"ABSTRAKPenelitian ini bertujuan untuk menghasilkan karbon aktif dari ampas tebu dengan luas permukaan melebihi 800 m2/gram dan mengetahui pengaruh metode aktivasi, suhu aktivasi dengan KOH, dan waktu aktivasi dengan KOH terhadap luas permukaan karbon aktif yang dihasilkan.Aktivasi kimiawi dilakukan dengan menggunakan KOH pada suhu 600oC, 700oC, dan 800oC selama ½ jam dan 1 jam. Sebagai pembanding dilakukan aktivasi fisika tanpa KOH pada suhu 700oC selama 1 jam. Karbon aktif yang diperoleh dikarakterisasi luas permukaannya. Luas permukaan tertinggi 1135 m2/gram diperoleh dari aktivasi menggunakan KOH selama ½ jam pada suhu 800oC. Dengan metode aktivasi fisika diperoleh luas permukaan 293 m2/gram.

---

ABSTRACTThis research aims to produce activated carbon made from sugarcane bagasse with a surface area exceeding 800m2/gram and determine the effect of activation method, temperature of KOH activation, and time of KOH activation of the surface area of activated carbon. Chemical activation performed using KOH at a temperature of 600oC, 700oC, and 800oC for ½ hour and 1 hour. As a comparison, physics activation performed without KOH at a temperature of 700oC for 1 hour.Surface area of activated carbon was characterized. The highest surface area is 1135m2/gram obtained from KOH activation for ½ hour at temperature of 800oC. Through the physical activation, the surface area is 293m2/gram."

"Pemilihan jenis adsorben merupakan hal penting dalam proses adsorpsi. Adsorben yang paling sering digunakan adalah karbon aktif karena memiliki luas permukaan yang besar sehingga daya adsorpsinya lebih besar dari pada adsorben lainnya. Pada penelitian pembuatan karbon aktif dari ampas tebu ini dilakukan dengan metode aktivasi menggunakan gas CO2. Dengan laju alir gas CO2 300 ml/menit, 400 ml/menit, dan 500 ml/menit. Aktivasi dilakukan pada temperatur 700 °C, 800 °C,dan 900 °C selama 2 jam. Ampas tebu dipilih karena mengandung karbon yang cukup. Selain itu, ketersediaan ampas tebu melimpah di Indonesia dan sebagai representatif dari sumber daya alam yang terbarukan. Karbon aktif yang diperoleh dikarakterisasi luas permukaannya. Proses dengan aktivasi CO2 ini diharapkan dapat diperoleh karbon aktif dengan luas permukaan yang cukup tinggi sehingga akan membantu dalam proses adsorpsi. Hasil yang diperoleh menunjukkan bahwa semakin tinggi waktu aktivasi dan laju alir CO2, maka luas permukaan yang direpresentasikan dengan bilangan iod semakin meningkat. Luas permukaan karbon aktif tertinggi yang direpresentasikan dengan bilangan iod sebesar 730 mg/g diperoleh dengan aktivasi pada laju alir CO2 sebesar 500 mL/menit dan temperatur aktivasi 900°C.

---

Selection type of adsorbent is important in the adsorption process. The most commonly used adsorbent is activated carbon because it has a large surface area so that the adsorption energy is greater than the other adsorbents. To study the manufacture of activated carbon from bagasse was carried out by the method of activation using carbon dioxide gas. With CO2 flow rate 300 mL/min, 400 mL/min, and 500 mL/min. Activation is done at a temperature of 700 °C, 800 °C, and 900 °C. Bagasse chosen because they contain enough carbon. Moreover, the availability of bagasse abundant in Indonesia and as a representative of a renewable natural resource. Activated carbon were then characterized its surface area. With carbon dioxide activation process is expected to obtain activated carbon with high surface area that will help in the process of adsorption. The results showed that the higher the activation time and the flow rate of CO2, the surface area represented by the iodine number is increasing. The surface area of activated carbon is represented by the highest iodine number of 730 mg / g obtained by activation of the CO2 flow rate of 500 mL / min and a temperature of 900 ° C."

