Hasil Pencarian  ::  Simpan CSV :: Kembali

Abstrak :
Suatu disain eksperimental menggunakan metode Taguchi dipelajari untuk proses laminasi ekstrusi polypropylene pada film oriented polypropylene. Langkah-langkah yang dilakukan adalah mengumpulkan data-data sekunder yaitu data disain sistem proses, data material dan kualitas produk, lalu mendisain eksperimen, melakukan eksperimen, melakukan analisa-analisa dan menetapkan setting parameter-parameter proses. Eksperimen dilakukan menggunakan orthogonal array L8 dengan dua tingkat pengujian untuk kondisi malam dan siang hari. Parameter-parameter proses yang dipergunakan sebagai faktor-faktor eksperimen yang dapat dikendalikan adalah temperatur ruang pengeringan, temperatur polypropylene pada ekstruder, bukaan katup air cooling roll, tekanan silicon roll, kecepatan lembaran film, tegangan lembaran film oriented polypropylene dan kecepatan putar extruder screw. Performa yang diperiksa adalah ketebalan film hasil laminasi yang diharapkan tepat 35,0 µm dan kekuatan ikatannya yang diharapkan setinggi mungkin. Parameter proses yang siknifikan pada sensitifitas proses terhadap ketebalan hasil laminasi, yang dipergunakan untuk mengatur ketebalan laminasi adalah kecepatan lembaran film dan kecepatan putar extruder screw. Parameter proses yang siknifikan pada sensitifitas proses terhadap kekuatan ikatan laminasi, yang dipergunakan untuk mengatur kekuatan ikatan adalah bukaan katup air cooling roll dan kecepatan putar extruder screw. Parameter proses yang siknifikan pada ketidak-sensitifan terhadap gangguan-gangguan pada ketebalan hasil laminasi adalah kecepatan putar extruder screw, temperatur ruang pengeringan, tegangan lembaran film dan kecepatan lembaran film. Parameter proses yang siknifikan pada ketidak-sensitifan terhadap gangguan-gangguan pada kekuatan ikatan adalah bukaan katup air cooling roll. Dari hasil analisa terhadap pengaruh parameter proses pada performa, disusun setting parameter proses yang optimal.

---

An experimental design of Taguchi method was studied for extrusion laminating process of polypropylene on oriented polypropylene film. The steps were collecting secondary data included process system design data, material data and product quality, then designing experiment, running experiment, analyzing, and determining the setting of optimal process parameters. The experiment performed using L8 orthogonal array with two level of test in day and night condition. The process parameters that used as experimental control factors are temperature of drying box, temperature of polypropylene in extruder, water valve opener of cooling roll, pressure of silicon roll, line speed, tension of oriented polypropylene film and extruder screw speed of revolution. Performances were inspected are the thickness of film has laminated that desired 35,0 µm and the bonding strength that desired as high as possible. The process parameters that significant to process sensitivity for the thickness that use to adjust the thickness are line speed and extruder screw speed of revolution. The process parameters that significant to process sensitivity for the bonding strength that use to adjust the bonding strength are water valve opener of cooling roll and extruder screw speed of revolution. The process parameters that significant to process insensitivity in the noise at the thickness are extruder screw speed of revolution, temperature of drying box, tension of film and line speed. The process parameters that significant to process insensitivity in the noise at the bonding strength is water valve opener of cooling roll. The setting of optimal process parameter was determined from the result of analyzing process parameters that affected performances.

Abstrak :
ABSTRAK
Penelitian telah dilaksanakan di Laboratorium Pusat Pramuteknik Petrokimia PERTAMINA dan Laboratorium XRD Jurusan Fisika Universitas Indonesia. Percobaan dilakukan dengan peralatan dan mesin-mesin dalam Skala semi industri.

Bahan plastik yang berbentuk pelet diekstrusi menjadi lembaran, dan dipotong-potong menjadi pita. Pita-pita ini kemudian diorientasi dalam media air panas dengan variasi :berikut :

1. Ratio penarikan (Draw ratio, DR) dari 5 sampai 7,5 dengan suhu orientasi konstant 98°C. Suhu dari 60°C sampai 98°C dengan ratio penarikan konstan 6.

