"Polyhydroxyalkanoate (PHA) is one of the alternatively biodegradable plastics which can be synthesized from a particular micro-organism after the fermentation process, considering the optimization of nutrients. In this research, the yeast strain Rhodotorula graminis TISTR 5124 was selected to be fermented with a carbon source in the standard nutrient in order to conduct a preliminarily study on the best conditions for this yeast in PHA production. The growth rate curve of yeast in the composition of imbalanced nutrients, i.e. the limitation of phosphorus and nitrogen, was also investigated and compared with another sample cultured in standard nutrients. Experimental results indicated that the condition that gave the maximum growth rate of this yeast strain was a P-limited condition at 81 hours, whereby the cell number of 3.1×109cells/mL was obtained and corresponded to the optical density (OD) of 0.95 measured at a wavelength of 600 nm. The synthesized PHA extracted from yeast cells after 81 hours of incubation was examined by Fourier transform infra-red (FT-IR) and nuclear magnetic resonance (1H NMR) spectroscopy. The results indicated stretching vibrations similar to the copolymer PHBV (or a PHA derivative). Maximum PHA content of 54.4% was found in the P-limited condition which corresponded to a PHA yield of 65.1 (g/g-total sugar consumed) in which the yeast consumed the least glucose amount of 3.2 g/L, but grew the most rapidly. Rhodotorula graminis TISTR 5124 is therefore promising as a good candidate for alternatively biodegradable plastics, considering the potential to produce PHA and its derivatives. This process can be beneficial as an option to replace conventional plastics in the future."

"Polyhydroxyalkanoate(PHA) is one of the alternatively biodegradable plastics which can besynthesized from a particular micro-organism after the fermentation process,considering the optimization of nutrients. In this research, the yeaststrain Rhodotorula graminis TISTR 5124 was selected to be fermented with a carbonsource in the standard nutrient in order to conduct a preliminarily study on thebest conditions for thisyeast in PHA production. The growth rate curve of yeast in the composition of imbalancednutrients, i.e. the limitationof phosphorus and nitrogen, was also investigated and compared with another sample cultured in standard nutrients. Experimental results indicated that thecondition that gave the maximum growth rate of this yeast strain was aP-limited condition at 81 hours, whereby the cell number of 3.1×109cells/mL wasobtained and corresponded to the optical density (OD) of 0.95 measured at awavelength of 600 nm. The synthesized PHA extracted from yeast cells after 81hours of incubation was examined by Fouriertransform infra-red (FT-IR) and nuclear magnetic resonance (1H NMR) spectroscopy. The results indicated stretchingvibrations similar to the copolymer PHBV (or a PHA derivative). Maximum PHA content of 54.4% wasfound in the P-limited condition which correspondedto a PHA yield of 65.1 (g/g-total sugar consumed) in which the yeast consumed the least glucose amount of 3.2 g/L, butgrew the most rapidly. Rhodotorulagraminis TISTR 5124 is therefore promising as a good candidate for alternativelybiodegradable plastics, considering the potential to produce PHA and its derivatives. This process can be beneficial as an option to replace conventional plastics inthe future."

"ABSTRAKBiomaterial mampu luruh berbasis Fe-Mn-C diproduksi melalui prosesmetalurgi serbuk besi, mangan dan karbon diteliti dengan paduan Fe-26Mn-1,4Cdan Fe-33Mn-2,6C. Biomaterial mampu luruh berbasis Fe-Mn-C telah ditelitidengan pengujian struktur mikro dan fasa, kekerasan Rockwell A, serta polarisasidan pencelupan pada larutan Hanks? dan ringer laktat. Struktur mikro dan fasayang terbentuk adalah austenit-ferit dengan austenit yang dominan terbentuk padakedua paduan. Kekerasan sampel paduan Fe-26Mn-1,4C adalah 50 HRA danpaduan Fe-33Mn-2,6C adalah 58 HRA karena porositas yang terbentuk padapaduan Fe-26Mn-1,4C lebih banyak (9,8%) dibandingkan dengan paduan Fe-33Mn-2,6C (4,7%). Laju korosi yang didapatkan lebih tinggi pada paduan Fe-26Mn-1,4C dibandingkan dengan Fe-33Mn-2,6C pada pengujian polarisasidengan larutan Hanks? dan ringer laktat. Laju korosi paduan Fe-26Mn-1,4C danpaduan Fe-33Mn-2,6C pada pengujian pencelupan mengalami penurunan denganwaktu pencelupan yang bertambah.

