"Pengembangan nanomaterial TiO2 pada media keramik untuk aplikasi self cleaning telah dilakukan. Preparasi katalis dilakukan dengan metode sol-gel dengan variasi volume TiAcAc/H2O dan dilapiskan pada permukaan keramik dengan spray coating, kemudian dikalsinasi pada suhu 100°C-1180°C selama 30 menit. Keramik yang telah dilapisi katalis menunjukan penurunan sudut kontak air, dan sifat self cleaning yang aktif. Penambahan katalis pada permukaan keramik tidak mempengaruhi sifat mekanik dan matching color dibandingkan keramik standar. Hasil karakterisasi dengan alat XRD menunujukan adanya TiO2 dengan fasa rutile dengan ukuran kristal antara 60 nm - 77 nm.

---

Nanomaterial development of TiO2 at ceramic media for self cleaning application has been studied. Catalyst was prepared using sol-gel method with volume variation of TiAcAc/H2O and coated at ceramic surface with spray coating method, then calcinated at temperature from 100°C-1180°C for 30 minutes. Ceramic that has been coated shown a decreasing in contact angle water and active for self cleaning characteristic. Catalyst addition at ceramic surface didn't influence mechanical characteristic and matching color compared to ceramic standard. Characterization result using XRD showed TiO2 content in rutile phase with crystal size between 60 nm - 77 nm."

"Dewasa ini pengembangan nanomaterial TiO2 dalam bentuk film sedang mendapat perhatian karena kemudahan dalam aplikasinya. Aplikasi yang populer adalah untuk material antifogging dan self-cleaning. Aditif umumnya ditambahkan pada katalis ini untuk meningkatkan aktivitasnya. PEG (polyethylene glycol) digunakan untuk meningkatkan porositas, memperkecil ukuran kristal serta menurunkan kemungkinan terjadinya peretakan (cracking) film saat proses kalsinasi. SiO2 ditambahkan untuk meningkatkan keasaman dari katalis sehingga mampu meningkatkan hidrofilisitas dari katalis meskipun pada kondisi kurang cahaya. Dalam metode sol-gel rasio larutan prekursor dengan air sangat berpengaruh karena air memegang peranan penting dalam hidrolisis. Dalam penelitian ini rasio larutan prekursor dan air dan berat molekul PEG akan dipelajari lebih dalam. Selain itu uji self-cleaning terhadap kondisi optimum juga akan dilakukan. Fotokatalis dalam percobaan ini dipreparasi dengan precursor TiAcAc dengan metode sol-gel dan kristalisasi panas. Sol dengan variasi TiAcAc/Air, dan berat molekul PEG serta penambahan PEG dan SiO2 kemudian dilapiskan pada penyangga kaca preparat dengan metode spin coating sedangkan pada keramik dilakukan metode spray coating yang dilanjutkan dengan pemanasan pada suhu 100_C dan kalsinasi mencapai suhu 520_ C. Selanjutnya untuk mengetahui hasil dari preparasi katalis ini akan dilakukan karakterisasi dengan FTIR, DRS dan TEM. Uji aktivitas juga dilakukan untuk mengetahui kemampuan swa bersih dan anti kabut dari material yang dihasilkan yang meliputi pengukuran sudut kontak dengan alat contact angle meter dan pengamatan langsung dengan menggunakan kamera digital. Pengembangan nanomaterial dengan metode sol-gel dan kristalisasi panas dengan penambahan dopan PEG dan SiO2 berhasil dilakukan, merujuk pada hasil DRS yang menunjukkan band-gap makin besar, ukuran partikel makin kecil setelah diuji dengan TEM, serta hasil uji sudut kontak yang memperlihatkan penurunan sudut kontak air. Hal ini juga didukung hasil uji kualitatif dimana kabut dan kotoran tidak menempel setelah kaca dan keramik dilapisi oleh katalis. Variasi TiAcAc/H2O yang dilakukan menunjukkan kecenderungan kenaikan aktivitas katalis sesuai dengan hasil FTIR dan uji sudut kontak yang dilakukan, sedangkan variasi berat molekul PEG tidak begitu berpengaruh pada aktivitas katalis yang digunakan.

