"Justifikasi beras ketan hitam sebagai inhibitor organik ditentukan dengan membandingkan laju korosi baja SPCC yang diuji rendam di larutan HCl 0,1 M dengan dan tanpa penambahan beras ketan hitam 500 gpl. Hasilnya beras ketan hitam dapat menekan laju korosi dengan efisiensi 63,952 - 81,2412 % selama waktu uji rendam 3 - 7 hari. Penelitian ini merupakan penelitian tahap awal sehingga mekanisme penghambatannya secara mendetail tidak mencakup bagian dari penelitian ini. Namun pendekatan secara elektrokimia dilakukan untuk membantu justifikasinya dan meramalkan mekanisme yang terjadi dari perubahan potensial logam dan pH larutan.

---

Justification black glutinous rice as an organic inhibitor was determined by comparing corrosion rate of immersed SPCC steel in 0.1 HCl solution with and without addition of 500 gpl black glutinous rice.

The result black glutinous rice can inhibit corrosion rate of SPCC steel with the efficiency reaches 63,952 - 81,2412 % during 3 - 7 days of immersion test duration. This study was a early stage research so its detailed inhibition mechanism beyond this study objectives. But electrochemically approach study was done to help its justification and predicted the mechanism it took out of the changing of steel potential and pH solution."

"Korosi merupakan salah satu permasalahan penting yang harus dihadapi oleh berbagai macam sektor industri di Indonesia. Korosi memberikan efek dari segi ekonomi maupun dari segi keselamatan kerja. Salah satu cara pencegahan dan pengendalian korosi adalah dengan penambahan inhibitor. Umumnya inhibitor korosi berasal dari senyawa-senyawa organik dan anorganik yang mengandung gugus-gugus yang memiliki pasangan elektron bebas, seperti nitrit, kromat, fospat, urea, fenilalanin, imidazolin, dan senyawasenyawa amina. Namun demikian, pada kenyataannya bahwa bahan kimia sintesis ini merupakan bahan kimia yang berbahaya, harganya lumayan mahal, dan tidak ramah lingkungan, sehingga industri-industri kecil dan menengah jarang menggunakan inhibitor pada sistem pendingin, sistem pemipaan, dan sistem pengolahan air produksi mereka, untuk melindungi besi/baja dari serangan korosi. Untuk itu penggunaan inhibitor yang aman, mudah didapatkan, bersifat biodegradable, biaya murah, dan ramah lingkungan sangatlah diperlukan. Penelitian ini bertujuan untuk mengetahui pengaruh beras ketan hitam sebagai inhibitor organik pada lingkungan asam asetat 1,5 M dan mengetahui efisiensi beras ketan hitam terhadap waktu pengujian. Pengujian laju korosi menggunakan metode kehilangan berat dimana sampel baja SPCC direndam dalam air tanah selama 3, 5, dan 7 hari. Dalam penelitian ini dapat disimpulkan beras ketan hitam bekerja baik dilingkungan asam asetat 1,5 M karena terjadi penurunan laju korosi antara perendaman dengan inhibitor dan perendaman tanpa inhibitor terhadap lamanya waktu pengujian. Penurunan laju korosi terbesar pada hari ke-7, dimana efisiensi inhibitornya sebesar 88,9798825%."

"Korosi merupakan salah satu permasalahan penting yang harus dihadapi oleh berbagai macam sektor industri di Indonesia. Korosi memberikan efek dari segi ekonomi maupun dari segi keselamatan kerja. Salah satu cara pencegahan dan pengendalian korosi adalah dengan penambahan inhibitor.Umumnya inhibitor korosi berasal dari senyawa-senyawa organik dan anorganik yang mengandung gugus-gugus yang memiliki pasangan elektron bebas. Namun demikian, pada kenyataannya bahwa bahan kimia sintesis ini merupakan bahan kimia yang berbahaya, harganya lumayan mahal, dan tidak ramah lingkungan. Untuk itu penggunaan inhibitor yang aman, mudah didapatkan, bersifat biodegradable, biaya murah, dan ramah lingkungan sangatlah diperlukan.Penelitian ini bertujuan untuk mengetahui pengaruh beras ketan hitam sebagai inhibitor organik pada lingkungan NaCl 3,5% dan mengetahui efisiensi beras ketan hitam terhadap waktu pengujian. Pengujian laju korosi menggunakan metode kehilangan berat dimana sampel baja SPCC direndam dalam air tanah selama 3, 5, dan 7 hari.Dalam penelitian ini dapat disimpulkan beras ketan hitam bekerja baik dilingkungan air tanah karena terjadi penurunan laju korosi antara perendaman dengan inhibitor dan perendaman tanpa inhibitor terhadap lamanya waktu pengujian. Penurunan laju korosi terbesar pada hari ke-7, yaitu sebesar 34,4587%.

