"The characteristics of coatings formed by Plasma Electrolytic Oxidation (PEO) are affected by the composition of metal substrates. In this work, the effect of alloying element Ca (0, 1 and 2 wt%) on the degradation behavior and apatite-forming ability of PEO coated AZ61 magnesium alloys was clarified by means of polarization measurements in 0.9% NaCl solution and an in-vitro test in Simulated Body Fluid (SBF), respectively. The AZ61 alloys were subjected to plasma electrolytic oxidation at a constant current of 200 A/m2 at 25°C for 8 min in 0.5 M Na3PO4 solution. The surface investigation suggested no significant effect of Ca content on the morphology of the PEO coating formed on the AZ61 specimens. The coatings exhibited an eruption-like structure decorated with micropores and microcracks. Their average thicknesses were 13.2, 17.4 and 14.3 µm for AZ61, AZ61-1Ca and AZ61-2Ca, respectively. The polarization measurements showed no significant difference in the corrosion potentials (-1.60 VAg/AgCl) and corrosion current densities (1.61×10-5 A cm-2) of all the coated specimens. Similarly, there was no significant effect of Ca on the apatite-forming ability in SBF, as indicated by the lack of apatite deposition on all the coated specimens after 14 days of immersion. Further sealing of the PEO coatings by chemical treatment in NaOH solution is suggested to enhance the corrosion resistance."

"Penggunaan paduan magnesium sebagai material bio-metalik memiliki potensi untuk terurai secara alami dalam cairan tubuh dan berperan penting dalam struktur tulang. Dalam aplikasinya, modifikasi permukaan paduan magnesium diperlukan untuk meningkatkan sifat mekanik dan anti-korosinya. Salah satu metode pelapisan menjanjikan adalah Plasma Electrolytic Oxidation (PEO). Pada penelitian ini, dilakukan pelapisan paduan magnesium AZ31 dengan metode PEO menggunakan pendekatan one-step dan two-step. Parameter ditetapkan sama dalam penggunaan kedua metode ini yaitu meliputi waktu, rapat arus, sumber tegangan, dan suhu. Pada metode two-step PEO, lapisan HA (hidroksiapatit) disisipkan ke dalam lapisan oksida yang terbentuk. Hasil penelitian menunjukkan bahwa metode two-step PEO menghasilkan lapisan dengan karakteristik lebih baik dibandingkan metode one-step PEO. Lapisan two-step PEO memiliki persentase pori lebih kecil, ketebalan lapisan lebih besar, dan nilai spesifik abrasi lebih rendah. Selain itu, fasa kristalin baru, yaitu Ca5(PO4)3OH atau HA, terdeteksi dalam lapisan two-step PEO. Penggunaan metode two-step PEO dengan penambahan hidroksiapatit memberikan hasil lebih baik dalam hal karakterisasi morfologi dan sifat ketahanan aus. Dalam konteks aplikasi biomedis, hal ini menunjukkan potensi penggunaan paduan magnesium dengan metode pelapisan two-step PEO sebagai material cocok untuk aplikasi tulang dan gigi manusia.

---

The use of magnesium alloy as a bio-metallic material has the potential to decompose naturally in body fluids and plays an essential role in bone structure. In its application, surface modification of magnesium alloy is required to improve its mechanical and anti-corrosion properties. One of the promising coating methods is Plasma Electrolytic Oxidation (PEO). In this study, the coating of magnesium alloy AZ31 was carried out using a one-step and two-step approach using the PEO method. The parameters used in both methods include the same time, current density, voltage source, and temperature. In the two-step PEO method, a HA (hydroxyapatite) layer is inserted into the formed oxide layer. The results showed that the two-step PEO method produced layers with better characteristics than the one-step PEO method. The PEO two-step coating has a smaller pore percentage, a larger layer thickness, and a lower abrasion-specific value. In addition, a new crystalline phase, namely Ca5(PO4)3OH or HA, was detected in the two-step PEO layer. The two-step PEO method with hydroxyapatite adds better morphology characterization and wear resistance properties. This demonstrates the potential use of magnesium alloys coated by the two-step PEO method as suitable materials for human bone and tooth applications in biomedical applications."

