"Pada penelitian ini, telah dilakukan sintesis nanopartikel TiO2 melalu proses sol─gel dengan variasi rasio air terhadap prekursor (Rw) yaitu 0.85, 2.00 dan 3.50 selama proses formulasi yang kemudian diikuti perlakukan termal lanjut berupa pengeringan, anil dan pasca-hidrotermal. Karakterisasi XRD dilakukan untuk mengukur besar ukuran kristalit nanopartikel yang dihasilkan. Dari hasil perhitungan, metode pasca-hidrotermal menghasilkan produk dengan ukuran kristalit paling tinggi dibandingkan perlakukan anil dan pengeringan. Ukuran kristalit tertinggi dimiliki sampel Rw = 3.50 cair dengan besar ukuran kristalit 8,566 nm, diikuti Rw = 3.50 gel sebesar 7,614 nm, Rw = 2.00 sebesar 6,853 nm dan Rw = 0.85 sebesar 6,527 nm. Lebih jauh lagi, nanotube TiO2 difabrikasi melalui teknik hidrotermal dengan melarutkan nanopartikel TiO2 hasil perlakuan anil dan serbuk P-25 Degussa ke dalam larutan alkalin sodium hidroksida berkonsentrasi tinggi di dalam otoklaf tersegel. Detil struktur dan morfologi sampel diuji dengan SEM. Hasil investigasi menunjukkan bahwa nanopartikel dengan Rw = 2.00 berhasil dibuat menjadi nanotube dengan diameter 115─269 nm.

---

In this study, TiO2 nanoparticles was synthesized via sol−gel process with various water to inorganic precursor ratio (Rw) of 0.85, 2.00 and 3.50 upon sol preparation, followed with subsequent drying, conventional annealing and posthydrothermal treatments. The resulting nanoparticles were characterized using XRD to measure the crystallite size. On the basis of results obtained, the posthydrothermal resulted TiO2 samples with largest crystallite size in comparison to drying and annealing. The largest crystallite size of hydrothermally treated samples is Rw = 3.50 cair with 8,566 nm, followed by Rw = 3.50 gel with 7,614 nm, Rw = 2.00 with 6,853 nm and Rw = 0.85 with 6,527 nm. Furthermore, nanotube TiO2 have been fabricated through a hydrothermal technique where anneal treated nanopartikel TiO2 sol-gel and P-25 Degussa nanopowder was dissolved in highly concentrated alkaline solution of sodium hydroxide (NaOH) in a sealed autoclave. The detail of the structure and morphology of the resulting nanotubes were characterized using SEM. The result of investigation showed that nanoparticle with Rw = 2.00 can be fabricated became nanotubes with its diameter 155─269 nm."

"ZnO berbentuk batang nano dengan ukuran dan bentuk yang cukup seragam dibuat dengan membuat lapisan tipis dari benih nano ZnO sebagai bibit di atas kaca ITO TCO untuk dilakukan proses hidrothermal. Sampel dikarakterisasi dengan scanning electron microscopy (SEM). Benih nano disintesis dengan menggunakan zinc acetate dihydrate, 2-methoxyethanol dan ethanolamine. Larutan yang berisi benih nano di diamkan dalam waktu 2, 4, dan 6 hari, sehingga menghasilkan besar benih nano yang bervariasi dengan ukuran diameter rata-rata yaitu sebesar 82,33; 332,39; dan 1384,78 nm. Besar ukuran benih nano akan menentukan ukuran dan bentuk dari batang nano yang akan terbentuk setelah proses hidrothermal. Batang nano yang terbentuk dirakit menjadi rangkaian sel surya tersensitasi zat pewarna organik. Sel surya diuji coba untuk mengetahui tegangan terbuka yang dihasilkan dengan perbedaan ukuran batang nano yang berasal dari perbedaan waktu tahan pembuatan benih nano dan menghasilkan tegangan terbuka pada waktu penahanan larutan masing-masing 2, 4, dan 6 hari, yaitu sebesar 341,83; 270,93; dan 256,20 mV pada kondisi cahaya ruang, sedangkan 397,67; 486,03; dan 456,10 mV pada kondisi cahaya yang terfokus.