2. Pengukuran sifat fisik dari pita yang telah diorientasi meliputi denier, kuat tarik, mulur dan densitas, sedangkan sifat termal diukur dengan alat Differential Scanning Calorimeter dan titik leleh diukur dengan alat Thermovar.

3. Pengukuran derajat kristalinitas dan derajat keteraturan struktur kristal menggunakan alat Difraksi Sinar X.

Hasil penelitian menunjukkan bahwa kenaikan derajat kristalinitas akibat proses orientasi menyebabkan terjadinya peningkatan linier sifat fisik dan termal.

Abstrak :
Saat ini, plastik menjadi perhatian terkait dengan degradasi dan isu-isu lingkungan. Hal ini menyebabkan penelitian untuk mengembangkan bahan ramah lingkungan. Untuk meminimalkan dampak dari masalah tersebut, baru-baru ini penggunaan serat alam sebagai pengisi diperkenalkan karena biodegradabilitas dan ketersediaan. Serat alami yang menjanjikan adalah serat ijuk dari Arenga pinnata tanaman sebagai pengisi dan polypropylene polimer (PP) sebagai matriks. Sayangnya, serat alam dan polimer memiliki sifat yang berbeda, polimer memiliki sifat polar sedangkan serat alam bersifat non-polar sehingga mengurangi kompatibilitas dan dihasilkan kristalinitas yang sangat rendah. Untuk meningkatkan kompatibilitas dan kristalinitas, serat ijuk diberikan perlakuan dengan beberapa tahapan termasuk alkalinization dengan 5% dan 10% natrium hidroksida (NaOH), oksidasi dengan 3% dan 6% sodium hypochlorite (NaClO) dan hidrolisis dengan asam sulfat 20% (H2SO4) di urutan. Tujuan dari perlakuan bertahap adalah untuk menghapus komponen seperti lignin, lilin, hemiselulosa, memfragmentasi lignin yang tersisa secara oksidatif dan menghilangkan bagian amorf masing-masing. Fourier-Transform Infrared (FT-IR) mengidentifikasi tingkat kompatibilitas sementara itu Differential Scanning Calorimetry (DSC) menunjukan kristalinitas dan Scanning Electron Microscope (SEM) menampilkan permukaan morfologi polypropylene. Percobaan mengungkapkan bahwa efek dari serat ijuk dengan perlakuan bertahap dari 5% NaOH dan 10% NaOH menghasilkan kristalinitas polypropylene sekitar 31,2% dan 27,64% masing-masing dibandingkan dengan kristalinitas sebelum menambahkan "ijuk" serat untuk 16,8%. Hal ini menunjukkan bahwa seluruh perlakuan meningkatkan kompatibilitas dan kristalinitas polypropylene. Selain itu, penggunaan 5% NaOH menawarkan kristalinitas lebih baik dari polypropylene non-diobati. Percobaan menyimpulkan bahwa dengan menambahkan alkalinized serat ijuk perlakuan bertahap dapat meningkatkan kompatibilitas dan kristalinitas dari polypropylene. ...... Nowadays, plastics becomes concern associated with its degradation and environmental issues. It has led studies to develop an environmental-friendly material. To minimize the impact of those problems, recently the usage of natural fibers as a filler are introduced because of biodegradability and availability. The promising natural fiber is ijuk fiber from Arenga pinnata plant as a filler and polypropylene (PP) polymer as a matrix. Unfortunately, the natural fibers and polymers have the different properties on which polymers are polar while natural fibers are non-polar so that reducing the compatibility and resulting the poor crystallinity. To enhance the compatibility and crystallinity, ijuk fibers were prepared by multistage treatments including alkalinization with 5% and 10% sodium hydroxide (NaOH), oxidation with 3% and 6% sodium hypochlorite (NaClO) and hydrolysis with 20% sulphuric acid (H2SO4) in sequences. The purposes of multistage treatments are to remove the components such as lignin, wax, hemicellulose, to cause an oxidative fragmentation of remaining lignin and to annihilate the amorphous parts respectively. Fourier-Transform Infrared (FTIR) confirms the compatibility meanwhile Differential Scanning Calorimetry (DSC) reveals the crystallinity and Scanning Electron Microscope (SEM) displays surface morphology of polypropylene. The experiments were revealing that the effects of ijuk fibers by the multistage treatments of 5% NaOH and 10% NaOH resulting the crystallinity of polypropylene around 31,2% and 27,64% respectively compared to the crystallinity before adding the ijuk fibers for 16,8%. It indicates that the entire treatments increasing the compatibility and crystallinity of polypropylene. In addition, the use of 5% NaOH offers the better crystallinity than non-treated polypropylene. The experiments conclude that by adding alkalinized ijuk fibers of multistage treatments can increase the compatibility and crystallinity of polypropylene.

