"The most pavement type in Indonesia is flexible pavement, of which rutting as one of the pavement defect is caused by heavy load and high temperature . Rutting can cause the decrease of road service and followed by crack which leading to worse damage of pavement. The purpose of the study is to find out the performance of Stone Mastic Asphalt using asphalt cement pen 60 mixed with semi extraction of asbuton and the method of the research is laboratory experiments. The results showed that the addition of semi extraction asbuton significantly increases the resistance of the SMA mixtures to rutting, increasing modulus of asphalt mixtures and improve drain down and flushing. However the the resistance of mixture to particle loose decreases even though it is still in the limit requirement and it tends to become less brittle. As the addition of semi extraction asbuton increases some Stone Mastic Asphalt performance, and decreases the others, so that the determination of semi extraction asbuton proportion has to be minimum but still meet the requirement os asphalt mixture, by carrying further research about fatigue resistance of Stone Mastic Asphalt."

"ABSTRAKPerkerasan jalan raya dirancang dengan ketentuan mampu memenuhi faktor ketahanan terhadap deformasi akibat pengulangan beban roda. Deformasi alur terjadi ketika terjadi peningkatan tegangan tarik pada suhu tinggi akibat beban roda. Hubungan antara jumlah lintasan roda dengan tegangan permanen dapat diketahui melalui uji alur roda. Penelitian ini untuk mengetahui pengaruh nano crumb rubber dalam upaya peningkatan ketahanan aspal campuran panas terhadap pengaruh suhu akibat beban roda kendaraan khususnya pada jalan lalu lintas berat. Limbah ban bekas yang telah dihaluskan sampai butiran ukuran nano yang disebut dengan nano crumb rubber (NCR). Material ini ditambahkan pada agregat halus, pada umumnya disebut dengan pencampuran kering. Penambahan NCR sebesar 0%, 25%, 50%, 75%, dan 100% terhadap kandungan filler pada campuran aspal panas (ACWC). Dengan metode ini didapatkan bahwa terjadi penurunan dari segi kualitas, dilihat dari hasil stabilitas yang menurun cukup jauh. Penelitian dilanjutkan dengan melakukan penambahan NCR sebanyak 2,5% dan 5% dari berat aspal. Sehingga dapat diketahui pengaruh penambahan Nano Crumb Rubber yang didapat melalui uji Wheel Tracking Machine. Dari pengujian WTM didapatkan bahwa penambahan NCR dalam campuran beraspal akan meningkatkan kualitas dari campuran tersebut, pada suhu rendah peningkatan kualitas 2,5% NCR tidak setinggi penambahan 5% NCR, akan tetapi penambahan 5% NCR lemah terhadap suhu yang tinggi. Pada suhu pengujian 60°C 2,5% merupakan yang terbaik.

---

ABSTRACT

Highway Pavement is designed with the provision of being able to meet the resistance factor to deformation due to repetition of wheel load. Rutting occurs when there is an increase in tensile stress at high temperatures due to wheel load. The relationship between the number of trajectories of wheels with permanent stress can be known through the wheel tracking test. This study was to determine the effect of nano crumb rubber in an effort to increase the resistance of hot mix asphalt to the influence of temperature due to vehicle wheel loads, especially on heavy traffic roads. Waste from used tires to nano-size granules called nano crumb rubber (NCR). This material is subtitute to fine aggregates, generally called dry mixing. The addition of NCR is 0%, 25%, 50%, 75%, and 100% of the filler content in hot asphalt mixtures (ACWC). With this method, it was found that there was a decrease in quality, from the results of the stability which decreased quite far. The research was continued by adding NCR as much as 2.5% and 5% of the asphalt weight. So that it can be seen the effect of adding Nano Crumb Rubber obtained through the Wheel Tracking Machine test. From the WTM test it was found that the addition of NCR in the asphalt mixture would improve the quality of the mixture, at low temperatures the increase in the quality of 2.5% NCR was not as high as the addition of 5% NCR, but the addition of 5% NCR was weak to high temperatures. At the test temperature 60 ° C 2.5% is the best."

"Proses perencanaan campuran aspal sangat bergantung pada proporsi material yang ditentuan oleh jenis gradasi agregat serta jenis dan kadar aspal yang digunakan. Dalam penelitian ini digunakan 2 sampel gradasi sebagai pembanding yaitu gradasi menerus (Spek IV laston Binamarga) dan gradasi senjang (Spek Lataston HRS-WC). Sampel diuji pada suhu 90 dengan 50 tumbukan, 110 dengan 2x50 tumbukan, serta 90 dengan 2x120 tumbukan. Hasil penelitian menunjukkan untuk nilai deformasi dan kecepatan deformasi pada sampel dengan gradasi menerus nilainya lebih besar daripada sampel dengan gradasi senjang hampir di semua variasi. Nilai VIM dan VMA pada gradasi senjang Lebih besar daripada gradasi menerus, sedangkan untuk nilai stabilitas sampel dengan gradasi senjang memiliki nilai yang lebih besar daripada sampel dengan gradasi menerus.