---

ABSTARCTBiodegradable material based on Fe-Mn-C produced by powdermetallurgy process of iron, manganese and karbon is observed by Fe-26Mn-1,4Calloy and Fe-33Mn-2,6C alloy. Biodegradable material based on Fe-Mn-C hasbeen studied with microstructure and phase examination, Rockwell A hardnesstest and polarization and immersion test with Hanks? solution and ringer lactate.The microstructure and phase formed is austenite-ferrite with austenite asdominant phase on both alloys. The Rockwell A hardness for Fe-26Mn-1,4C alloyis 50 HRA and for Fe-33Mn-2,6C alloy is 58 HRA because the porosity is higherin Fe-26Mn-1,4C alloy (9.8%) than in Fe-33Mn-2,6C alloy (4.7%).The corrosionrate is higher for Fe-26Mn-1,4C alloy compared to Fe-33Mn-2,6C alloy by usingpolarization test with Hanks? solution and ringer lactate. The corrosion rate Fe-26Mn-1,4C alloy and Fe-33Mn-2,6C alloy by using immersion test with Hanks?solution is decreased while the time of immersion increased."

"Pendahuluan: Magnesium (Mg) memiliki karakter biomekanik menyerupai tulang dengan mechanical strength melebihi keramik namun mempunyai tingkat korosi yang tinggi. Salah satu cara untuk mengurangi tingkat korosi Mg adalah dengan mencampurnya dengan material lain atau melapisinya. Karbonat apatit (CA) dipilih untuk menjadi campuran komposit Mg karena osteokonduktivitasnya yang baik. Penelitian ini bertujuan untuk mengevaluasi biodegradabilitas implan komposit MgxCA yang dibuat dengan teknik ekstrusi pada tikus Sprague Dawley.Metode: Penelitian ini merupakan uji post-test only in vivo experimental pada tikus Sprague Dawley (SD) pada bulan Juli hingga Desember 2021. Sebanyak 33 tikus SD dibagi menjadi 6 kelompok perlakuan yaitu kelompok dengan plat Mg0CA, Mg5CA, Mg10CA, Mg15CA, titanium, serta prosedur sham. Pemeriksaan meliputi diameter paha, pembentukan gas pasca operasi (krepitasi), kondisi luka, kadar laboratorium, dan analisis histopatologis pada hari ke 15 dan 30.Hasil: Tidak ditemukan perbedaan yang signifikan pada diameter paha, krepitasi, dan kondisi luka antar kelompok perlakuan selama 5 hari pasca-operasi (p>0.05). Didapatkan perbedaan yang signifikan pada pembentukan gas pada hari ke 15 dimana implantitanium menunjukan pembentukan gas yang lebih rendah (p=0.002) namun kembali menjadi tidak signifikan pada hari ke 30 (p>0.05). Pemeriksaan laboratorium dan histopatologis tidak menunjukan perbedaan yang bermakna baik secara lokal ataupun sistemik (p>0.05).Kesimpulan: Kombinasi magnesium dengan karbonat apatit dari teknis fabrikasi ekstrusi merupakan implan yang biodegradable dengan biokompatibilitas yang tidak toksik baik secara lokal ataupun sistemik.

---

Introduction : Magnesium (Mg) has a biomechanical character resembling bone with mechanical strength exceeding ceramics but has a high corrosion rate. One way to reduce the corrosion level of Mg is to mix it with other materials or coatingit. Carbonate apatite (CA) was chosen to be a Mg composite mixture because of its good osteoconductivity. This study aimed to evaluate the biodegradability of MgxCA composite implants made by extrusion technique in Sprague Dawley.

