Hasil Pencarian  ::  Simpan CSV :: Kembali

"Dalam tugas akhir ini akan dibahas tentang alat penyimpanan informasi pada mesin digital, yaitu Magnetic core memory, Flip-flop, Register yang merupakan rangkaian dari Flip-flop. Flip-flop dirangkaikan dengan gerbang-gerbang logika membentuk diagram logika. untuk penghematan tempat, diagram di minimisasi dengan metoda Peta Karnough dan metoda Quine McClunskey. Dalam minimisasi ini diagram logika diekspresikan sebagai fungsi Biner. "

"Register is one of the computer components that have a key role in computer organisation. Any kind of computer contains millions of registers that are manifested by flip-flop. This research focused on the investigation of the flip-flop performance based on its type (D, T, S-R, and J-K) and architecture (structural, behavioural, and hybrid). Those type of flip-flop on each architecture would be tested in different bit of shift register with parallel load applications. The experiment criteria that would be assessed are power consumption, resources required, memory required, latency, and efficiency. Based on the experiment, it could be shown that D flip-flop and hybrid architecture showed the best per-formance in memory required, latency, power consumption, and efficiency. Meanwhile, the greater the register number, the less efficient the system would be.

---

Memori adalah salah satu komponen utama penyusun segala komputer. Memori memiliki jutaan register yang dimanifestasikan oleh flip-flop. Peneitian ini focus pada investigasi ari kinerja flip-flop berdasarkan tipe (D, T, S-R, dan J-K) dan arsitekturnya (structural, behavioural, dan hibrid). Flip-flop dengan tipe-tipe berbeda pada arsitektur masing-masing akan di tes pada aplikasi shift register with parallel load dengan jumlah bit yang berbeda-beda. Kriteria yang akan diuji adalah konsumsi daya, sumber daya yang dibutuhkan, memori yang dibutuhkan, latensi, dan efisiensi. Berdasarkan eksperimen yang dilakukan, dapat disimpulkan bahwa kinerja paling baik ditunjukkan pada D flip-flop dan arsi-tektur hybrid pada parameter, memori, latensi, konsumsi daya, dan efisiensi. Sementara itu, semain besar register, semakin tidak efisien sistem."

"ABSTRAKTelah dilanjutkan suatu studi teoritik dan eksperimental tentang magnet permanen Nd-Fe-B. Studi teoritik melibatkan teori klasik Stoner-Wohlfarth (S-W) dengan mengikut sertakan efek interaksi antar partikel (yang absen pada asumsi S-W). Hasil komputasi menunjukkan bahwa efek interaksi menurunkan koersifitas intrinsik magnet Nd-Fe-B. Terdapat kesesuaian secara kualitatip antara nilai komputasi dan nilai eksperimental meskipun terdapat perbedaan yang sangat besar secara kuantitatip. Baik model komputasi yang dikembangkan maupun optimasi sifat dari pengukuran eksperimental masih harus sama-sama menjalani perbaikan.Studi eksperimental melibatkan dua proses berbeda untuk memproduksi magnet permanen Nd-Fe-B yaitu masing-masing proses konvensional sintering dan proses modern meltspinnig. Pada proses konvensional telah berhasil dipertahankan fasa utama Nd2Fe14B yang merupakan fasa magnetik magnet permanen setelah melalui tahapan sintering dan aniling meskipun masih teramati adanya fasa oksida yang seharusnya dihindarkan. Magnet permanen Nd-Fe-B untuk tiga komposisi berbeda (komposisi stoildometri; komposisi kaya Nd dan komposisi yang mengandungg Dy) telah dipelajari. Ketiga jenis magnet mencapai densitas medekati 100 % nilai teoritik dengan penggunaan tekanan sebesar 121 MPa untuk menghasilkan green compact dengan densitas 77 % dan densifikasi dicapai setelah proses anil pada temperatur -- 1100 °C selama 1 - 2 jam. Studi XRD menunjukkan bahwa magnet sinter komposisi stoildometri masih mengandung fasa kedua (a-Fe) yang diduga berasal dan sistem milling sedangkan magnet sinter Nd-Fe-B kaya Nd memiliki fasa kedua fasa kaya Nd. Magnet sinter yang dihasilkan menunjukkan koersivitas yang sangat tinggi demikian sehingga medan luar 1,5 T tidak cukup tinggi untuk menginduksi magnetisasi magnet. Ini memberikan loop histeresis yang tidak dapat dievaluasi.Penelitian terhadap pita alloy Nd-Fe,Co-B material magnetik dengan teknik meltspinning menunjukkan bahwa pita alloy membentuk struktur nanokomposit sistem Nd.(Fe-Co)14BIFe-Co . Struktur nanokomposit ini memberikan ratio antara remanen dan polarisasi total > 0,5 meskipun diturunkan dari loop minor. Pengukuran temperatur transisi menyimpulkan bahwa subsitusi Co terhadap Fe pada fasa Nd2Fe14B meningkatkan Tc secara progresif dari 310 °C sampai 650 °C. Ukuran-ukuran kristal kedua fasa adalah sangat lulus (berskala manometer) sehingga memberikan efek interaksi. Namun efek interaksi tidak signifikan pada nilai Tc."