---

ZnO nanorod arrays with quite homogeneous size and shape were fabricated by applying ZnO seed-layer as nucleation on the ITO TCO glass to the hydrothermal reaction. The samples were characterized by scanning electron microscopy (SEM). Nanoseed were synthesized by using zinc acetate dihydrate, 2-methoxyethanol and ethanolamine. Solution that contains nanoseed were held 2,4, and 6 days until produced nanoseeds with different size and diameter of nanorod are 82,33; 332,39; dan 1384,78 nm . Nanoseed size determined the shape and size of nanorod that would be formed after the hidrothermal process. Dye sensitized solar cell were fabricated by using nanorod that were formed before. Dye sensitized solar cell were tested to examine the open circuit voltage that were produced by dye sensitized solar cell with different holding time of nanoseeds and produced open circuit voltage with each holding time of 2, 4, and 6 days, are 341,83; 270,93; and 256,20 mV respectively at room lightning, whereas at focused lightning, DSSC produced 397,67; 486,03; and 456,10 mV."

"Fabrikasi Dye-Sensitized Solar Cell (DSSC)menggunakan klorofil dan rhodamin B telah berhasil dilakukan.Bahan semikonduktor sebagai elektroda kerja dalam DSSC yang digunakan adalah TiO2nanotube yang ditumbuhkan pada plat titanium dengan teknik anodisasi, dilanjutkan dengan kalsinasi pada 500⁰C untuk membentuk fasa kristal TiO2. Karakterisasi terhadap Ti/TiO2-NT meliputi Field Emission Scanning Electron Microscope(FE-SEM), UV-VisDiffuse Reflectance Spectrometry (DRS), X-ray Diffraction (XRD), Fourier Transform Infra Red (FTIR), dan Linear Sweep Voltametry (LSV). Gambar FE-SEM menunjukkan bahwa TiO2 bermorfologi tube dengan diameter 88.99nm. Pola XRD menunjukkan puncak TiO2 anatase pada sudut 2θ: 25, 37,48,54, dan 55 derajat. Karakterisasi UV-Vis menunjukkan nilai bandgap TiO2 sebesar 3.24 eV. Spektrum FTIR menunjukkan keberadaan vibrasi ikatan ~Ti-O-Ti~. Kurva LSV menunjukkan bahwa TiO2 aktif pada daerah UV. Plat Ti/TiO2 dilapisi oleh zat warna melalui teknik elektroforesis dengan variasi waktu 8,10,12, dan 14 menit. Spektrum UV-Vis DRS dari TiO2 yang terlapisi zat warna menghasilkan puncak khas dari masing-masing zat warna, menunjukkan bahwa zat warna telah menempel pada TiO2. Pengujian terhadap performa DSSC menunjukkan nilai efiensi sebesar 0.3565% untuk Ti/TiO2-NT/Klorofil; 0.4351% untuk Ti/TiO2-NT/Rhodamin B; dan 0.3963% untuk Ti/TiO2-NT/Klorofil-Rhodamin B.Indonesia