---

Asphalt mix design process is dependent on the proportion of material that is determined by the type of aggregate gradation and the type and asphalt content used. In this research 2 samples used for comparison of gradation. gradation Continuous( Spek IV Laston Binamarda) and gap graded (Spek Lataston HRSWC). Samples were tested at 900C 2x50 blows, 1100C with 2x75 blows, and 900C with 2x120 blows. The results showed for the deformation and deformation rate on the sample with continuous gradation have greater value than sample with a graded gap in almost every variation. VIM and VMA values in graded gap Bigger than continuous gradation, whereas for the stability of the sample with a graded gap has a greater value than the sample with continuous gradation."

"Lawele Granular Asphalt (LGA) merupakan aspal alam, yaitu aspal buton yang berada di Pulau Buton, Indonesia. Namun, penggunaan LGA dinilai belum maksimal, sehingga teknologi dalam pemanfaatan LGA masih terus dikembangkan. Penelitian ini dilakukan untuk mengoptimalkan penggunaan LGA dengan memaksimalkan proses ekstraksi LGA dalam campuran menggunakan oli bekas dan meningkatkan ketahanan campuran terhadap perubahan suhu dengan menggunakan Nano Crumb Rubber (NCR). Penambahan aditif ONCR dilakukan dengan nilai 5%, 10%, 15%, dan 20% terhadap kandungan aspal minyak serta 0% sebagai campuran pembanding. Stabilitas pada pengujian marshall menunjukan penurunan seiring dengan bertambahnya kadar ONCR. Berdasarkan spesifikasi pembanding, spesifikasi CPHMA, didapatkan KAO sebesar 8,55% pada penambahan ONCR 10% dan 8,92% pada penambahan ONCR 0%. Pengujian lebih lanjut dilakukan untuk mengetahui stabilitas dinamis campuran menggunakan Wheel Tracking Machine (WTM) pada suhu pengujian 26 °C, 35 °C, 45 °C, dan 60 °C. Campuran dengan penambahan aditif ONCR 0% menunjukan kinerja yang lebih baik dibandingkan campuran dengan penambahan ONCR 10%. Selain itu, performa ketahanan terhadap suhu ONCR 0% memiliki hasil yang lebih baik dibandingkan dengan ONCR 10%, yang ditandai dengan nilai deformasi alur yang lebih kecil pada setiap seuhu pengujiannya. Penambahan aditif ONCR dengan komposisi 85% oli bekas dan 15 % NCR tidak bisa meningkatkan kualitas campuran aspal. Penggunaan oli bekas pada campuran berperan signifikan dalam meningkatkan fleksibilitas aspal, yang ditandai dengan penurunan titik lembek campuran.

---

Lawele Granular Asphalt (LGA) is natural asphalt, namely with buton asphalt that stored in Buton Island, Indonesia. However, the use of LGA is considered not optimal, so that, the technology to optimize the use of LGA still being developed. This research was conducted to optimize the use of LGA by maximalizing the LGA extraction process using used oil and increasing the mixture resistance to temperature change by using Nano Crumb Rubber (NCR). The addition of ONCR additive was carried out with value of 5%, 10%, 15%, and 20% to the content of oil asphalt also 0% for the comparison mixture. Stability in marshall testing showed a decrease with the increasing content of ONCR. Based on the comparison specifications, CPHMA specification, the value of optimum asphalt content obtained on the amount of 8,55% for the addition of 10% ONCR and 8,92% for the addition of 0% ONCR. Further test was carried out to determine the dynamic stability of the mixture by using the wheel tracking machine (WTM) at 26 °C, 35 °C, 45 °C, and 60 °C test temperatures. Mixture with the addition of 0% ONCR showed better performance than the 10% ONCR mixture. In addition, the 0% ONCR mixture temperature resistance performance showed better result compared to the 10% ONCR mixture, which is characterized by smaller rutting deformation values at each test temperature. The addition of ONCR additives with a composition of 85% of used oil and 15% of NCR could not improve the quality of the asphalt mixture. The use of used oil in the mixture has a significant role in increasing the flexibility of the asphalt mixture, which is characterized by a decrease in the softening point of the mixture."

