"Chlorella pyrenoidosa (C. pyrenoidosa) contains Chlorella Growth Factor (CGF), which consists of protein and polysaccharides. CGF is located inside the nucleus of cells and is beneficial to humans as a food supplement, an immunity booster, and an antioxidant. CGF formation of C. pyrenoidosa is influenced by medium composition. C. pyrenoidosa INK was cultured in a modified basal medium (MBM) with various concentrations of Mg2+ (0.5, 1.0, and 1.5 g/L) and Fe2+ (3.5×10-4 and 5.0×10-4 g/L). The experiments were run and analyzed under a completely randomized design using a 2-L bottle with three replications.The results showed that MBM with 1.0 g/L of Mg2+ and 3.5×10-4 g/L of Fe2+ yielded the optimal growth curve for C. pyrenoidosa. Analysis of protein content was carried out using the Lowry method with a spectrophotometer at λ=750 nm, and the obtained results were 0.0974 mg/mL (extract) and 6.4097 mg/ml (supernatant). Furthermore, analysis of glucose content was carried out using the phenol sulfate method (λ = 490 nm), and the obtained results were 49.331 ppm (extract) and 1566.911 ppm (supernatant). Analysis of amino acids in CGF using liquid chromatography-mass spectrometry (LC-MS) indicated the presence of tyrosine, proline, glutamate, alanine, valine, tryptopan, phenylalanine, methionine, and leucine-isoleucine.

---

Pengaruh Konsentrasi Mg2+ dan Fe2+ dalam Media Kultur terhadap Pembentukan CGF oleh Mikroalga Chlorella pyrenoidosa INK dan Analisis Asam Amino dengan Kromatografi Cair-Spektrofotometri Massa. Chlorella pyrenoidosa (C. pyrenoidosa ) mengandung Chlorella Growth Factor (CGF), yang terdiri dari protein dan polisakarida. CGF terletak di dalam inti sel dan bermanfaat bagi manusia sebagai suplemen makanan, booster imunitas, dan antioksidan. Pembentukan CGF oleh C. pyrenoidosa dipengaruhi oleh komposisi medium. C. pyrenoidosa INK dikultur dalam media basal dimodifikasi (MBM) dengan berbagai konsentrasi Mg2+ (0,5, 1,0, dan 1,5 g/L) dan Fe2+ (3,5×10-4 dan 5,0×10-4 g/L). Percobaan dilakukan menggunakan rancangan acak lengkap dalam botol 2L dengan tiga kali pengulangan.Hasil penelitian menunjukkan bahwa MBM mengandung Mg2+ 1.0 g/L dan Fe2+ 3.5×10-4 g/L menghasilkan kurva pertumbuhan C. pyrenoidosa yang optimal. Analisis kandungan protein dilakukan dengan metode Lowry menggunakan spektrofotometer pada λ=750 nm, menghasilkan 0,0974 mg/mL (ekstrak) dan 6,4097 mg/mL (supernatan). Selanjutnya, analisis kadar glukosa dilakukan dengan metode fenol sulfat (λ=490 nm), hasil yang diperoleh 49,331 ppm (ekstrak) dan 1566,911 ppm (supernatan). Analisis asam amino dalam CGF menggunakan spektrometri massa kromatografi cair (KC-SM) menunjukkan adanya tirosin, prolin, asam glutamat, alanin, valin, triptopan, fenilalanin, metionin, dan leusin-isoleusin."

"Litium titanat (Li4Ti5O12) adalah material yang sedang dikembangkan sebagai anoda pada baterai ion litium untuk meningkatkan kinerjanya. Litiun titanat (Li4Ti5O12) sering dikatakan sebagai zero strain material karena stabil saat charge dan discharge sehingga perubahan volume sangat rendah (<1%), tidak terjadi SEI, terhindar dari kerusakan struktur permukaan yang dapat menurunkan kapasitas, dan dapat digunakan untuk high rate. Namun LTO memiliki kelemahan yaitu konduktivitas listrik dan kapasitas yang rendah. Oleh karena itu pada penelitian ini anoda Li4Ti5O12 dilakukan doping Mg dan Mn dalam bentuk Li4-xMgxTi5-xMnxO12 dengan variasi (x=0;0,05;0,10). Proses sintesis LTO co-doping MgMn menggunakan metode solid state dengan bantuan sonikasi. Penggunaan dopan Mg2+ dapat memecah aglomerasi, memperkecil ukuran butir yang dapat meningkatkan nilai konduktivitas listrik, dan meningkatkan kapasitas pengisian baterai. Dopan Mn4+ dipilih karena dapat meningkatkan konduktivitas listrik dan kapasitas dari baterai. Hasil SEM-EDS pada sampel LTO/MgMn0,05 menunjukkan morfologi dengan aglomerasi sedikit dan ukuran partikel paling kecil yaitu 0,33761 μm. Hasil EDS menunjukkan kehadiran unsur yang dinginkan pada co-doping yaitu Mg, Mn, Ti, dan O dan persebarannya relatif merata. Hasil XRD menunjukkan bahwa fasa Mg(OH)2 dan MnO2 tidak ditemukan di dalam struktur co-doping LTO yang mengindikasikan bahwa atom Mg dan Mn telah bergabung dengan struktur LTO. Berdasarkan hasil uji EIS diperoleh nilai Rct terendah pada sampel LTO/MgMn0,10 sebesar 274,4 Ω. Performa baterai tertingi berdasarkan hasil uji CD pada C-rate 1C diperoleh oleh LTO/MgMn0,05 dengan kapasitas sebesar 110,86 mAh/g.

