Hasil Pencarian  ::  Simpan CSV :: Kembali

"Tesis ini untuk mempelajari pengaruh ekstrak batang secang (caesalpinia sappan l) sebagai inhibitor korosi ramah lingkungan terhadap baja karbon API 5L Gr B di lingkungan 3.5% NaCl. Metode pengujian dilakukan dengan Linier Polarisasi dan EIS (Electroscopy Impedance Spectroscopy). Ekstrak batang secang dapat menurunkan laju korosi sampai dengan efisiensi sebesar 53.18% berdasarkan hasil pengujian polarisasi dan efisiensi sebesar 84.64% sesuai hasil pengujian EIS. Efisiensi inhibitor paling efektif dihasilkan pada konsentrasi 2.0 ml/400 ml NaCl. Dari hasil pengujian kinerja inhibitor berkurang seiring dengan kenaikan temperatur larutan ekstrak secang. Inhibitor merupakan tipe campuran (mixed inhibitor) dengan kecenderungan lebih dominan ke arah katodik. Hasil evaluasi menunjukan fenomena mekanisme absorbsi molekul inhibitor secang terjadi secara fisika (physicasorption) berdasarkan model Langmuir Isother.

---

This thesis is to investigate secang hearthwood extraction (caesalpinia sappan l) as a corrosion inhibitor on carbon steel metal (API 5L Gr B) in 3.5% NaCl environment. This research utilize polarization linier and EIS (Electrochemical Impedance Spectroscopy) for the measurement method. Secang extraction is adequate to reduce corrosion rate until efficiency of 53.18% based on polarization measurement and efficiency of 84.64% as EIS measurement result. The most effective concentration of inhibitor reducing the corrosion rate is reached at 2.0 ml/400 ml 3.5% NaCl. Investigation show inhibitor efficiency will decrease as temperature increasing. Polarization study indicate secang is mixed type inhibitor, with predominant cathodic effectiveness. As the evaluation, the phenomena of inhibitor molecule adsorption is physicsorption mechanism and obeys Langmuir Isotherm model."

"Kebutuhan akan inhibitor korosi ramah lingkungan semakin berkembang, sehingga penelitian untuk mencari alternatif ekstrak tumbuhan sebagai inhibitor korosi semakin meningkat. Kayu secang dipercaya memiliki kandungan antioksidan yang dapat berperan dalam menghambat laju korosi yang pada material. Penelitian ini dilakukan untuk melihat efek penambahan ekstrak Kayu Secang (KS) terhadap laju korosi dari Baja API 5L X52 dalam Larutan 3,5% NaCl dan juga melihat sifat sinergis inhibitor saat ekstrak KS dikombinasikan dengan ekstrak Kubis Merah (KM) yang sebelumnya telah dilaporkan efektif sebagai inhibitor korosi.Beberapa pengujian dilakukan untuk mengevaluasi KS sebagai inhibitor korosi. Metode Polarisasi dan EIS digunakan untuk melihat efektifitas ekstrak KS dan kombinasinya dengan ekstrak KM sebagai inhibitor korosi dengan variasi konsentrasi yang ditambahkan. FTIR digunakan untuk mengkarakterisasi gugus fungsi yang terkandung dalam ekstrak KS dan KM. Model adsorpsi isotherm digunakan untuk melihat mekanisme adsorpsi dari ekstrak.Dari hasil Polarisasi menunjukan penambahan ekstrak KS akan menurunkan laju korosi dari 0,172 mm/tahun menjadi 0,04 mm/tahun hingga konsentrasi 0,75 ml dalam 200 ml 3,5% NaCl, dan pengujian EIS mendukung hasil tersebut. Pengabungan ekstrak KS dengan KM menunjukan efek anti-sinergi melihat dari nilai sinergistik parameter yang didapat <1. Peningkatan efisiensi inhibisi pada komposisi 0,1 ml dan 0,2 ml KS dalam 2,5 ml KM, diperkirakan karena ekstrak yang ditambahkan belum mencapai titik optimum.Hasil FTIR menunjukan ekstrak KS memiliki gugus C=O yang berperan dalam proses adsorpsi dan gugus ?OH (hydroxil) yang menunjukan sifat antioksidan. Ekstrak KS dan juga campurannya teradsorpsi mengikuti model Langmuir isotherm dimana adsorpsi yang terjadi adalah monolayer dan tidak ada reaksi antar molekul. Nilai energi bebas menunjukan bahwa proses adsorpsi terjadi secara spontan dan jenis ikatan yang terjadi dalam proses adsorpsi adalah secara fisik/physicsorption dengan nilai -20,79 KJ/mol untuk ekstrak KS, dan -7,08 KJ/mol untuk Ekstrak KS+KM