---

In the recent time, the development of TiO2 nanomaterial film has been interesting because of its practical applications. Its well known functions are as an antifogging and self cleaning material. Additives are usually added in order to improve its activity. PEG (polyethylene glycol) is generally used as an additive to increase porosity, minimize particle size and prevent film cracking during calcination. SiO2 could make surface more acid, so it can in crease hydrophilicity of TiO2 material even in non-irradiation places. In the sol-gel method, ratio between precursor solution and water ratio became important because water lead the hydrolysis.

In this research, ratio between precursion solution and PEG molecular weigt effect will be studied. Beside those, there are test of self-cleaning on the optimum condition. Photocatalyst in this experiment is prepared by using TiAcAc precursor by using sol-gel method. Sol with varies composition of PEG and SiO2 addition then coated in soda lime plate and ceramics as support by using spin coating method and spray coating method then dried in 100_C and calcined until 520_C. After the preparation, then catalyst has been characterized using FTIR, DRS and TEM.

Activity test was also done to know self-cleaning and anti fogging performance of this material by using contact angle meter and by direct observation using digital camera. Development of nanomaterial with sol-gel method and hot crystallization and the addition of dopan PEG and SIO2 is quite success according to DRS result that shows the increasing of band gap, the decrease of particle size from TEM result and also the decrease of contact angle. These results are supported also from qualitative test which showed antifogging and self-cleaning activity of catalyst coated glass. Variation of Tiacac/H2O showed the result tends to the decrease of activity. From this research, we find also variation of PEG molecular weight does not give a lot of effects for catalyst activity."

"Pelapisan TiO2 pada permukaan keramik dengan metode spray coating serta uji kekuatan mekanik telah dilakukan. Uji kekuatan mekanik ini terdiri dari : ketahanan abrasi, ketahanan asam-basa, dan uji kelicinan (sliperness). TiO2 yang dilapiskan pada keramik menghasilkan ketahanan abrasi dan ketahanan asam-basa yang memenuhi standar.

Hasil uji kelicinan (sliperness) menunjukkan bahwa keramik yang dilapisi TiO2 memiliki nilai kelicinan yang masih memenuhi syarat keamanan yang ditetapkan sedangkan untuk pengujian matching color hasil yang diperoleh menunjukkan bahwa semakin besar konsentrasi larutan TiO2 yang digunakan untuk melapisi keramik maka penampakan warnanya tidak memenuhi standar. Efek self cleaning pada keramik cukup baik tetapi kurang optimal karena kristal TiO2 yang diperoleh adalah rutile.

---

TiO2 was coated onto ceramics surface using spray coating method, and the mechanical strength was tested. The mechanical strength test consist of : abrasion test, acid-base test, and sliperness test. TiO2 which had coated on ceramics surface fulfill the requirements needed for abrasion and acid-base test.

The result of sliperness test showed that ceramics which had coated with TiO2 fulfill the standard safety requirements. Matching color test showed that the increasing in TiO2 concentration used for ceramics coating had made color differences that didn't met the standard. Self cleaning effect of the ceramics was good enough but didn't gave the optimum performance because the TiO2 formed a rutile crystal."

