Studi pengaruh penambahan Cu terhadap karakteristik struktur, sifat termal dan sifat kekerasan dari paduan Sn-Cu = Study of Cu addition effect to structures, thermal and hardness characteristics of Sn-Cu alloys

Muhammad Hafiz Sjafril; Budhy Kurniawan, supervisor (Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2010)

 Abstrak

Masalah kontaminasi lingkungan yang diakibatkan oleh penggunaan timbal menjadi perhatian yang serius beberapa tahun belakangan ini. Persoalan ini kemudian menggerakkan para pelaku industri untuk perlahan-lahan meninggalkan material solder yang mengandung timbal dan mengembangkan alternatif material solder yang bebas timbal, diantaranya paduan Sn-Cu. Dalam penelitian tugas akhir ini, paduan Sn-Cu dibuat dengan menggunakan lnetode peleburan yang dilakukan pada atmosfer nitrogen. Variasi sampel paduan yang dibuat adalah paduan hypoeutektik, eutektik dan hypereutektik Sn-Cu.
Dari hasil karakterisasi XRD memperlihatkan bahwa puncak-puncak utama yg teridentifikasi merupakan milik β-Sn dengan struktur Kristal tetragonal dengan disertai pertumbuhan puncak yang dimiliki senyawa intennetalik Cu6Sn5. Karakterisasi termal dari semua paduan yang didapatkan rnenggunakan DSC menunjukkan penurunan titik lebur paduan Sn-Cu keseluruhan akibat penambahan Cu. Ini terlihat dari besarnya titik lebur paduan Sn99.8%-Cu0.2% yaitu 224.5°C kemudian menurun menjadi 220.1°C pada paduan Sn98.1%-Cu1.9%. Pengaruh penambahan Cu juga terlihat pada sifat kekerasan dari semua variasi paduan Sn-Cu yaitu kekerasan paduan meningkat seiring Cu yang bertambah pada paduan. Hal ini dikonfirmasi dari hasil test menggunakan vicker hardness fest. Peningkatan ini cukup signifikan yaitu dari 0.56 kgf/mm2 pada paduan Sn99.8%-Cu0.2% menjadi 41.2 kgf/mm2 pada paduan Sn98.1%-Cu1.9%. Kenaikan nilai kekerasan ini diakibatkan oleh pembentukan senyawa intermetalik Cu6Sn5 sebagaimana dibuktikan dari hasil XRD.

Environment contamination issue caused by lead utilization had become a serious interest for years back then. This issue afterwards, force industrial performer to slowly leaves solder material based on lead and developed lead-free solder materials. Sn-Cu alloys on this thesis paper have been done using fusion method within nitrogen atmosfer. All variation made consist of hypoeutectic, eutectic and hypereutectic Sn-Cu alloy.
Structural characterization for all variation shows that primary peaks that observed have been identiyied as ,β-Sn peak with growth of intermetallic compound Cu6Sn5 peak. Thermal studies using DSC revealed that addition of Cu could lowering melting point ofSn-Cu totally. Lowering of melting point can be seen from Sn99.8%-Cu0.2% alloy which have 224.5°C decrease to 220.1°C for Sn98.1%-Cu1.9% alloy. Cu addition also have impact to raise hardness value of Sn-Cu alloy obtain from Wckers Hardness test. Hardness value of Sn99.8%-Cu0.2% alloy raise significantly from 0.56 kgf/mm2 to 41.2 kgf/mm2 for Sn98.1%-Cu1.9%. Increase on this hardness value caused by growth of intermetallic compound Cu6Sn5 when increasing Cu, which this result correspond with XRD result.

 File Digital: 1

 Metadata

Jenis Koleksi : UI - Skripsi Open
No. Panggil : S29361
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Program Studi :
Subjek :
Penerbitan : Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2010
Bahasa : ind
Sumber Pengatalogan :
Tipe Konten :
Tipe Media :
Tipe Carrier :
Deskripsi Fisik : xv, 44 hlm. : ill. ; 28 cm.
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S29361 14-22-90506680 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20327994
Cover