---

Fabrication of Dye-Sensitized Solar Cell (DSSC) employing chlorophyll and rhodamine B has been successfully carried out. TiO2 nanotubes which was grown on titanium plate by an anodizationtechniques, followed by calcination at 500⁰C to form a crystalline phase of TiO2, was used as working electrode in the DSSC. Characterization of the Ti/TiO2-NT included Field Emission Scanning Electron Microscope (FE-SEM), UV-Vis Diffuse Reflectance Spectrometry (DRS), X-ray Diffraction (XRD), Fourier Transform Infra Red (FTIR), and Linear Sweep Voltametry (LSV). FE-SEM images showed the tube morphologies of TiO2 with a diameter of 88,99 nm. XRD pattern showed the TiO2 anatase peak at 2θ : 25, 37, 48, 54, dan 55 degree. UV-Vis DRS characterization revealed that the bandgap of the prepared TiO2is 3.24 eV. FTIR spectrum showed the presence of ~Ti?O-Ti~ vibration. LSV curves obtained indicate that the TiO2is active in the UV region . The Ti/TiO2 plate then was being coated with the dye through electrophoresis technique with time variation of 8, 10, 12, and 14 minutes. UV-Vis DRS spectrum of the dyes coated TiO2 showed that all typical dyes realted peaks were observed, indicate that the dyes was attached to the Ti/TiO2-NT. Performance tests of the assembled DSSC showed the efficiencies of 0.3565%for the Ti/TiO2-NT/Chlorophyll; 0.4351% for the Ti/TiO2-NT/Rhodamine B; and 0.3963% for the Ti/TiO2-NT/Chlorophyll/Rhodamine B respectively."

"Pada penelitian ini, sintesis dan karakterisasi dari nanomaterial aerogel titania (TiO2) untuk tujuan aplikasi sel surya tersensitasi zat pewarna (DSSC) telah dilakukan. Aerogel TiO2 dengan luas permukaan yang tinggi telah berhasil dipreparasi melalui dua tahapan: proses sol–gel dengan rasio hidrolisis (Rw) 2.00, diikuti oleh proses ekstraksi super kritis kontinu menggunakan CO2. Untuk tujuan perbandingan, xerogel juga disintesis dengan metode pengeringan biasa pada temperatur ruang. Metode kalsinasi bertahap digunakan untuk merubah kedua sampel menjadi anatase polikristalin dengan memanaskannya pada 1500C dan 3000C, masing-masing selama 3 jam di bawah pengaruh gas N2 dan melanjutkan hingga temperatur kalsinasi di 4200C selama 2 jam, di bawah tiupan gas oksigen. Karakterisasi dari aerogel dan xerogel didapatkan menggunakan DTA, BET, XRD, UV-vis DRS, dan FTIR. Kedua sampel diintegrasikan menjadi DSSC, yang pengukuran tegangan sirkuit terbukanya (Voc) dilakukan di bawah sinar putih menggunakan multimeter. Hasil penelitian menunjukkan aerogel yang dipreparasi memiliki luas permukaan yang lebih tinggi (1975 m2/g) dari xerogel (271 m2/g). Telah dibuktikan pula bahwa proses kalsinasi bertahap mampu meningkatkan ukuran kristalit dari aerogel hingga 9,21 nm dengan tetap mempertahankan luas permukaannya (71,90 m2/g) lebih tinggi dari xerogel (67,90 m2/g). Hasil pengukuran Voc menunjukkan tegangan terbuka yang lebih tinggi pada DSSC aerogel (21,40 mV) daripada DSSC xerogel (1,10 mV).

---

In this work, synthesis and characterization of nanomaterial titania (TiO2) aerogels for the purpose of dye-sensitized solar cells (DSSC) application have been performed. TiO2 aerogels with high surface area were succesfully prepared by two steps: sol–gel process with hydrolysis ratio (Rw) of 2.00, followed with continuous supercritical extraction with CO2. For comparison purposes, xerogels were also synthesized by conventional drying at room temperature. Multi-step calcination method was used to transform both samples to polycrystalline anatase by heating at 1500C and 3000C for 3 hours each under the influence of N2 gas and continuing to calcination temperature at 4200C for 2 hours, under oxygen flow (muffle).

The characteristics of aerogels and xerogels were obtained by DTA, BET, XRD, UV-vis DRS, and FTIR. Both samples were integrated into DSSC, which open voltage measurement (Voc) were performed under white light using multimeter. The results suggest aerogels prepared had higher surface area (1975 m2/g) than xerogels’ (271 m2/g). It was also proven multi-step calcination could increase crystallite size of aerogels to 9,21 nm by maintaining its surface area (71,90 m2/g), which is higher than that of xerogels (67,90 m2/g). The Voc measurement reveals a higher voltage on aerogel’s DSSC (21,40 mV) than that of xerogel (1,10 mV)."

