"enelitian ini bertujuan untuk mencari pelarut yang sesuai untukpencangkokkan Glisidil metakrilat (GMA) pada serat rayon terikat silang N,N’-metilendiakrilamida (NBA) melalui teknik ozonasi dalam udara, yang memilikikarakter sebagai matriks penukar ion yang tahan ternadap kondisi asam danbasa. Gugus peroksida dan nidroperoksida dibentuk terlebih dahulu padapermukaan serat rayon melalui ozonasi. Selanjutnya, serat rayon di ikatsilang dengan pengikat silang NBA dalam media gas N2 pada berbagaikonsentrasi monomer, waktu ozonasi dan suhu reaksi. Serat yang telahterikat silang ini kemudian diuji ketahanannya dalam asam dan basa. Untukpenoangkokkan GMA dilakukan ozonasi kembali pada serat terikat silangselama 4 jam. Penoangkokkan GMA dilakukan pada beberapa pelarut(metanol, metanol:air (4:6), etanol, aseton, n-neksan, N-metnyl-2-pirolidon,dan 1,4-dioksan) Selanjutnya dengan menggunakan pelarut metanol dancampuran metanol:air (416) dipelajari pengaruh konsentrasi, suhu dan waktupencangkokkan. Kemudian pada GMA tercangkok dilakukan modifikasidengan cara mereaksikannya dengan asam iminodiasetat (IDA) untukmenghasilkan serat rayon-g-(GMA-IDA). Karakterisasi dilakukan denganmenggunakan spektrofotometer FTIR, derajat pengembangan (% swelling)dan penentuan kapasitas pertukaran ionnya. Ketahanan serat rayonternadap asam dan basa diperoleh pada ikat silang NBA dengan konsentrasi 5%, lame ozonasi 4 jam dan suhu reaksi 8O°C_ Kadar pencangkokkan (%G)GMA tertinggi sebesar 56,6O%; 56,18%; dan 57,42% diperoleh dari hasilpencangkokkan GMA 20% (%v/v), suhu reaksi 60°C dalam pelarut metanol,metanol:air (416) dan 1,4-dioksan, waktu kopolimerisasi 2 jam. Hasil reaksiGMA dengan IDA menghasilkan perbandingan mol 1:1. Pengamatan dataspektrum FTIR menunjukkan telah terjadi ikat silang NBA dan modifikasidengan GIVIA-IDA pada matriks serat rayon. Hasil uji pertukaran iondiperoleh kapasitas pertukaran ion tertinggi sebesar 4,18 mek/g."

"Adsorben untuk ion logam berat dengan gugus pengkelat amina telah dibuat dengan memodifikasi serat rayon terikat silang N,N’-Metilenbisakrilamida (NBA) tercangkok Glisidil Metakrilat (GMA), R-NBA-g-GMA, dengan Dietilentriamin (DETA). Kondisi optimum reaksi modifikasi ini yaitu pada suhu 70 °C, waktu reaksi 8 jam, dengan konsentrasi DETA 25% dalam pelarut 1,4-dioksan. Adsorben terfungsionalisasi DETA (R-NBA-g-GMA-DETA) kemudian dilakukan pengujian untuk adsorpsi ion Cu(II), Pb(II) dan Cd(II) pada berbagai pH. Hasil penelitian menunjukkan bahwa adsorben ini memiliki koefisien distribusi dan selektivitas tertinggi untuk ion Cu(II) pada pH 5. Proses adsorpsi cenderung mengikuti model kinetika orde dua semu dan model isoterm Langmuir dengan kapasitas maksimum teoritis sebesar 1,45 mmol/gram adsorben. Studi desorpsi dan regenerasi menunjukkan bahwa adsorben ini memiliki laju desorpsi yang tinggi dan dapat diregenerasi untuk digunakan kembali.

---

Adsorben untuk ion logam berat dengan gugus pengkelat amina telah dibuat dengan memodifikasi serat rayon terikat silang N,N’-Metilenbisakrilamida (NBA) tercangkok Glisidil Metakrilat (GMA), R-NBA-g-GMA, dengan Dietilentriamin (DETA). Kondisi optimum reaksi modifikasi ini yaitu pada suhu 70 °C, waktu reaksi 8 jam, dengan konsentrasi DETA 25% dalam pelarut 1,4-dioksan. Adsorben terfungsionalisasi DETA (R-NBA-g-GMA-DETA) kemudian dilakukan pengujian untuk adsorpsi ion Cu(II), Pb(II) dan Cd(II) pada berbagai pH. Hasil penelitian menunjukkan bahwa adsorben ini memiliki koefisien distribusi dan selektivitas tertinggi untuk ion Cu(II) pada pH 5. Proses adsorpsi cenderung mengikuti model kinetika orde dua semu dan model isoterm Langmuir dengan kapasitas maksimum teoritis sebesar 1,45 mmol/gram adsorben. Studi desorpsi dan regenerasi menunjukkan bahwa adsorben ini memiliki laju desorpsi yang tinggi dan dapat diregenerasi untuk digunakan kembali."