"Teknologi fotokatalis TiO2 terus mengalami perkembangan dari waktu ke waktu dan banyak dimanfaatkan dalam berbagai macam aplikasi. Salah satu bentuk pemanfaatan fotokatalis TiO2 adalah sebagai material anti kabut dan swa bersih. Dengan sifat hidrofilik yang dmiliki material ini, tetesan air yang jatuh ke permukaan yang dilapisi katalis TiO2 tidak membentuk butiran melainkan terdispersi sehingga mampu mencegah terbentuknya kabut yang menghalangi visualisasi pada kaca. Selain itu, sifat super-hidrofilik pada TiO2 dapat menyebabkan kotoran yang menempel pada permukaan kaca yang dilapisi TiO2 akan terdegradasi dan dapat dibersihkan dengan lebih mudah. Untuk dapat meningkatkan performa dari katalis, dilakukan penambahan beberapa jenis aditif ke dalam fotokatalis TiO2. PEG (polyethylene glycol) adalah salah satu jenis aditif yang sering digunakan karena diyakini mampu meningkatkan porositas, memperkecil ukuran kristal serta menurunkan kemungkinan terjadinya peretakan (cracking) film saat proses kalsinasi. Selain PEG, SiO2 juga diyakini mampu meningkatkan keasaman dari katalis sehingga mampu meningkatkan hidrofilisitas dari katalis meskipun pada kondisi kurang cahaya. Pada percobaan ini, kedua macam aditif ini digunakan secara simultan untuk dapat memperbaiki performa dari katalis film yang dihasilkan. Fotokatalis dalam percobaan ini dipreparasi dengan precursor TiAcAc dengan metode sol-gel dan kristalisasi panas. Sol dengan penambahan PEG dan SiO2 yang bervariasi kemudian dilapiskan pada penyangga kaca preparat dan keramik dengan metode spin coating yang dilanjutkan dengan pemanasan pada suhu 100_C dan kalsinasi mencapai suhu 520_C. Selanjutnya untuk mengetahui hasil dari preparasi katalis ini akan dilakukan karakterisasi dengan XRD, SEM/EDAX , FTIR, dan BET untuk mengetahui karakteristik fotokatalis yang terbentuk. Uji aktivitas juga dilakukan untuk mengetahui kemampuan swa bersih dan anti kabut dari material yang dihasilkan yang meliputi pengukuran sudut kontak dengan alat contact angle meter dan pengamatan langsung dengan menggunakan kamera digital. Dari hasil karakterisasi dan uji aktivitas, didapatkan kondisi optimum yang mendukung untuk aplikasi swa bersih dan anti kabut ini adalah komposisi penambahan PEG 15% dan SiO2 30% berat. Pada komposisi ini didapati bahwa material memiliki luas permukaan, ukuran partikel, porositas, aktivitas serta hidrofilisitas yang baik yang mendukung untuk aplikasi swa bersih dan anti kabut.

---

Photocatalyst technology of TiO2 has been developing and employed in many applications. One of its applications is used as self-cleaning and anti fogging material. The hydrophilic and superhydrophilic properties of its material allow water to spread completely across the surface rather than remaining as droplets so it can perform selfcleaning and anti-fogging effect. To improve performance of its material, some additives have been added to TiO2 photocatalyst. PEG (polyethylene glycol) is polymer that widely used as an additive because it can increase porosity, minimize particle size and prevent film cracking during calcination. SiO2 with its acidity also widely used as additive because it can increase hydrophilicity of TiO2 material even in dark place. In this experiment, these additives will be used simultaneously to get the better performance of catalyst.

Photocatalyst in this experiment is prepared by using TiAcAc precursor by using solgel method. Sol with varies composition of PEG and SiO2 addition then coated in soda lime plate and ceramics as support by using spin coating method then dried in 100_C and calcined until 520_C. After the preparation, then catalyst has been characterized using XRD, SEM/EDAX, FTIR, and BET to know the character of material. Activity test also done to know self-cleaning and anti fogging performance of this material by using contact angle meter and by direct observation using digital camera. From characterization and activity test results, it found that optimum condition of PEG and SiO2 addition is reached in PEG 15% and SiO2 30% (weight). In this composition, its material has large surface area, particle size, porosity and hydrophilicity that support for self-cleaning and anti fogging application."