Method: This study is a post-test only in vivo experimental on Sprague Dawley (SD) mice from July to December 2021. A total of 33 SD rats were divided into 6 treatment groups, namely groups with plates Mg0CA, Mg5CA, Mg10CA, Mg15CA, titanium, and sham procedures. The examination includes thigh diameter, postoperative gas formation (crepitation), wound condition, l levelof the aboratorium, and histopathological analysis on days 15 and 30.

Result:No significant differences were found in thigh diameter, crepitation, and wound condition between treatment groups during 5 days post-operative (p>0.05). There was a significant difference in gas formation on day 15 where titanium implants showed lower gas formation (p = 0.002) but again became insignificant on day 30 (p > 0.05). Laboratory and histopathological tests showed no significant differences either locally or systemically (p>0.05).

Conclusion: The combination of magnesium with apatite carbonate from extruded fabrication techniques is a biodegradable implant with biocompatibility with non-toxic properties either locally or systemically. "

"Asam suksinat yang digunakan pada berbagai indsutri sebagian besar diproduksi melalui proses kimiawi, yaitu hidrogenasi katalitik menggunakan bahan bakar fosil yang prosesnya berpengaruh buruk bagi lingkungan. Maka, penelitian produksi melalui fermentasi sedang banyak dilakukan. Namun, fermentasi menghasilkan banyak produk samping serta pengotor sehingga dibutuhkan metode separasi yang memiliki selektivitas dan efektivitas tinggi. Salah satu metode yang umum digunakan adalah ekstraksi reaktif menggunakan amina tersier sebagai ekstraktan dan alkohol primer sebagai diluen. Pada penelitian ini digunakan tributylamine sebagai ekstraktan dan 1-decanol sebagai diluen dengan memvariasikan konsentrasi ekstraktan. Ekstraksi dilakukan kepada larutan model fermentasi yang mengandung empat komponen yaitu asam suksinat, asam format, asam asetat, dan asam laktat dengan memvariasikan konsentrasi asam suksinat. Ketiga variasi konsentrasi ini digunakan untuk menentukan konsentrasi optimal untuk ekstraksi reaktif asam suksinat dari larutan model fermentasi. Larutan hasil ekstraksi kemudian dianalisis menggunakan High-Performaces Liquid Chromatography (HPLC) untuk mengetahui konsentrasi asam suksinat untuk kemudian dilakukan perhitungan koefisien distribusi, loading ratio dan efisiensi ekstraksi. Berdasarkan hasil yang diperoleh, larutan model dengan konsentrasi awal asam suksinat 10 g/L memberikan koefisien distribusi dan loading ratio tertinggi yaitu 9,02 dan 0,20 secara berurutan. Efisiensi ekstraksi tertinggi diperoleh pada variasi konsentrasi asam suksinat 5 g/L dengan nilai 90%. Nilai koefisien distribusi dan efisiensi ekstraksi tertinggi diperoleh pada penggunaan ekstraktan dengan konsentrasi 1,25 mol/kg diluen dan loading ratio tertinggi diperoleh pada penggunaan ekstraktan dengan konsentrasi 0,50 mol/kg diluen.

