Hasil Pencarian  ::  Simpan CSV :: Kembali

"Composite resin are restorative materials having color similar to teeth and have been widely used in dentistry. The successful application of composite resin influences the duration of the restoration in the oral cavity. The aim of this research is to describe the influence of artificial saliva contamination and the application of re-conditioning on tensile bond strength of composite resin to dentin. In the control group, the dentin were etched, bonding were applied and composite resin were restored on the dentin. In the group with artificial saliva contamination without re-conditioning, the dentin were etched, bonding were applied and then contaminated with artificial saliva, dried and then restired with composite resin. While the group with artificial saliva contamination with re-conditioning, the dentin were etched, bonding were applied and contaminated with artificial saliva, and then etched and applied bonding agent and restored composite resin.Bond strength test used “Universal testing machine, AG 5000. The results showed that highest value of tensile bond strength of composite resin to dentin was at the control group. It can be concluded that artificial saliva contamination decreased tensile bond strength while re-conditioning application increased it."

"ABSTRAKLatar Belakang: LCU prototip dengan metode PWM-kombinasi dengan iradiansi sinar 800, 900, dan 1.000 mW/cm2 telah dibuat untuk mencegah kenaikan suhu pulpa akibat polimerisasi. Tujuan: Menganalisis kekerasan komposit resin yang dipolimerisasi dengan LCU berbeda iradiansi sinar. Metode: Spesimen merupakan komposit resin yang dipolimerisasi dengan LCU prototip (PWMkombinasi) beriradiansi sinar 800, 900, atau 1.000 mW/cm2 atau dengan LCU pembanding (900 mW/cm2). Kekerasan komposit resin diukur menggunakan sistem Knoop. Hasil: Kekerasan komposit resin antar kelompok berbeda bermakna (p<0,05) kecuali yang diberi iradiansi sinar 900 mW/cm2 dari LCUprototip dan LCU pembanding. Kesimpulan: Kekerasan komposit resin dipengaruhi oleh iradiansi sinar dari LCU prototip. LCU prototip atau LCU pembanding dengan iradiansi 900 mW/cm2 menghasilkan kekerasan komposit resin yang sama.

---

ABSTRACTBackground: Prototype light curing unit (LCU) with PWM-combined lightirradiance of 800, 900, and 1.000 mW/cm2 was made to prevent the pulp temperature rise due to the polymerization. Objective: To analyze the hardness of resin composites polymerized by LCU different light irradiation. Methods: The specimen is resin composites polymerized by prototype LCU light irradiance 800, 900, or 1.000 mW/cm2 or with comparison LCU (900 mW/cm2). Hardness of resin composite test performed by Knoop system. Result: There is significant differences (p<0.05) among the groups except those between using the prototype LCU and comparison LCU that have irradiance of 900 mW/cm2. Conclusions: The hardness of resin composite was influenced by the irradiance of prototype LCU. The hardness of resin composite from prototype LCU is equal to those from comparison LCU irradiance of 900 mW/cm2."

"Latar belakang: Light Curing Unit (LCU) LED metode pulsa iradiansi 900 mW/cm2 telah dikembangkan untuk menghasilkan suhu pada ruang pulpa lebih rendah dibandingkan metode kontinu akibat polimerisasi resin komposit Nanofill pada durasi penyinaran 20 detik. Tujuan: menganalisis pengaruh durasi dan metode penyinaran pulsa terhadap kekerasan permukaan dan Depth of Cure resin komposit Nanofill. Metode: Spesimen resin komposit Nanofill (diameter 6 mm dan tebal 2 mm) disinar dengan LCU LED metode pulsa beriradiansi 900 mW/cm2 selama 5, 10, dan 20 detik, lalu direndam di dalam 5 ml akuades (37˚C 24 jam). Setiap spesimen diuji dengan Knoop Microhardness Tester sebanyak 5 kali pada permukaan atas dan bawah dan dihitung depth of cure. Hasil: Terjadi peningkatan kekerasan permukaan yang disinar dengan LCU metode penyinaran pulsa dan kontinu selama 5 hingga 20 detik yaitu 45,9±1,6/26,4±1,6 KHN hingga 68,8±1,8/57,4±1,6 KHN, dan 46,8±1,6/28,2±1,5 KHN hingga 69,3±1,2/57,8±1,1 KHN. Terdapat perbedaan bermakna (p<0,05) pada kekerasan permukaan di kelompok durasi penyinaran dengan uji One-way Anova dan post hoc Tamhane. Pada nilai depth of cure resin komposit Nanofill yang disinar antara kedua metode penyinaran tidak terdapat perbedaan bermakna (p>0,05) secara statistik. Kesimpulan: Resin komposit Nanofill yang disinar pada durasi lebih lama menunjukkan kekerasaan permukaan atas maupun bawah lebih tinggi dibandingkan dengan durasi lebih pendek. Demikian pula, depth of cure pada durasi lebih lama menunjukkan nilai lebih tinggi. Penyinaran metode pulsa iradiansi 900 mW/cm2 dan kontinu iradiansi 900 mW/cm2 menunjukkan kekerasan permukaan dan depth of cure yang sama."