"Magnesium dan paduannya memiliki karakteristik biodegradable sebagai bahan implan non-permanen. Namun, tantangan utama yang dimiliki oleh magnesium adalah ketahanan korosi yang rendah. Salah satu modifikasi permukaan yang dapat meningkatkan ketahanan korosi Mg dan paduannya adalah Plasma Electrolytic Oxidation (PEO). Namun, lapisan oksida pada magnesium hasil PEO protektif sehingga pembentukan mineral tulang berlangsung lambat. Dalam penelitian ini ion Ca2+ ditambahkan dalam bentuk Ca(OH)2 dalam larutan Na3PO4 dan KOH. Untuk mempermudah masuknya Ca ke dalam lapisan PEO, ultrasonikasi diberikan selama proses PEO. Variasi waktu PEO selama 10, 15, dan 20 menit. Berdasarkan hasil analisis fasa XRD, terdapat fasa Mg, Mg3(PO4)2 pada semua fasa lapisan dan tambahan fasa Ca5(PO4)3OH pada lapisan UPEO. Penggunaan ultrasonikasi cenderung menghasilkan permukaan lapisan dengan porositas yang lebih tinggi hingga 16,65%. Hasil uji PDP menunjukkan nilai Icorr terendah dimiliki oleh sampel 20 PEO. Lapisan PEO dan UPEO menghasilkan nilai kekerasan hingga 6 kali lebih tinggi dari substrat. Penambahan Ca dalam elektrolit dan penggunaan ultrasonikasi pada PEO tidak memberikan perubahan karakteristik lapisan secara signifikan.

---

Magnesium and its alloys have biodegradable characteristics. The main challenge that magnesium has is its low corrosion resistance. One of the surface modifications that can increase the corrosion resistance of Mg and its alloys is Plasma Electrolytic Oxidation (PEO). However, the oxide layer on magnesium produced by PEO was protective so that the formation of bone was slow. In this study, Ca2+ ions were added in the form of Ca(OH)2 in a solution of Na3PO4 and KOH. To accelerate of Ca into the PEO layer, ultrasonication is given during the PEO. PEO time variations for 10, 15, and 20 minutes. Based on the results of the XRD phase, there are Mg, Mg3(PO4)2 in all layer phases and Ca5(PO4)3OH phases in the UPEO layer. UPEO tends to produce a layer surface with a higher porosity up to 16.65%. The PDP test results show the lowest Icorr value is owned by a sample of 20 PEO. The PEO and UPEO coating produces a hardness value of up to 6 times higher than the substrate. The addition of Ca in the electrolyte and the use of ultrasonication in PEO did not significantly change the coating characteristics."

"Magnesium dan paduannya telah digunakan di berbagai industri karena memiliki rasio kekuatan terhadap berat yang tinggi, modulus elastisitas dan densitas yang rendah, serta sifat mampu bentuk dan manufaktur yang baik. Namun, magnesium memiliki ketahanan korosi dan aus yang rendah. Untuk mengatasi hal tersebut, diperlukan rekayasa permukaan pada paduan magnesium. Plasma Electrolytic Oxidation (PEO) menghasilkan lapisan keramik oksida yang dapat meningkatkan ketahanan korosi dan aus paduan magnesium. Jenis elektrolit yang digunakan karakteristik dan waktu hidup plasma. Dalam penelitian ini, proses PEO dilakukan pada paduan AZ91 dalam elektrolit berbasis campuran silikat, fosfat, dan hidroksida yaitu Na3PO4, Na2SiO3, dan KOH. Proses PEO dilakukan dengan menggunakan rapat arus konstan sebesar 533 A/m2 selama 10 menit. Parameter proses tersebut dipilih untuk memperlama waktu hidup plasma. Pada penelitian sebelumnya, plasma hanya dapat hidup selama 2 menit. Hasil analisis SEM-EDS menunjukkan bahwa lapisan PEO yang dihasilkan memiliki dua tipe warna, yaitu abu-abu dan putih dengan morfologi dan komposisi berbeda. Bagian putih memiliki morfologi yang tidak seragam dan banyak retakan, dibandingkan dengan bagian abu-abu yang memiliki sedikit pori dan retakan. Ketebalan lapisan yang terbentuk sebesar 53 ± 3 μm. Berdasarkan hasil analisis fasa XRD, terdapat fasa kristal dan amorf Mg2SiO4, Mg3(PO4)2, dan MgO pada lapisan PEO. Hasil tersebut dikonfirmasi oleh hasil analisis EDS dengan terdeteksinya unsur-unsur terkait. Bagian putih memiliki konsentrasi Si yang lebih tinggi dibandingkan bagian abu-abu. Bagian abu-abu memiliki daya tahan abrasi yang lebih tinggi dibandingkan lapisan putih yang ditunjukkan dari nilai spesifikasi abrasinya, yaitu 0,684 × 10-5 mm3/mm dibanding 1,48 × 10-5 mm3/mm. Hasil karakterisasi dan uji mekanik menunjukkan lapisan PEO yang terbentuk tebal dan memiliki ketahanan aus yang baik karena plasma dapat hidup sampai 10 menit.

