Hasil Pencarian  ::  Simpan CSV :: Kembali

"High Strength Low Alloy Steel is highly used in marine environment. Highly aggressive attack from cl- ions plus continuously exposure from oxygen worse its condition. Reheated micro alloyed steel is deformed in 30%, 40% , and 50% rolling deformation, resulting varieties corrosion rate depend on its deformation when it is exposed in chloride environment. Austenite prior grain diameter in its sample also varieties. Effect of strain induced Nb (CN) precipitation also give varieties result on its ferrite grain diameter. Approaching in corrosion rate is from its corrosion thermodynamic especially in free energy theory. Where grain boundaries free energy is high, so if number of grain boundaries increased it is also increasing free energy of sample. Analysis is in observation effect of grain diameter and number of grain boundaries on its corrosion rate. Knowing that giving varieties increase deformation will decreasing its ferrite and austenite grain diameter. Method that is used to represents marine environment is salt spray method using 3.5% Sodium Chloride. Experiments is held in 48 hours and it is repeat 3 times. Another approach that is using is, approaching in free energy theory where it is connect with its potential after deformation. Corrosion rate results is match with free energy theory, where with the increasing of deformation degree so the corrosion rate will be increase. It is match with its free energy number when the grain size is decrease, number of corrosion potential will show the corrosion resistance it is low."

"Dewasa ini penggunaan baja berkekuatan tinggi semakin meningkat terutama dalam sektor konstruksi dan infrastruktur. Baja berkekuatan tinggi yang diproduksi melalui thermo-mechanical control process memiliki kombinasi kekuatan dan ketangguhan yang sangat baik. Namun proses pengelasan yang dilakukan untuk menyambung baja mengakibatkan terjadinya perubahan sifat mekanik pada sambungan las. Penelitian ini bertujuan untuk melihat pengaruh variasi komposisi nikel pada kawat las dan masukan panas terhadap struktur mikro dan sifat mekanik baja kekuatan tinggi yang dilas dengan metode pengelasan busur rendam (SAW). Material yang digunakan pada penelitian ini adalah pelat baja struktural berkekuatan tinggi, SM570-TMC, yang memiliki kekuatan luluh 460 MPa, kekuatan tarik 570 MPa dan ketebalan 12 mm. Disain sambungan dari pelat baja ini adalah butt joint dengan single v-groove sebesar 30 derajat, root gap sebesar 5 mm. Pelat baja ini dilas dengan variabel masukan panas berbeda (2,2 kJ dan 3 kJ), dengan menggunakan tiga jenis kawat las yang masing-masing memiliki kandungan nikel 0%, 1%, dan 2,1%. Pengamatan struktur mikro dilakukan menggunakan mikroskop optik dan scanning electron microcopy (SEM). Struktur mikro area kampuh las untuk semua sambungan terdiri dari polygonal ferrite (PF), side plate ferrite (SPF), grain boundary ferrite (GBF) dan acicular ferrite (AF). Area HAZ mengalami pertumbuhan butir yang ditandai dengan ukuran butir yang lebih besar dari kampuh las dan logam dasar. Pada pengelasan dengan masukan panas tinggi, ukuran butir HAZ lebih besar dari ukuran butir dengan masukan panas rendah. Uji tarik, ketangguhan impak dan kekerasan mikro dilakukan untuk menentukan sifat mekanik hasil pengelasan. Pengujian ketangguhan impak dilakukan pada temperatur 25oC, 0oC dan - 20oC.

---

Nowadays the demand for high strength low alloy steel (HSLA) utilization is increasing. HSLA steel produced by thermo-mechanical controlled process (TMCP) has a good combination of strength and toughness. However, thermal cycles during welding lead to deterioration of mechanical properties of welded joint. This research aims to determine the effect of nickel content difference in welding wire and heat input on microstructure and mechanical properties of HSLA steel welded by submerged arc welding method (SAW). Material used in this research is HSLA steel plate SM570-TMC, which has yield strength 460 MPa, tensile strentgh 570 MPa and thickness 12 mm. Joint design is butt joint with 30-degree single v-groove and 5 mm root gap. The plates are welded with the heat input variable (2,2 kJ dan 3 kJ), using three different electrodes which have different nickel content (0%, 1%, dan 2.1%). Microstructures were observed using optical microscope and scanning electron microcopy (SEM). Microstructure in weld metal consist of polygonal ferrite (PF), side plate ferrite (SPF), grain boundary ferrite (GBF) and acicular ferrite (AF). HAZ microstructure is coarser than weld metal and base metal due to grain growth. In high heat input welding, HAZ grain size is higher than HAZ in low heat input joint. Tensile test, Impak test and hardness test were utilized to measure the mechanical properties of welded joint. Impact tests were done in weld metal and HAZ area at temperature of 25oC, 0oC and -20oC."