---

Lithium titanate (Li4Ti5O12) is a material being developed as an anode in lithium-ion batteries to improve its performance. Lithium titanate (Li4Ti5O12) is often said to be a zero strain material because it is stable during charge and discharge so that the volume change is very low (<1%), SEI does not occur, avoids surface structure damage that can reduce capacity, and can be used for high rates. However, LTO has the disadvantage of low electrical conductivity and capacity. Therefore in this study, the Li4Ti5O12 anode was doped with Mg and Mn in the form of Li4-xMgxTi5-xMnxO12 with variations (x=0; 0.05; 0.10). The MgMn co-doping LTO synthesis process uses the solid-state method with the help of sonication. The use of Mg2+ dopants can break the agglomeration, reduce the grain size which can increase the electrical conductivity value, and increase the battery charging capacity. Mn4+ dopants were chosen because they can increase the electrical conductivity and capacity of the battery. The SEM-EDS results on the LTO/MgMn0.05 sample showed a morphology with the least agglomeration and the smallest particle size of 0.33761 μm. The EDS results show the presence of the desired elements in co-doping, namely Mg, Mn, Ti, and O and their distribution is relatively even. The XRD results showed that the Mg(OH)2 and MnO2 phases were not found in the LTO co-doping structure which indicated that the Mg and Mn atoms had joined the LTO structure. Based on the results of the EIS test, the lowest Rct value was found in the LTO/MgMn0.10 sample of 274.4 Ω. The highest battery performance based on the results of the CD test at C-rate 1C was obtained by LTO/MgMn0.05 with a capacity of 110.86 mAh/g."

"Ion Magnesium (Mg2+) merupakan salah satu kation divalen yang berperan dalam kondensasi kromosom. Penelitian mengenai pengaruh Mg2+ terhadap kondensasi kromosom dengan menggunakan kromosom yang berasal dari berbagai sel, terutama sel kanker, telah dilakukan. Namun, hingga saat ini, belum ada penelitian yang menggunakan kromosom yang berasal dari sel normal (non-kanker). Salah satu sel yang dapat digunakan adalah limfosit dari sel darah. Penelitian ini bertujuan untuk mengevaluasi pengaruh Mg2+ terhadap struktur kromosom limfosit dengan menggunakan teknik GTL-banding dan karyotyping. Kromosom pada tahap metafase diperoleh dengan mengultur sel darah dan dilanjutkan dengan banding menggunakan Leishman stain. Pengaruh Mg2+ diteliti dengan memberikan larutan XBE5 yang mengandung 5 mM Mg2+ sebagai kontrol, XBE yang mengandung 0 mM Mg2+, dan 1 mM EDTA sebagai chelator kation. Kromosom pada masing-masing perlakuan diberikan penilaian berdasarkan Quality Assesment yang disusun oleh Association for Clinical Cytogenetics berdasarkan International System for Human Cytogenetics Nomenclature (ISCN). Hasil yang diperoleh menunjukkan bahwa kromosom kontrol yang mengandung 5 mM Mg2+ memiliki struktur padat dengan pola banding yang jelas dan intensitas band tebal, sedangkan kromosom pada kelompok perlakuan XBE (0 mM Mg2+) dan 1 mM EDTA memiliki struktur tidak padat dan fibrous dengan pola banding kurang jelas dan intensitas band yang tipis. Nilai rata-rata±SD kromosom kelompok XBE (4,389±0,607) dan EDTA (4,611±0,607) lebih tinggi dibandingkan kontrol XBE5 (4,222±0,427). Hal ini menunjukkan bahwa Mg2+ memiliki pengaruh terhadap struktur kromosom limfosit manusia.