---

Magnesium and its alloys have been used in various industries due to their high strength-to-weight ratio, low modulus of elasticity and density, as well as good formability and manufacturability. However, magnesium has low corrosion resistance and wear resistance. To overcome these challenges, surface engineering is required for magnesium alloys. Plasma Electrolytic Oxidation (PEO) produces a ceramic oxide layer that can enhance the corrosion resistance and wear resistance of magnesium alloys. The type of electrolyte used determines the characteristics and lifetime of the plasma. In this study, the PEO process was performed on the AZ91 alloy using an electrolyte based on a mixture of silicate, phosphate, and hydroxide, namely Na3PO4, Na2SiO3, and KOH. The PEO process was carried out using a constant current density of 533 A/m2 for 10 minutes. These process parameters were chosen to prolong the plasma lifetime. In previous studies, the plasma could only last for 2 minutes. The results of SEM-EDS analysis showed that the produced PEO layer had two different colors, namely gray and white, with different morphologies and compositions. The white part exhibited non-uniform morphology and numerous cracks compared to the gray part, which had fewer pores and cracks. The thickness of the formed layer was measured to be 53 ± 3 μm. Based on XRD phase analysis, crystal and amorphous phases of amorf Mg2SiO4, Mg3(PO4)2, and MgO were detected in the PEO layer. These findings were confirmed by EDS analysis, which detected related elements. The white part had a higher concentration of Si compared to the gray part. The gray part exhibited higher abrasion resistance compared to the white layer, as indicated by the abrasion specification values, which were 0,684 × 10-5 mm3/mm and 1,48 × 10-5 mm3/mm, respectively. The characterization and mechanical testing results indicated that the formed PEO layer was thick and had good wear resistance due to the plasma lifetime reaching 10 minutes."

"Plasma Electrolytic Oxidation (PEO) merupakan pelapisan permukaan logam dengan plasma anodisasi untuk menghasilkan lapisan tahan karat dan keras. Sifat lapisan yang dihasilkan dikendalikan oleh parameter proses seperti arus dan waktu pembentukan. Proses PEO dilakukan dengan 2 variasi yaitu variasi waktu dan variasi arus dalam larutan 0,5 M Na3PO4. Pada variasi waktu, arus yang digunakan adalah 0,5 A dengan waktu 1, 3, dan 5 menit. Sedangkan pada variasi arus digunakan arus 0,2; 0,3; 0,4 A dan dilakukan pada waktu konstan selama 3 menit. Temperatur elektrolit dijaga tetap 30°C dan diaduk dengan magnetic stirrer dengan kecepatan konstan 300 rpm. Perubahan morfologi sebagai fungsi arus dan waktu diamati menggunakan scanning electron microscope dan energy dispersive X-ray spectroscopy (SEM-EDS). Analisis fasa dilakukan dengan X-ray Diffraction (XRD). Perubahan kekerasan diamati melalui uji kekerasan micro-Vickers. Perubahan sifat korosi diuji dengan metode electrochemical impedance spectroscopy (EIS) dan potentiodynamic polarization (PDP). Hasil karakterisasi menunjukkan fasa kristal yang terbentuk pada lapisan PEO adalah fasa Mg3(PO4)2 yang diidentifikasikan pada puncak 35°, 37°, 49° dan 62° pada pola XRD. Nilai kekerasan lapisan PEO yang terbentuk pada 1, 3 dan 5 menit masing-masing adalah 315,67; 427,67; dan 382,67 HV sedangkan pada arus 0,2; 0,3; dan 0,4 A diperoleh nilai kekerasan lapisan masing-masing sebesar 355; 421,67; dan 459 HV. Hasil uji polarisasi menunjukkan peningkatan ketahanan korosi yang ditunjukkan dengan berkurangnya rapat arus korosi. Semakin kecil rapat arus korosinya maka laju pembentukkan korosi semakin berkurang. Pada variasi waktu 1, 3 dan 5 menit nilai rapat arus korosinya adalah 3,24 x 10-5; 7,76 x 10-7; dan 1,11 x 10-6 A/cm2 sedangkan pada variasi arus 0,2; 0,3; dan 0,4 A nilai rapatarus korosinya adalah 2,26 x 10-6; 3,12 x 10-6; dan 7,60 x 10-7 A/cm2. Hasil EIS menunjukkan bahwa nilai R1 semakin besar yang artinya ketahanan resistansi polarisasi semakin besar dengan meningkatnya waktu dan arus pembentukan. Pada variasi waktu 1, 3 dan 5 menit nilai R1 adalah 42,35; 564,7; dan 574,4 Ω.cm2 sedangkan pada variasi arus 0,2; 0,3; dan 0,4A nilai R1 adalah 254,5; 169; 627,5 Ω.cm2 setelah dicelupkan selama 3 jam.

