"Analisis Struktur kristal paduan La0.67Ca0.33Mn1-xTixO3 telah dilakukan sintesis dan karaketrisasi paduan La0.67Ca0.33Mn1-xTixO3 (x=0.02 ; x=0.04 ;x=0.06 ;x=0.08 x=0.10 ;x=0.12 ).Sintesa bahan menggunakan metode reaksi padatan (solid state method) dari oksida-oksida penyusun La2O3,CaCO3,MnO2 dan TiO2.Campuran ini di milling selama 5jam ,15 jam dan 25 jam dan proses pemanasan dengan variasi suhu 1000°C, 1100°C dan1200 0C selama 12 jam. Hasil pengukuran dengan difraksi sinar-X (XRD)menunjukkan bahwa sintesa bahan atau paduan La0.67Ca0.33Mn1-xTixO3 fasa tunggal(single phase) dengan struktur kristal Orthorombik, space group Pnma (No.62) dan parameter kisi untuk x=0,08sebagai berikut : a = 5,4786(4) Å; b = 7,7503(1) Å; c = 5,4837(6) Å.

---

Synthesis and characterization of the Giant Magnetoresistance on the La 0.67 Ca0.33Mn1-x Tix O3 compound have been perfomed .Synthesis on the La0.67Ca0.33Mn1-xTixO3 material use solid state method from compiling oxides of La2O3,CaCO3, MnO2 dan TiO2.This mixture milled during 5 hour,15 hour and 25 hour and sintered at 1000°C, 1100°C and 1200°C for 12 hour.

The result of XRay diffraction measurement show that the materials is single phase i.e La0.67Ca0.33Mn1-xTixO3 with the crystal structure of orthorhombic , space group is Pnma (No.62) and lattice parameter for x=0.008 are a = 5,4786(4) Å; b = 7,7503(1) Å; c = 5,4837(6) Å."

"Telah dilakukan penelitian pengaruh doping Ag terhadap sifat listrik dan efek magnetoresistansi material La0,8-xAgxCa0,2MnO3 x = 0; 0,05; 0,1; 0,15. Material disintesis dengan metode sol-gel dan disintering pada temperatur 900 oC selama 24 jam. Material lanthanum manganit telah banyak diteliti karena memiliki sifat-sifat yang menarik, baik dalam segi struktural, sifat listrik, serta sifat magnet nya. Struktur material dikarakterisasi menggunakan Difraksi Sinar-X XRD dan menunjukkan bahwa pada doping x = 0 dan 0,05, material memiliki fase tunggal single phase yaitu fase manganite, sedangkan pada doping x = 0,1 dan 0,15, material terdiri dari fasa campuran, yaitu fasa manganite dan Ag. Scanning Electron Microscopy SEM digunakan untuk observasi morfologi serta menunjukkan kehomogenan material. Dengan doping Ag, ukuran grain boundary dari material membesar. Hasil karakterisasi dari Electron Dispersive Spectroscopy EDS mengkonfirmasi keberadaan unsur Ag pada material. Karakterisasi menggunakan Cryogenic Magnetometer dilakukan untuk menguji sifat listrik dari material seiring dengan peningkatan doping Ag. Seiring dengan peningkatan konsentrasi doping Ag, resistivitas material mengecil serta temperatur transisi metal-isolator TMI bergeser kearah temperatur ruang. Efek magnetoresistansi menurun saat doping x = 0,05 dan meningkat kembali saat x = 0,1 dan 0,15.

---

The research about effect of dopant Ag on electrical and magnetoresistance properties of La0,8 xAgxCa0,2MnO3 x 0 0,05 0,1 0,15 has been done. The materials were synthesized via sol gel method, sintered at temperature 900oC for 24 hours. Lanthanum manganite material has been widely investigated because its interesting properties, such as physical, electrical, and magnetic properties.

The structural of the materials were characterized using X Ray Diffraction XRD, show in doping x 0 and 0,05, material has single phase manganite phase, whereas in doping x 0,1 and 0,15, material consists of mixed phases, manganite and Ag phases. Scanning Electron Microscopy SEM was used to observe morphology of the materials and showed homogeneity of the materials. By doping Ag, grain boundary size of the material increase.