"Penelitian ini membahas produksi karbon aktif berbahan baku bambu dengan metode aktivasi menggunakan larutan KOH pada suasana gas nitrogen untuk mengontrol pembentukan pori karbon aktif. Aktivasi kimia dilakukan dengan rasio massa KOH : massa karbon yaitu 3:1 pada suhu 600°C, 700°C, dan 800°C selama 30 menit dan 60 menit. Sebagai pembanding dilakukan aktivasi fisika tanpa penambahan activating agent pada suhu 700°C selama 60 menit. Luas permukaan paling tinggi sebesar 802,60 mg/g (sekitar 824,83 m2/g) diperoleh dari aktivasi kimia selama 30 menit pada suhu 800°C, sedangkan luas permukaan paling rendah sebesar 283,39 mg/g (sekitar 291,23 m2/g) diperoleh dari aktivasi fisika.

---

This research is about production of activated carbon made from raw bamboo with activation method using KOH as activating agent in an atmosphere of nitrogen gas to control pores formed in the activated carbon. Chemical activation was done with mass ratio of activating agent : carbon is 3:1 on 600°C, 700°C, and 800°C for 30 minutes and 60 minutes, and physical activation was done without using activating agent on 700°C for 60 minutes. The highest surface area, 802,60 mg/g (about 824,83 m2/g), was obtained by KOH activation on 800°C for 30 minutes, and the lowest, 283,39 mg/g (about 291,23 m2/g), was obtained by physical activation."

"Pemanasan global menjadi momok yang menakutkan bagi manusia, seiring dengan meningkatnya konsumsi energi primer berbahan bakar fosil yang menimbulkan gas efek rumah kaca. Hal ini mendorong para peneliti di seluruh dunia untuk merubah kebiasaan tersebut ke energi baru terbarukan (EBT). Namun, EBT baik itu fotovoltaik (PLTS) maupun pembangkit listrik tenaga bayu (PLTB) keduanya memiliki sifat intermittent sehingga dibutuhkan alat penyimpanan energi untuk menanggulangi sifat intermittent. Salah satu alat penyimpan energi adalah Kapasitor Lithium Ion (KLI). Penyimpanan energi jenis ini mempunyai karakteristik densitas daya dan energi spesifik yang berada diantara baterai lithium ion dan kapasitor konvensional, sehingga diharapkan mampu memiliki kapasitas mendekati Baterai Lithium Ion dengan densitas daya yang dimiliki mendekati Kapasitor konvensional. Salah satu alternatif bahan material yang dapat digunakan untuk pembuatan KIL yaitu, sampah organik, khususnya dalam penelitan ini ampas tebu. Hasil penggilingan tebu berupa ampas kasar kemudian di olah menjadi karbon aktif dengan memperhatikan variasi suhu aktivasi KOH. Karbon aktif pada skripsi ini memiliki luas permukaan mencapai 2136,66 m2/g terjadi pada suhu aktivasi 800°C. Berdasarkan hasil yang diperoleh melalui prediksi machine learning didapatkan nilai kapasitansi dengan suhu aktivasi 800oC, 700oC dan 600oC masing-masing sebesar 141,214 F; 80,955 F dan 102,855 F dengan MAE sebesar 28,11. Suhu aktivasi memiliki peran penting dalam penentuan hasil luas permukaan dan kapasitansi pada Kapasitor Lithium Ion.

---

Global warming is a frightening specter for humans, along with the increased consumption of fossil fuel-based primary energy that causes greenhouse gases. This prompted researchers around the world to change these habits to renewable energy (EBT). However, both photovoltaic (PLTS) and wind power plants (PLTB) both have intermittent characteristic so, that energy storage system are needed to cope with intermittent characteristic. One of the energy storage devices is Lithium Ion Capacitors (KIL). This type of energy storage has specific power and specific energy characteristics that are between lithium ion batteries and conventional capacitors, so it is expected to be able to have a capacity close to Lithium Ion Batteries with power density that are close to conventional capacitors. One alternative material that can be used for the manufacture of KIL is organic waste, especially in this research is sugarcane bagasse. The results of sugarcane milling in the form of coarse pulp then processed into activated carbon with temperature variation in KOH activation. Activated carbon in this thesis has a surface area of 2136.66 m2 / g which occurs at an activation temperature of 800 ° C. Based on the results obtained through machine learning prediction, the capacitance values with activation temperatures of 800 oC, 700 oC and 600 oC were 141.214 F; 80,955 F and 102,855 F with MAEs of 28.11. Activation temperature has an important role in determining the results of surface area and capacitance in Lithium Ion Capacitors."