---

Plasma Electrolytic Oxidation (PEO) is a coating for metal surface by plasma anodization to produce corrosion resistant and hard coating. The resulting coating properties were controlled by process parameters such as formation current and time. The PEO process in this research uses 2 variation: time and current formation in 0,5 M Na3PO4 solution. At the time variation, the current used is 0,5 A with time of 1, 3 and 5 minutes. Whereas in the current variation used 0,2;0,3 and 0,4 A for 3 minutes. The electrolyte temperature was kept at 30 oC and stirred with a magnetic stirrer at 300 rpm. Morphological changes were investigated by using scanning electron microscope and energy dispersive X-ray spectroscopy (SEM-EDS). Phase analysis was performed by X-ray Diffraction (XRD). Hardness changes were observed using micro-Vickers hardness test. Changes in corrosion properties were investigated by electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization (PDP). The phases formed in the PEO layer is Mg3(PO4)2 which identified at the peaks of 35°, 37°, 49° and 62° in the XRD pattern. Hardness of AZ31 alloys at 1, 3 and 5 minutes was 315,67 HV, 427,67 HV and 382,67 HV whilte at currents 0,2;0,3 and 0,4 A is 355 HV, 421,67 HV dan 459 HV. The polarization test results showed an increase in corrosion resistance which is approved by the reduced corrosion current density. The smaller the corrosion current, the rate of corrosion formation decreases. At the time variation of 1, 3 and 5 minutes the value of the corrosion current density is 3,24 x 10-5, 7,76 x 10-7, and 1,11 x 10-6 A/cm2 whereas in the variation of current 0,2; 0,3; and 0,4 A thecorrosion current density is 2,26 x 10-6; 3,12 x 10-6; and 7,60 x 10-7 A/cm2. EIS results showed that the higher value of R1 means the greater the polarization resistance. At the time variation of 1, 3 and 5 minutes the value of R1 are 42.35. 564.7, 574.4 Ω.cm2 whereas in the current variation of 0,2;0,3 and 0,4 A the value of R1 are 254.5, 169, 627.5 Ω.cm2 after being immersed for 3 hours."

"Magnesium (Mg) merupakan logam ringan yang memiliki beragam aplikasi, termasuk dalam industri otomotif dan sebagai bahan implan biodegradable. Meskipun penting, kelemahan utama magnesium adalah ketahanan korosinya yang rendah terutama dalam lingkungan yang mengandung klorida. Oleh karena itu, perbaikan sifat korosi magnesium diperlukan melalui rekayasa permukaan. Salah satu metode yang efektif dalam rekayasa permukaan magnesium adalah metode plasma electrolytic oxidation (PEO). Penelitian ini bertujuan untuk memahami pengaruh perbedaan kation yang digunakan sebagai elektrolit untuk PEO terhadap sifat mekanik dan ketahanan korosi lapisan PEO pada paduan magnesium AZ31. Elektrolit yang dimaksud adalah KOH dan NaOH. Dalam penelitian ini, dilakukan proses PEO pada paduan magnesium AZ31 menggunakan larutan basa seperti KOH, NaOH, dan campuran KNa. Proses ini menggunakan rapat arus 1000 A/m2 pada suhu 30ºC dalam waktu 10 menit. Sampel yang dihasilkan kemudian dianalisis menggunakan beberapa metode, termasuk pengamatan morfologi dan komposisi dengan SEM-EDS, uji mekanik untuk mengukur ketahanan aus dan kekerasan, serta eksperimen elektrokimia dengan EIS dan PDP. Larutan KOH, NaOH, dan KNa dapat meningkatkan ketahan korosi dan sifat mekanik lapisan PEO pada paduan magnesium AZ31. Data uji korosi menunjukkan bahwa larutan KOH memiliki tingkat korosi paling tinggi dibandingkan dengan NaOH dan KNa dengan nilai rapat arus dan resistansi polarisasi sebesar 7,31 × 10-5 A/cm2 dan 280 Ω.cm2 . Uji mekanik mengindikasikan peningkatan kekerasan dan ketahanan aus pada sampel yang diuji dengan larutan campuran KNa dengan nilai kekerasan sebesar 71 Hv dan nilai spesifik abrasi sebesar 9,07 × 10-6 mm3 /mm. Hal ini disebabkan oleh nilai at% dari unsur O pada elektrolit KNa lebih tinggi dibandingkan elektrolit NaOH dan KOH.