"Penelitian ini bertujuan untuk menghasilkan serat rayon terikat silangyang memiliki ketahanan terhadap kondisi asam dan basa dengan gugusfungsional Akrilamida (AAm) dan Glisidil Metakrilat-Asam Iminodiasetat(GMA-IDA). Percobaan ini menggunakan teknik ozonasi dalam udara untuk menghasilkan gugus peroksida dan hidroperoksida yang dapat menginisiasi reaksi kopolimerisasi cangkok. Serat rayon terozonasi dicangkok dengan agen pengikat silang N,N?-Metilendiakrilamida (NBA) dalam media gas N2 dengan berbagai variasi laju alir ozon, lama ozonasi, konsentrasi monomer, dan suhu reaksi untuk mengetahui kondisi optimal pencangkokkan NBA pada serat selulosa. Serat yang telah terikat silang melalui pencangkokkan NBA kemudian diuji ketahanannya dalam asam dan basa. Ozonasi selanjutnya pada serat yang telah terikat silang digunakan untuk mencangkokkan monomer. Pada pencangkokkan monomer AAm, didapatkan bahwa lama ozonasi pada pencangkokkan NBA untuk menghasilkan serat terikat silang,berpengaruh pada kadar pencangkokkan AAm. Makin lama ozonasi untuk NBA, maka kadar pencangkokkan AAm menjadi berkurang. Padapencangkokkan GMA, didapatkan bahwa konsentrasi optimum GMA yang bisa tercangkok pada serat terikat silang adalah sebesar 30% GMA dengan suhu 60°C. Selanjutnya GMA yang sudah tercangkok pada serat terikat silang direaksikan dengan IDA menghasilkan R-co-NBA-g-(GMA-IDA). Spektrum FT-IR menunjukkan telah tercangkoknya monomer-monomer pada serat melalui pengamatan gugus fungsi yang ada."

"Industri Tekstil dan Produk Tekstil (TPT) mendapat dukungan kebijakan dari pemerintah Indonesia dalam meningkatkan kinerja terutama ekspor. Periode krisis tahun 1998-2003, bahwa kinerja ekspor industri serat sintetik sebagai industri hulu TPT Indonesia cukup baik. Perusahaan besar dalam industri serat sintetik mempunyai pangsa pasar yang cukup besar untuk menguasai pasar. Namun kinerja kemampulabaan dan kinerja pajak rendah. Penjualan hubungan istimewa lazim dilakukan perusahaan serat sintetik yang merupakan anak perusahaan dari suatu korporasi yang terintegrasi, salah satu bentuk transfer pricing. Transaksi ini memungkinkan perusahaan melakukan perilaku usaha tidak sehat transfer pricing (pasal 21 UU Persaingan). Dalam persaingan oligopolistik, transfer pricing mempunyai peran ganda baik sebagai suatu strategi dan sebagai alat penghematan pajak.Tujuan penelitian ini adalah: pertama, memperdalam analisis transfer pricing (kewajaran harga dan biaya) dari sudut pandang konsep persaingan usaha dan perpajakan. Kedua, mengembangkan model analisis transfer pricing untuk meneliti kewajaran harga dan biaya dalam rangka pengujian pemenuhan kewajiban perpajakan perusahaan serat sintetik Indonesia. Ketiga, meneliti hubungan antara ketidakwajaran harga dan biaya secara perpajakan dengan persaingan usaha dalam industri serat sintetik Indonesia.Hasil penelitian tidak membuktikan secara eksplisit peiaku usaha melakukan transfer pricing untuk pemasokan barang dan atau jasa dengan cara melakukan jual rugi atau menetapkan harga yang sangat rendah dengan maksud untuk menyingkirkan atau mematikan usaha pesaingnya di pasar serat sintetik Indonesia yang mengakibatkan terjadinya persaingan usaha tidak sehat. adanya ketidakwajaran yang menjadi indikasi awal transfer pricing. Implikasi kebijakan fiskal jangka pendek. Pertama, dalam ha! pemenuhan kewajiban perpajakan fiskus perlu melakukan pemeriksaan atas pas penjualan dan pembelian dengan pihak hubungan istimewa, selisih kurs dan hutang. Kedua, dengan penyesuaian-penyesuaian hasil diatas dapat disusun Profit Level Indicator (PLI). Kebijakan fiskal Jangka Panjang ; bahwa otoritas fiskal mampu mengimplementasikan suatu standar (PLI) dan mekanisme pengujian transfer pricing terhadap perusahaan-perusahaan secara berkesinambungan dapatlah diharapkan terciptanya suatu detterent effect. Hasil penelitian ini memberikan wawasan bagi otoritas persaingan (KPPU) untuk mengembangkan analisis transfer pricing dengan metodologi perpajakan. Namun, diperlukan penelitian lebih lanjut dengan menggunakan alat-alat analisis ekonomi untuk mengadopsi kerangka pemeriksaan perpajakan atas transfer pricing pada persaingan usaha."