Abstrak :
Pertumbuhan plastik tahun ke tahun sangatlah signifikan, namun masalah limbah plastik menjadi salah satu isu yang mengiringi perkembangan dari plastik. Salah kelola limbah plastik di Indonesia menjadi faktor utama mengapa pertumbuhan limbah plastik dari tahun ke tahun semakin meningkat. Oleh karena itu, daur ulang plastik menjadi salah satu cara yang efektif untuk mengelola limbah plastik ini. Penelitian ini berfokus pada komposisi dari material virgin dan recycled serta penambahan heat stabilizer untuk meningkatkan performa dari limbah plastik yang berasal dari industri otomotif. Beberapa pengujian dilakukan seperti pengujian termal, mekanik, reologi, dan morfologi untuk melihat karakteristik dari limbah plastik dan optimalisasinya dengan variabel komposisi dan penambahan heat stabilizer. Hasil penelitian ini menunjukkan bahwa terjadinya penuruan sifat mekanik, reologi, dan termal dari limbah plastik dibandingkan dengan material virginnya. Hal ini disebabkan karena adanya degradasi termooksidatif yang dialami oleh limbah plastik pada saat diolah kembali dengan menggunakan mesin esktrusi. Penambahan material virginnya mampu untuk meningkatkan sifat mekanik dari material paduan, namun penambahannya tidak terlalu signifikan. Penambahan heat stabilizer mampu untuk meningkatkan ketahanan limbah plastik terhadap degradasi termooksidatif yang dibuktikan dengan pengujian oxidative induction time (OIT) dan pengujian tarik setelah proses heat aging. Komposisi optimum dari paduan material virgin dan recycled adalah 100% material virgin dengan penambahan heat stabilizer sebesar 0.3%. ......The growth of plastic from year to year is very significant, but the problem of plastic waste is one of the issues that accompany the development of plastic. Mismanagement of plastic waste in Indonesia is the main factor why the growth of plastic waste is increasing from year to year. Therefore, plastic recycling is an effective way to manage this plastic waste. This research focuses on the composition of virgin and recycled materials and the addition of heat stabilizers to improve the performance of plastic waste from the automotive industry. Several tests were carried out such as thermal, mechanical, rheological, and morphological tests to see the characteristics of plastic waste and its optimization with variable composition and the addition of heat stabilizers. The results of this study indicate that there is a decrease in the mechanical, rheological, and thermal properties of plastic waste compared to virgin material. This is due to the thermooxidative degradation experienced by plastic waste when it is reprocessed using an extrusion machine. The addition of virgin material is able to improve the mechanical properties of the alloy material, but the addition is not too significant. The addition of a heat stabilizer is able to increase the resistance of plastic waste to thermooxidative degradation as evidenced by oxidative induction time (OIT) testing and tensile testing after the heat aging process. The optimum composition of the blend of virgin and recycled materials is 100% virgin material with the addition of a 0.3% heat stabilizer.