Electron Dispersive Spectroscopy EDS result confirmed existence of Ag in the material and the materials having desired composition. Characterization using Cryogenic Magnetometer was used to examined electrical property of the materials with increasing of Ag doping. As the Ag doping concentration increases, resistivity of the material decreases and the metal isolator transition temperature TMI shifts towards room temperature. Magnetoresistance effect decreases when doping x 0,05 and increase again when doping x 0,1 and 0,15."

"ABSTRAKUntuk memperoleh informasi yang akurat mengenai posisi data yang diambil dibawah permukan air laut Maka diperlukan posisi kedalaman air wahana dan arah wahana terhadap kutub utara. Informasi ini penting karena dengan digabungkan dengan panjang tali alat maka dapat diperoleh panjang alat secara garis lurus dari GPS di kapal. Alat ini mengubah tekanan air yang diterimanya menjadi perubahan tahanan. Selanjutnya diumpankan tegangan ekstisasi pada sensor tersebut, dimana akan keluar tegangan yang besarnya sebanding dengan kedalaman air laut. Dengan sensor tekanan ke tahanan piezoresistive yang mampu mengukur sampai kedalaman 200 meter dengan keluaran tegangan sampai 2,5 volt. Dengan menggunakan mikrokontroler serial 80 dari Ateml sinyal analog tadi diubah ke sinyal digital 11 bit sehingga mampu mengukur sampai ketelitian 9,77 cm kedalaman. Tegangan ini kemudian diolah oleh rangkaian elektronik sehingga hasil akhirnya berupa petunjuk kedalaman dalam bentuk display dan data serial.Demikian juga dengan arah kompas, medan magnet bumi mengubah tahanan dari bahan permaloy menjadi berubah tergantung besarnya medan magnet yang diterima oleh bahan tersebut, bahan disusun menjadi konfigurasi jembatan wheatstone untuk kemudian diberi tegangan eksitasi seperti susunan sebelumnya pada sensor kedalaman, keluaran dari sensor ini berupa lebar pulsa dimana besarnya sudut azimuth berbanding lurus dengan lebar pulsa yang dihasilkan. Lebar pulsa ini kemudian dihitung dengan perbandingan terkecil sampai terendah berpadanan dengan sudut 0 derajat sampai 360 derajat"

"Sampel La0,5Ba0,5Mn1-xTixO3 dengan x = 0 ; 0.05 ; 0.10 dan 0.15 dari bahan dasar La2O3, BaCO3, MnCO3, dan TiO2 disentesis dengan menggunakan metode mechanical alloying. Keempat bahan dasar tersebut dicampur dengan menggunakan Planetary Ball Milling selama 25 jam, dikompaksi, kalsinasi pada suhu 8000C selama 10 jam dan disintering pada suhu 12000C selama 12 jam. Identifikasi fasa dilakukan dengan menggunakan difraksi sinar X dan refinement GSAS dan diperoleh sampel La0,5Ba0,5Mn1-xTixO3 single phase untuk semua komposisi x, yang memiliki struktur kristal Monoklinik. Pengukuran terhadap nilai konduktivitas dan magnetoresistansi (MR) sampel diukur menggunakan Four Point Probe (FPP), sedangkan nilai magnetisasinya diukur menggunakan permagraph. Berdasarkan hasil pengukuran tersebut disimpulkan bahwa semakin besar doping Ti yang diberikan pada sampel La0,5Ba0,5Mn1-xTixO3 membuat nilai magnetisasi dan konduktivitas sampel semakin menurun. Nilai negatif magnetoresistansi sampel pada umumnya mengalami penurunan. Untuk x = 0.15 nilai negatif magnetoresistansi sampel paling besar yaitu 4,26%. Penurunan nilai magnetisasi dan konduktivitas sampel seiring bertambahnya komposisi x yang diberikan, karena adanya kompetisi exchange interaction yang terjadi pada sistem, yaitu adanya interaksi Double Exchange (DE). Interaksi Double Exchange (DE) terjadi antara ion Mn3+-O-Mn4+ yang saling berdekatan.