"Telah disintesis serat rayon terikat silang N,N?-Metilendiakrilamida (NBA) sebagai matriks pencangkokkan asam akrilat (AA) yang memiliki derajat pengembangan dalam air berkisar antara 300-400% serta tahan terhadap kondisi asam dan basa. Inisiasi ikat silang dan pencangkokkan monomer dilakukan dengan metode ozonasi dalam udara. Metode ini dapat digunakan untuk memisahkan, mengontrol dan mengoptimasi pembentukan ikat silang dan pencangkokkan monomer AA dalam media N2. Gugus peroksida dan hidroperoksida yang terbentuk pada serat rayon pada berbagai variasi laju alir, waktu ozonasi, berat dan kerapatan serat ditentukan dengan metode iodometri dalam fasa organik. Pembentukan ikat silang dilakukan pada berbagai konsentrasi monomer dan suhu reaksi. Pencangkokkan AA pada serat yang telah terikat silang dilakukan melalui variasi waktu ozonasi kembali dan konsentrasi monomer. Serat rayon-co-NBA-g-Poliakrilat yang dihasilkan dikarakterisasi menggunakan FTIR. Kadar peroksida pada serat semakin tinggi dengan meningkatnya laju alir dan waktu ozonasi. Hasil yang diperoleh menunjukkan makin tinggi derajat ikat silang, makin sedikit AA yang dapat tercangkok. Derajat pengembangan dan ketahanan serat terhadap kondisi asam dan basa dipengaruhi oleh banyaknya ikat silang dan kadar AA tercangkok. Semakin banyak jumlah ikat silang pada serat, derajat pengembangan akan menurun dan ketahanan terhadap kondisi asam dan basa meningkat.

---

Cross-linked rayon fiber with N,N'-Methylenediacrylamide (NBA) as graft copolymerization matrix of acrylic acid (AA) has been synthesized. The grafted fibers which is resistant to acidic and alkaline conditions shown degree of swelling between 300-400%. The initiation of the cross-link formation and graft copolymerization of monomer were carried out by ozonation method in the air.

This method can be used to separate, to control and to optimize the cross-link process and graft copolymerization of AA in the media of N2. Peroxide and hydroperoxide groups formed on the rayon fibers at various flow rate, ozonation time, weight and density were determined by iodometric method in the organic phase.

Cross-linked rayon fibers was prepared at various monomer concentrations and reaction temperature. The graft copolymerization of acrylic acid on the crosslinked fiber is conducted at various ozonation time and AA concentration. Rayon fiber-co-NBA-graft-Polyacrylic were characterized using FTIR. Peroxide concentration on the rayon fibers increases with flow rate and ozonation time.

The result showed the increases in degree of cross-linking will decreases the amount of AA grafted. It was observed that the fiber swelling and resistant to acidic and alkaline conditions were depend on degree of crosslinking and the total of carboxylic group grafted onto rayon fiber. The higher concentration of crosslinking agent, the degree of swelling will be lower and stability in acidic and alkaline condition will be increases."