"Vortex tube adalah separator energi yang menggunakan aliran tangensial (vortex). Dengan inlet berupa jet tangensial, terjadi medan aliran vortex yang menyebabkan perbedaan temperatur diantara duo outlet. 5atu outlet di bagian peripheral mempunyai temperatur lebih tinggi, yang outlet di bagian tengah mempunyai temperatur lebih rendah dibanding inlet. Tujuan dari penelitian ini adalah untuk mernpelajari medan aliran di dalam vortex tube dengan CFI), dengan menggunakan model turbulen RNG. Analisa medan aliran ini mencakup: flow pattern: distribusi kecepatan oksial, kecepatan total, distribusi tekanan static dan tekanan total, distribusi temperatur total. Hasii ini akan divalidasi dengan hasil pengukuran temperatur total melalui eksperimen. Proses komputasi menggunakan model komputer dengan dimensi soma dengan eksperimen, model turbulensi RNG, dengan input kecepatan yang dihitung berdasarkan pengukuran laju aliran rnassa inlet dan outlet dalam eksperimen. Keunikan model eksperimen ini terletak pada swirling generator yang mempermudah input tangensial udara kompresor, walaupun disederhanakan dalam model komputer. Selain itu, komputasi ini berhasil memadelkan katup jarum, sehingga komputasi ini memberikan hasil yang lebih akurat di daerah katup Sarum. Hasil komputasi menunjukkan adanya daerah aliran-bolik (reversal flow) di dalam vortex tube. Aliran batik ini terjadi terutama pada daerah sumbu sampai jarak radial 0.5 RID, dan jarak aksial dari inlet sampai 7.8 XID. Hasil penting lainnya adalah bentukon duo bush vorteks, vorteks luar yang membentuk distribusi kecepatan seperti vorteks Rankine, don vorteks dalam yang membentuk distribusi kecepatan seperti vorteks bebas, dengan kecepatan di sumbu yang lebih tinggi dibandingkan kecepatan pada radius yang lebih besar. Batas ke duo vorteks tersebut terletak di antar 0.4 sampai dengan 0.5 RID. Hasil komputasi juga memperlihatkon pengaruh dominan dari medan aliran terhadap temperatur total. Data eksperimen memvalidasi trend temperatur total raja, tanpa kesesuaian nilai temperatur total.

---

Vortex tube is energy separator using tangential inlet. The vortex flow-field created temperature differences at the two outlets. One outlet at the tube's periphery had higher temperature, and the other outlet at the center with lower temperature. The temperature differences at both outlets might be reached 80K at 6 bar pressure inlet.Computational model was built up in such way, with the same dimensions, velocity inlet and pressure outlet that counted down from the parameters that have been used in the experiment as the boundary conditions. RNG turbulence-model was used to solve the governing equations. The unique swirling generator was used in the experiment to simplify the distribution for air tangential-inlet, although it is simplified in the computer model. Besides, the needle valve has been able to be modeled. It brings more accurate of the flow field's result at the valve's area.

The results: the figures of the flow patterns: axial velocity, velocity magnitude, static and total pressure, and the distribution of total temperature. The result of total temperature distribution is validated with the experiment's result.The computational result shows a reversal flow in the certain area in the vortex tube. The reversal flow occurs in the axis until radial distance 0.5 Rib, with axial distance from inlet area until 7.8 XIS. Be-side, there is curve of two integrated vortex. The outer vortex formed like Rankine vortex, and the inner vortex with free-vortex distribution, which has higher velocity in the core than the peripheral. The flow field dominates the total temperature distribution, thus they are formed likely, with radii of both inner and outer vortex between 0.4 and 0.5 RID, as the velocity magnitude distribution curve. The experimental data figures the same trend as the computational result, but with non-suited value."