---

La0,5Ba0,5Mn1-xTixO3 sample with concentration x = 0 ; 0.05 ; 0.10 ; and 0.15of La2O3, BaCO3, MnCO3, and TiO2 are synthesized using mechanical alloying. The fourth of basic matter are mixed with using Planetary Ball Milling during 25 hours, compacted, calcinations on 8000C during 10 hours and sinter at 12000C during 12 hours. Phase identification is carried out using X ray diffraction and GSAS refinement, getting La0,5Ba0,5Mn1-xTixO3 which single phase for all x composition, that have Monoklinik crystal structure. Conductivity and magnetoresistance (MR) are measured using Four Point Probe (FPP), while magnetization is measured using permagraph.

From the measurement we get that the bigger Ti doping the more magnetization and conductivity is decreases. For negative magnetoresistance generally is increase, the biggest negative magnetoresistance is 4,26% for x = 0.15. The decreases of magnetization and conductivity sample with increasing composition x is given, due to there were competition exchange interaction in the system, that is interaction Double Exchange (DE). interaction Double Exchange (DE) happened between Mn3+-OMn 4+ ion adjacent to each other."

"Sampel La0,67Ba0,33Mn1-xTixO3 dengan x = 0; 0,02; 0,04 dan 0,06 dari bahan dasar La2O3, BaCO3, MnCO3, dan TiO2 disentesis dengan menggunakan metode mechanical alloying. Identifikasi fasa dilakukan dengan menggunakan difraksi sinar X dan refinement GSAS diperoleh single phase dengan struktur kristal monoklinik. Pengukuran terhadap nilai resistansi dan magnetoresistansi (MR) sampel diukur menggunakan Four Point Probe (FPP) sedangkan nilai magnetisasi diukur menggunakan permagraph. Berdasarkan hasil pengukuran pemagraph didapatkan La0,67Ba0,33Mn1-xTixO3 bersifat soft magnetik dan penambahan Ti menurunkan nilai magnetisasi. Berdasarkan hasil pengukuran FPP nilai resistansi meningkat seiring penambahan Ti. Nilai magnetoresistansi sampel pada umumnya mengalami penurunan kecuali pada x= 0,06. Untuk x=0 rasio magnetoresistansi paling besar yaitu -3,437 % pada temperatur ruang. Penambahan Ti menyebabkan rasio ion Mn4+ berkurang tersubtitusi ion Ti4+ terjadi pelemahan interaksi Double Exchange sehingga meningkatkan nilai resistansi dan menurunkan rasio magnetoresistansi.

---

Perovskite compounds La0,63Ba0,33Mn1-xTixO3 with composition x = 0 ; 0,02 ; 0,04 and 0,06 were made by synthesizing the basic materials La2O3, MnCO3, BaCO3, and TiO2 by mechanical alloying methods. This four basic ingredients are mixed using Vibrating Ball Milling for 10 hours, calcined at 800oC temperature for 10 hours, in compacting, and sintering at 1100oC temperature for 12 hours. Then be indentified by X-Ray difraction phase and GSAS refinement and obtained sample La0,67Ba0,33Mn1-xTixO3 single phase for all composition x, which has monoclinic crystal structure. magnetization measurements were conducted with pemagraph, while the Four Point Probe (FPP) is performed to measure the value of resistance and magnetoresistance (MR) in the sample. Based on the results of measurements obtained pemagraph La0, 67Ba0, 33Mn1- xTixO3 are soft-magnetic and the addition of Ti lowers the value of the magnetization.

Based on the measurement results FPP the resistance value increases with the addition of Ti. Sample magnetoresistance values generally decreased except for x=0,06. For x = 0 the large magnetoresistance ratio is -3.437% at room temperature . The addition of Ti causes Mn4 + ion ratio decreases substituted Ti4+ ions weakening Double Exchange interaction thus increasing resistance and lowering the value of magnetoresistance ratio."