"Penelitian ini merupakan salah satu bentuk pemanfaatan limbah agrikultur yang melimpah di Indonesia sehingga limbah ini akan mendapatkan peningkatan nilai guna. Tujuan penelitian ini adalah untuk mendapatkan karbon aktif fisik dan mengetahui kondisi optimum pembuatan karbon aktif. Bahan baku pembuatan karbon aktif ini adalah bagas tebu yang merupakan limbah pabrik gula. Beberapa metode yang sudah pernah dilakukan terhadap bahan baku ini dalam pembuatan karbon aktif adalah aktivasi thermal N2 dan kimia dengan berbagai activating agent, tetapi aktivasi dengan aliran gas karbon dioksida belum pernah dilakukan. Penelitian ini menghasilkan sembilan sampel karbon aktif dengan variasi laju alir karbon dioksida 300, 400, dan 500 cc/mnt dan variasi waktu aktivasi 30, 60, dan 120 menit dengan temperatur 900oC. Kondisi operasi optimum pada variabel penelitian ini didapatkan pada laju alir 500 cc/mnt selama 120 menit dengan mendapatkan luas permukaan karbon aktif yang direpresentasikan dengan daya serap iod sebesar 769.5 mg/g. Hubungan variabel yang ditemukan adalah semakin besar laju alir gas karbon dioksida dan/atau semakin lama waktu aktivasi akan memperbesar luas permukaan karbon aktif. Luas permukaan karbon aktif ini lebih besar daripada karbon aktif aktivasi thermal N2, tetapi lebih kecil dari aktivasi kimia KOH.

---

This research is a form of utilization of agricultural industry wastes so that the waste can gain significant enhancement of value. Purposes of this research is to get the physical condition of activated carbon and knowing the optimum condition to make the activated carbon. The agricultural industry waste that is used in the research is sugarcane bagasse that is waste of sugar industry. Researches that has been done with sugarcane bagasse is using physics activation of N2 and chemical activation using various activating agent, but the method in this research is activation using carbon dioxide gas flow that hasn't been done with this raw material.

The target is this research manufacture nine samples that are consists of variation of carbon dioxide gas flow 300, 400, and 500 cc/minute and activation time 30, 60, and 120 minutes at temperature 900oC. The optimum operating condition reached at 500 cc/minute gas flow and 120 minutes activation time that give an activated carbon with surface area that is represented by iod adsorption 769.5 mg/g. Correlation between this two free variables are the more fast carbon dioxide gas flow and/or more long activation time makes the larger activated carbon surface area. Surface area of the activated carbon in this research is bigger than physics activation of N2, but smaller than chemical activation using KOH."

"Penelitian ini bertujuan untuk mengetahui pengaruh metode aktivasi terhadap luas permukaan dan kualitas karbon aktif yang dihasilkan dari tongkol jagung. Metode aktivasi yang digunakan adalah metode aktivasi kimia menggunakan KOH dan aktivasi fisika menggunakan gas alir N2 dan CO2. Aktivasi dilakukan pada laju alir 100, 200 dan 300 mL/menit. Sebagai pembanding dilakukan aktivasi fisika saja dan aktivasi kimia saja. Karbon aktif terbaik diperoleh melalui metode aktivasi kimia-fisika menggunakan gas N2 dengan laju alir 100mL/menit. Melalui proses tersebut diperoleh karbon aktif dengan bilangan iod sebesar 1065,15 mg/g, rendemen 55,65%, kadar air 20,62%, kadar abu 1,96%, dan kadar zat volatile 22,18%.