"Titanium dioksida merupakan material yang banyak digunakan pada berbagai aplikasi seperti pigmen pemutih pada cat, kosmetik, sel surya, sensor gas dan lapisan tipis pembersih mandiri (self cleaning). Pada aplikasi lapisan tipis self cleaning, efek fotokatalisis dan hidrofilisitas memainkan peranan penting. Efektifitas kedua proses ini bergantung pada besar ukuran dan tingkat kristalinitas partikelnya. Walaupun koloid partikel nano (TiO2) sudah beredar secara komersil, namun kedua hal di atas yaitu ukuran kecil dan kristalin tetap menjadi suatu tantangan hingga saat ini. Oleh karena itu, tujuan utama penelitian ini adalah mendapatkan partikel berukuran kecil, terdistribusi seragam dan tingkat kristalinitas yang tinggi. Untuk merealisasikan hal ini, telah dilakukan sintesis partikel nano TiO2 dengan metode sol-gel, kemudian dilanjutkan proses anil dan hidrotermal. Karakterisasi XRD dilakukan untuk mengukur kristalinitas, sedangkan aktifitas hidrofilisitas diukur berdasarkan besarnya sudut kontak di atas substrat kaca yang telah dilapisi TiO2. Dari hasil yang didapat, metode hidrotermal menghasilkan produk dengan tingkat kristalinitas lebih tinggi dibanding dengan anil konvensional. Sampel hasil hidrotermal memiki ukuran sebesar 8.16 nm sedangkan anil konvensional 3.16 nm. Sudut kontak yang dihasilkan sampel hidrotermal sebesar 13.00Û sedangkan sampel anil konvensional sebesar 26.83Û. Hasil pada sampel hidrotermal terkait dengan lebih banyaknya jumlah elektron-lubang yang dihasilkan sehingga berpengaruh pada penyerapan air secara fisik dan pembasahan.

---

Titanium dioxide is a material that is widely used in various applications such as paint pigment, cosmetics, solar cells, gas sensors and self-cleaning thin film. For self-cleaning film, photocatalysis and hydrophilicity effects play an important role. Effectiveness of this process depends both on the large size and the crystallinity level of particle. Though colloidal nanoparticles (TiO2) are commercially available in market, but both aspects i.e., size small and high nanocrystallinity remains a big challenge up to the present. Therefore, the main goal of this research is to obtain the small-sized nanoparticles, which are uniformly distributed and have high level of nanocrystallinity.

In order to realize this, a synthesis was carried out for TiO2 nanoparticles using the sol-gel method, and then followed with thermal annealing and hydrothermal. XRD characterization was performed to measure the crystallinity, while hydrophilic activity was evaluated by Face Contact Angle Meter to measure contact angle of water droplet on TiO2 coated glass substrates.

On the basis of results obtained, the hydrothermal provide samples with higher crystallinity in comparison to that of conventional annealing. The crystallite size of hydrothermally treated samples is 8.16 nm where the conventionally annealed samples can only provide an average size of 3.16 nm. The contact angle of the former is 13.00_, where the latter can only provide contact angle of 26.83_. The results obtained on hydrothermally treated samples can be associated with higher number of electron-holes which are responsible for the physical absorption of water and related wetting mechanism."

"ABSTRAKPengembangan kain nilon swabersih dan swasteril berbasis fotokatalisismenggunakan film Ag ? TiO2 ? Aerosil telah dilakukan dengan cara melapiskansol titania dengan penambahan dopan Perak (Ag) dan Aerosil dengan variasitertentu. Aerosil digunakan sebagai aditif untuk menempelkan titania pada kainnilon. Komposisi aerosil yang optimal baik dari segi morfologi film maupunkemampuan fotokatalisis dalam mendegradasi rhodamin B sebesar 10%.Komposisi dopan perak (Ag) yang terbaik untuk mendesinfeksi bakteriEscherichia coli sebesar 1%. Komposisi komposit Ag : Aerosil : TiO2 yang palingoptimal adalah dengan rasio berat 1 : 10 : 100.