---

Most of the succinic acid used for industrial purposes is produced through a chemical process using fossil fuels as the raw material, where it is an environmentally unfriendly processes. Therefore, the research for bio-succinic acid production through fermentation is being conducted. But, fermentation produces a lot of by-products so an effective and highly selective separation method is needed. One of the commonly used separation methods is reactive extraction using tertiary amines as the extractants and primary alcohol as the diluent. This study uses tributylamine as the extractant and 1- decanol as the diluent with varying the concentration of extractant. The extraction is done to a model fermentation solution that consists of four components which are succinic acid, formic acid, acetic acid, and lactic acid with the initial concentration of succinic acid as the variations. These variations are used to determine the optimal concentration for succinic acid extraction from the fermentation broth model. The extracted liquid is then analyzed using High-Performances Liquid Chromatography (HPLC) to determine the concentration of succinic acid that then used for the calculation of distribution coefficient, loading ratio and extraction efficiency. Based on the result, the highest distribution coefficient and loading ratio of 9,02 and 0,20, respectively, were obtained at the model fermentation broth with an initial concentration of 10 g/L. Meanwhile, the highest extraction efficiency was obtained at model fermentation broth with an initial concentration of 5 g/L, which was 90%. The highest distribution coefficient and extraction efficiency were obtained on the usage of extractant with a concentration of 1,25 mol/kg diluent and the highest loading ratio was obtained on the usage of extractant with a concentration of 0,50 mol/kg diluent."

"Bawang lanang hitam merupakan produk hasil fermentasi dari bawang lanang yang dipanaskan pada suhu dan kelembaban tinggi terkontrol dan memiliki banyak manfaat kesehatan karena bioaktivitasnya tinggi. Konsumsi bawang hitam menjadi populer sehingga menyebabkan usaha bawang lanang hitam semakin menjanjikan. Rice cooker merupakan instrumen yang sederhana dan umum digunakan oleh pelaku UMKM dalam memproduksi bawang lanang hitam. Penelitian ini bertujuan untuk memperoleh data yang akan digunakan sebagai acuan untuk memproduksi bawang lanang hitam yang berkualitas, berkhasiat, dan aman. Pada penelitian ini dilakukan fermentasi bawang lanang dari tiga daerah berbeda: Temanggung, Brebes, dan Boyolali menggunakan metode rice cooker mode hangat selama 21 hari kemudian dilakukan penentuan parameter standardisasi serbuk dan ekstrak etanol bawang lanang hitam berdasarkan Farmakope Herbal Indonesia dan Parameter Standar Umum Ekstrak Tumbuhan Obat. Hasil parameter standardisasi serbuk bawang lanang hitam adalah bentuk lonjong kisut, warna hitam pekat, rasa asam, sedikit asin dan pahit, dan bau khas; nilai susut pengeringan 1,16–1,18%; kadar sari larut air dan etanol 20,47–30,09% dan 3,67–21,42%; Kadar abu total dan abu tidak larut asam 3,99–4,42% dan 0,06–0,36%; kadar alisin 0,25–0,48 mg/g terhadap serbuk. Hasil parameter standardisasi ekstrak etanol bawang lanang hitam adalah bentuk ekstrak kental dan lengket, warna hitam kecokelatan, rasa pahit-asam dan bau khas; kadar air 2,00–13,60%; kadar abu total dan abu tidak larut asam 3,73–4,13% dan 0,47–0,55%; kadar alisin 0,43–0,97 mg/g terhadap ekstrak. Kandungan kimia yang terdapat pada ekstrak etanol bawang lanang hitam adalah flavonoid, fenol, terpenoid, dan alisin.

---

Single bulb black garlic is a fermented product of single bulb garlic from heating process at controlled high temperature and humidity, it has many health benefits due to its high bioactivity. Consumption of black garlic has become popular, causing nice potential bussiness idea. Rice cooker is a simple instrument and is commonly used by SMEs in producing single bulb black garlic. This study aimed to obtain data that will be used as a reference for producing quality, efficacious, and safe single bulb black garlic. In this study, single bulb garlic from three different areas: Temanggung, Brebes, and Boyolali were fermented using rice cooker method warm mode for 21 days and then determined the standardization parameters for powder and ethanol extract of single bulb black garlic based on the Indonesian Herbal Pharmacopoeia and General Standard Parameters of Medicinal Plant Extract. The results showed that single bulb black garlic powder have wrinkled oval shape, dark black color, sour, salty and bitter taste, and aromatic odor; drying loss content 1,16–1,18%; water and ethanol soluble content 20,47–30,09% and 3,67–21,42%; total ash and acid insoluble ash content 3,99–4,42% and 0,06–0,36%; allicin content 0,25–0,48 mg/g to power. The results of the standardization parameters for the ethanol extract were semisolid sticky paste, a brownish black color, and aromatic odor; moisture content 2,00–13,60%; total ash and acid insoluble content 3,73–4,13% and 0,47–0,55%; allicin content 0,43–0,97 mg/g to extract. Ethanol extract of single bulb black garlic contained flavonoids, phenols, terpenoids, and allicin."