---

This research aims to determine the effect of activation methods on surface area and quality of activated carbon produced from corn cobs. In this research controlled by chemical activation method using KOH and physical activation method using N2 and CO2 gasification at a flow rate of 100, 200 and 300 mL/min. For comparison, the study was also carried out the manufacture of activated carbon by physical activation method and chemical activation method. The best activated carbon obtained by chemical-physical activation method using N2 gasification with a flow rate of 100mL/min. This method produced activated carbon with iodine number of 1065,15 mg/g, yield (55,65%), moisture content (20,62%), ash content (1,96%), and volatile matter (22,18%)."

"Pada penelitian ini, ingin dilihat pengaruh akivasi kimia dan fisika pada pembuatan karbon aktif berbahan baku sekam padi. Aktivasi kimia dilakukan dengan mengimpregnasi arang sekam dengan KOH dengan rasio massa arang sekam dan KOH 1:4 (berat kering). Dan aktivasi fisika dilakukan dengan mengalirkan gas N2 100 mL/ min dan gas CO2 yang divariasikan 100, 200, 300, dan 400 mL/min pada suhu 800°C selama 1 jam. Bilangan iod tertinggi didapatkan dari karbon yang diaktivasi kimia fisika dengan laju N2 100 mL/min dan CO2 100 mL/min yaitu sebesar 793,04 mg/g, sedangkan bilangan iod terendah didapatkan pada karbon ayang diaktivasi kimia fisika yang dialirkan N2 100 mL/min saja 583,26 mg/g. Sebagai pembanding, juga dilakukan pembuatan karbon aktif dengan metode aktivasi fisika saja dan kimia saja. Untuk karbon yang diaktivasi fisika saja dan kimia saja diperoleh bilangan iodin karbon aktif sebesar 421,09 mg/g dan 496,09 mg/g. Karbon aktif yang memiliki bilangan iod tertinggi memiliki kadar air 13,062 %, kadar abu 8,588 %, dan bagian yang hilang pada pemanasan 950°C 23,123 %.

---

The main purpose of this study is want to see the influence of chemical and physical activation in producing activated carbon made from rice husk. The chemical activation was done by KOH impregnation on rice husk that had been carbonized with a mass ratio of rice husk charcoal and KOH 1:4 (dry weight). And physical activation was done by flewing N2 gas 100 mL / min and CO2 with flow rate varied 100, 200, 300, and 400 mL / min at a temperature of 800°C for 1 h. The highest iodine number of activated carbon obtained from chemical physics at a rate of N2 100 mL / min and CO2 100 mL / min, that is 793,04 mg / g, while the lowest iodine number obtained on activated carbon yang physical chemistry N2 flow 100 mL / min only 583.26 mg / g. For comparison, also made the activated carbon made by physical activation only method and chemistry only. For activated carbon that made by physical and chemical activation only just acquired iodine number at 421,09 mg / g and 496,09 mg / g. Activated carbon that has the highest iodine number has 13,062% moisture content, ash content 8,588%, and the missing parts on heating 950°C 23,123%."

"Dalam penelitian ini dilakukan pembuatan karbon aktif yang berbahan baku dari cangkang sawit dan melihat pengaruh aktivasi kimia dan fisika terhadap sifat karbon aktif yang dihasilkan. Karbonisasi dilakukan pada suhu 400oC. Pada aktivasi kimia digunakan aktivator H3PO4 4M , sedangkan pada aktivasi fisika digunakan aliran gas N2 dan gas CO2 yang laju alirnya divariasikan ( 100 mL/menit, 200 mL/menit, 300 mL/menit dan 400 mL/menit). Karakterisasi karbon aktif yang dipelajari dalam penelitian ini adalah rendemen, kadar air, kadar zat mudah menguap, kadar abu dan bilangan iodin. Hasil penelitian menunjukkan bahwa karbon aktif terbaik berdasarkan daya jerap iodinnya adalah karbon yang mengalami aktivasi kimia (perendaman H3PO4) dan aktivasi fisika dengan menggunakan gas N2 dengan laju alir sebesar 100 mL/menit dilanjutkan gas CO2 dengan laju alir sebesar 200 mL/menit. Karbon ini memiliki bilangan iodin sebesar 678,15 mg/g dengan rendemen sebesar 63,02%, kadar air 14,11%, kadar zat mudah menguap 28,57%, dan kadar abu 4,17%.

