Uji Kinerja Membran CA-PEG 200 dengan Pencangkokan PEGMEA untuk Pemisahan Gas Campuran Biner CO2 dan CH4 = Performance Test of CA-PEG 200 Membrane with PEGMEA Grafting for CO2 and CH4 Binary Gas Mixture Separation
Muthia Rizki Hidayati;
Sutrasno Kartohardjono, supervisor; Intan Clarissa Sophiana, examiner; Eva Fathul Karamah, examiner
(Fakultas Teknik Universitas Indonesia, 2024)
|
|
Kandungan CO2 yang tinggi di dalam gas alam harus dihilangkan karena bersifat korosif dan menurunkan efisiensi gas termal pada industri gas bumi. Teknologi pemisahan CO2 dari gas alam berupa teknologi membran mulai banyak dikembangkan karena energi yang diperlukan untuk pemisahan tergolong rendah dan ramah lingkungan. Selulosa asetat (CA) merupakan polimer bahan organik dengan harga yang relatif murah dan efektif untuk pemisahan CO2 dari gas alam. Akan tetapi, permeabilitas CA terhadap CO2 masih tergolong rendah sehingga perlu modifikasi lebih lanjut untuk mencapai kinerja pemisahan yang tinggi. Fokus penelitian ini adalah pengujian kinerja membran yang telah dimodifikasi menjadi fixed carrier membrane (FCM) melalui penambahan polietilen glikol (PEG) dan polietilen glikol metil eter akrilat (PEGMEA) sebagai zat aktif membran untuk meningkatkan permeabilitas gas CO2 dan selektivitas pada membran. Pengujian kinerja membran dilakukan menggunakan gas murni CO2 dan CH4 serta gas campuran biner CO2/CH4 dengan memvariasikan tekanan gas umpan. Hasil penelitian menunjukkan bahwa pengujian menggunakan membran CA murni menunjukkan nilai permeabilitas CO2 sebesar 327 barrer dan selektivitas CO2/CH4 terbaik sebesar 3,94 pada tekanan 30 psi. Di sisi lain, pengujian dengan membran CA yang sudah dimodifikasi dengan PEG dan PEGMEA menghasilkan nilai permeabilitas dan selektivitas yang lebih baik dibandingkan membran selulosa asetat murni. Membran dengan PEG dan PEGMEA 3% memberikan permeabilitas CO2 sebesar 373 barrer dan selektivitas CO2/CH4 terbaik sebesar 12,8 pada tekanan 30 psi. The high CO2 content in natural gas must be removed because it is corrosive and reduces the efficiency of thermal gas in the natural gas industry. The technology for separating CO2 from natural gas in the form of membrane technology is starting to be widely developed because the energy required for separation is low and environmentally friendly. Cellulose acetate (CA) is an organic polymer material that is relatively cheap and effective for separating CO2 from natural gas. However, CA's permeability to CO2 is still relatively low so further modification is needed to achieve high separation performance. The focus of this research is testing the performance of a membrane that has been modified to become a fixed carrier membrane (FCM) through the addition of polyethylene glycol (PEG) and polyethylene glycol methyl ether acrylate (PEGMEA) as membrane active substances to increase CO2 gas permeability and membrane selectivity. Membrane performance testing was carried out using pure CO2 and CH4 gas and CO2/CH4 binary mixture gas by varying the feed gas pressure. The research results showed that tests using a pure CA membrane showed a CO2 permeability value of 327 barriers and the best CO2/CH4 selectivity of 3.94 at a pressure of 30 psi. On the other hand, tests with CA membranes that had been modified with PEG and PEGMEA produced better permeability and selectivity values ââthan pure cellulose acetate membranes. Membranes with 3% PEG and PEGMEA provide CO2 permeability of 373 barriers and the best CO2/CH4 selectivity of 12.8 at a pressure of 30 psi. |
 S-Muthia Rizki Hidayati.pdf :: Unduh
|
| No. Panggil : | S-pdf |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Teknik Universitas Indonesia, 2024 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | computer |
| Tipe Carrier : | online resource |
| Deskripsi Fisik : | xiv, 58 pages ; illustration ; 28 cm + appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S-pdf | 14-24-39958666 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 9999920544179 |