---

The needs of green corrosion inhibitors is growing, thus searching for the alternative plants extract to be used as corrosion inbitor is increasing. Caesalpinia sappan L (KS) believed to contain antioxidant that may play role in inhibiting the corrosion rate of material. This study was conducted to understand the inhibitive properties owned by the extract of KS on the API 5L X52 Material in 3.5%NaCl and to assess the sinergistic effect when KS is combined with Red Cabbage (KM) extract which already proven as alternative corrosion inhibitor.

Several tests were conducted to evaluate KS as green corrosion inhibitor. Tafel Polarization and EIS methods were used to assess the effectiveness of KS and its combination with KM as corrosion inhibitor at various concentration in 3.5% NaCl. FTIR method was used to characterize the functional groups contained in the extract. Adsorption isotherm was used to recognize the adsorption mechanism of the extracts.

The polarization results shows the inhibitive properties of KS thus reduce the corrosion rate of material from 0.172mm/year to 0.04mm/year with addition of 0.75ml of KS in 200ml 3.5%NaCl, meanwhile EIS result supports the polarization results. Mixing of KS and KM shows anti-synergistic effect, which shown on synergistic parameter value <1 for any volume addition of KS. An increase in inhibition efficiency on 0.1ml and 0.2ml KS composition of the mixture is expected due the mixture has not reached the critical point.

While FTIR results show KS and KM both has a C = O functional groups that play a role in the adsorption process and the -OH (hydroxil) which shows antioxidant properties. From the verification plot of several isotherm models, the KS extract and its mixture follows Langmuir Isotherm, which mean the inhibitive layer adsorbed is considered monolayer and there is no reaction between the active molecules. Thus from the calculation of adsorption free energy we have -20.79KJ/mol for KS and - 7.08KJ/mol, thereof the adsorption process considered as physicsorption and the adsorption occurs due to electrostatic bond. The minus (-) sign indicates the adsorption process is spontaneous."

"ABSTRAKKandungan antioksidan pada teh rosela merah, asam askorbat, dapatdikembangkan sebagai inhibitor untuk menghambat laju korosi untuk baja karbonrendah di lingkungan NaCl 3,5%. Metode yang digunakan adalah metodekehilangan berat dengan variasi waktu perendaman (3, 6, 9, 12 hari). Pada semuawaktu perendaman, konsentrasi teh rosela merah yang digunakan adalah 10 gpl,sedangkan penambahan inhibitor teh rosela merah sebanyak 2 ml. Hasil penelitianini dapat ditunjukkan oleh nilai efisiensi yang diperoleh, efisiensi terendah sebesar8% pada waktu pengujian 3 hari, sedangkan efisiensi optimum sebesar 16% padapengujian 9 hari.

---

AbstractThe content of antioxidants in red roselle tea, ascorbic acid, can be developed asan inhibitor to inhibit corrosion rate for low carbon steel in 3.5% sodium chloridesolution. The method that used is a method of weight loss with variation ofimmersion time (3, 6, 9, 12 days). In all the immersion time, concentration of redroselle tea that used was 10 gpl, while the addition of inhibitors of red rosella teaas much as 2 ml. The results could be demonstrated by the efficiency valuesobtained, the lowest efficiency of 8% at 3 days of testing, while the optimumefficiency of 16% at 9 days of testing."