---

Magnesium (Mg) is a lightweight metal with diverse applications, including the automotive industry and as a material for biodegradable implants. Despite its significance, magnesium's primary weakness lies in its low corrosion resistance, particularly in chloride-containing environments. Therefore, improving magnesium's corrosion resistance is essential through surface engineering. One effective method for surface engineering of magnesium is the Plasma Electrolytic Oxidation (PEO) technique. This research aims to understand the influence of different cations used as electrolytes for PEO on the mechanical properties and corrosion resistance of PEO coatings on the AZ31 magnesium alloy. The electrolytes in focus are KOH and NaOH. In this study, the PEO process was conducted on the AZ31 magnesium alloy using basic solutions such as KOH, NaOH, and a mixture of KNa. The process employed a current density of 1000 A/m2 at a temperature of 30ºC for 10 minutes. The produced samples were then analyzed using various methods, including morphology and composition observation with SEM-EDS, mechanical testing for wear resistance and hardness measurement, as well as electrochemical experiments using EIS and PDP. KOH, NaOH, and KNa solutions successfully enhanced the corrosion resistance and mechanical properties of PEO coatings on the AZ31 magnesium alloy. Corrosion test data indicated that the KOH solution exhibited the highest corrosion rate compared to NaOH and KNa, with corrosion current density and polarization resistance values of 7,31 × 10-5 A/cm2 and 280 Ω.cm2 , respectively. Meanwhile, mechanical tests indicated improved hardness and wear resistance in samples treated with the KNa mixed solution, showing a hardness value of 71 Hv and specific abrasion value of 9,07 × 10-6 mm3 /mm. This can be attributed to the higher atomic percentage of oxygen in the KNa electrolyte compared to NaOH and KOH."

"Plasma electrolytic oxidation (PEO) merupakan metode rekayasa permukaan logam untuk menghasilkan lapisan oksida yang keras dan tahan korosi. Sifat lapisan oksida yang dihasilkan bergantung pada jenis substrat dan komposisi larutan yang digunakan. Dalam penelitian ini, PEO dilakukan pada substrat AZ31B pada kondisi rapat arus tetap 800 A/m2 dan suhu 30°C. Larutan terdiri atas campuran garam basa dan etanol. Larutan A terdiri atas campuran 0,5 M Na3PO4 dan etanol dengan komposisi 9:1, larutan B campuran Na3PO4, NaOH dan Na2CO3 dengan komposisi 8:1:1, larutan C, D, dan E campuran Na3PO4, NaOH, Na2CO3, dan etanol dengan komposisi 7:1:1:1, 6:1:2:1, dan 6:2:1:1. Morfologi dan komposisi lapisan oksida diamati dengan scanning electron microscope dan energy dispersive spectroscopy (SEM – EDS). Komposisi kristal dianalisis dengan x-ray diffraction (XRD). Nilai kekerasan mekanik diuji dengan mesin microVickers Hardness. Perilaku korosi sampel diuji dengan metode electrochemical impedance spectroscopy (EIS) dan potentiodynamic polarization (PDP). Etanol di dalam larutan tidak mempengaruhi morfologi dan komposisi coating. Semua coating memiliki kandungan fasa kristal Mg3(PO4)2 pada puncak 29° hingga 35°. Nilai kekerasan coating yang terbentuk di larutan A, B, C, D, dan E adalah 451,8; 388; 237; 156,8; 158,4 HV. Nilai kekerasan yang rendah pada coating C, D, dan E disebabkan oleh rendahnya konsentrasi Na3PO4 yang menurunkan populasi plasma selama proses coating. Selain itu, kehadiran ion karbonat di dalam larutan mentriger peningkatan pori di dalam coating. Hasil uji polarisasi menunjukkan peningkatan ketahanan korosi dua orde dibanding substrat. Penambahan etanol ke dalam larutan cenderung menurunkan sedikit ketahanan korosi coating.