"Inhibisi merupakan salah satu metode penghambatan laju korosi, salah satu jenis dari inhibitor adalah inhibitor organik yang memiliki sifat biodegradable sehingga bersifat lebih ramah lingkungandan relatif lebih murah dibandingkan inhibitor anorganik.Penelitian ini dilakukan untuk mempelajari perilaku inhibisi dari campuran ekstrak melinjo dan kunyit pada pipa baja API-5L di lingkungan NaCl 3,5% dengan menggunakan metode kehilangan berat dan polarisasi. Dalam penelitian ini variasi kadar ekstrak melinjo dan kunyit dicampur dengan berbagai kadar. Sebagai single inhibitor melinjo menghasilkan efisiensi yang lebih tinggi dari sebagian besar kadar campuran. Pada percobaan polarisasi efisiensi terbaik ada pada campuran 6 ml kedua ekstrak dengan acampuran 8 ml kedua ekstrak sebagai efisiensi kedua terbaik.

---

Inhibition is one of corrosion protection method, one kind of corrosion inhibitor is organic inhibitor which has biodegradable characteristic thus the inhibitor is environmental friendlier than conventional inorganic inhibitor. This research was done to study the inhibition activity of combination between melinjo and turmeric extract for API-5L steel pipe in NaCl 3,5% environment. Weight loss and polarization method were used to measure the inhibitor efficiency.

In this study concentration of melinjo extract and turmeric extract were varied.It was found that as a single inhibitor melinjo extract has more efficiency than the combination inhibitor. In polarization method it was found that the combination of 6 ml of the two extract has the highest efficiency followed by the combination of 8ml."

"ABSTRAKPerkembangan biomaterial berbasis Mg dan Fe dalam satu dekade terakhir telah dipelajari secara ekstensif sebagai material biodegradable untuk aplikasi medis. Namun perkembangan material ini mengalami keterbatasan atau stagnan dalam hal kesesuaiannya untuk aplikasi klinis. Dalam tiga tahun terakhir, paduan berbasis Zn mulai menjadi alternatif untuk diteliti sebagai pengganti biomaterial berbasis Mg dan Fe. Paduan berbasis Zn memiliki laju degradasi yang sedang namun memiliki sifat mekanik yang rendah, sehingga perlu ditambahkan unsur lain untuk memperbaiki sifat mekaniknya. Pada penelitian ini unsur yang ditambahkan yaitu zirkonium (Zr) dengan variasi komposisi sebesar 0.5%, 1%, dan 2%. Metode pemaduan yang digunakan yaitu pengecoran dengan temperatur sebesar 550°C. Dari hasil analisa struktur mikro, penambahan Zr pada paduan Zn akan membentuk presipitat di pinggiran dekat dengan batas butir dan semakin banyak kadar Zr yang ditambahkan, ukuran butir yang terbentuk semakin kecil. Ukuran butir dari Zn murni sampai penambahan 2%Zr secara berurutan yaitu 266.40µm, 20.16µm, 16.70µm, 15.85µm. Dari hasil analisa XRD, penambahan Zr sebesar 0.5%, 1%, 2%, akan membentuk fasa Zn dan fasa Zn22Zr. Nilai kekerasan yang dihasilkan dari Zn murni sampai penambahan 2%Zr secara berurutan yaitu 35.162HV, 41.988HV, 42.324HV, 57.112HV. Semakin banyak kadar Zr yang ditambahkan pada paduan Zn maka nilai kekerasan yang dihasilkan semakin besar.