"Korosi dapat menghambat produksi minyak dan gas serta menyebabkan kerugian untuk industri. Salah satu cara untuk mencegah dan mengurangi dampak korosi adalah dengan menambahkan inhibitor pada lingkungan korosif. Inhibitor ramah lingkungan atau yang biasa disebut green inhibitor belakangan ini banyak diteliti karena dapat mencegah terjadinya korosi namun tetap ramah lingkungan dan hemat biaya. Kayu sarampa (Xylocarpus moluccensis) merupakan salah satu tanaman potensial yang dapat digunakan sebagai inhibitor korosi. Pengujian yang dilakukan pada penelitian ini meliputi pengujian polarisasi, EIS, FTIR, flavonoid dan phenolic content, serta pengujian AFM. Hasil pengujian polarisasi menunjukkan efisiensi optimal inhibitor ekstrak kayu sarampa sebesar 68% pada temperatur 40°C dengan konsentrasi 500 ppm. Jenis inhibitor ekstrak kayu sarampa adalah tipe campuran yang telah diketahui dari nilai Ecorr. Nilai Rct yang dihasilkan dari kurva EIS Nyquist menunjukkan adanya peningkatan seiring dengan meningkatnya temperatur. Dengan adanya waktu perendaman selama 60 menit dapat meningkatkan efisiensi inhibitor mencapai 80% dan nilai Rct juga meningkat. Dari hasil perhitungan dengan metode Langmuir diketahui bahwa mekanisme adsorpsi ekstrak kayu sarampa adalah fisisorpsi dan adsorpsi terjadi secara eksotermik. Hasil FTIR menunjukkan adanya gugus O-H yang dapat berperan sebagai antioksidan sehingga dapat menghambat korosi. Setelah dilakukan uji morfologi dengan AFM, diketahui bahwa permukaan baja karbon yang direndam dengan inhibitor akan memiliki permukaan yang lebih halus.

---

Corrosion can hinder oil and gas production and cause industrial losses. One way to prevent and reduce the impact of corrosion is to add inhibitors to the corrosive environment. Environmentally friendly inhibitors or commonly called green inhibitors have recently been widely studied because they can prevent corrosion but are still environmentally friendly and cost effective. Sarampa wood (Xylocarpus moluccensis) is a potential plant that can be used as a corrosion inhibitor. The tests carried out in this study included testing for polarization, EIS, FTIR, flavonoids and phenolic content, as well as testing for AFM. The results of the polarization test showed that the optimal efficiency of the inhibitor of sarampa wood extract was 68% at a temperature of 40°C with a concentration of 500 ppm. The inhibitor type of sarampa wood extract is a mixed type which is known from the Ecorr value. The Rct value generated from the EIS Nyquist curve shows an increase with increasing temperature. With the immersion time for 60 minutes can increase the efficiency of the inhibitor up to 80% and the Rct value also increases. From the results of calculations using the Langmuir method, it is known that the adsorption mechanism of sarampa wood extract is physisorption and adsorption occurs exothermic. FTIR results indicate the presence of O-H groups that can act as antioxidants so that they can inhibit corrosion. From morphological tests with AFM, it is known that the surface of carbon steel soaked with inhibitor will have a smoother surface. "

"ABSTRAKTesis ini mempelajari pengaruh injeksi ekstrak buah mengkudu sebagai greeninhibitor corrosion terhadap baja karbon rendah dalam lingkungan NaCl 3,5%.Berdasarkan pengujian weight loss diperoleh informasi bahwa pada perendaman12 hari dengan konsentrasi 3mL menunjukkan laju korosi terendah yaitu 1.385 mpydengan efisiensi 76,92 %. Pengujian dengan polarisasi menunjukkan bahwa denganvariasi konsentrasi inhibitor diperoleh laju korosi terendah pada konsentrasi 3 mLyaitu 6,68 mpy dengan efisiensinya 68,08 %. Mekanisme inhibisi inhibitor ekstrakbuah mengkudu pada permukaan baja karbon dapat diamati dari kurva polarisasiyang memberikan informasi bahwa inhibitor dari ekstrak buah mengkudu termasukmixed type inhibitor yang merupakan ciri khas inhibitor organik dengan modeladsorpsi Langmuir yang menunjukkan telah terbentuk lapisan monolayer.

---

ABSTRACTThe effect of injecting noni fruit extracts, as a green inhibitor corrosion for a lowcarbon steel in 3.5% NaCl solution has been studied in this thesis. Based on theweight loss experiment, it was known that immersing a low carbon steel in 3mL3.5% NaCl solution for 12 days produced the the lowest corrosion rates of 1.385mpy with 76.92%inhibitor efficiencies. On the other hand, polarization experimentshowed the minimum corrosion rate of 6.68 mpy with 68.08% inhibitor efficiencies.Inhibition mechanism of noni fruit extract on carbon steel surface can be observedfrom the polarization curves. From that curve, it was shown that the monolayercoating has been formed. This phenomena was the characteristic of the organicinhibitor with the Langmuir adsorption models."