"Nanopartikel TiO2 anatase telah berhasil disintesis menggunakan prekursor titanium tetraisopropoxide dan katalis tetramethylammonium hydroxide dengan metode sol-gel yang kemudian dilanjutkan dengan proses hidrotermal dan kalsinasi. Perlakuan hidrotermal dilakukan dengan variasi temperatur 100, 125, dan 150oC, yang secara khusus ditujukan untuk menginvestigasi pengaruh temperatur proses hidrotermal terhadap peningkatan kristalinitas dan ukuran kristalit. Hasil yang didapatkan kemudian diaplikasikan untuk fabrikasi sel surya tersensitasi zat pewarna dye-sensitized solar cell, DSSC dengan melihat performa efisiensi konversi - dari DSSC yang di fabrikasi dengan menggunakan zat pensensitasi hasil ekstraksi anthocyanin dari pewarna alam buah senduduk Melastoma malabathricum L.. Metode karakterisasi material yang digunakan adalah X-ray Diffraction XRD, Scanning Electron Microscope SEM , Fourier transform infrared FTIR, ultraviolet-visible Spectroscopy UV-Vis, dan differential scanning calorimetry DSC, sementara pengujian performa untuk mengetahui efisiensi - dilakukan menggunakan Semiconductor Parameter Analyzer dengan menganalisis karakteristik kurva arus dan tegangan J-V. Hasil penelitian menunjukkan bahwa dengan meningkatnya temperatur proses hidrotermal, terdapat peningkatan kristalinitas dan ukuran kristalit yang cukup signifikan serta berbanding lurus. Semakin tinggi kristalinitas, ukuran kristalit juga mengalami peningkatan. Efisiensi DSSC yang didapatkan cukup menjanjikan dengan hasil perhitungan maksimal 5,69 untuk temperatur proses hidrotermal 150oC dan menggunakan zat pensensitasi dari anthocyanin yang diekstrak menggunakan etanol dan 20 wt. air suling. Hasil ekstraksi anthocyanin dari pewarna alam buah senduduk dalam penelitian ini memiliki potensi untuk digunakan sebagai zat pensensitasi pada DSSC.

---

Anatase TiO2 nanoparticles have been successfully synthesized using Titanium Tetraisopropoxide as precursor and Tetramethylammonium hydroxide as catalyst through a sol gel method followed by hydrothermal treatment and calcination. Hydrothermal treatment was carried out at temperature variations of 100, 125, and 150oC, which is specifically aimed at investigating the effect of hydrothermal temperature on the crystallinity enhancement and crystallite size of the anatase TiO2 nanoparticles. The as synthesized TiO2 nanoparticles have been applied for dye sensitized solar cell DSSC, focused on the performance conversion efficiency of DSSC fabricated using sensitizer extracted from natural dye of Melastoma malabathricum L.

Characterization of the as synthesized materials was performed using X ray Diffraction XRD, Scanning Electron Microscope SEM , Fourier transform infrared FTIR, ultraviolet visible Spectroscopy UV Vis, and differential scanning calorimetry DSC, while the performance conversion efficiency was carried out using Semiconductor Parameter Analyzer through the characteristics of current versus voltage J V curve.

This results shows that increasing temperature of hydrothermal treatment results in significant crystallinity enhancement and an increase in crystallite size. The efficiency obtained is quite promising with maximum calculation of 5.69 for hydrothermal treatment temperature of 150oC sensitized using natural dye extracted with ethanol containing 20 wt. distilled water. This natural dye extracted from M. malabathricum L. has the potential to be used as sensitizer in DSSC device."