"Aspal alam dari Pulau Buton (asbuton) belum dimanfaatkan secara maksimal hingga saat ini. Salah satu cara pemanfaatannya adalah proses ekstraksi untuk melarutkan padatan karbonat dari asbuton menggunakan larutan asam lemah. Larutan yang digunakan adalah larutan acidic brine water yang dibuat dengan injeksi gas CO2 dalam larutan NaCl. Ekstraksi tersonikasi dilakukan pada berbagai kondisi operasi, yaitu suhu (25 hingga 110oC), tekanan (atmosfer hingga 3 bar), konsentrasi NaCl (0,1 hingga 2 M), laju alir gas CO2 (0,2 hingga 1 liter/menit), dan rasio asbuton-pelarut (0,02 hingga 0,1 g/ml). Seluruh variabel tersebut mempengaruhi jumlah padatan karbonat yang terlarut. Jumlah padatan terlarut yang maksimal diperoleh pada kondisi 90oC, 3 bar, larutan 0,5 M NaCl, laju alir CO2 0,6 l/menit, dan rasio 0,02 g/ml. Produk aspal yang dihasilkan mengandung 50,47% aspal, 24,47% padatan karbonat, dan 25,06% mineral lainnya.

---

Natural asphalt from Buton Island (asbuton) has not been fully utilized up to now. One way of its utilization was extraction process to dissolve carbonate solids in asbuton using weak acid solution. The solution was acidic brine water solution that made by CO2 injection in NaCl solution. Sonicated extraction was performed at various operating conditions, namely temperature (25 to 110oC), pressure (1 to 3 bar), NaCl concentration (0.1 to 2 M), flow rate of CO2 (0.2 to 1 liter/minute), and asbuton-solvent ratio (0.02 to 0.1 g/ml). All variables affect the amount of dissolved carbonate solids. Maximum of dissolved solids reached at temperature of 90oC, pressure of 3 bar, NaCl concentration of 0.5 M, CO2 flow rate of 0.6 liter/minute, and ratio of 0.02 g/ml. Asphalt product contained 50.47% asphalt, 24.47% carbonate solids, and 25.06% other minerals."

"Dengan ketersediaan aspal yang berasal dari pulau buton yakni Lawele Granular Asphalt sebagai bahan campuran aspal dapat dilakukan untuk meminimalisir pemakaian aspal minyak yang semakin menipis ketersediaannya. Serbuk karet ban berukuran nano (Nano crumb rubber) juga digunakan sebagai bahan tambah pada campuran aspal agregat karena ketersediaannya yang melimpah. Jenis aspal yang digunakan pada penelitian ini adalah aspal Lawele Granular Asphalt (LGA) dengan variasi kadar aspal 6,6%; 7,3%; 7,9%; 8,55% dan 9,21%. Campuran hangat aspal dan agregat ditambahkan dengan oli bekas dan serbuk karet ban bekas dengan variasi kadar 0% dan 1%. Campuran aspal didominasi oleh LGA dengan nilai yang mungkin untuk memenuhi standar Cold Paving Hot Mix Asbuton (CPHMA). Penambahan oli bekas dalam campuran berguna sebagai peremaja fisik untuk meningkatkan angka penetrasi aspal. Kinerja dari variasi campuran aspal ditentukan dengan uji Marshall test dan Marshall immersion test. Sedangkan nilai modulus resilient campuran panas aspal ditentukan dengan uji resilient modulus dengan alat UMATTA pada temperatur yang bervariasi untuk mengetahui perilaku benda uji terhadap beban kejut. Hasil akhir dari penelitian ini diharapkan dapat mengetahui pengaruh temperatur terhadap modulus resilient campuran hangat aspal, agregat dan LGA dengan campuran aspal murni, LGA dan additive berupa oli bekas dan Nano Crumb Rubber

---

The availability of asphalt from Buton Island in large quantities, an optimizing the utilization of asbuton from Lawele Bay, namely Lawele Granular Asphalt as an asphalt mixture, can minimize the use of asphalt which is gradually depleting its availability and reducing the cost of road construction and maintenance due to asphalt. material prices are quite high. Nano-sized rubber tire powder (Nano crumb rubber) is also used as an additive to asphalt and aggregate mixture because of its abundant availability. The type of asphalt used in this study was Lawele Granular Asphalt (LGA) asphalt with a variation of asphalt content of 6.6%; 7.3%; 7.9%; 8.55% and 9.21%. A warm mixture of asphalt and aggregate was added with waste-engine oil and tire rubber with various levels of 0% and 1%. The asphalt mixture is dominated by LGA with the value that conformthe specification of Cold Paving Hot Mix Asbuton (CPHMA) standard. The addition of waste-engine oil in the mixture is used as a physical rejuvenator to increase the value of asphalt penetration. The quality of the asphalt mixture variations was determined by the Marshall test and Marshall immersion test. While the resilient modulus asphalt mixture is determined by resilient modulus test with UMATTA with varying temperatures. The asphalt mixture test to this temperature change to determine the resilience of the aggregate asphalt mixture of Lawele Granular Asphalt product to the temperature change as it is on the road surface condition."