"ABSTRAKAlloy FeSi adalah material softmagnetik yang banyak digunakan sebagai inti dalam transformator. Material ini memiliki sifat yakni magnetisasi saturasinya tinggi, koersivitasnya rendah, permeabilitasnya tinggi. Bertambahnya Si akan mengurangi koersivitas dan meningkatkan resistivitas sehingga core loss akibat hysterisis dan Eddy current menurun, dan didapatkan sifat magnetik material yang baik untuk apikasi transformer. Tetapi penambahan Si diatas 3 % menyebabkan alloy bersifat brittle. Penambahan Al pada alloy FeSi diharapkan dapat memperbaiki sifat magnetik dan sifat mekanik, sehingga efisiensi dari transformator dapat meningkat. Untuk itu dilakukan penelitian studi sifat magnetik beserta komposisi dan mikrostruktur dari FeSiAl. Dengan kadar Si 3% dan variasi kadar Al 4%,5% dan 6% serta kadar Fe100-3%-%Al . Dalam penelitian ini sifat magnetik yang diukur adalah koersivitas yang diperoleh dari hysterisis loop. dengan menggunakan alat VSM (Vibrating sample magnetometer). Dari hasil penelitian ini tampak bahwa koersivitas menurun dengan pertambahan Al yang berarti sifat magnetiknya lebih baik. Mikro struktur material diteliti dengan menggunakan XRD dan foto mikro yang menunjukkan fasa ketiga sampel sebagai body centered cubic.

---

ABSTRAK

The alloy FeSi is a softmagnetic material oftenly used as the core component of a transformer. This material has the properties of high saturation of magnetization, low coercivity and high permeability. Increased Si will reduce the coercivity and increase the resistance, so there is a reduction of core loss due to hysterisis and eddy current?properties of magnetic material that is good for application in transformers. But increasing Si more than 3% causes the alloy to become brittle. Adding aluminium to FeSi is hoped to improve the magnetic and mechanical properties of the alloy, so as to increase the efficiency of a transformer. To achieve the aims, a research was carried out to study the composition and microstructure of FeSiAl, with 3% Si concentration and varied concentrations of aluminium (4%, 5% and 6%), and Fe100-3%-%Al concentration. In this research, the magnetic property measured was coercivity obtained from loop hysterisis using VSM (vibrating sample magnetometer). In the research, it was observed that coercivity was reduced with the addition of Al, which means the alloy had better magnetic properties. The microstructure of the material was studied using XRD and microphotograph that showed the phase of the three samples as being body-centered cubic."

"Information about magnetic structure can not be obtained through X ray diffraction method. Therefore data from neutron diffraction are needed to find out substance magnetic structure. From that structure, we can get information about magnetic crystal structure and magnetic momentum or the structure of the spin. The research is aimed to find out magnetic structure at CaMnO3 dan LaMnO3 in powder. The preparation of CaMnO3 and LaMnO3 substance is made through powder method and stoikiometric calculation. Basic substance of CaMnO3 is CaCO3 and MnO2, while basic substance of LaMnO3 is La2O3 and MnO2. After the substances are mixed, time varied milling, temperature varied sintering and annealing are conducted. It is hoped that the substances will be united or form a new phase.The magnetic structure study of CaMnO3 and LaMnO3 at this research are explained by neutron powder diffraction. CaMnO3 is good analisis at crystal system on orthorhombic space group Pnma with lattice parameter at 12 k is a = 5.2692 Å, b = 7.4403 Å, c = 5.2596 Å. LaMnO3 is good analisis at crystal system on monoklinik space group P1121/a with lattice parameter at 12 K is a = 5.4726 Å, b = 7.7613 Å, c = 5.5324 Å. Magnetic parameter Mn atomic has charge ordered of CaMnO3 and LaMnO3 is Mn4+ ion and Mn3+ ion.Result at research with High Resolution Powder Diffractometer, HRPD to find, CaMnO3 has properties magnetic at Mn atomic with indeks miller hkl (011) angle θ 2 = 24.486 on 12 K. LaMnO3 has properties magnetic at Mn atomic with indeks miller hkl (200) and angle θ 2 = 38.966°. Magnetic structure Mn atomic at 4b(0,0, 2 1 ) simetri of CaMnO3 is four possible nonkolinear ferromagnetic, with value magnetic momen is m(Mn) = 1.73 B µ . Magnetic structure Mn atomic of LaMnO3 at 2c(0,0, 2 1 ) is two possible (antiferomagnetik and ferromagnetic) and 2d( 2 1 , 2 1 ,0) simetri is two possible antiferromagnetic, with value magnetic momen is m(Mn) = 2.23 B µ ."