"Potensi mineral ilmenit sangat besar di Indonesia, namun sampai saat ini belum bisa dioptimalkan. Untuk itu pemanfaatan mineral ilmenit menjadi hal yang penting tidak hanya digunakkan untuk mengekstraksi TiO2 namun juga untuk diaplikasikan pada sel surya tersensitasi zat pewarna (DSSC) guna mencukupi kebutuhan energi dunia khususnya Indonesia. Pada penelitian ini, fabrikasi DSSC dibuat dari material ilmenit Bangka, TiO2 hasil sintesis ilmenit Bangka dan TiO2 komersial P-25 Degussa. Material ilmenit yang digunakan adalah ilmenit 100, 200 dan 325 mesh, sedangkan sintesis TiO2 dibuat dari mineral ilmenit 100 mesh. Karakterisasi material dievaluasi dengan menggunakkan XRD, SEM, dan UVVIS. Selanjutnya, material tersebut kemudian diintegrasikan kedalam prototipe DSSC. Kelayakan dan performa DSSC tersebut diukur berdasarkan pengukuran tegangan sirkuit terbuka (Voc) yang dilakukan di bawah penyinaran sinar putih menggunakan multimeter. Hasil penelitian menunjukkan material ilmenit dengan ukuran partikel 325 mesh memiliki tingkat performa yang lebih tinggi (56 mV) dibandingkan dengan ilmenit 200 mesh (52,8 mV) dan 100 mesh (46 mV). Untuk material TiO2 sintesis (14,2 mV) memiliki tingkat performa yang lebih rendah dibandingkan dengan baik P-25 Degussa (60 mV), maupun material ilmenit.

---

The potential of ilmenite mineral in Indonesia is huge, but until today it is not yet optimized. Therefore the utilization of ilmenite mineral becomes important, not only used to extract TiO2 but also to be applied in dye sensitized solar cell (DSSC) aimed at fulfilling the world's energy needs especially Indonesia. In this study, DSSC prototype is fabricated from ilmenite Bangka, TiO2 derived from Bangka ilmenite and TiO2 commercial P-25 Degussa. The ilmenite used is ilmenite 100, 200 and 325 mesh, while the synthesized TiO2 was made from 100 mesh ilmenite mineral. The characterization of the material was performed by using XRD, SEM, and UV-VIS. Furthermore, the material is integrated into DSSC prototypes. The feasibility and performance of the DSSC was evaluated by measuring the open circuit voltage (Voc) under white light illumination using a multimeter. The results showed ilmenite with particle size 325 mesh has a higher level of performance (56 mV) compared to ilmenite 200 mesh (52,8 mV) and 100 mesh (46 mV). For synthesized TiO2 (14.2 mV) had a lower level of performance than either P-25 Degussa (60 mV), and ilmenite."

"Dye-Sensitized Solar Cell (DSSC) telah menarik perhatian sebagai salah satu sumber energi alternatif yang terbarukan. Di daerah tropis, dimana cahaya matahari hampir tersedia sepanjang tahun, DSSC dapat menjadi sumber energi yang sangat berguna. Penelitian tentang DSSC telah dilakukan secara intensif oleh kelompok peneliti terutama di negara-negara maju. Saat ini, kami bekerja pada pembuatan DSSC dengan mensintesis TiO2 nanotube melalui proses anodisasi pada plat titanium dengan larutan elektrolit garam amonium florida dalam gliserol. Kemudian TiO2 nanotube dikarakterisasi dengan termal insitu XRD, UV-Vis DRS dan SEM, yang mengindikasikan terjadinya fase kristal anatase pada perlakuan panas suhu 400˚C. Film anatase yang terbentuk menunjukkan morfologi nanotube yang sangat teratur, dengan ketebalan film sekitar 1,6 μm. Nanotube memiliki rata-rata ketebalan dinding, diameter pori dan diameter luar sekitar 19 nm, 67 nm dan 105 nm. Kemudian zat warna alizarin yang berfungsi sebagai sensitizer dilekatkan pada TiO2 nanotube (TiO2-NT/alizarin) dengan metode elektroforesis. Ti/TiO2-NT/alizarin tersebut selanjutnya dirakit menjadi sel DSSC menggunakan iodium sebagai elektrolit dan film Pt pada kaca ITO sebagai elektroda counter. Hasil pengukuran menunjukkan bahwa rangkaian sel DSSC menghasilkan nilai efisiensi maksimum pada waktu anodisasi 4 jam dan waktu elektroforesis zat warna 12 menit.