"Dalam satu dekade terakhir, Indonesia menghadapi peningkatan tantangan pertahanan, keamanan, dan ketertiban negara dengan berbagai macam intensitas kewaspadaannya. Untuk mengatasi hal tersebut, industri Alat Peralatan Pertahanan dan Keamanan negara perlu berbenah dan menyesuaikan diri dengan perkembangan teknologi. Negara membutuhkan teknologi bahan inovatif untuk membuat alat komponen pertahanan dan keamanan seperti helm anti peluru yang kuat, ringan, praktis, nyaman digunakan, serta menggunakan bahan yang ramah lingkungan. Perkembangan dunia saat ini banyak menggunakan serat sintetis, yang walaupun memiliki kekuatan tinggi, biayanya cukup tinggi dan memiliki implikasi buruk bagi lingkungan sebelum dan sesudah proses sintesisnya. Oleh karena itu, penelitian ini mencoba untuk memberikan solusi bahan pembuatan helm anti peluru dengan konsep komposit berpenguat dari serat alam, yaitu serat kenaf (Hibiscus Cannabicus) yang memiliki potensi kekuatan mekanis yang baik, lebih murah dalam proses manufakturnya, ramah lingkungan, dan yang paling penting banyak ditemukan di Indonesia. Metode pembuatan dilakukan dengan teknik open molding, yaitu hand lay-up. Serat kenaf yang digunakan sebagai penguat memiliki struktur rajutan (woven) yang dikombinasikan dengan matriks resin epoksi. Lembaran penguat serat kenaf rajutan divariasikan jumlahnya berdasarkan pendekatan massa ideal standar acuan pasukan angkatan darat. Setelah itu dilakukan uji balistik level I dengan peluru jenis caliber 22 sesuai standar National Institute of Justice 0108.01. Kemudian juga, untuk setiap sampel dilakukan uji kekerasan dan uji flexural strength untuk mengamati sifat mekanis lain yang mendukung performa balistik. Uji balistik dilakukan terhadap 3 variasi sampel, yaitu serat kenaf rajutan dengan 3 lembaran, 6 lembaran, serta 9 lembaran. Hasil pengujian balistik menunjukkan bahwa peluru caliber 22 berhasil menembus ketiga sampel, namun dengan respon yang cukup signifikan perbedaannya pada masing-masing sampel. Hasil perforasi kemudian diamati morfologi patahannya pada tampak depan dan belakang sampel secara makro dengan pengujian macrostructure fractography serta secara mikro dengan pengujian SEM. Sampel komposit dengan jumlah lembaran tertinggi (9 lembaran) mengalami perforasi sebagian, sedangkan kedua sampel lain mengalami perforasi penuh. Penelitian menunjukkan bahwa peningkatan jumlah lembaran serat kenaf rajutan meningkatkan secara signifikan energi absorpsi, dan potensial untuk dikembangkan selanjutnya sebagai material tahan balistik untuk helm anti peluru.

---

In the past decade, Indonesia has confronted increasing challenges towards the nations defense, security, and order with its various intensities of alertness. To overcome this, the nations Defense and Security Equipment industry must adapt itself to the development of technology. The nation needs innovative material technology to make components of the defense and security equipment tools such as strong, light, comfortable, practical bullet-proof helmets, made from environmentally safe materials. Many current developments use synthetic fibers, which although has high strength, is relatively expensive and has bad implications towards the environment, before and after the synthesis process. Thus, this research tries to give a solution for the alternative material used to make bullet-proof helmets with the concept of reinforced composite from a natural fiber, the kenaf fiber (Hibiscus Cannabicus), which has good mechanical strength potential, cheaper manufacturing process, environmentally friendly, and most importantly, found in abundance in Indonesia. The manufacturing method is done with the open molding technique, namely the hand lay-up. The kenaf fiber used as reinforcement has a woven structure that is combined with epoxy resin matrix. The woven kenaf fiber reinforcement plies vary in number, based on the standard ideal mass reference to ground-force troops. After that, a level I ballistic test is conducted with a caliber 22 bullet, according to the standard from National Institute of Justice 0108.01. Furthermore, each sample goes through a hardness and flexural strength test to observe other mechanical properties that support the ballistic performance. The ballistic testing is done to 3 varieties of samples, which are woven kenaf fiber with 3, 6, and 9 plies. The results show that the caliber 22 bullet penetrated all 3 samples but with significantly different responses from each sample. Perforation results were then observed in the fracture morphology from the front and back view of the samples in macro with macrostructure fractography, and in micro with SEM. The composite sample with the highest number of plies (9 plies) experienced partial perforation, while the other 2 samples experienced full perforation. This research shows that with the increasing number of kenaf fiber plies, the ability to absorb energy is significantly increased, thus has potential to be further developed as anti-ballistic material used for bullet-proof helmets. "