---

AbstractDevelopment of Self-Cleaning and Self-Sterile Nylon Based on Photo CatalyticUsing Ag ? TiO2 ? Aerosil Film has been done by coating titanium film withsilver and aerosil as additive in certain variation. Aerosil was used as an additivefor keeping titanium on nylon fabric. Optimum composition of aerosil in termsboth film morphology and ability to degrading organic compounds rhodamin Bphoto catalytically was about 10%. Optimum composition of silver (Ag) todisinfect Escherichia coli bacteria was about 1%. Optimum weight ratiocomposition of Ag : Aerosil : TiO2 composite was 1 : 10: 100."

"Pembuatan TiO2 nanotube telah berhasil dilakukan. TiO2 nanotube dihasilkan dari proses anodisasi plat Ti dalam larutan elektrolit garam flourida dalam etilen glikol. Proses anodisasi dilakukan dengan menggunakan potensial 40 V selama 1 jam. TiO2 nanotube yang terbentuk kemudian didispersikan dalam larutan hidrogen peroksida, sehingga membentuk koloid TiO2. Penggunaan koloid TiO2 salah satunya adalah untuk melapisi TiO2 pada permukaan bahan agar memiliki kemampuan self cleaning. Pelapisan TiO2 pada kain dan kaca telah berhasil dilakukan. Pelapisan TiO2 pada kain diperlukan penambahan spacer kimia dan perendaman kain dalam koloid TiO2. Pada pelapisan permukaan kaca dengan TiO2 dilakukan dengan cara penetesan koloid TiO2 pada permukaan kaca. Permukaan bahan yang telah dilapisi TiO2 dikarakterisasi dengan menggunakan SEM, UV-Vis DRS, FTIR, dan Contact Angle Meter. Setelah terlapisi dengan TiO2 permukaan kain kaca diuji kemampuan self cleaning dengan menggunakan zat warna Rhodamin B. Telah didapatkan hasil pengujian aktivitas fotokatalis dari kain dan kaca yang telah terlapisi TiO2 dengan menggunakan iluminasi sinar matahari dan sinar UV. Kain yang telah terlapis TiO2 dapat mendegradasi zat warna sebesar 60,67% dengan iluminasi sinar UV selama 100 menit dan sebesar 75,63 % dengan iluminasi sinar matahari selama 180 menit. Kaca yang telah terlapis TiO2 dapat mendegradasi zat warna sebesar 53,01% dengan iluminasi sinar UV selama 60 menit, tidak terdeteksi pada 80 dan 100 menit dan sebesar 39,65% dengan iluminasi sinar matahari selama 20 menit, tidak terdeteksi pada 40, 60, 80 dan 100 menit.

---

Preparation of TiO2 nanotubes have been successfully carried out. The TiO2 nanotubes were produced by anodizing Ti plate in proper electrolyte solution. Anodizing process is performed by using a potential of 40 V for 1 hour. The formed TiO2 nanotubes were then dispersed in the water containing hydrogen peroxide, to obtain TiO2 colloidal. The water base colloidal of TiO2 then was applied to prepare a cloth/fabric and glass those have a self cleaning property. TiO2 coating on the fabric required the addition of a chemical spacer and soaking fabrics in TiO2 suspension.

While surface coating of the glass with TiO2 done by dripping of glass surface in the colloidal of TiO2. The materials those have been coated with TiO2 the were characterized by using SEM, UV-Vis DRS, FTIR, and Contact Angle Meter. In addition the TiO2 coated glass fabric was tested its self-cleaning ability by using Rhodamine B dyes, under illumination of sunlight and UV rays.

The test result of cloth/fabric which has been coated TiO2 showed that under UV light illumination for 100 minutes, it can degrade the dye by 60,67%, while under with sunlight illumination for 180 minutes can degrade up 75,63%. For the glass that has been coated with TiO2, the test showed that, under illumination of UV light for 60 minutes, it can degrade 53,01% of the dye, not detected for 80 and 100 minutes and under illumination of the sunlight for 20 minutes can degrade 39,65% of the dyes, not detected for 40,60,80 and 100 minutes."