---

Plasma Electrolytic Oxidation (PEO) is a method of engineering metal surface treatment to produce a hard and corrosion-resistant oxide layer. The result properties of oxide layer depend on type of substrate and composition solution was used. PEO process is carried out a constant current 800 A/m2 at temperature 30℃. The solution composed of mixture alkaline salts and ethanol. Solution A mixture of 0,5 M Na3PO4 and ethanol with composition of 9:1, solution B a mixture Na3PO4, NaOH and Na2CO3 with composition of 8:1:1, solution C, D, and E a mixture of Na3PO4, NaOH and Na2CO3 with ethanol with composition of 7:1:1:1; 6:1:2:1; and 6:2:1:1. Morphology and composition of the oxide layer were observed by scanning electron microscope and energy dispersive spectroscopy (SEM – EDS). The crystal composition was analyzed by x-ray diffraction (XRD). The value of mechanical hardness was tested with a microVickers Hardness machine. The corrosion behavior of the samples was tested by electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization (PDP) methods. The presence of ethanol in the solution didn’t affect morphology and composition of coating. All coatings contain Mg3(PO4)2 crystal phase at peak 29° to 35°. The hardness value of coating formed in solution A, B, C, D and E is 451.8; 388; 237; 156.8; 158.4 HV. The low hardness values in coatings C, D, and E were caused by the low concentration of Na3PO4 which reduced plasma population during the coating process. In addition, the presence of carbonate ions in the solution triggers an increase in the pores in the coating. The results of the polarization test showed can increase corrosion resistance of two orders compared to substrate. Addition of ethanol to solution tends to slightly lower the corrosion resistance of coating."

"Paduan aluminium banyak digunakan dalam berbagai aplikasi, terutama di bidang otomotif dan penerbangan karena keunggulannya. Aluminium bersifat ringan, kekuatan tinggi, serta densitas rendah. Namun, sifat mekanik dan ketahanan korosinya perlu ditingkatkan. Plasma Electrolytic Oxidation (PEO) adalah metode terbaru untuk melindungi aluminium dengan menumbuhkan lapisan keramik oksida pada permukaannya. Dalam penelitian ini, proses PEO dilakukan pada paduan aluminium seri 1100 dan 7075-T735 dengan elektrolit campuran 30 g/Na2SiO3, 30 g/l KOH, dan 20 g/l TEA dengan rapat arus 200 A/m2 selama 6 menit. Kedua jenis seri paduan tersebut digunakan sebagai pembanding dalam proses PEO dimana seri 1100 tergolong Al murni sedangkan seri 7075 memiliki banyak presipitat. Hasil uji korosi dengan menggunakan uji elektrokimia menunjukkan bahwa sampel AA7075-T735 berlapis PEO memiliki ketahanan korosi yang paling baik. Hal ini dibuktikan dengan nilai rapat arus korosi (icorr) terendah, yaitu mencapai 5,91x10-7 A.cm-2 dan loop kapasitif yang paling besar serta ketidakhadiran loop induktif pada kurva Nyquist. Dari uji hilang berat juga diperoleh hasil rata-rata hilang berat yang lebih rendah pada sampel AA7075-T735 dibandingkan dengan AA1100. Ketahanan korosi sampel berlapis PEO mengikuti perilaku substratnya. Sampel AA1100 mengalami degradasi coating yang lebih dominan daripada AA7075-T735. Hal ini berkaitan dengan porositas dan kepadatan lapisan PEO pada kedua sampel.

---

Aluminum alloys are widely used in various applications, especially in the automotive and aviation industries, due to their advantages. Aluminum is lightweight, has high strength, and low density. However, its mechanical properties and corrosion resistance need improvement. Plasma Electrolytic Oxidation (PEO) is the latest method used to protect aluminum by growing a ceramic oxide layer on its surface. In this study, the PEO process was applied to aluminum alloys of series 1100 and 7075-T735 using an electrolyte mixture of 30 g/L Na2SiO3, 30 g/L KOH, and 20 g/L TEA with a current density of 200 A/m2 for 6 minutes. Both alloy series were used as comparators in the PEO process, with series 1100 being classified as pure Al, while series 7075 has numerous precipitates. Corrosion tests using electrochemical analysis showed that the PEO-coated AA7075-T735 sample exhibited the best corrosion resistance. This was evident from its lowest corrosion current density (icorr) value, which reached 5.91x10-7 A.cm-2 , as well as the largest capacitive loop and the absence of an inductive loop in the Nyquist curve. Weight loss tests also indicated that the average weight loss was lower in the AA7075-T735 sample compared to AA1100. The corrosion resistance of the PEO-coated samples followed the behavior of their substrates. The AA1100 sample experienced more dominant coating degradation compared to AA7075-T735, which was related to the porosity and density of the PEO layer in both samples."