---

ABSTRACTThe development of Mg and Fe based biomaterials in the past decade has been extensively studied as biodegradable material for medical applications. The development of this material is limited or stagnant in terms of suitability for clinical applications. In the past three years ago, Zn-based alloys began to be an alternative to be studied as a substitute for Mg and Fe based biomaterials. Zn-based alloys have a moderate degradation rate but have a low mechanical properties, so other elements need to be added to improve their mechanical properties. In this study the added element is zirconium (Zr) with a composition variation of 0.5%, 1%, and 2%. The alloying method used is casting with a temperature of 550°C. The results of the microstructure analysis, the addition of Zr to Zn alloys will form precipitates in the side the grain boundaries and more addition of Zr composition, the smaller grain size formed. The grain size from pure Zn until the addition of 2% Zr in sequence are 266.40µm, 20.16µm, 16.70µm, 15.85µm. The XRD analysis, from addition of Zr of 0.5%, 1%, 2%, will form the Zn phase and the intermetallic phase Zn22Zr. The hardness value obtained from pure Zn until 2% Zr in sequence are 35.162HV, 41.988HV, 42.324HV, 57.112HV. The more Zr composition are added to the Zn alloy, the greater value of the hardness formed."

"Penggunaan polimer biodegradable sebagai matriks pada material komposit mulai dipertimbangkan untuk digunakan pada berbagai macam aplikasi karena memiliki sifat yang ramah lingkungan karena memiliki kemampuan yang dapat terdegradasi dengan baik dan cepat. Namun, polimer biodegradable memiliki beberapa kekurangan seperti sifat mekanisnya yang buruk. Metode yang dapat dilakukan untuk memperbaiki sifat mekanis dari polimer biodegradable ini adalah dengan menambahkan serat alami yang bertujuan sebagai penguat ke dalam matriks polimer sehingga membentuk material komposit. Untuk memperoleh produk dengan sifat mekanis yang sesuai dengan melakukan eksperimen secara langsung dibutuhkan proses yang panjang dan memakan biaya yang besar. Oleh karena itu, pembelajaran mesin hadir sebagai solusi dalam menciptakan proses pemilihan material yang efektif, akurat, singkat, dan hemat. Dalam penelitian ini, prediksi kekuatan tarik material polimer biodegradable berpenguat serat alami melibatkan empat model pembelajaran mesin dengan Extreme Gradient Boosting (XGB) sebagai model terpilih karena performanya yang stabil dan baik dengan metrik evaluasi skor R^2 sebesar 0,866, RMSE sebesar 7,26, dan MAE sebesar 4,84. Dilakukan proses validasi dengan melakukan perbandingan nilai yang model hasilkan dengan nilai aktual berdasarkan penelitian yang telah dilakukan terdahulu dan memperoleh performa yang baik dan optimum dengan selisih akurasi, yaitu rentang 1,02% sampai 27,19%.

---

The use of biodegradable polymers as matrices in composite materials is starting to be considered for use in a wide variety of applications due to their environmentally friendly properties as they have the ability to degrade well and quickly. However, biodegradable polymers have some drawbacks such as poor mechanical properties. A possible method to improve the mechanical properties of these biodegradable polymers is to add natural fibers that act as reinforcement into the polymer matrix to form a composite material. Obtaining a product with suitable mechanical properties by conducting direct experiments is a lengthy and costly process. Therefore, machine learning comes as a solution in creating an effective, accurate, short, and economical material selection process. In this study, the tensile strength prediction of natural fiber-reinforced biodegradable polymer materials involves four machine learning models with Extreme Gradient Boosting (XGB) as the selected model due to its stable and good performance with the evaluation metrics of R^2 score of 0.866, RMSE of 7.26, and MAE of 4.84. The validation process was carried out by comparing the values generated by the model with the actual values based on previous research and obtained good and optimum performance with a difference in accuracy, which ranges from 1.02% to 27.19%."