Hasil Pencarian  ::  Simpan CSV :: Kembali

"Failures of magnesia-chrome refractory at Peirce Smith Converter caused unstable production process. This research was carried out to find failures factor by determined shell temperatures distribution, thickness of refractories consumption and testing of converter slag samples Final result of this research have indicated that refractories failure was caused by non any form of silica flux and scraps that was influenced by feed chutes design that didn?t work optimally to distribute silica flux and scrap good than it made high local temperature in converter increased Redesign chute have done to make balance of silica flax, scrap adding and operating temperatures distribution than be hoped it able to increase the lifetime of refractory."

"Pemodelan proses yang baik membutuhkan model sifat-sifat termodinamika yangakurat dan elisien dalam perhilungan untuk rentang tekanan, temperature dan komposisiyang lebar.Metode yang efektif dalam menentukan sifat-sifat termodinamika adalah denganmenggunakan persamaan keadaan yang mengambil bentuk umum persamaan van derWaals.Persamaan keadaan yang paling baik untuk dikembangkan adalah persamaankubik tiga parameter dengan parameter a sebagai fungsi temperature. Perbaikanperhitungan volume cair jenuh dapat dilakukan dengan menerapkan translasi volumepada persamaan keadaan yang diinginkan.Aplikasi volume translasi dapat meningkatkan akurasi perhirungan volume cairjenuh. Pada aplikasinya translasi volume mempunyai akurasi yang tinggi padapersamaan Peng-Robinson, dimana faktor koreksinya merupakan fungsi temperatur."

"Latar belakang: Hidroksiapatit merupakan salah satu bahan alloplast yang banyak digunakan di bidang kedokteran gigi. Komposisi hidroksiapatit sama dengan komposisi anorganik tulang dan gigi manusia sehingga bersifat biokompatibel dan bioaktif. Selain itu, hidroksiapatit juga bersifat osteokonduktif. Salah satu metode pembuatan hidroksiapatit yaitu metode disolusi-presipitasi dalam kondisi hidrotermal. Pembuatan blok hidroksiapatit dengan metode disolusi-presipitasi pada suhu 100°C selama 48 jam masih menghasilkan fasa lain selain hidroksiapatit, yaitu dicalcium phosphate anhydrous (DCPA). Fasa DCPA dan/atau fasa DCPD (dicalcium phosphate dehydrate) dapat terbentuk dalam pH asam. Sedangkan, hidroksiapatit dapat terbentuk pada pH basa. Oleh karena itu, pH dapat dijadikan indikator secara tidak langsung mengenai hasil fasa yang terbentuk. Gipsum dipilih sebagai prekursor karena mengandung ion kalsium (Ca2+). Sedangkan, larutan Na3PO4 digunakan karena mengandung ion fosfat (PO43-), bersifat tidak toksik, dan memiliki pH basa. Tujuan: Penelitian ini bertujuan untuk mengetahui pengaruh perbedaan suhu terhadap perubahan pH larutan Na3PO4 dalam pembuatan blok hidroksiapatit dari blok gipsum.Metode Penelitian: Penelitian ini menggunakan blok gipsum dan larutan Na3PO4 sebagai prekursor untuk membuat blok hidroksiapatit. Spesimen yang digunakan berupa 30 mL larutan 1 mol/L Na3PO4 sebanyak dua beaker glass larutan. Sebelum dilakukan perendaman, pH larutan diukur terlebih dahulu untuk mengetahui pH awal larutan 1 mol/L Na3PO4. Lima belas blok gipsum direndam dalam 30 mL larutan 1 mol/L Na3PO4 dengan suhu yang berbeda yaitu 100°C, 140°C, dan 180°C pada kondisi hidrotermal selama 48 jam. Setelah perendaman, blok dan larutan 1 mol/L Na3PO4 dipisahkan. Kemudian, pH larutan 1 mol/L Na3PO4 diukur kembali menggunakan pH meter Eutech Instruments pH 700 untuk mendapatkan pH larutan 1 mol/L Na3PO4 setelah digunakan untuk perendaman selama 48 jam. Hasil: Nilai pH larutan 1 mol/L Na3PO4 sebelum digunakan untuk perendaman yaitu 13,04. Sedangkan, nilai pH larutan 1 mol/L Na3PO4 setelah digunakan untuk perendaman pada suhu 100°C, 140°C, dan 180°C berturut-turut yaitu 12,72; 12,67; dan 12,30. Kesimpulan: Peningkatan suhu yang digunakan menyebabkan penurunan pH larutan 1 mol/L Na3PO4. Namun, pH akhir larutan masih cukup basa untuk hidroksiapatit terbentuk. Namun, penelitian lebih lanjut masih perlu dilakukan mengenai pengukuran pH larutan Na3PO4 dengan sampel yang lebih banyak.