"

Plasma electrolytic oxidation (PEO) merupakan metode konversi permukaan logam menjadi lapisan oksida dengan bantuan plasma yang bertujuan untuk meningkatkan sifat mekanik permukaan dan ketahanan korosi logam. Retakan dan pori menurunkan ketahanan korosi dan sifat mekanik lapisan. Dalam penelitian ini digunakan zat aditif SiO₂ dan metode post-alkali treatment pada lapisan PEO yang ditumbuhkan pada paduan magnesium AZ31 dan commercially pure titanium (CP-Ti). PEO dilakukan di dalam larutan 95 g/l Na₃PO₄ + 2 g/l KOH menggunakan rapat arus DC  sebesar 300 A.m^-2 selama 10 menit. NP-SiO₂ sebanyak 2 g/l ditambahkan di dalam larutan PEO. Setelah logam terlapisi, post-alkali treatment dilakukan di dalam larutan 0,5 M NaOH pada suhu 80 ºC selama 30 menit. Morfologi permukaan dan kandungan unsur lapisan dianalisis menggunakan SEM-EDS dan XPS. Komposisi fasa kristal diteliti menggunakan X-ray Difraction (XRD). Sifat mekanik lapisan PEO diuji dengan metode vickers microhardness dan ketahanan aus dievaluasi menggunakan metode Ogoshi. Sifat korosi dianalisis dengan uji polarisasi, EIS, dan uji rendam. Sifat bioaktivitas diteliti dengan cara perendaman sampel dalam larutan SBF. Hasil penelitian menunjukkan penambahan aditif SiO₂ dan post-alkali treatment dapat meningkatkan ketahanan korosi dan sifat mekanik lapisan PEO pada logam Mg dan Ti. Pada PEO-Mg, lapisan PEO/SiO₂+AT memiliki nilai rapat arus korosi paling rendah dan nilai kekerasan paling tinggi dibandingkan dengan sampel lainnya yaitu berturut-turut 7,34x10^-7 A.cm^-2 dan 359 HV. Tren yang sama juga dihasilkan pada PEO-Ti, lapisan PEO/SiO₂+AT memiliki nilai rapat arus korosi relatif rendah dan nilai kekerasan paling tinggi dibandingkan dengan sampel lainnya yaitu berturut-turut 3,4x10^-9 A.cm^-2 dan 305 HV.

---

Plasma electrolytic oxidation (PEO) is a method of converting metal surfaces into an oxide layer with the help of plasma which aims to improve the surface mechanical properties and corrosion resistance of metals. Cracks and pores reduce the corrosion resistance and mechanical properties of the coating. In this research, SiO₂ additives and post-alkali treatment methods were used on PEO layers grown on AZ31 magnesium alloy and commercially pure titanium (CP-Ti). PEO was carried out in a solution of 95 g/l Na₃PO₄ + 2 g/l KOH using a DC current density of 300 A.m^-2 for 10 minutes. SiO₂ additive with a concentration of 2 g/l was added to the PEO solution. After the metal is coated, post-alkali treatment is carried out in a 0.5 M NaOH solution at a temperature of 80 ºC for 30 minutes. The surface morphology and element content of the layers were analyzed using SEM-EDS and XPS. The composition of the crystal phase was investigated using XRD. The mechanical properties of the PEO coating were tested using the vickers microhardness and the wear resistance was evaluated using the Ogoshi method. Corrosion properties were analyzed by polarization test, EIS, and immersion test. The bioactivity properties were studied by immersing the samples in SBF. The research results show that the addition of SiO₂ and post-alkali treatment can improve the corrosion resistance and mechanical properties of PEO layers on Mg and Ti metals. In PEO-Mg, the PEO/SiO²+AT layer has the lowest corrosion current density value and the highest hardness value compared to other samples, namely 7.34x10^-7 A.cm^-2 and 359 HV respectively. The same trend was also produced on PEO-Ti, the PEO/SiO²+AT layer had a relatively low corrosion current density value and the highest hardness value compared to other samples, namely 3.4x10^-9 A.cm^-2 and 305 HV respectively.