"Magnet permanen berbasis Sm-Fe-N merupakan magnet kelas baru yang ditemukan pada tahun 1990. Sejak ditemukan fasa magnetik ini telah banyak studi lanjutan yang dilakukan terutama sekali untuk meningkatkan sifat magnetiknya. Dalam penelitian ini telah dilakukan analisis sifat magnetik dan struktur material magnet permanen berbasis Sm-Fe-N dengan komposisi nominal (SmxFe1oo-x)o.97N3, x = 6; 7,5; 9; 11,5 (at. %). Preparasi sampel dilakukan dengan teknik metalurgi serbuk menggunakan ball mill berenergi tinggi dan paduan nitrida didapatkan melalui reaksi gas-padatan. Kompaksi dilakukan dengan teknik kompaksi kejut. Hasil identifikasi fasa dengan difraksi sinar-x menunjukkan bahwa fasa mayoritas yang hadir adalah Sm2Fe17N3 dengan struktur Th2Zn17 (rhombohedral) dihitung sekitar 90 %. Disamping itu hadir pula fasa kedua yaitu a-Fe sebagai konsekuensi komposisi di luar stoikiometri. Khusus untuk komposisi pada x = 11,5 terdapat kehadiran fasa SmN sebesar 0,14 %. Hasil perhitungan konstanta kisi dengan metode Cohen memperlihatkan kesesuaian dengan nilai publikasi dan variasi komposisi magnet Sm-Fe-N tidak menyebabkan distorsi pada kisikisi kristal Sm2Fe17N3. Hasil analisis sifat magnetik diketahui terdapat peningkatan koersivitas dengan pertambahan kandungan Sm dalam' komposisi. Sedangkan harga remanen yang didapat melewati batas teoritis Stoner-Wohlfarth - 0,8 T. Namun secara umum remanen menurun dengan adanya peningkatan Sm. Demikian pula terjadi penurunan pada energi produk maksimum, (BH)n,. dengan bertambahnya kandungan Sm dalam komposisi.

---

Sm-Fe-N based permanent magnet belong to a new class of magnets were discovery in 1990. Since the discovery, a number of studies have been made to improve the magnetic properties. In this work, magnetic properties and materials structure of Sm-Fe-N based permanent magnets with (Sm)(Feio0.. )o,97N3 x = 6; 7,5; 9; 11,5 atomic persent composition have been analysed. Samples were prepared by powder metallurgy using high energy ball mills, then samples were nitrided using solid-gas reaction and subsequently compacted by shock compaction method.

Phase identification by XRD indicated that Sm2Fei7N3 is the majority magnetic phase with a volume fraction up to - 90 °I°. In addition, it was also identified an a-Fe as the second phase due to unstoichiometric composition of the magnet. Specially for x = 11,5 (at.%) also identified an SmN phase about 0,14 %. Lattice constants value of main phase that determined by Cohen's method is similar to that of published result. It is also shown that compositions of the magnets have no effect to lattice constants of main Sm2Fei7N3 phase.

The result of magnetic properties is increasing the coercivity with additional content of Sm composition. But the remanen value which is obtained more than Stoner-Wohlfarth theory - 0,8 T. In general, the remanen reduces by adding Sm. Also the maximum of product energy, (BH)max, is reduced by adding the content of Sm in the composition."