---

Magnesium ion (Mg2+ ) is one of the divalent cations that have an important role in chromosome condensation. Researches about the role of Mg2+ have been conducted on the chromosome from various type of cells, especially human cancer cell line. However, there has not been any research conducted using human normal cells such as blood cells lymphocyte chromosome. This study aims to evaluate the effects of Mg2+ on chromosome structure from lymphocyte using GTL-banding and karyotyping. Metaphase chromosomes were obtained by culturing blood cells, followed by banding using Leishman stain. Magnesium ion role was assessed by using XBE5 solution that contains 5 mM Mg2+ as control, XBE solution that contains 0 mM Mg2+, and 1 mM EDTA solution as a cation chelator. The chromosome value from each treatment was evaluated using Quality Assessment from Association for Clinical Cytogenetics according to the International System for Human Cytogenetics Nomenclature (ISCN). The result shows that the control chromosome (XBE5) had a compact structure with a clear banding pattern and bold band intensity, while those treated with XBE and EDTA had a less compact and fibrous structure with an unclear banding pattern and thin band intensity. In addition, the average chromosome score±SD of the XBE (4.389±0.607) and EDTA-treated (4.611±0.607) chromosomes were higher than those of control (4.222±0.427). These data indicated that Mg2+ affects the structure of the human lymphocyte chromosome."

"Ion Magnesium (Mg2+) merupakan salah satu kation divalen yang berperan dalam kondensasi kromosom. Penelitian mengenai pengaruh Mg2+ terhadap kondensasi kromosom dengan menggunakan kromosom yang berasal dari berbagai sel, terutama sel kanker, telah dilakukan. Namun, hingga saat ini, belum ada penelitian yang menggunakan kromosom yang berasal dari sel normal (non-kanker). Salah satu sel yang dapat digunakan adalah limfosit dari sel darah. Penelitian ini bertujuan untuk mengevaluasi pengaruh Mg2+ terhadap struktur kromosom limfosit dengan menggunakan teknik GTL-banding dan karyotyping. Kromosom pada tahap metafase diperoleh dengan mengultur sel darah dan dilanjutkan dengan banding menggunakan Leishman stain. Pengaruh Mg2+ diteliti dengan memberikan larutan XBE5 yang mengandung 5 mM Mg2+ sebagai kontrol, XBE yang mengandung 0 mM Mg2+, dan 1 mM EDTA sebagai chelator kation. Kromosom pada masing-masing perlakuan diberikan penilaian berdasarkan Quality Assesment yang disusun oleh Association for Clinical Cytogenetics berdasarkan International System for Human Cytogenetics Nomenclature (ISCN). Hasil yang diperoleh menunjukkan bahwa kromosom kontrol yang mengandung 5 mM Mg2+ memiliki struktur padat dengan pola banding yang jelas dan intensitas band tebal, sedangkan kromosom pada kelompok perlakuan XBE (0 mM Mg2+) dan 1 mM EDTA memiliki struktur tidak padat dan fibrous dengan pola banding kurang jelas dan intensitas band yang tipis. Nilai rata-rata±SD kromosom kelompok XBE (4,389±0,607) dan EDTA (4,611±0,607) lebih tinggi dibandingkan kontrol XBE5 (4,222±0,427). Hal ini menunjukkan bahwa Mg2+ memiliki pengaruh terhadap struktur kromosom limfosit manusia.

---

Magnesium ion (Mg2+ ) is one of the divalent cations that have an important role in chromosome condensation. Researches about the role of Mg2+ have been conducted on the chromosome from various type of cells, especially human cancer cell line. However, there has not been any research conducted using human normal cells such as blood cells lymphocyte chromosome. This study aims to evaluate the effects of Mg2+ on chromosome structure from lymphocyte using GTL-banding and karyotyping. Metaphase chromosomes were obtained by culturing blood cells, followed by banding using Leishman stain. Magnesium ion role was assessed by using XBE5 solution that contains 5 mM Mg2+ as control, XBE solution that contains 0 mM Mg2+, and 1 mM EDTA solution as a cation chelator. The chromosome value from each treatment was evaluated using Quality Assessment from Association for Clinical Cytogenetics according to the International System for Human Cytogenetics Nomenclature (ISCN). The result shows that the control chromosome (XBE5) had a compact structure with a clear banding pattern and bold band intensity, while those treated with XBE and EDTA had a less compact and fibrous structure with an unclear banding pattern and thin band intensity. In addition, the average chromosome score±SD of the XBE (4.389±0.607) and EDTA-treated (4.611±0.607) chromosomes were higher than those of control (4.222±0.427). These data indicated that Mg2+ affects the structure of the human lymphocyte chromosome."