---

Dye-Sensitized Solar Cell (DSSC) has attracted attention as one of future renewable alternative energy source. In tropical area, where the solar light is almost available all the year, DSSC can be very useful. Research on DSSC has been conducted intensively by research groups mostly in advance countries. We recently start work on DSSC issue by employing highly ordered TiO2 nanotube, prepared by anodization of titanium metal sheet in the present of aqueous ammonium fluoride in glycerol. The prepared TiO2 nanotube was characterized by mean insitu thermal treatment XRD, UV-Vis DRS and SEM, which indicate the occurrence of anatase crystal phase upon heat treatment at 4000C. The formed anatase film showed morphology of highly ordered nanotube array, with about 1.6 μm film thickness, having average of wall thickness and internal diameter of 19 nm and 67 nm, respectively. The typical dyes sensitizer (e.g. alizarin) then was attached to the TiO2 nanotube (TiO2-NT/alizarin) by electrophoresis method. The Ti/TiO2-NT/alizarin then was assembled in typical DSSC, employing iodine as an electrolyte and Pt film supported on an ITO glass, as the counter electrode and light window as well. The measurement result indicates that the series of DSSC cells produce the maximum efficiency at 4 hours anodization and 12 minutes electrophoresis dye."

"ABSTRAKDalam penelitian ini, telah berhasil disintesis partikel karbon nano melalui serangkaian proses kimia, yang melibatkan dehidrasi kimia dengan asam sulfat, yang diikuti dengan pirolisis. Sampel yang digunakan divariasikan berdasarkan prekursornya, yaitu gula dan sukrosa, penambahan katalis logam, dan perlakuan termal awal. Partikel karbon nano yang didapat kemudian diakrakterisasi senyawa yang terkandung dan ukuran kristalitnya dengan dengan difraksi sinar X XRD , kemudian di konfirmasi keberadaan senyawa dan gugus fungsinya dengan FTIR dan morfologi diamati dengan mikroskop elektron SEM . Hanya sampel dengan prekursor gula tanpa penambahan katalis logam dan dengan memberikan pemanasan awal serta sampel dengan prekursor sukrosa dengan penambahan katalis saja lah yang memiliki dimensi ukuran partikel rata-rata hingga skala nano, yaitu secara berurutan 600 nm dan 900 nm. Kedua sampel ini kemudian dijadikan elektroda lawan dan diuji nilai efisiensi konversi kinerjanya dengan menggunakan Semiconductor Paramater Analyzer dengan menganalisis karakteristik kurva arus dan tegangan I-V . Hasil pengujian menunjukkan bahwa sampel dengan prekursor gula tanpa penambahan katalis logam dan dengan memberikan pemanasan awal mampu memperlihatkan nilai efisiensi konversi kinerja sebesar 3,5 , sedangkan untuk prekursor sukrosa dengan penambahan katalis mampu memperlihatkan nilai efisiensi konversi kinerja sebesar 0,04.

---

ABSTRACTIn this study, carbon nanoparticles were successfully synthesized through a series of chemical processes, which involved chemical dehydration with sulfuric acid, followed by pyrolysis. The sample used was varied based on its precursors, namely sugar and sucrose, addition of metal catalysts, and initial thermal treatment. The carbon nanoparticles obtained were then characterized by the compounds contained and the size of the crystallite by XRD X-ray diffraction, then confirmed the presence of compounds and functional groups with FTIR and morphology observed with SEM electron microscopy. Only samples with sugar precursors without the addition of metal catalysts and by providing preheating and samples with sucrose precursors with the addition of a catalyst alone have the dimensions of the average particle size up to the nanoscale, ie, 600 nm and 900 nm respectively. Both of these samples are then used as opposing electrodes and tested the conversion efficiency value of their performance using the Semiconductor Paramater Analyzer by analyzing the characteristics of the I-V current and voltage curves. The test results showed that samples with sugar precursors without the addition of metal catalysts and by providing preheating were able to show a value of performance conversion efficiency of 3.5, whereas for sucrose precursors with the addition of catalysts were able to show the value of performance conversion efficiency of 0.04."