"Indonesia memiliki potensi cengkeh yang melimpah,daunnya dapat gugur setiap minggunya 0.96 kg/pohon. Inhibitor yang digunakan adalah ekstrak daun cengkeh dengan konsentrasi 1ml,2ml,3ml,4ml,5ml dan minyak cengkeh dengan konsentrasi 2ml,4ml,6ml,8ml,10ml. Pengujian dilakukan dengan metode linear polarisasi, Fourier Transform Infrared Spectroscopy ( FTIR ), Gas Chromatography Mass Spectroscopy ( GCMS ), dan Eletrochemical Impedance Spectroscopy ( EIS ). Konsentrasi optimum pada ekstrak daun cengkeh berada pada konsentrasi 4 ml dengan laju korosi 0.042 mm/year dan efisiensi 46.6 % sedangkan minyak cengkeh konsentrasi optimumnya berada pada konsentrasi 8 ml dengan laju korosi 0.001 mm/year dengan efisiensi 98.6 %. FTIR menunjukkan gugus - gugus fungsi yang berada di dalam inhibitor dan diperkuat dengan hasil GCMS untuk mengetahui senyawa aktif yang berada dalam inhibitor. Pengujian FTIR juga menunjukkan bahwa gugus - gugus fungsi pada inhibitor menempel pada permukaan sampel ketika sampel di rendam. Mekanisme adsorpsi dari kedua inhibitor adalah physical adsorption dengan nilai ΔGads pada inhibitor ekstrak daun cengkeh sebesar -7.575 kJ/mol, dan - 12.142 kJ/mol untuk inhibitor minyak cengkeh. EIS menunjukkan adanya peningkatan nilai tahanan charge transfer pada setiap kenaikan konsentrasi inhibitor dan nilai dari Cdl menurun yang menunjukkan bahwa terjadi pembentukan lapisan protektif. Nilai charge transfer dari inhibitor minyak cengkeh lebih besar yang berarti minyak cengkeh memiliki kemampuan inhibisi lebih baik dan ini diperkuat dari hasil polarisasi. Kedua jenis inhibitor ini termasuk dalam jenis inhibitor campuran (mix type inhibitor).

---

Indonesia has abundant potential clove, leaves can fall every week 0.96 kg/tree. Inhibitor which used on this research are clove leave extract with concentration 1ml,2ml,3ml,4ml,5ml and clove oil with concentration 2ml,4ml,6ml,8ml,10ml. Inhibitor are examined by linear polarization, Fourier Transform Infrared Spectroscopy ( FTIR ), Gas Chromatography Mass Spectroscopy ( GCMS ), and Electrochemical Impedance Spectroscopy ( EIS ). The result show that optimum concentration of clove leave extract is at 4 ml with corrosion rate 0.042 mm/year and efficiency 46.6% where as optimum concentration of clove oil is at 8 ml with corrosion rate 0.001 mm/year and efficiency 98.6 %. FTIR obtain functional group which contained in inhibitor and GCMS result also show active compound in inhibitor. FTIR show that functional group in inhibitor adsorp on the metal surface when sample is soaked in inhibitor. Adsorption mechanism of these inhibitor is physical adsorption with ΔGads of clove leave extract inhibitor is -7.575 kJ/mol, and - 12.142 kJ/mol for clove oil inhibitor. EIS show increasing charge transfer resistance with increasing inhibitor concentration and decreasing Cdl also show there are protective film forming. The charge transfer resistance of clove oil inhibitor higher, means clove oil has better inhibition than clove leaves extract. Both of these inhibitor are included in mix type inhibitor."