Abstrak :
Polypropylene (PP) adalah termoplastik yang sangat luas pemakaiannya. Kombinasi antara permintaan yang tinggi dan kemudahan daur ulang menyebabkan aplikasi PP daur ulang menjadi hal yang sangat biasa dan diterima secara umum. Dalam penelitian ini, penulis membandingkan struktur dan sifat mekanik PP murni, PP daur ulang dan PP daur ulang komersial yang dipakai sebagai gantungan pakaian. Pengujian termal dengan DSC menunjukkan bahwa daur ulang tidak menyebabkan perubahan titik leleh yang signifikan, yaitu tetap berada pada kisaran 160 oC - 163°C. Identifikasi bahan dengan FTIR menunjukkan bahwa PP daur ulang komersial mengandung campuran unsur Polyethylene (PE) yang tidak terdapat pada PP murni dan PP daur ulang. Hasil uji tarik dan uji kekerasan tidak menunjukkan perubahan yang signifikan antara PP murni dan PP daur ulang. Di sisi lain, uji tarik menunjukkan bahwa kuat tarik PP daur ulang komersial lebih rendah 22,1% daripada PP murni, modulus Young turun 8,1%, dan strain-at-break berkurang secara drastis sebesar 65,7%. Uji kekerasan dengan Shore Hardness menunjukkan bahwa kekerasan relatif tidak berubah karena daur ulang. Hal ini didukung dengan SEM yang memperlihatkan citra PP daur ulang komersial memiliki permukaan yang relatif lebih datar dengan ukuran butir lebih kecil daripada PP murni, yang menunjukkan bahwa bahan bersifat lebih brittle. ......Polypropylene (PP) is a type of thermoplastic that is widely used in our daily activities. A combination of high demand and easinest recycling maker the recycled PP has been generally accepted. In this study, a study of the structure and mechanical characteristics of original PP, recycled PP, and commercial recycled PP is compared, especially the ones that is applied as cloth hanger. DSC thermal tests showed that the recycling process did not cause a significant change to the material?s melting point, which stays in the range of 160 oC - 163°C. Meanwhile, FTIR tests showed that the commercially recycled PP contains of Polyethylene (PE), which element was not found in original PP and recycled PP. On the other side, tensile test showed that the tensile strength, Young modulus and strain-at-break are lower than those of original PP by 22,1 % ; 8,1 % and 65,7 % respectively. Tensile and hardness test demonstrated there is no significant differences between original PP and recycled PP. Furthermore, Shore Hardness tests show the recycling process has a little effect on the material?s hardness. These fact is also supported by morphological observation using SEM that the surface contour of the images of commercial recycled PP is relatively more flat and has smaller grain size than those of original PP, which indicates that the commercial recycled PP is relatively more brittle.

Abstrak :
Polypropylene diperkuat serat flax dipersiapkan untuk mengetahui pengaruh penambahan serat dan coupling agent terhadap sifat - sifat mekanik dari komposit. Komposit flax/polypropylene dibuat dengan kandungan yang berbeda (10,20 dan 30 % berat). Sedangkan untuk coupling agent dengan tipe maleic anhydride polypropylene dilakukan penambahan 4% pada masing - masing komposisi komposit. Proses pembuatan material dilakukan dengan cara ekstrusi dan injeksi. Sifat - sifat mekanik yang diteliti yaitu tarik, tekan, tekuk, puntir dan impak. Modulus dan tegangan maksimum dari flax/polypropylene meningkat dengan penambahan serat. Pengaruh yang sama juga dihasilkan melalui penambahan coupling agent. ......Flax fibre reinforced polypropylene were prepared to investigate the influence of fibre loading and coupling agent on the mechanical properties of the composite. Flax/polypropylene composite was made with different content (10, 20 and 30 wt %). Whereas, coupling agent of maleic anhydride polypropylene was added by 4% to each composite composition. The process making of materials was performed by extrusion and injection. The mechanical properties of composite such as tensile, compression, flexural, torsion and impact were investigated. Modulus and maximum stress of flax/polypropylene increased with increase of fibres loading. The same effect was also generated through the addition of coupling agent.

Abstrak :
ABSTRAK
Polypropylene merupakan jenis plastik polimer yang banyak digunakan sebagai kemasan produk. Banyaknya limbah berbahan dasar polypropylene ini sulit terurai, menjadi salah satu alasan untuk menggunakannya sebagai pengganti agregat kasar pada beton. Untuk mencapi mutu beton yang struktural, diperlukan komposisi material penyusun beton yang tepat. Dalam penelitian ini volume perbandingan agregat kasar polypropylene terhadap volume semen yang digunakan adalah 2,6; 2; dan 1,8 dimana hasil kuat tekan kubus yang diperoleh adalah 243,762 kg/cm2; 268,744 kg/cm2; dan 285,623 kg/cm2, dengan nilai modulus elastisitas 7584,048 MPa; 2520,158 MPa; 3913,633 MPa dan poisson rsquo;s ratio sebesar 0,178; 0,164; 0,219. Selain itu, nilai kuat lentur yang dihasilkan sebesar 2,94 MPa; 2,43 MPa; dan 3,41 MPa. Beton ringan ini termasuk kedalam klasifikasi beton ringan mutu sedang berdasarkan ACI 213R-87.