"

"Magnesium memiliki nilai massa jenis lebih ringan diantara logam-logam komoditi penyuplai industri otomotif lainnya yaitu 1,74 gr/cm3. Berat magnesium sendiri lebih ringan 30% terhadap aluminium dan 70% terhadap baja. Perbaikan sifat-sifat mekanik dan ketahanan korosi pada paduan Mg-Al-Zn dapat dilakukan secara intrinsic melalui penambahan unsur paduan, perlakuan panas dan modifikasi teknik fabrikasi. Peningkatan sifat mekanik pada paduan (90-x)Mg9AlZnxCa dilakukan dengan penambahan unsur Ca yang divariasikan konsentrasi (0; 1; 1,5 dan 2 % berat) dengan Teknik fabrikasi pembuatan paduan (90-x)Mg-9Al-1Zn-xCa melalui proses semi-solid casting metoda Thixoforming menjadi parameter penting untuk menghasilkan suatu produk komponen otomotif. Sampel yang diuji memiliki multi fasa yaitu fasa a-Mg struktur kristal Hexagonal space group P63/mmc, fasa kedua β-Mg17Al12 struktur kristal kubik space group I-m43 m dan fasa Al2Ca termasuk dalam struktur kristal kubik dengan space grup Fd-3m. Hasil SEM-EDS menunjukkan terbentuknya fasa Al2Ca pada batas butir dapat menghambat pertumbuhan butir baru dan mengurangi terbentuknya fasa β-Mg17Al12.Pada sampel as-cast penambahan Ca 1 wt.% terjadi penurunan fraksi massa fasa a-Mg dan peningkatan fraksi massa fasa β-Mg17Al12. Pada sampel dengan penambahan Ca 1,5 dan 2 wt.% menunjukkan penurunan fraksi massa fasa a-Mg dan fasa β-Mg17Al12 serta adanya pembentukan fasa baru yaitu fasa Al2Ca. Pada sampel 1 wt.% Ca hasil proses thixoforming mengakibatkan penurunan fraksi massa fasa a-Mg, sedangkan fraksi massa fasa β-Mg17Al12 terjadi peningkatan yang signifikan. Pada sampel dengan penambahan Ca 1,5 dan 2 wt.% menunjukkan penurunan fraksi massa fasa a-Mg dan fasa β-Mg17Al12 serta adanya peningkatan pembentukan fasa baru yaitu fasa Al2Ca. Kekerasan tertinggi dihasilkan pada sampel 1 % berat Ca setelah dilakukan proses thixoforming dan ageing (T6) selama 20 jam sebesar 92,48 BHN. Pada pengukuran butir dengan metoda Jeffries teridentifikasi terjadi penghalusan butir sampai 17µm.

---

Magnesium has a lighter density value than other commodity metals supplying the automotive industry, namely 1.74 gr/cm3. The weight of magnesium itself is 30% lighter for aluminum and 70% for steel. Improvement of mechanical properties and corrosion resistance of Mg-Al-Zn alloys can be made intrinsically by adding alloying elements, heat treatment, and modification of fabrication techniques. The improvement of the mechanical properties of the alloy (90-x)Mg9AlZnxCa was carried out by adding elements of Ca with varying concentrations (0; 1; 1.5 and 2% by weight) with the fabrication technique of making alloys (90-x)Mg-9Al-1Zn-xCa through Thixoforming metal casting semi-solid process is a vital parameter to produce an automotive component product. The samples tested had multiple phases: the a-Mg phase with the Hexagonal space group P63/mmc crystal structure, the second phase β-Mg17Al12 cubic crystal structure with the space group I-m43 m, and the Al2Ca phase included in the cubic crystal structure with the space group Fd-3m. The SEM-EDS results show that the formation of the Al2Ca phase at the grain boundaries can inhibit the growth of new grains and reduce the formation of the β-Mg17Al12 phase.

In the sample addition of Ca one wt.%, there was a decrease in the mass fraction of the a-Mg phase and an increase in the mass fraction of the β-Mg17Al12 phase. The samples with the addition of Ca 1.5 and 2 wt.% showed a decrease in the mass fraction of the a-Mg and β-Mg17Al12 phases and the formation of a new phase, namely the Al2Ca phase. In the sample of 1 wt.% Ca, the thixoforming process resulted in a decrease in the mass fraction of the a-Mg phase, while the mass fraction of the β-Mg17Al12 phase experienced a significant increase. The sample with the addition of Ca 1.5 and 2 wt.% showed a decrease in the mass fraction of the a-Mg and β-Mg17Al12 phases and an increase in the formation of a new phase, namely the Al2Ca phase. The highest hardness produced in 1% by weight of Ca sample after thixoforming and aging (T6) for 20 hours was 92.48 BHN. In the grain measurement using the Jeffries method, the grains are refined to 17µm"