"Peningkatan kebutuhan bahan penghambat korosi yang aman dan ramah lingkungan menjadi perhatian utama, terutama dalam industri berbasis baja karbon rendah. Salah satu penyebab utama kerusakan pada material ini adalah korosi yang dipercepat oleh penggunaan larutan asam seperti H2SO4. Salah satu cara untuk mengurangi laju korosi dari material adalah dengan menambahkan inhibitor organik dari ekstrak tumbuhan yang mengandung senyawa bioaktif. Pada penelitian ini, dilakukan penambahan variasi konsentrasi inhibitor dari ekstrak akar pepaya (Carica papaya L.) dengan melarutkan ke dalam larutan 1M asam sulfat (H2SO4), dimana asam sulfat merupakan senyawa yang digunakan untuk acid pickling pada baja. Dilakukan uji Optical Emission Spectroscopy (OES) untuk mengetahui komposisi kimia dari material uji sesuai dengan spesifikasi material API 5L dan uji Fourier Transform Infra Red (FTIR) untuk mengetahui senyawa yang terkandung dalam ekstrak akar pepaya yang akan digunakan sebagai inhibitor pada baja karbon rendah API 5L grade B. Dilakukan juga pengujian Linear polarisasi untuk mengetahui efisiensi laju korosi pada penambahan variasi ekstrak inhibitor akar pepaya. Kemudian, dilakukan pengujian Electrochemical impedance spectroscopy (EIS) untuk menginterpretasikan sistem variasi konsentrasi inhibitor akar pepaya pada rangkaian listrik. Hasil pengujian menunjukkan bahwa material uji sesuai dengan spesifikasi API 5L grade B, ekstrak akar pepaya mengandung senyawa bio aktif flavonoid, saponin, alkaloid, dan tanin yang terbukti menurunkan laju korosi dengan variasi konsentrasi dari 4 ml sampai 20 ml terbukti menurunkan laju korosi dari 1,172 mm/year menjadi 0,074 mm/year dengan efisiensi maksimum 93,68% pada konsentrasi 20 ml.

---

The increasing need for safe and environmentally friendly corrosion inhibiting materials is a major concern, especially in low carbon steel-based industries. One of the main causes of damage to these materials is accelerated corrosion by the use of acidic solutions such as H2SO4. One way to reduce the corrosion rate of the material is to add organic inhibitors from plant extracts containing bioactive compounds. In this study, the addition of various concentrations of inhibitors from Akar Pepaya extract (Carica papaya L.) was carried out by dissolving it in 1M sulfuric acid (H2SO4) solution, where sulfuric acid is a compound used for acid pickling on steel. Optical Emission Spectroscopy (OES) test was conducted to determine the chemical composition of the test material in accordance with API 5L material specifications and Fourier Transform Infra Red (FTIR) test to determine the compounds contained in Akar Pepaya extract which will be used as an inhibitor on API 5L grade B low carbon steel. Linear polarization testing was also carried out to determine the efficiency of the corrosion rate in the addition of akar pepaya inhibitor extract variations. Then, Electrochemical impedance spectroscopy (EIS) testing was carried out to interpret the system of variations in Akar Pepaya inhibitor concentration in electrical circuits. The test results show that the test material is in accordance with API 5L grade B specifications, Akar Pepaya extract contains bioactive compounds flavonoids, saponins, alkaloids, and tannins which are proven to reduce the corrosion rate with a concentration variation from 4 ml to 20 ml which is proven to reduce the corrosion rate from 1,172 mm/year to 0,074 mm/year with a maximum efficiency of 93,68% at a concentration of 20 ml."

"Ekstrak syzygium cumini (ESC) dievaluasi sebagai inhibitor korosi ramah lingkungan pada sampel carbon steel API 5L dalam larutan korosif HCl 1M dengan variasi komposisi 0, 100, 200, 300, 400 dan 500 ppm pada temperatur 303-323 K. Efisiensi penghambatan korosi diukur menggunakan metode elektokimia potensiodinamik polarisasi dan electrochemical impedance spectroscopy. Efisiensi inhibisi meningkat seiring peningkatan konsentrasi ESC namun berbanding terbalik dengan peningkatan temperatur. Berdasarkan hasil uji elektrokimia, efisiensi inhibisi tertinggi 90% diperoleh dengan penambahan 500 ppm ESC. Residence time meningkatkan efisiensi inhibisi hingga 97% pada waktu perendaman 60 menit. ESC diklasifikasikan kedalam tipe inhibitor campuran dan mengalami mekanisme inhibisi dengan cara adsorpsi monolayer secara physisorption, dengan mengikuti model isoterm adsorpsi Langmuir. Hasil spektrum FTIR membuktikan bahwa ESC mengandung gugus hidroksil fenol, karbonil dan aromatik yang berguna dalam aktifitas antioksidan. Selain itu, karakterisasi AFM menunjukan tingkat kekarasan rata-rata menurun dari 48.8 nm ke 7.2 nm, kehalusan permukaan menunjukan terbentuknya lapisan film pelindung pada permukaan carbon steel.