---

ABSTRACT
Polypropylene is kind of polymer that is used as product warp. That many un degraded waste made by polypropylene is the main reason of using it as lightweight coarse aggregates concrete. To achive the structural concrete, required the right composition of concrete materials. In this reseacrh, ratio the volume of coarse aggregate to the volume of cement used are 2,6 2 and 1,8 where the resulting compressive cube strength are obtained 243,762 kg cm2 268,744 kg cm2 dan 285,623 kg cm2, with modulus of elasticity 7584,048 MPa 2520,158 MPa 3913,633 MPa and poisson rsquo s ratio are 0,178 0,164 0,219. Besides that, the resulting of flexural strength are obtained 2,94 MPa 2,43 MPa and 3,41 Mpa. This lightweight concrete is classified as moderate lightweight concrete based on ACI 213R 87.

Abstrak :
ABSTRAK
Perkembangan ilmu pengetahuan dan teknologi membuat banyak inovasi yang muncul termasuk dalam dunia teknik sipil. Beton ringan dengan 100 agregat kasar terbuat dari bahan polypropylene termasuk salah satu inovasi yang sedang dikembangkan. Sifat mekanik dari beton ringan ini masih diteliti, termasuk sifat susut beton ini. Penelitian ini akan membahas susut yang terjadi pada beton ini. Regangan susut yang terjadi pada beton ini rata-rata adalah sebesar 0.001 mm/mm. Hasil tersebut sama walaupun terdapat dua metode pengujian, yaitu kontak dan non-kontak. Untuk membuktikan, dilakukan permodelan secara numerik dengan memasukkan variabel selisih suhu beton. Hasil deformasi yang didapatkan dari eksperimen dan numerik berbeda sekitar 0.1 ndash; 0.5 kali lipat.

---

ABSTRACT
The development of science and technology made many innovations that emerged including in the civil engineering world. Lightweight concrete with 100 coarse aggregate made of polypropylene material is one of the innovations under development. The mechanical properties of these lightweight concrete are still being investigated, including the shrinking properties of these concrete. This study will discuss the shrinkage that occurs in this concrete. The shrinkage strain occurring in this concrete averaged 0.001 mm mm. The results are the same although there are two testing methods, namely contact and non contact. To prove, numerical modeling is done by entering the variable of temperature difference of concrete. The results of deformations obtained from experiments and numerically differ by about 0.1 0.5 fold.

Abstrak :
ABSTRAK
Natural fiber reinforced polymer composites are widely developed because of their relative low price and eco-friendly. One of natural fiber sourches is pandanus tectorius leaf. This study aimed to determine the effect of variations in fiber volume fraction on tensile strength, impact strength, bending strength and morphological on sea pandanus fibers- polypropylene composites.Tensile test spesimen refer to ASTMD 638, impact test spesimen refes to ASTMD 5942-96, bending test spesimen refer to ASTMD 790 -02. The increasing of the volume fraction increased the tensile strength and impact strength. The tensile test results showed the highest tensile strength results for composites with a volume fraction of 35% was 25.82 MPa. The impact test results showed that the highest impact strength was obtained in the 35 % volume fraction of 0.0062 Joule/mm2. The bending test results showed that the highest bending strength was obtained in the 20% volume fraction of 24.96 MPa. Based on SEM test results, there were voids, cracks, fibers pull out on the composite.

Abstrak :
This study aims to evaluate the effectiveness of a polypropylene hollow fiber membrane contactor in removing dissolved ammonia in wastewater using sulfuric acid solution as an absorbent. In the ammonia removal experiments, wastewater and absorbent solutions flowed through the shell side and the lumen side of the contactor, respectively. The pH of wastewater, rate of circulation and ammonia initial concentration were operating variables which influenced the efficiency of the removal process. The efficiency of ammonia removal increases with the wastewater pH level when it is at the same circulation rate and time. In addition, the increase in the circulation rate of the wastewater will increase the efficiency of ammonia removal and the overall mass transfer coefficient. Meanwhile, the efficiency of ammonia removal and the overall mass transfer coefficient decreased with initial ammonia concentration in the wastewater solution.