"Katun merupakan salah satu bahan pakaian yang umumnya sering ditemui dan digunakan. Pembersihan katun dari kotoran yang menempel memerlukan usaha dan biaya. Titanium dioksida (TiO2) menjadi salah satu bahan yang sering dan ekstensif dipelajari sebagai bahan swabersih, self-cleaning. Namun, pelapisan TiO2 secara langsung pada katun menghasilkan tingkat keberhasilan pelapisan yang rendah. Diperlukan spacer, yaitu bahan kimia (gugus fungsi) yang dicangkokkan kepada rantai selulosa pada katun untuk membantu pengikatan TiO2. Lapisan TiO2 pada permukaan katun akan membuat katun menjadi material yang memiliki kemampuan membersihkan diri sendiri (self-cleaning). Sebelum pelapisan, kain katun dipotong sebesar 3x3 cm dan di treatment menggunakan H2O2 10 %, NaOH 1 M, dan ammonia pekat. Pelapisan dilakukan menggunakan asam suksinat sebagai spacer dan suspensi TiO2 dengan cara dip coating. UV-VIS DRS, FT-IR, SEM, pengukuran sudut kontak air dilakukan untuk mengkarakterisasi permukaan katun yang dilapisi oleh TiO2. Permukaan katun yang telah berhasil dilapisi TiO2 ditandai oleh kemunculan indikasi band gap optis sebesar 3,43 eV; dan keberadaan puncak serapan IR pada daerah bilangan gelombang 676 cm-1 (indikasi adanya ~Ti-O-Ti~). Hasil SEM menunjukkan morfologi permukaan katun yang menunjukkan adanya lapisan TiO2 yang menempel. Sudut kontak yang didapat pada keadaan gelap sebesar 108, 48o dan pada saat diiiluminasi dengan lampu UV selama 150 detik sebesar 9,505o, yang menunjukkan permukaan katun memiliki sifat ampifilik. Katun yang dilapisi oleh TiO2 mampu mendegradasi senyawa methylene blue hingga 94.34 % dalam keadaan diiiluminasi dengan lampu UV selama 100 menit dan 86.5 % dalam keadaan diiiluminasi dengan sinar matahari selama 6 jam.

---

Cotton is one of the most common Clothing found and used. Cleaning of the dirt cotton requires more effort and expense. Titanium dioxide (TiO2) became one of the ingredients that often and extensively studied as self-cleaning materials. However, TiO2 coating directly on cotton have low success rate. Required spacer, namely chemical (functional group) is grafted to the cellulose chains in cotton to help the binding of TiO2. TiO2 layer on the surface of cotton into cotton will make a material that has the ability to clean it yourself (self-cleaning. Before coating, cotton cut by 3x3 cm and treatment using 10 % H2O2, 1 M NaOH, and concentrated ammonia. Coatings using succinic acid as a spacer and TiO2 suspension by dip coating technique. UV - VIS DRS, FT - IR, SEM, contact angle measurements were performed to characterize the surface of cotton coated by TiO2. Surfaces coated cotton that has been successfully characterized by the TiO2 band gap of 3.43 eV and the existence of the IR absorption peaks at wavenumber region 676 cm-1 (indicative of the presence of ~ Ti - O - Ti ~). SEM results showed that cotton surface morphology indicates that TiO2 layer attached. Contact angle obtained in the dark at 108, 48o and when illuminated with UV light for 150 seconds at 9.505 °, which shows the surface of cotton has amphiphilic properties. Cotton coated with TiO2 able to degrade compounds up to 94.34 % methylene blue in illuminated with UV light for 100 minutes and 86.5 % when illuminated by sunlight for 6 hours."