---

Background: Hydroxyapatite is one of the alloplastic materials that is widely used in dentistry. The composition of hydroxyapatite is similar with the inorganic composition of human bone so that it is biocompatible and bioactive. Besides, hydroxyapatite is also osteoconductive. One of the fabrication methods of hydroxyapatite is the dissolution-precipitation method under hydrothermal conditions. The fabrication of hydroxyapatite block with the dissolution-precipitation method at 100°C for 48 hours still produced other phase except hydroxyapatite, specifically dicalcium phosphate anhydrous (DCPA). DCPA and/or dicalcium phosphate dehydrate (DCPD) phase can be obtained if the pH is acidic. Meanwhile, hydroxyapatite can be fabricated on the alkaline pH condition. Therefore, the pH value can be the indirect indicator to predict the phase product. Gypsum was chosen as a precursor because it has calcium ions (Ca2+). Na3PO4 solution was used because it contained phosphate ions (PO43+), non-toxic, and has an alkaline pH value.

Objective: This study aimed to determine the effect of temperature differences on changes of the pH value of Na3PO4 solution in the fabrication of hydroxyapatite block from gypsum block.

Methods: This study used gypsum block and Na3PO4 solution as precursors to fabricate hydroxyapatite block. The specimens of this study were two beaker glasses of 30 mL of 1 mol/L Na3PO4 solution. Before the immersion, the pH value of the solution was measured first to determine the initial pH value of 1 mol/L Na3PO4 solution. Fifteen specimens of gypsum blocks were immersed in 30 mL of 1 mol/L Na3PO4 solution with different temperatures specifically 100°C, 140°C, and 180°C under the hydrothermal condition for 48 hours. After the immersion, the blocks and the 1 mol/L Na3PO4 solution were separated. Then, the pH value of 1 mol/L Na3PO4 solution was measured using Eutech Instruments pH 700 pH meter to obtain the pH of 1 mol/L Na3PO4 solution after being used for immersion for 48 hours.

Results: The pH value of 1 mol/L Na3PO4 solution before being used for the immersion was 13,04. Meanwhile, the pH value of 1 mol/L Na3PO4 solution after being used for the immersion at 100°C, 140°C, and 180°C respectively were 12.72, 12.67, and 12.30.

Conclusions: The increase in the temperature caused the derivation of the pH value of 1 mol/L Na3PO4 solution. Nevertheless, the final pH value was still alkaline enough for hydroxyapatite to be formed. However, further research still needs to be done to measure the pH value of the Na3PO4 solution with more samples."

"Quality of asphalts mixing in construction work as road povement material, on site was ejected bymany factors. One of that is temperature when act of cramming periode. For having od one forcematerial with good quality, controlling to act of cramming temperature was handel since the mix out frommixing plane (AMP) until spreading period and force density on site. Temperature dicease in spreadingand density periode. Exactly will result quality and ashpalt mix will decrease. To getting know abouttemperatur density on ashpalt posed Therefore in this research made laboratorium experiment where isdensity temperature variable star from 140°C decrease until 70°C with interval decreasing 10° Ctemperature. Result of observation in laboratorium experiment. Show that force density temperaturebelow 124,5"C resulting technical attitudes that is not foraging. For those is suggested that forces densitytemperature is around 124,5°C - 140°C."

"Salah satu metode unruk menurunkan nickel loss pada proses converterdengan Pierce Smith Converter adalah dengan melakukan settling time pada saatsebelum skimming dan sesudah blowing. Dengan begitu diharapakan nlkel yangbercampur bersama slag mempunyai cukup waktu untuk berpenetrasi ke bawah.Selain itu besar kecilnya nickel loss juga kernungkinan dipengamhi olehparameter proses yang lain seperti grade nickel EFM ( Electric Furnace Matte )yang masuk ke converter dan temperatur proses.Penelitian pada proses converter dilakukan dengan tahapan, pertamamengambil data EFM untuk mengetahui grade nickel EFM sehingga bisadibandingkan dengan nickel loss yang terjadi_ Kedua, mengukur temperatur EFMdan temperatur slag yang dapat menggambarkan temperatur proses dari converter.Ketiga, rnengambil sampel slag converter untuk mengetahui berapa komposisinikel pada pada low nickel slag (nickel loss) converter apabila dilakukan nonsettling time, settling time 3 menit dan settling time 5 menit.Hasil penelitian menunjukan apabila proses converter tidak dilalcukansettling time menghasilkan nickel loss sebesar 0,59%, dengan settling time 3 menitdihasilkan nickel loss sebesar 0,5l% dan dengan settling time 5 menit nickel lossyang teljadi sebesar 0,50%. Berdasarl-can perhitungan waktu operasi converterdiketahui bahwa untuk settling time baik yang 3 menit ataupun 5 menit dapatdilakukan tanpa memgikan waktu operasi. Keuntungan perusahaan yang dapatdiambil apabila dilakukan settling time 3 menit sebesar $ l.7’l2.210,52 dan untuksettling time selama 5 menit sebesar $ l_993_736,7 setiap tahun, dengan asumsiharga nikel $ 1 per pounds (lbs).Penelitian juga menunjukan bahwa grade nickel EFM berpengaruhterhadap nickel loss dan Total Operating Time (TOT) converter, di mana semakinrendah grade nickel EFM malta semakin tinggi nickel loss yang teljadi dan prosesconverter semakin lama. Temperatur juga berpengaruh terhadap nickel lossconverter, yaitu semakin tinggi temperatur proses converter maka semakin rendahnickel loss yang terjadi,"