"Anoda Li4Ti5O12 (LTO) yang didoping dengan Mg dan Fe dalam bentuk Li4-xMgxTi5-xFexO12 (x = 0, 0.05, 0.1) telah berhasil disintesis menggunakan metode solidstatedengan bantuan sonikasi menggunakan sumber prekursor TiO2 dan Fe2O3, baikkomersial maupun hasil sintesis. Hasil SEM menunjukkan sampel dengan co-doping Mgdan Fe pada LTO komersial memiliki morfologi yang relatif sama dan seragam dan terjadipengurangan ukuran partikel co-doping LTO dengan x = 0.05. Namun, co-doping LTOhasil sintesis tidak ditemukan adanya reduksi pada ukuran partikel yang mengindikasikanbahwa co-doping Mg dan Fe tidak berpengaruh pada ukuran partikel. Hasil EDSmenunjukkan kehadiran unsur Mg, Fe, Ti, dan O yang menunjukkan bahwa unsur yangdiinginkan pada sampel co-doping dan persebarannya relatif merata. Karakterisasi XRDmenunjukkan bahwa fasa Mg(OH)2 dan Fe2O3 tidak ditemukan di dalam struktur codopingLTO yang mengindikasikan bahwa atom Mg dan Fe telah bergabung denganstruktur LTO. Sampel dengan prekursor TiO2 dan Fe2O3 komersial dan TiO2 sintesisdengan Fe2O3 hasil purifikasi pada komposisi x = 0,1 memiliki fasa pengotor terendahdibandingkan LTO komersial dan LTO sintesis murni yaitu 12,7% dan 9,9%. Nilai Rctsemua sampel co-doping menunjukkan nilai Rct lebih kecil dibandingkan nilai Rct LTOmurni (Rct co-doping < Rct LTO murni). Hal ini menunjukkan bahwa co-doping Mg danFe mengurangi hambatan difusi LTO, sehingga meningkatkan transfer muatan dankonduktivitas listrik. Dengan demikian, menunjukkan bahwa pergerakan ion Li+ lebihmudah pada sampel LTO yang didoping. Sampel LTO sintesis dengan menggunakanprekursor Fe2O3 hasil purifikasi (x = 0,1) memiliki nilai Rct paling rendah dibandingkansemua sampel yaitu 85,41 Ω dan memiliki nilai koefisien difusi ion litium dankonduktivitas paling besar yaitu 2,081 x 10-11 cm2.s-1 dan 2,913 S.cm-1. Selain itu,memiliki nilai ΔE yang paling rendah, sehingga memiliki derajat polarisasi terendah danreversibilitas yang paling baik. Pada C-rate tinggi (15C), sampel LTO sintesis denganpenambahan Fe2O3 hasil purifikasi (x=0,1) memiliki kapasitas tertinggi dibandingkansampel co-doping LTO sintesis lainnya yaitu 21,716 mAh/g. Sedangkan pada co-dopingLTO komersial, LTO komersial dengan prekursor Fe2O3 komersial (x=0,1) memilikikapasitas tertinggi yaitu 47,70 mAh/g

---

Li4Ti5O12 (LTO) anode doped with Mg and Fe in the form of Li4-xMgxTi5-xFexO12

(x = 0, 0.05, 0.1) was successfully synthesized using the solid-state method with

sonication using TiO2 and Fe2O3 precursor sources, both comercial and synthetic. SEM

results showed that the co-doped samples of Mg and Fe on commersial LTO had

relatively the same and uniform morphology and particle size reduced of the LTO codoped

particles with x = 0.05. However, co-doping of synthesized LTO was not found in

any reduction in particle size, indicating that Mg and Fe co-doping had no effect on

particle size. The EDS results showed the presence of Mg, Fe, Ti, and O elements which

indicated that the desired element in the co-doping sample and its distribution was

relatively even. XRD characterization showed that Mg(OH)2 and Fe2O3 phases were not

found in the LTO co-doping structure indicating that Mg and Fe atoms had joined the

LTO structure. Samples with commercial TiO2 dan Fe2O3 precursor and synthesized TiO2

with purified Fe2O3 at the composition x = 0.1 had the lowest impurity phase compared

to commersial LTO and synthetic LTO, namely 12.7% and 9.9%. The Rct value of all codoping

samples shows that the Rct value is smaller than the Rct value for pure LTO (codoping

Rct < pure LTO Rct). This suggests that the co-doping Mg and Fe reduces the

diffusion resistance of LTO, thereby increasing charge transfer and electrical

conductivity. Thus, it shows that the movement of Li+ ions is easier in the co-doped LTO

samples. Synthesized LTO samples using the purified Fe2O3 precursor (x = 0.1) has the

lowest Rct value compared to all samples, namely 85.41 Ω and has the greatest value of

lithium ion diffusion coefficient and conductivity values of 2.081 x 10-11 cm2.s-1 and 2.913

S.cm-1. In addition, it has the lowest ΔE value, so it has the lowest degree of polarization

and the best reversibility. At a high C-rate (15C), the synthetic LTO sampel with the

addition of purified Fe2O3 (x = 0.1) has the highest capacity compared to other synthetic

LTO co-doping samples, namely, 21.716 mAh/g. While in commersial LTO co-doping,

sampel commercial Fe2O3 precurcor (x = 0.1) has the highest capacity of 47.70 mAh/g."