"Pembuatan suspensi koloidal TiO2 nanotube berhasil dilakukan melalui. proses anodisasi plat Ti menggunakan metode Free Standing. Proses anodisasi dilakukan dengan menggunakan potensial 40 V selama 1 jam dan menggunakan larutan elektrolit garam flourida dalam etilen glikol. TiO2 nanotube yang terbentuk kemudian didispersikan dalam larutan hidrogen peroksida, untuk kemudian diresuspensi kembali sehingga membentuk koloid TiO2 berbasis medium air. Hasil karakterisasi koloid menggunakan PSA menyatakan bahwa ukuran partikel TiO2 dalam koloid sebesar 111,4 nm, dan hasil karakterisasi menggunakan UV-Vis menyatakan bahwa koloid bersifat stabil dalam waktu 3 minggu. Penggunaan koloid TiO2 berbasis medium air salah satunya adalah untuk melapisi TiO2 pada permukaan bahan agar memiliki kemampuan swabersih. Pelapisan TiO2 pada kaca telah berhasil dilakukan. Pelapisan permukaan kaca dengan TiO2 dilakukan dengan melapiskan koloid TiO2 secara spray coating. Pelapisan dilakukan dengan memvariasikan jumlah semprotan yaitu 5, 10, 15, 20, dan 25 semprotan. Permukaan kaca yang telah dilapisi TiO2 dikarakterisasi dengan menggunakan SEM, UV-Vis DRS, FTIR, dan Contact Angle Meter. Diperoleh kaca dengan jumlah pelapisan paling optimal yaitu 20 kali semprotan, dengan nilai sudut kontak sebesar 7,82o dan persen loading sebesar 9,6x10-5 gram/cm2. Setelah terlapisi dengan TiO2 permukaan kaca diuji kemampuan swa bersih dengan menggunakan zat warna Rhodamin B. Telah didapatkan hasil pengujian aktivitas fotokatalis dari kain dan kaca yang telah terlapisi TiO2 dengan menggunakan iluminasi sinar matahari dan sinar UV. Kaca yang telah terlapis TiO2 dapat mendegradasi zat warna sebesar 33,62% dengan iluminasi sinar UV selama 30 menit. Dan kaca yang diiluminasi dengan sinar matahari mampu mendegradasi zat warna sebesar 81,42% selama 30 menit. Semakin lama waktu penyinaran, semakin banyak zat warna yang terdegradasi.

---

The preparation of TiO2 nanotube colloidal suspension was successfully conducted via a free standing anodization process of Ti plate. The anodization process was conducted in electrolyte solution of fluoride salt in ethylene glycol, under 40 V bias potential for one hour. The TiO2 nanotube formed was then dispersed in hydrogen peroxide solution, in order to be resuspended later to form water based TiO2 colloid. The characterization result of the colloidal suspension using PSA instrument, showed that the particle size of TiO2 in the colloid was 111,4 nm. Another characterization result of the colloid using UV-Vis spectrophotometer, showed that the colloid was stable for three weeks. The prepared water based TiO2 colloidal was applied for TiO2 coating on a certain material surface that enables the material to have self-cleaning ability. Coating of TiO2 on to glass surface was successfully conducted in this experiment. The coating of glass surface with TiO2, was conducted by spray coating the TiO2.

The coating was done by varying the number of sprays from 5, 10, 15, 20, and 25 sprays. The glass layer that has been coated by TiO2, was characterized using SEM, UV-Vis DRS, FTIR, and Contact Angle Meter. The optimal TiO2 coating of glass surface was found to be 20 sprays of the TiO2 colloid, with it?s angular contact value of 7,82o and it?s loading percentage of 9,6x10-5 gram/cm2. After the glass surface was coated with TiO2, the self-cleaning ability of the glass surface was tested using a Rhodamin B dyes sunlight illumination and UV light illumination. The TiO2 coated glass was able to degrade 33,62% of the coloring material under UV light illumination, for 30 minutes. While, the TiO2 coated glass was able to degrade 81,42% of the coloring material under sunlight illumination, for 30 minutes. The longer the time of illumination, the amount of coloring material degraded is higher."