---

Corrosion is one important problem that must be faced by a variety of industrial sectors in Indonesia. Corrosion effect from the economic and safety terms. One way of prevention and control is by adding corrosion inhibitors. Corrosion inhibitors are generally derived from compounds containing organic and inorganic cluster-cluster which has a lone pair of electrons. However, the fact that these synthetic chemicals are hazardous chemicals, the price is quite expensive and not environmentally friendly. Therefore the use of inhibitors that are safe, easily available, biodegradable, low cost, and environmentally friendly is essential.

This study aimed to investigate the influence of black glutinous rice as the organic inhibitors in 3.5% NaCl environment and knowing the efficiency of black glutinous rice with respect to time of testing. Tests for the corrosion rate using weight loss method in which SPCC steel samples immersed in ground water for 3, 5, and 7 days.

In this study we can conclude the black sticky rice works well within the ground water due to the decrease in corrosion rate between immersion with inhibitor and without inhibitor to the duration of immersion test of time. Largest decrease in corrosion rate on day 7th, that is equal to 34.4587%."

"Korosi merupakan salah satu permasalahan penting yang harus dihadapi oleh berbagai macam sektor industri di Indonesia. Korosi memberikan efek dari segi ekonomi maupun dari segi keselamatan kerja. Salah satu cara pencegahan dan pengendalian korosi adalah dengan penambahan inhibitor. Umumnya inhibitor korosi berasal dari senyawa-senyawa organik dan anorganik yang mengandung gugus-gugus yang memiliki pasangan elektron bebas, seperti nitrit, kromat, fospat, urea, fenilalanin, imidazolin, dan senyawasenyawa amina. Namun demikian, pada kenyataannya bahwa bahan kimia sintesis ini merupakan bahan kimia yang berbahaya, harganya lumayan mahal, dan tidak ramah lingkungan, sehingga industri-industri kecil dan menengah jarang menggunakan inhibitor pada sistem pendingin, sistem pemipaan, dan sistem pengolahan air produksi mereka, untuk melindungi besi/baja dari serangan korosi. Untuk itu penggunaan inhibitor yang aman, mudah didapatkan, bersifat biodegradable, biaya murah, dan ramah lingkungan sangatlah diperlukan. Penelitian ini bertujuan untuk mengetahui pengaruh beras ketan hitam sebagai inhibitor organik pada lingkungan air tanah dan mengetahui efisiensi beras ketan hitam terhadap waktu pengujian. Pengujian laju korosi menggunakan metode kehilangan berat dimana sampel baja SPCC direndam dalam air tanah selama 3, 5, dan 7 hari. Dalam penelitian ini dapat disimpulkan beras ketan hitam bekerja baik dilingkungan air tanah karena terjadi penurunan laju korosi antara perendaman dengan inhibitor dan perendaman tanpa inhibitor terhadap lamanya waktu pengujian. Penurunan laju korosi terbesar pada hari ke-7, yaitu sebesar 53,0006%."

"Perilaku inhibisi ekstrak ubi ungu berdasarkan pengaruh perbedaan konsentrasi yang ditambahkan (2 ml, 4 ml, dan 6 ml) pada baja karbon rendah di lingkungan air demineralisasi yang disuntikan gas CO2 telah diteliti dengan menggunakan metode kehilangan berat. Ekstrak ubi ungu dipilih sebagai inorganic inhibitor karena mengandung senyawa antioksidan yang dapat menghambat laju korosi. Waktu perendaman sampel baja SPCC untuk semua penambahan konsentrasi adalah sama, yaitu selama 5 hari. Hasil penelitian menunjukkan ekstrak ubi ungu merupakan inhibitor korosi yang cukup efektif untuk baja karbon rendah di lingkungan asam lemah, karena penghambatan laju korosi terjadi cukup signifikan dengan efisiensi sebesar 14.31 ? 36.45 % dengan penambahan konsentrasi 2 - 6 ml ekstrak ubi ungu.