"ABSTRAKModifikasi serat rayon menggunakan teknik radiasi sebagai adsorben uraniumtelah dilakukan. Modifikasi dilakukan dengan cara kopolimerisasi cangkokdengan teknik radiasi secara simultan menggunakan monomer N,N'-metilendiakrilamid (NBA), monomer glycidil metacrylate (GMA), sertacampuran NBA dan GMA yang dicangkokkan pada serat rayon, juga dilakukanpengikatan asam sitrat sebagai ligan pada serat tercangkok monomer, sehinggadiperoleh kopolimer cangkok Rayon-g-NBA, Rayon-g-NBA-CA, Rayon-g-GMA,Rayon-g-GMA-CA, Rayon-g-NBA-GMA, dan Rayon-g-NBA-GMA-CA.Penelitian ini bertujuan untuk membuat serat penukar ion yang dapatmengadsorpsi uranium dengan kapasitas tukar ionnya yang baik. Parameter yangdipelajari adalah pengaruh dosis serap, volume monomer, konsentrasi monomer,dan rasio volume larutan. Serat yang telah dimodifikasi dikarakterisasi sifatfisiknya diantaranya ditentukan persen cangkok, topologi, sifat termal,kristalinitas, serta kapasitas tukar ionnya. Hasil yang diperoleh adalah kondisioptimum untuk memodifikasi serat rayon. Dosis radiasi yang digunakan 0,5 kGyuntuk R-g-NBA dan R-g-GMA; 0,75 kGy R-g-NBA-CA, R-g-GMA-CA, dan Rg-NBA-GMA; dan 1 kGy untuk R-g-NBA-GMA-CA. Volume monomeroptimum untuk semua serat termodifikasi dengan berat serat 100 mg adalah 10mL, konsentrasi optimum adalah 5%, rasio volume larutan adalah 8:2 untuk R-g-NBA-CA, 5:5 untuk R-g-GMA-CA, dan R-g-NBA-GMA, dan 4:2:4 untuk R-g-NBA-GMA-CA. Dari karakterisasi yang dilakukan terlihat bahwa pencangkokanberhasil dilakukan dengan melihat persen grafting, spektra IR, sifat panas,diameter, dan kristalinitas dari serat termodifikasi dibandingkan dengan serat asli.Serat termodifikasi dengan GMA dan asam sitrat (R-g-GMA-CA) memberikanhasil terbaik dengan kapasitas adsorpsi terhadap uranium terbesar yaitu 0,3 meq/gserat.

---

AbstractRayon fiber modification using radiation techniques for uranium metal adsorbenthas been conducted. Modifications conducted by grafting copolymerization withsimultaneous radiation technique using the monomer N, N'-metilendiakrilamid(NBA), glycidil metacrylate monomer (GMA), as well as a mixture of NBA andGMA is grafted on a rayon fiber, also made of citric acid as a ligand binding tothe grafted fiber monomer, in order to obtain a graft copolymer Rayon -g-NBA,Rayon-g-NBA-CA, Rayon-g-GMA, Rayon-g-GMA-CA, Rayon-g-GMA-NBA,and Rayon-g-NBA-GMA-CA. The study aims to create an ion exchange fiberswhich can adsorb uranium with a fine ion exchange capacity. Parameters studiedare, respectively, the influence of absorbed doses, the volume of monomers,monomer concentrations, and the ratio of solution volumes. Modified fibers werecharacterized physical properties of which are determined percentage of,respectively, persent grafts, topologies, thermal properties, crystallinities, and ionexchange capacities. The results obtained are optimum conditions for modifyingthe rayon fiber. Dose of 0.5 kGy of radiation used for R-g-NBA and R-g-GMA;0.75 kGy for R-g-NBA-CA, R-g- GMA-CA and R-g-NBA-GMA, and 1 kGy forR-g-NBA-GMA-CA. Optimum monomer volume for all the fibers modified withfiber weight of 100 mg was 10 mL, the optimum concentration was 5%, thesolution volume ratio is 8:2 for the R-g-NBA-CA, 5:5 for R-g-GMA-CA- and Rg-NBA -GMA, and 4:2:4 for the R-g-NBA-GMA-CA. From the characterizationperformed shows that the transplant has been successed by observing at,respectively, the percentage of graftings, IR spectras, thermal properties,diameters, and crystallinities of the fiber-modified compared to its original fiber.Fibers modified with GMA and citric acid (R-g-GMA-CA) provided the bestresults with the adsorption capacity of the largest uranium metal is 0.3 meq / gfiber."