"ABSTRAKStudi sifat kemagnetan dan analisis kinetika alloy magnetic berbasis Nd-(Fe,Co)-B telah dilakukan. Ingot dan pita-pita alloy magnetic Nd10(Fel-xCox)14B6 (at %) dengan komposisi x = 0 ; 0.1; 0.2 ; dan 0.5 dibuat masing-masing dengan arc melting furnace dan Teknik melt spinning dengan kecepatan substrat 30 m s pita-pita sampel kemudial dianil dengan temperature 700 C selama 2 sampai 120 menit untuk meningkatkan derajat kristalisasi fasa yang terbentuk adalah Nd2(Fe,Co)14B sebagai fasa utama, dan fasa minar alpha-Fe serta Co. studi XD menunjukkan bahwa volume sel satuan fasa utama berkurang dengan peningkatan subsitusi Co. ukuran butir rata-rata fasa utama dievaluasi dengan menggunakan formula Scherrer dan ditemukan bahwa semua butiran berukuran dalam skala nanometer. Pengukuran sifat kemagnetan menggunakan VSM untuk alloy yang dipelajari diketahui bahwa nilai koersivitas masimum 499 kAm diperoleh untuk alloy dengan komposisi x = 0,1 setelah aniling pada temperature at 700 C selama 2 menit Remanen dari semua pita-pita alloy berkisar antara 0.80-1.10 T Peningkatan nilai remanen disebabkan oleh exchange coupling annatar fasa Nd2(Fe,Co)14B dan partikel alpha-Fe yang berukuran ultra halus (nanometer) di dalam alloy Nd-Fe-B dengan kandungan Nd rendah. Produk energi maksimum dari pita alloy yang telah dianil berkisar antara 28-115 kJ m3. Pengukuran temperature Curie, Tc dengan menggunakan differential scanning calorimeter (DSC) dari pita-pita kristalin menunjukkan bahwa terjadi kenaikan nilai Tc dari 304 C untuk alloy x = 0 sampai 650 C untuk alloy x = 0.5. kinetika kristalisasi dari fasa amorf alloy Nd10(Fe1-xCox)84B6 juga telah dianalisis dengan menggunakan DSC. Energi aktivasi Ec dan konstanta Avrami, n untuk kristalisasi alloy dengan komposisis X = 0 dan x = 01 dihitung dengan menggunakan metode Kissinger yang telah dimodifikasi. Hasil-hasil analisis kinetika menunjukkan bahwa transformasi fasa dikontrol oleh proses difusi dengan laju pertumbuhan dan nukleasi konstan.

---

ABTRACT

Magnetic studies and kinetic analysis on melt spun ribbon of Nd-(Fe,Co)-B based permanent magnets have been done. Ingot and ribbon samples of Nd10(Fel-xCox)14B6 (at %) with x = 0 ; 0.1; 0.2 ; and 0.5 compositions were prepared by arc melting furnace and melt spinning with substrate velocity of 30 mis respectively. The ribbon samples were subsequently annealed at 700 C for 2-120 minutes to promote crystallization. The phases present in the samples are Nd2(Fe,Co)14B type as main phase, alpha-Fe, and Co as the addition. X-ray diffraction studies indicate that the volume of unit cell of main phase tends to decrease by Co substitution. The mean grain size of main phase was also evaluated by line broadening analysis, using the Scherrer formula and found that all the grains were in nanometer scale. From magnetic measurements by VSM for the alloys under studied, it is found that the maximum coercivity of 499 kA per m was observed in the ribbon alloy of x = 0.1 composition after annealing at 700 C for 2 minutes. Remanence of all as-spun and heat treated ribbons are in the range of 0.80 to 1.10 T (above the theoretical value based on Stoner-Wohlfarth theory.L12; Js = saturation magnetization). The enhancement of remanence raised due to exchange coupling between nanosized Nd2(Fe,Co)14B and cc -Fe particles in the Nd-Fe-B alloys with lower Nd content. Maximum energy products of the annealed ribbon are in the range of 28 to 115 kJ per m3. The Curie temperature, T, measurement of crystallized melt spun ribbon by Differential Scanning Calorimeter (DSC) show an increase the value of L from - 304 C for alloy x = 0 to -650 C for alloy x = 0.5. The kinetic of crystallization process of amorphous Nd1o(Fe1-x Cox)14B6 alloy have also been analyzed by DSC employed modified Kissinger method from which activation energy, Ec and Avrami constant, n for the crystallization were determined for alloys with composition x = 0 and x = 0.1. Results of kinetic analysis show that the phase transformation is a diffusion-controlled transformation with initial growth of particles nucleated at a constant rate."