan ukuran kristalin pada sampel HA80/SF20/Gel5% bernilai 166 Ã
sedangkan pada sampel HA70/SF30/Gel5% bernilai 134 Ã
. Hal ini menunjukkan bahwa pelebaran puncak dipengaruhi oleh ukuran kristalin. Karakteristik FTIR untuk gugus fungsi pada sampel HA70/SF30/Gel5% lebih lemah dibandingkan dengan HA70/SF30, artinya kandungan H2O HA70/SF30/Gel5% lebih rendah daripada HA70/SF30. Selanjutnya hasil analisis morfologi permukaan didapatkan partikel aglomerat dengan pori-pori yang saling berhubungan serta penambahan gelatin dapat menyebabkan aglomerasi partikel berbentuk serpihan. Pada hasil uji micro-Vickers menunjukkan dugaan sementara bahwa gelatin dalam komposit HA/SF/Gel mengakibatkan nilai kekerasan semakin tinggi, yaitu pada HA70/SF30/Gel5% dengan nilai 0,049 Hv. Biomaterials in bone tissue engineering must meet the characteristics, namely biocompatibility, effectiveness, and non-toxicity. This research aims to study the characteristics of hydroxyapatite and silk fibroin composites with and without gelatin prepared by ex-situ assisted by microwave irradiation. The characterization tests carried out in this research were X-Ray Diffraction, Fourier Transform Infrared, dan Scanning Electron Microscopy. The mechanical tests carried out in this research were micro-Vickers. The XRD results show that the crystalline size in the HA80/SF20/Gel5% sample is 166 Ã , while in the HA70/SF30/Gel5% sample it is 134 Ã . This shows that peak broadening is influenced by crystalline size. The FTIR characteristics for functional groups in the HA70/SF30/Gel5% sample are weaker than those of HA70/SF30, meaning that the H2O HA70/SF30/Gel5% lower than HA70/SF30. Furthermore, the results of surface morphology analysis showed agglomerate particles with interconnected pores and the addition of gelatin could cause agglomeration of flake-shaped particles. On test results micro-Vickers shows a temporary assumption that gelatin in the HA/SF/Gel composite results in a higher hardness value, namely at HA70/SF30/Gel5% with a value of 0,049 Hv. |
 S-Diah Ayu Susilowati.pdf :: Unduh
|
| No. Panggil : | S-pdf |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2023 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LIbUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | computer |
| Tipe Carrier : | online resource |
| Deskripsi Fisik : | xi, 66 pages : illustration + appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI;Perpustakaan UI;Perpustakaan UI |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S-pdf | 14-24-83899117 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 9999920540840 |