"Penelitian ini bertujuan untuk mendapatkan aspal dari Asbuton melalui ekstraksi CaCO3 menggunakan H2CO3 dalam brine water sebagai pelarut. Kadar CaCO3 yang tinggi pada Asbuton akan menurunkan kualitas Asbuton sebagai campuran aspal panas sehingga harus dikurangi. Gas CO2 dilarutkan dalam brine water membentuk H2CO3 dan menghasilkan kalsium bikarbonat (Ca(HCO3)2) pada proses ekstraksi. Gas CO2 diperoleh kembali dari pemanasan larutan (Ca(HCO3)2). Parameter keberhasilan ditinjau dari prosentase CaCO3 terlarut, make-up CO2, dan kebutuhan energi. Hasil optimum dan ekonomis diperoleh pada kondisi 2 bar, 85oC, rasio 0,02 g/mL, laju alir larutan 6 mL/menit, dan larutan NaCl 0,5 M selama 140 menit serta dapat melarutkan CaCO3 sebesar 34%. Produk aspal mengandung 57% aspal, 14% CaCO3, dan 29% mineral lainnya, membutuhkan make-up CO2 0,15 L/g Asbuton dan energi 0,28 kWh/g Asbuton. Aspal ini memenuhi spesifikasi untuk campuran aspal panas dengan jenis 5/55 dan dapat diterapkan pada untuk campuran aspal jenis AC Pen 60.

---

The purpose of this reasearch is to obtain asphalt from Asbuton rock through extraction CaCO3 using H2CO3 in brine water as solvent. The high content of CaCO3 in Asbuton will decrease the quality of Asbuton as the hot mix asphalt so it must be reduced. Gas CO2 is dissolved in brine water to produce H2CO3 and calcium bicarbonate (Ca(HCO3)2) is produced in extraction process. Gas CO2 be recovered by heating Ca(HCO3)2 solution. The success parameters is evaluated from percentage of CaCO3 that is dissolved, make-up of CO2, and energy needs.

The optimum and economical results obtained at conditions 2 bars, 85oC, ratio 0.02 g/mL, flow rate 6 mL/min, and concentration of NaCl solution 0.5 M up to 140 minutes and can dissolve CaCO3 34%. Asphalt product contained 57% asphalt, 14% CaCO3, and 29% other minerals, needs make-up CO2 0.15 L/g Asbuton and energy 0.28 kWh/g Asbuton. The Asphalt specification suitable for hot mix asphalt with type 5/55 and can be applied to the asphalt mixture type of AC Pen 60."

"ABSTRAKVolume pembangunan prasarana jalan di Indonesia, berupa jalan baru maupun perbaikan jalan lama, semakin meningkat. Di lain pihak, usia lapis perkerasan jalan tidak sesuai dengan umur rencana, sehingga terjadi kerusakan belum pada waktunya berupa gelombang, alur dan retak. Kerusakan ini disebabkan kendala antara lain : (i) Iklim tropis, (ii) beban kendaraan yang sukar dikendalikan, (iii) sebagian struktur jalan relatip kurang mantap. Untuk mengatasi masalah tersebut, baru-baru ini diperkenalkan rancangan campur aspal panas Split Mastik Aspal sebagai lapis penutup untuk penahan lentur. Split Mastik Aspal adalah campuran bergradasi terbuka dengan bahan pembentuk terdiri dari: agregat kasar, agregat halus, bahan pengisi dan aspal. Sedangkan Asbuton Mikro selain mengandung mineral berukuran debu sampai pasir, juga mengandung bahan bitumious yang akan dimanfaatkan sebagai bahan pengisi (filler). Dengan adanya bitumen pada Asbuton Mikro tersebut, diharapkan dapat memberikan ikatan yang kuat antara aspal dan agregat, dan dengan adanya mineral diharapkan dapat mengisi rongga antara butir ? butir agregat. Dalam penelitian ini, variasi bahan pengisi adalah 4.5%, 5.5%, 6.5% dengan kandungan aspal 5.5%, 6% 6.5%, 7% dan penambahan arbocel (bahan tambah) 0%, 0.1%, 0.2%. Dilakukan Test Marshall, sehingga hasil yang diperoleh dari penelitian ini diharapkan dapat mempelajari karakteristik campuran aspal dengan bahan pengisi, terhadap komposisi campuran pada lapisan perkerasan campuran Split Mastik Aspal. Dari hasil perhitungan Marshall, ternyata bahwa bahan pengisi Asbuton Mikro sangat mempengaruhi nilai stabilitas, nilai kelelehan dan nilai kekakuan. Hasil dari penelitian ini menunjukan bahwa Asbuton Mikro dapat digunakan sebagai bahan pengisi (filler) untuk pengganti abu batu atau semen pada lapisan perkerasan campuran Split Mastik Aspal."