---

Syzygium cumini extract (ESC) was evaluated as an environmentally friendly corrosion inhibitor on API 5L carbon steel samples in 1M HCl corrosive solution with composition variations of 0, 100, 200, 300, 400 and 500 ppm at a temperature of 303 – 323 K. Corrosion inhibition efficiency was measured using Polarization potentiodynamic electrochemical methods and electrochemical impedance spectroscopy. The inhibition efficiency increased with increasing ESC concentration but inversely with increasing temperature. Based on the results of electrochemical tests, the highest inhibition efficiency of 90% was obtained with the addition of 500 ppm ESC. Residence time increases the inhibition efficiency up to 97% at a 60 minute immersion time. ESC is classified into mixed type inhibitor and undergoes an inhibition mechanism by physisorption monolayer adsorption, obey to Langmuir adsorption isotherm model. The results of the FTIR spectrum prove that ESC contains phenolic, carbonyl and aromatic hydroxyl groups which are useful in antioxidant activity. Furthemore, the AFM characterization showed that the average roughness decreased from 48.8 nm to 7.2 nm, the surface smoothness indicated the for mation of a protective film on the carbon steel surface. "

"ABSTRAKBaja karbon merupakan material umum yang digunakan sebagai bahan konstruksi pipa dalam industri minyak. Namun, sifat baja karbon sangat rentan untuk terjadinya korosi. Pada penelitian ini digunakan ekstrak tanaman daun pletekan fraksi air dan fraksi kloroform sebagai inhibitor korosi pada baja karbon. Efisiensi Inhibitor ditentukan berdasarkan metode weight loss. Karakterisasi ekstrak fraksi kloroform dan fraksi air serta lapisan yang terbentuk pada permukaan baja karbon diamati dengan Fourier Transform Infra Red FTIR , Morfologi permukaan baja karbon dengan Scanning Electron Microscopy-Energy Disspersive X-Ray SEM-EDS , serta keberadaan produk korosi Fe2O3 dengan X-Ray Diffraction XRD . Keberhasilan inhibitor korosi dalam melindungi baja karbon terlihat dari persen efisiensi inhibitor. Hasil seleksi didapatkan inhibitor terbaik adalah fraksi kloroform dengan efisiensi inhibitor sebesar 93,08 pada konsentrasi 750 ppm dan suhu 30oC dalam media HCl dan 94,44 dalam media brine. Adsorpsi inhibitor korosi fraksi air dan fraksi kloroform pada permukaan baja karbon mengikuti isoterm adsopsi Langmuir.

---

ABSTRACTCarbon steel is a common material used as a construction material in the oil industry pipes. However, the nature of the carbon steel is very susceptible to corrosion. In this study used extracts of the leaves of plants pletekan water fraction and chloroform fraction as a corrosion inhibitor in carbon steel. Inhibitor efficiency is determined by the method of weight loss Characterization extract chloroform fraction and water fraction and a layer formed on the surface of carbon steel were observed by Fourier Transform Infra Red FTIR , morphology carbon steel surface by Scanning Electron Microscopy Energy Dispersive X ray SEM EDS , as well as the presence of corrosion products Fe2O3 with X Ray Diffraction XRD . The success of corrosion inhibitors to protect carbon steel is determined by percent efficiency inhibitor. The result of selection is best inhibitors obtained chloroform fraction with inhibitor efficiency at 93.08 at a concentration of 750 ppm and the temperature in the media 30 C HCl and 94.44 in the medium brine. Adsorption corrosion inhibitor water fraction and chloroform fraction on the surface of carbon steel followed Langmuir isotherm adsorption."