---

Behavioral inhibition of purple sweet wine based on the effect of different concentrations were added (2 ml, 4 ml, and 6 ml) on low carbon steel sample in demineralization water with CO2 inject, environment has been investigated using weight loss method. Purple sweet potato extract is selected as green corrosion inhibitors because they contain antioxidant compounds that can inhibit the corrosion rate. SPCC steel sample immersion time for all the additional concentrations are equal, ie for 5 days.

Results showed purple sweet wine is commonly effective corrosion inhibitor for low carbon steel in weak acid environment, because it can inhibit the corrosion rate significantly with an efficiency of 14,31 ? 36,45% with the addition of purple sweet potato extract concentration of 2-6 ml."

"Ekstrak areca flower telah diteliti sebagai inhibitor korosi pada baja API 5L Gr. B pada lingkungan 1 M HCl dengan menggunakan pengujian Linear Polarisasi dan Electrochemical Impedance Spectroscopy EIS. Penambahan konsentrasi inhibitor 4 ml, 8 ml, 12 ml, 16 ml, dan 20 ml dapat meningkatkan efisiensi inhibitor. Efisiensi inhibitor optimum terjadi pada saat penambahan konsentrasi inhibitor 20 ml sebesar 96.6 pada pengujian Electrochemical Impedance Spectroscopy EIS. Senyawa polifenol dan flavonoid yang terkandung dalam areca flower dapat menginhibisi korosi secara adsorpsi fisika yang membentuk lapisan monolayer yang dapat menghambat terjadinya korosi. Adsorpsi terjadi secara spontan sesuai dengan adsorpsi isotermal Langmuir. Sesuai hasil pengujian polarisasi menunjukkan ekstrak areca flower memiliki tipe inhibisi campuran mixed-type . Nilai energi bebas adsorpsi -7.026 kJ/mol menunjukkan bahwa adsorpsi molekul inhibitor adalah adsorpsi fisika.

---

Areca flower has been investigated as green corrosion inhibitor on API 5L Gr B in solution 1 M HCl acidic using Linear polarization and Electrochemical Impedance Spectroscopy EIS . Addition of 4 ml, 8 ml, 12 ml, 16 ml, and 20 ml inhibitor corrosion increase efficiency of the inhibitor. Optimum inhibition efficiency occurs at addition at concentration 20 ml is 96.6 on Electrochemical Impedance Spectroscopy EIS testing. Polyphenolic and flavanoid compounds contained in the areca flower inhibit corrosion by physical adsorption, to form a monolayer which can inhibit corrosion. Adsorption occurs spontaneously in accordance with Langmuir isothermal adsorption. The polarization showed that the areca flower extract acts through mixed ndash type inhibition. The value of the free energy 7.026 kJ mol of adsorption indicated that the adsorption of inhibitor molecules was typical of physical adsorption."

"Aniline-4-sulfonate merupakan senyawa dengan gugus utama berupa cincin benzen, nitrogen dan sulfonat. Pada penelitian ini, senyawa aniline-4-sulfonate digunakan sebagai inhibitor untuk menekan laju korosi baja API 5L GRB N di dalam larutan asam sulfat 1 M. Potensiostat, alat uji kekerasan, alat uji kekasaran, mikroskop optik dan SEM digunakan untuk analisa jenis korosi, efisiensi inhibisi, mekanisme inhibisi, perubahan kekerasan dan kekasaran permukaan. Hasil pengujian menggunakan potensiostat memperlihatkan bahwa korosi yang terjadi pada baja API 5L GRB N adalah jenis korosi merata. Penggunaan inhibitor aniline-4-sulfonate dapat menekan laju korosi dengan efisiensi sebesar 60,29% pada konsentrasi 24,06 x 10-3M dan dapat mengurangi kerusakan terhadap kekerasan dan kekasaran melalui suatu mekanisme inhibisi mengikuti isoterm adsorpsi Langmuir dengan akurasi kelinieran (R2) mendekati 1 (satu).