"ABSTRAKPenelitian struktur domain ferromagnet berbentuk kubus telah dilakukan dengansimulasi mikromagnetik OOMMF, berdasarkan persamaan Landau-Lifshitz-Gilbert. Dalam penelitian ini telah dilakukan pengamatan dinamika strukturdomain pada material feromagnet Permalloy (Py), Nickel (Ni), Besi (Fe), danKobalt (Co) berbentuk nanocubes (kubus) dengan variasi panjang sisi dari ukuran20 nm sampai dengan 100 nm, ukuran sel 2,5 × 2,5 × 2,5 􀝊􀝉ଷ, dan faktordamping α = 0,1. Suhu sistem adalah 0 kelvin. Proses simulasi mikromagnetik inidilakukan dalam dua bagian, (1) pengamatan struktur domain pada keadaanmedan eksternal nol, dan (2) diberi medan magnet eksternal. Bagian pertama,difokuskan pada pengamatan struktur domain dan energi sistem mikromagnetikpada kedaan tanpa medan magnet eksternal atau ground state. Dari hasilpengamatan, diperoleh bahwa terjadi transisi struktur domain dari domain tunggal(single-domain/SD) menjadi struktur vortex-wall (VW) yang berhubungan dengandiameter kritis atau panjang sisi kritis. Di bawah panjang sisi kritis, strukturdomain yang terbentuk adalah SD, sedangkan struktur VW teramati di ataspanjang sisi kritis. Hasil simulasi mikromagnetik memperlihatkan bahwa panjangsisi kritis mendekati prediksi teori. Selanjutnya dianalisis energi sistemmikromagnetik berhubungan dengan transisi struktur domain. Menariknya, padadaerah transisi terjadi perubahan energi demagnetisasi dan energi exchange.Dibawah panjang sisi kritis, energi demagnetisasi lebih besar daripada energiexchange. Berikutnya, energi exchange mengalami kenaikan di atas panjang sisikritis. Bagian kedua, dilakukan pengamatan jika material diberi medan magneteksternal.Pada bagian ini, difokuskan untuk memperoleh data karakteristikmagnet; seperti kurva histeresis, medan koersivitas, magnetisasi remanen, medanpembalikan, medan nukleasi, dan waktu pembalikan. Dari analisis kurvahisteresis, diperoleh medan koersivitas menurun dengan meningkatnya panjangsisi kubus. Hasil ini sesuai dengan hasil eksperimen. Tentang medan pembalikan,berhubungan dengan besar medan magnet eksternal yang diperlukan untukmembalik dari keadaan saturasi ke keadaan saturasi berikutnya. Teramati bahwamedan pembalikan Co mempunyai nilai paling besar dibandingkan Py, Fe, dan Ni,serta meningkat dengan bertambahnya panjang sisi kubus. Hal yang sangatmenarik, struktur domain dan profil energi pada keadaan remanen mirip dengankeadaan ground state. Hasil ini memperlihatkan bahwa feromagnetik nanocubesdapat dipertimbangkan dalam merealisasikan devais-devais berbasis magnet.