"Kebutuhan baja berkualitas tinggi dengan harga yang kompetitif serta biaya pemeliharaan yang rendah semakin meningkat dalam mendukung pembangunan infrastruktur di Indonesia. Salah satu solusi dalam mengatasi permasalahan tersebut adalah penggunaan baja tahan korosi atmosfer yang dapat diaplikasikan dalam kondisi tidak dicat sehingga dapat memberikan kontribusi penting dalam menurunkan biaya pemeliharaan. Oleh karena itu penelitian ini difokuskan pada optimalisasi penggunaan elemen paduan yaitu Cu 0,25-0,35wt%, Ni 0,10-0,20wt%, Cr 0,35-0,55wt%, P 0,09-0,11wt% dan Nb 0,005-0,015wt% serta penerapan Thermo Mechanical Control Process untuk menghasilkan produk baja berkualitas secara efisien. Hasil penelitian menunjukan bahwa baja yang dikembangkan telah memenuhi standar spesifikasi JIS G3125 SPAH dengan atmospheric corrosion index sebesar 7,95 yang mengindikasikan ketahanan baja terhadap korosi atmosfer di atas standar. Selain itu, mikrostruktur yang dihasilkan adalah polygonal ferrite dan 10,35% pearlite yang seragam dengan ukuran butir 5,1-6,5 µm dimana butir halus tersebut dapat meningkatkan ketahanan korosi karena aktivitas pelarutan Fe menjadi Fe2+ membentuk γ-FeOOH dan α-FeOOH meningkat. Jika dibandingkan dengan baja karbon biasa, baja yang dikembangkan memiliki ketahanan korosi lebih baik dikarenakan pembentukan lapisan karat amorphous ferric oxyhydroxide yang mengandung Cu, P, Cr serta goethite, lepidocrocite dan Fe3O4. Selain itu kehadiran Si dalam baja tersebut secara efektif dapat mengisi dan memperbaiki lapisan karat yang lemah.

---

The demand for high-quality steel with competitive prices and low maintenance costs is increasing to support infrastructure development in Indonesia. The use of atmospheric corrosion resistant steel that can be applied without painting is one of the best solutions to reduce maintenance costs. Therefore, this research is focused on optimizing the use of micro alloying elements such as Cu 0.25-0.35wt%, Ni 0.10-0.20wt%, Cr 0.35-0.55wt %, P 0.09-0.11wt% and Nb 0.005-0.015wt% and implementing the Thermo Mechanical Control Process so that it can produce a quality steel efficiently. The results of this research showed that the developed steel complies with the JIS G3125 SPAH with atmospheric corrosion index is 7.95, which is higher than standard. Thus, the microstructure of the product is uniform polygonal ferrite with 10.35% pearlite, with an average grain 5.1-6.5 µm classified as very fine grain. The fine grain microstructure can increase corrosion resistance because the increasing of the electrochemical dissolution of Fe into Fe2+ resulting γ-FeOOH and α-FeOOH. In addition, the developed steel has better corrosion resistance than the ordinary carbon steel due to a layer of amorphous ferric oxyhydroxide rust formation containing Cu, P, Cr as well as goethite, lepidocrocite and Fe3O4. Moreover, the presence of Si in the steel can effectively fill and repair weak rust layers."