"Penelitian ini adalah studi awal mengenai sel surya tersensitasi berbasis ZnO dengan zat pewarna organik. Tujuannya untuk mengetahui pengaruh dari tingkat pengisian dan besar kristalit TiO2 terhadap voltase DSSC. Hasil dari penelitian menunjukkan bahwa, besar kristalit berbanding terbalik dengan voltase yang dihasilkan. Semakin besar ukuran kristalit semakin kecil voltase yang dihasilkan dan sebaliknya semakin kecil ukuran kristalit semakin besar voltase yang dihasilkan. Sementara tingkat pengisian mempunyai pengaruh berbeda pada kristalit yang besar dan kristalit yang kecil. Selain itu, ukuran kristalit dan tingkat pengisian mempengaruh kestabilan layer oksida dan kemampuannya dalam menyerap molekul zat pewarna.

---

This research is an initial study about ZnO based dye sensitized solar cell (DSSC) with an organic dye. The purpose is to understand the effect of loading level and crystallite size to DSSC voltages.

The result of this research shows that, crystallite size is a contrary fraction with the voltages that produced by DSSC. The bigger size of crystallite the lower voltages outcome, on contrary the smaller size of crystallite the bigger voltages can be produced by DSSC. While loading level have a different affect in smaller and bigger crystallite. Afterwards, crystallite size and volume level affect the stability of the layer oxide and its ability to absorb dye molecules."

"Sumber bahan bakar fosil di Dunia saat ini semakin menurun. Oleh karena itu, sel surya tersensitasi zat pewarna (DSSC) adalah salah satu sumber energi alternatif yang dibutuhkan. Didalam struktur sel surya, lapisan material semikonduktor adalah bagian yang penting untuk mengubah energi foton menjadi listrik. Di dalam penelitian ini, nanopartikel seng oksida (ZnO) dibuat dengan menggunakan 3 variasi pelarut, yaitu etanol, metanol dan etilen glikol yang dimaksudkan untuk mengningkatkan kristalinitas yang akan meningkatkan performa dari DSSC. Nanopartikel tersebut dikalsinasi pada temperatur 150 dan 300oC selama 2 jam, kemudian dilanjutkan dengan perlakuan hidrotermal pada temperatur 100oC selama 24 dan 48 jam. Nanopartikel ZnO terbaik adalah hasil dari perlakuan hidrotermal 100oC selama 24 jam dengan ukuran kristalit 57.13 nm dan memiliki energi celah pita terkecil yaitu sebesar 3.23 eV. Dengan karakteristik tersebut, nanopartikel ZnO yang dihasilkan dalam penelitian ini cocok untuk aplikasi DSSC.

---

The fossil fuel reservation in the world is decreased significantly. Therefore, dye sensitized solar cell (DSSC) as one of alternative energy sources is needed. In the device structure, a layer of semiconductor material is an important part for photon energy conversion to electricity. In this study, zinc oxide (ZnO) nanoparticles were synthesized under 3 variations of solvent, i.e. ethanol, methanol and ethylene glycol as means to enhance the crystallinity which in turn can affect the performance of DSSC. The resulted nanoparticles were calcined at 150 and 300oC for 2 hours, followed with hydrothermal treatment at 100oC for 24 and 48 hours. The best ZnO nanoparticles were obtained under hydrothermal treatment for 24 hours with the biggest crystallite size of 57.13 nm and the smallest band gap energy of 3.23 eV. With these characteristics, the synthesized ZnO particles in this work is suitable for DSSC application."