---

ABSTRACTWe have systematically investigated domain structures of ferromagneticnanocubes model by means of public micromagnetic simulation, OOMMF basedon Landau-Lifshitz-Gilbert equation. Materials used in the micromagneticsimulation consisted of Permalloy (Py), Nickel (Ni), Iron (Fe), and Cobalt (Co).Edge length of nanocubes were carried out from 20 nm to 100 nm with cell size2.5 × 2.5 × 2.5 􀝊􀝉ଷ and the damping constant was fixed ߙ= 0.1. Thetemperature system was fixed absolute zero temperature. The micromagneticinvestigation of domain structures, we separated in two part, (1) the investigationdomain structures in zero external field condition, and (2) applied magnetic field.First part, we have focused to domain structure and magnetization energy in zeroexternal field condition or ground state. From the observation, we found that thetransition of domain structure from a single-domain (SD) to a vortex-wallstructure (VW) was related to critical diameter (critical edge length). Below thecritical edge length, all the cases exhibited a SD structures while a VW structurewas found above the critical edge length. The micromagnetic simulation resultsshowed that the critical edge length agrees with the theoretical prediction.Furthermore, we have analyzed the magnetization energy systems corresponded tothe transition domain structure. Interestingly, the transition domain structure isshown by changing the demagnetization and exchange energy. Below the criticaledge length, the magnetization energy was dominated by the demagnetizationenergy rather than exchange energy. Then, the exchange energy startly dominatedabove the critical edge length. Second part, we investigated the dynamics domainstructure with applied the external field. In this, we focused to find the magneticproperties; such as hysteresis loops, coercivity field, remanent magnetization,switching field, nucleation field, and switching time. From analyzing thehysteresis loops, we found that the coercivity field decreased as the diameterincreased. This results in agreement with the experiment results. Concern to theswitching field, the magnitude of applied field to switch from one saturation toanother saturation. We found that the switching field of Co the largest ofswitching field with respect to diameter. Mostly interesting, the domain structuressimilarly exhibited to the ground state condition at the remanent state as well asthe magnetization energy profiles. We concluded that behavior in ferromagneticnanocubes may allow us to consider in a practical design of magnetic recordingdevices."

"Paduan senyawa perovskite La0,85Ba0,15Mn1-xTixO3 dengan komposisi x = 0,0; 0,1; 0,15; dan 0,2 dibuat dengan mensintesis bahan dasar La2O3, MnCO3, BaCO3, dan TiO2 dengan metode Mechanical Alloying. Keempat bahan dasar tersebut dicampur dengan menggunakan Planetary Ball Milling selama 25 jam, dikalsinasi dengan suhu 800oC selama 10 jam, dikompaksi, dan di sintering dengan suhu 1200oC selama 12 jam. Kemudian dilakukan identifikasi fase dengan difraksi sinar X dan refinement GSAS dan diperoleh sampel La0,85Ba0,15Mn1-xTixO3 single phase untuk semua komposisi x, yang mempunyai struktur kristal monoklinik. Pengukuran magnetisasi sampel dilakukan dengan phermagraph, sedangkan Four Point Probe (FPP) dilakukan untuk mengukur nilai resistivitas dan magnetoresistansi (MR) pada sampel. Dari hasil Permagraph didapatkan kurva hyterisis yang menunjukkan bahwa pada saat sampel belum didoping Ti masih bisa termagnetisasi oleh medan magnet eksternal, tetapi setelah didoping Ti sifat magnetnya menjadi paramagnetik yang tidak dapat termagnetisasi. Sedangkan hasil pengukuran dengan FPP menunjukkan bahwa sampel mengalami penurunan resistivitas tetapi setelah mencapai medan magnet tertentu. Nilai rasio magnetoresistansi meningkat seiring dengan semakin besarnya medan magnet eksternal, tetapi menurun dengan bertambahnya doping Ti. Nilai Magnetoristansi terbesar pada saat x = 0 yaitu -3,44%.

---

Alloy perovskite compounds La0,85Ba0,15Mn1-xTixO3 with composition x = 0,0; 0,1; 0,15; and 0,2 were made by synthesizing the basic materials La2O3, MnCO3, BaCO3, and TiO2 by Mechanical Alloying methods. This four basic ingredients are mixed using Planetary Ball Milling for 25 hours, calcined at 800oC temperature for 10 hours, in compacting, and sintering at 1200oC temperature for 12 hours. Then be indentified by X-Ray difraction phase and GSAS refinement and obtained sample La0,85Ba0,15Mn1-xTixO3 single phase for all composition x, which has monoclinic cristal structure. Magnetization measurements were conducted with phermagraph, while the Four Point Probe (FPP) is performed to measure the value of resistivity and magnetoresistance (MR) in the sample.

From the results obtained Permagraph hyterisis curve which shows that when the Ti doped samples yet still be magnetized by an external magnetic field, but after the Ti doped the magnetic properties paramagnetic that can not be magnetized. While taking the measurements with FPP results indicate that the sample resistivity decreased but at a certain activation field. Magnetoresistance ratio also decreased but very small, with the largest negative magnetoresistance when x = 0 is -3.44%."