"Imidazolin merupakan senyawa heterosiklik yang telah banyak dikenal dalam industri perminyakan sebagai inhibitor korosi pada kilang minyak baja di perairan laut. Pada penelitian ini telah dilakukan sintesis senyawa turunan imidazolin menggunakan metode MAOS (Microwave Assisted Organic Synthesis) dengan mereaksikan tetraetilenpentamina (TEPA) dan asam oleat (AO) pada perbandingan ekivalen reaksi 1:1 membentuk imidazolin TEPA-AO dan 1:2 membentuk bis-imidazolin TEPA-AO dengan variasi waktu reaksi 7, 9, 11, dan 13 menit. Persen yield optimum senyawa imidazolin TEPA-AO diperoleh pada waktu sintesis 9 menit (82,62%) dan senyawa bis-imidazolin TEPA-AO pada 11 menit (88,56%). Kedua senyawa hasil sintesis kemudian dimurnikan dengan metode ekstraksi cair-cair dan dianalisis menggunakan kromatografi lapis tipis (KLT). Struktur kedua senyawa hasil sintesis telah dikonfirmasi berdasarkan data spektrum UV-Vis, FTIR, dan 1H-NMR. Penentuan aktivitas kedua senyawa hasil sintesis sebagai inhibitor korosi dilakukan pada baja karbon dalam larutan 1% NaCl dengan variasi konsentrasi (100, 200, 300, 400, dan 500 ppm) menggunakan metode polarisasi Tafel. Persen efisiensi inhibisi (%EI) tertinggi untuk kedua senyawa diperoleh pada penambahan konsentrasi 500 ppm berturut-turut sebesar 86,37% dan 89,70% untuk senyawa imidazolin TEPA-AO dan bis-imidazolin TEPA-AO. Untuk mengetahui mode inhibisi korosi pada baja karbon, ada tidaknya perubahan struktur senyawa setelah uji inhibisi korosi dianalisis menggunakan FTIR. Berdasarkan spektrum FTIR diperoleh bahwa masih terdapat puncak-puncak khas cincin senyawa imidazolin dan juga ditemukan perubahan struktur dari kedua senyawa hasil sintesis setelah dilakukan uji inhibisi korosi, sehingga dapat dikatakan mode inhibisi korosi dari kedua senyawa tersebut terjadi secara adsorpsi fisik dengan sedikit adsorpsi kimia. Dari penelitian ini dapat disimpulkan bahwa senyawa imidazolin TEPA-AO dan bis-imidazolin TEPA-AO dapat digunakan sebagai inhibitor korosi terhadap baja karbon dalam larutan 1% NaCl.

---

Imidazoline is a heterocyclic compound which has been widely known in the oilfields industry as corrosion inhibitor for oil refineries in sea environment. In this research, imidazoline derivatives was successfully synthesized by reacting tetraethylenepentamine (TEPA) and oleic acid (OA) using MAOS (Microwave Assisted Organic Synthesis) method at equivalent ratio of 1:1 to yield TEPA-OA imidazoline and 1:2 to yield TEPA-OA bis-imidazoline in various reaction times (7, 9, 11, and 13 minuntes). The optimum yield of TEPA-OA imidazoline was obtained at 9 minutes reaction time (82.62%) and TEPA-OA bis-imidazoline at 11 minutes (88.56%). Both of synthesized compounds then was purified by liquid-liquid extraction method and analyzed by thin layer chromatography (TLC). The structure of all synthesized compounds was confirmed based on UV-Vis, FTIR, and 1H-NMR spectral data. Corrosion inhibition activity of all synthesized compounds was determined towards carbon steel in 1% NaCl solution with variation of imidazoline concentration (100, 200, 300, 400, and 500 ppm) using Tafel polarization method. The highest percentage of inhibition efficiency (%IE) was obtained at 500 ppm with 86.37% dan 89.70% for TEPA-OA imidazoline and TEPA-AO bis-imidazoline, respectively. To analyze corrosion inhibition mode towards carbon steel, the structure of synthesized compound after corrosion inhibition test was analyzed using FTIR. Based on FTIR spectra, the structure of both synthesized compounds still had imidazolines ring-peaks characteristics and were slightly altered after corrosion inhibition test, therefore corrosion inhibition mode of synthesized compounds were physic- and slightly chemisorption. From this research, it can be concluded that TEPA-OA imidazoline and TEPA-OA bis-imidazoline compounds can be used as a corrosion inhibitor towards carbon steel in 1% NaCl solution."