"ABSTRAKPaduan Cu-Zn 70/30 atau dikenal juga sebagai Cartridge Brass memilikisifat konduktivitas panas dan listrik yang sangat baik, ketahanan korosi yangtinggi, serta kemampubentukan yang baik. Cu-Zn 70/30 sangat luas digunakansebagai core dan tank radiator otomotif, komponen amunisi, maupun perangkatbangunan dan arsitektur sehingga sangat rentan sekali terpapar oleh lingkunganyang korosif seperti air laut dan ammonia. Thermo-Mechanical ControlledProcessing (TMCP) adalah salah satu metode rangkaian pengontrolan pemanasandan pembentukan dengan tujuan meningkatkan kualitas sifat material. Olehkarena itu, pada penelitian ini digunakan metode TMCP dengan canai hangatuntuk meningkatkan sifat mekanik dan ketahanan korosi paduan Cu-Zn 70/30.Proses canai dilakukan dengan metode bolak-balik dengan deformasi sebesar 60%(30%-30%) dimana pada setiap pass-nya paduan Cu-Zn dipanaskan terlebihdahulu pada temperatur 300oC dengan waktu tahan berbeda mulai dari 30, 60, dan120 menit. Berdasarkan hasil penelitian didapatkan kesimpulan bahwa dengansemakin lamanya waktu pemanasan dan kemudian dideformasi lebih lanjut makaterjadi penurunan ukuran butir dari 92.2 μm menjadi 36.5 μm yang berpengaruhpada peningkatan kekerasan sebesar 174.12 HV dan kekuatan tarik mencapai525.4 MPa pada waktu tahan 120 menit. Selain itu, semakin lama waktupemanasan juga memberikan perilaku korosi yang berbeda pada dua lingkungankorosif. Pada lingkungan air laut (NaCl 3.5%), paduan kuningan cenderungmengalami penurunan laju korosi hingga 0.0218 mm/yr untuk weight loss dan0.1404 mm/yr untuk polarisasi. Sedangkan pada lingkungan ammonia (Mattsson?sSolution) terjadi hal yang berkebalikan dimana paduan kuningan cenderungmengalami kenaikan laju korosi hingga mencapai 0.1906 mm/yr untuk weight lossdan 5.1209 mm/yr untuk polarisasi. Ditambah lagi, terdapat indikasi adanyafenomena Anneal Hardening karena tersegregasinya atom terlarut pada dislokasiatau batas butir sehingga memberikan pengaruh yang cukup signifikan terhadapnilai kekerasan, kekuatan tarik, dan ketahanan korosi paduan Cu-Zn 70/30.

---

ABSTRACTCu-Zn alloy (70/30) also known as Cartridge Brass possesses high thermaland electrical conductivity, high corrosion resistance, and good formability. Thus,used extensively for core and tank automotive radiator, ammunition component,and architectural hardware. This wide applications are susceptible to exposure ofcorrosive environments such as seawater and ammonia environments. Thermo-Mechanical Controlled Processing (TMCP) is one method consists of controlledheating and controlled forming to produce high quality materials. Therefore, thisresearch focuses on the study of mechanical properties and corrosion resistanceCu-Zn 70/30 by implementing warm rolling TMCP method. Rolling process wasconducted in reversible way with deformation degree of 60% (30%-30%) andbefore each pass of the rolling the material is heated up to temperature 300oC withdifferent holding time from 30, 60, and 120 minutes. The results showed that asthe longer holding time of the heating and was continued by further deformation,it affects the grain size to be much smaller from 92.2 μm to 36.5 μm and thuscorresponds to the increasing of hardness value up to 174.12 HV dan UltimateTensile Strength (UTS) up to 525.4 MPa for 120 minutes of holding time. On theother hand, the longer holding time of heating, it gives brass different behaviour intwo different corrosive environments. In the seawater environment (NaCl 3.5%),brass tend to have lower corrosion rate in value of 0.0218 mm/yr and 0.1404mm/yr for weight loss and polarization respectively. On the contrary, in theammoniacal environment (Mattsson?s Solution) brass tend to have highercorrosion rate with value up to 0.1906 mm/yr and 5.1209 mm/yr for weight lossand polarization respectively. In addition, it indicates that Anneal Hardeningcaused by segregation of solute atoms into dislocations or grain boundary hastaken place that affect a significant change in hardness, tensile strength, andcorrosion resistance of Cu-Zn 70/30."