---

In this research be held the making of activated carbon by using palm empty bunches (PEB) as the primery ingredients and to see the effect of chemical and physical activation towards the condition of activated carbon produced. Carbonization is done in the temperature of 400oC. In the chemical activation H3PO4 4M is used as activator, meanwhile, in physical activation N2 and CO2 gases is used while varying the speed of flow (100 mL/min, 200 mL/min, 300 mL/min and 400 mL/min). The characteristic of activated carbon that will be studied in this research is yield, humidity, volatile matter, percentage of ash and iodin number.

The result shows that the best activated carbon is based on the iodin number is the carbon that have been through the chemical activation ( H3PO4 soaking) and physical activation by using N2 gas with the speed of flow 200 ml/min. This carbon has the iodin number for 678.15 mg/g with yield 63.02%, water content 14.11%, volatile matter 28.57%, and ash content 4.17%."

"Penelitian ini membuat karbon aktif dari limbah kulit kopi karena sampai saat ini pemanfaatan limbah kulit kopi belum maksimum. Aktivasi yang digunakan adalah aktivasi kimia menggunakan Kalium Karbonat karena berdasarkan penelitian-penelitian sebelumnya, luas permukaan yang dihasilkan dapat bersaing dengan activating agent lain. Variasi yang dilakukan adalah variasi rasio massa activating agent/massa bahan baku 1/1, 3/2, dan 2/1 dan variasi suhu 600°C, 700°C, dan 800°C. Luas permukaan diperoleh dari konversi bilangan iod dengan hasil tertinggi adalah 891 m2/gram yang didapatkan dari suhu aktivasi 800°C dan rasio impregnasi 3/2. Sebagai pembanding, luas permukaan yang diperoleh dari aktivasi fisika menggunakan CO2 adalah 176 m2/gram.

---

This research aims to produce activated carbon from coffee shell waste due to utilization of coffee shell waste that far from maximum. Activation that will be used in this research is chemical activation using Potassium Carbonate because in previous researches show that surface area obtained by this activating agent can compete with other activating agent. The variation in this research is impregnation ratio and temperature. The impregnation ratio is 1/1, 3/2, and 2/1 while the temperature variation is 600°C, 700°C, and 800°C. The surface area is obtained by conversion of iod number with the highest result is 891 m2/gram which produced at temperature 800°C and impregnation ratio 3/2. Physical activation using CO2 is done for comparison and obtains surface area 176 m2/gram."

"Pada penelitian ini dilakukan produksi karbon aktif berbahan baku jerami padi dengan karbonisasi dan dilanjutkan dengan aktivasi kimia menggunakan K2CO3. Penelitian ini bertujuan untuk menganalisis pengaruh lama waktu dan suhu aktivasi pada tahap aktivasi kimia terhadap luas permukaan karbon aktif. Proses aktivasi dilakukan pada variasi suhu 700°C, 800°C, 900°C dan lama waktu aktivasi divariasikan selama 60 menit, 90 menit, dan 120 menit. Hasil yang diperoleh menunjukkan bahwa peningkatan suhu dan lama waktu aktivasi menyebabkan luas permukaan terus mengalami peningkatan hingga suhu aktivasi 900oC dan lama waktu selama 90 menit. Luas permukaan karbon aktif tertinggi sebesar 1.003 m2/g diperoleh dengan aktivasi pada suhu 900oC dan lama waktu selama 90 menit. Activated carbon from rice straw waste is produced in this research with carbonization and followed by chemical activation using potassium carbonate. This research aims to analyze the effect of duration and temperature in activation process. The activation process is held in 700°C, 800°C, 900°C of temperature and 60, 90 and 120 minutes of duration. It shows that surface area is increased by the increasing of activation temperature and duration except the activated carbon with 900°C of activation temperature and 120 minutes of activation duration. Highest surface area is 1,003 m2/g from activated carbon with 900°C of activation temperature and 90 minutes of activation duration."