---

Aniline-4-sulfonate is compound with main groups are benzen ring, ammine, and sulfonate. On this research, aniline-4-sulfonate was used as corrosion inhibitor to reduced corrosion rate on API 5L GRB N steel in 1M sulphuric acid solution. Potensiostat, surface hardness tester, surface roughness terster, optical microscope, and SEM was used for corrosion type analysis, inhibition efficiency, inhibition mechanism, hardness and roughness damage.

Examination using potensiostat showed that corrosion on API 5L GRB N steel was general corrosion type. Aplication aniline-4-sulfonate as inhibitor can pressed corrosion rate with efficiency 60,29 % at concentration 24,06 x 10 -3M, reduced hardness and roughness damage with adsorption mechanism followed Langmuir's adsorption isotherm with linearity accuration (R2) was 0,998."

"ABSTRAKTeh rosella merah memiliki kandungan antioksidan yang cukup tinggi berupaasam askorbat. Asam askorbat ini mampu untuk menurunkan laju korosi yangterjadi pada baja karbon rendah di lingkungan HCl 1 Molar. Metode kehilanganberat digunakan untuk menguji keefektifan teh hijau sebagai inhibitor denganvariasi waktu pencelupan (3 hari, 6 hari, 9 hari, dan 12 hari). Hasil yangdidapatkan adalah nilai efisiensi tertinggi didapatkan pada variabel 3 hari yaitusebesar 63% dan nilai efisiensi terendah didapatkan pada variabel 12 hari yaitusebesar 41%.

---

AbstractRed roselle tea contains a large amount of antioxidant namely ascorbic acid.Ascorbic acid is able to reduce corrosion rate on low carbon steel in HCl 1 M.Weight loss methode is used to test the effectiveness of red roselle tea as aninhibitors with various immersion time (3 days, 6 days, 9 days, and 12 days). Theresult shows that the maximum value was found in 3-days immersion time with63% of efficiency and the minimum value was found in 12-days immersion timewith 47% of efficiency."

"Beton dengan baja tulangan sebagai penguat merupakan material konstruksi yang memiliki sifat mekanis yang sangat baik dan umur layanan yang relatif tinggi. Beberapa tahun terakhir ini telah muncul sejumlah kasus dalam pengaplikasian beton pada berbagai bidang struktural. Kasus yang sering muncul yaitu korosi pada baja tulangan dalam beton akibat serangan ion klorida yang umumnya terjadi pada bangunan-bangunan dan jembatan-jebatan yang terdapat di sekitar laut. Salah satu cara mengatasi masalah ini adalah dengan penambahan inhibitor korosi Ca(NO3)2. Mekanisme inhibisi inhibitor Ca(NO3)2 terhadap perilaku korosi baja tulangan diamati dengan menggunakan metode Electrochemical Impedance Spectroscopy (EIS).Penelitian dilakukan dengan mencelupkan baja karbon rendah yang telah dipreparasi ke dalam larutan pori artifisial yang mengandung 35 gpl NaCl dengan perubahan inhibitor Ca(NO3)2 masing-masing dengan konsentrasi 0 gpl (tanpa inhibitor), 1.302 gpl, 1.860 gpl, dan 2.418 gpl. Pengukuran dilakukan setiap minggu dari minggu kesatu hingga minggu kelima. Dengan metoda EIS, sistem baja tulangan dalam larutan pori digambarkan sebagai rangkaian listrik ekivalen yang harga tahanan dan kapasitasnya dapat diukur pada berbagai frekuensi (5000 Hz sampai 0.002 Hz). Interpretasi perilaku korosi baja tulangan digambarkan melalui enam model rangkaian ekivalen, dan penentuan model yang sesuai dilakukan dengan mengalurkan hasil pengukuran dan hasil interpretasi (fitting) model dalam bentuk kurva Nyquist dan kurva Bode.Hasil penelitian menunjukkan potensial larutan SPS + 35 gpl NaCl tanpa inhibitor berada antara -538 mV hingga -355 mV. Untuk larutan yang mengandung inhibitor Ca(NO3)2, konsentrasi 1.302 gpl menunjukkan efek inhibisi yang lebih baik. Namun demikian konsentrasi yang digunakan masih belum efektif dalam menginhibisi korosi baja tulangan dalam larutan. Efek inhibisinya dari akhir minggu kesatu hingga akhir minggu kelima ekivalen dengan model 2 yang menunjukkan bahwa telah terbentuk lapisan pasif yang belum merata di seluruh permukaan baja."