Abstrak :
Penelitian ini bertujuan untuk mengetahui pengaruh lama perendaman denture adhesive cream terhadap kuat rekat resin akrilik polimerisasi panas. Krim pada plat akrilik direndam dalam akuades selama 15 detik, 30 detik, dan 60 detik, kemudian kuat rekat diukur dengan alat PASCO-Economy Force Sensor CI-6476. Uji analisis statistik menggunakan Anova one-way. Hasil penelitian menunjukkan Kuat rekat meningkat dengan p<0,05 pada perendaman selama 15 detik dan 30 detik, sedangkan kuat rekat menurun dengan p<0,05 pada perendaman selama 60 detik. Disimpulkan bahwa krim yang direndam dalam akuades lebih dari 30 detik tidak dapat meningkatkan kuat rekat resin akrilik polimerisasi panas.

---

The purpose of this study was to investigate the influence of immersion time of denture adhesive cream in distilled water to the acrylic resin's adhesive strength. Cream on acrylic plate was immersed in distilled water for 15 seconds, 30 seconds, and 60 seconds. Adhesive strength was measured by PASCO-Economy Force Sensor CI-6476. Statistic analysis using one-way ANOVA showed that adhesive strength were significantly increased after immersion in 15 seconds and 30 seconds, and significantly decreased after immersion in 60 seconds. It was concluded that denture adhesive cream couldn't increase the acrylic resin's adhesive strength after immersed more than 30 seconds.

Abstrak :
ABSTRAK
Penelitian bertujuan untuk mengetahui pengaruh penyikatan dengan pasta theobromine dan sodium monofluorophosphate (MFP) terhadap ketahanan kekasaran permukaan email setelah demineralisasi Coca-cola® 75 menit. Spesimen dibagi menjadi tiga kelompok; disikat dengan pasta theobromine, pasta MFP, dan tanpa pasta. Kekasaran permukaan diukur dengan Surface Roughness Tester Mitutoyo. Hasil dianalisis dengan uji Repeated ANOVA dan Oneway ANOVA. Kelompok theobromine dan MFP menunjukkan peningkatan kekasaran yang signifikan (p<0,05) setelah penyikatan. Setelah perendaman, kelompok theobromine menunjukkan peningkatan kekasaran terendah (p>0,05). Dapat disimpulkan penyikatan dengan pasta theobromine mampu mempertahankan kekasaran permukaan email setelah demineralisasi Coca-cola® namun perubahan kekasarannya tidak berbeda signifikan dibandingkan penyikatan dengan pasta MFP.

---

ABSTRACT
The objective of this study was to determine the influence of brushing with theobromine and sodium monofluorophosphate toothpaste on enamel surface roughness resistance after demineralization in Coca-cola® 75 minutes. Specimens were divided into three groups; brushed with theobromine, sodium monofluorophosphate(MFP), and without toothpaste. Surface roughness were measured using Mitutoyo Surface Roughness Tester. Results were analyzed using Repeated ANOVA and Oneway ANOVA. Roughness of theobromine and MFP group were significantly increased (p<0,05) after brushing. After immersion, theobromine group showed the lowest increase in roughness (p>0,05). Brushing with theobromine can maintain email surface roughness after demineralization in Coca-cola® but not significantly different with brushing using MFP.

Abstrak :
ABSTRAK
Latar Belakang: Gel APF yang bersifat asam dapat meningkatkan kekasaran permukaan bahan restorasi, yang menyebabkan adhesi bakteri dan karies sekunder. Tujuan: Menganalisis pengaruh aplikasi gel APF terhadap kekasaran permukaan resin sealant. Metode: Tiga puluh enam spesimen resin sealant dibagi secara acak ke dalam enam kelompok, yaitu aplikasi gel APF dan akuades selama tiga puluh menit sebanyak satu, dua dan tiga kali. Nilai kekasaran permukaan rerata diukur dengan surface roughness tester Mitutoyo SJ201. Hasil: Kekasaran permukaan meningkat bermakna setelah satu kali aplikasi, dan menurun bermakna setelah dua kali aplikasi. (p<0,05)Kesimpulan: Gel APF menurunkan kekasaran permukaan resin sealant setelah dua kali aplikasi.

---

ABSTRACT
Background: Acidity of APF gel could increase restorative material surface roughness, leading to increased bacterial adhesion and secondary caries. Aim: To analyze the effect of APF gel application on the surface roughness of resin sealant. Method: Thirty six resin sealant specimens were randomly divided into six groups, APF gel and aquadest one, two and three times application for thirty minutes each. Mean roughness was measured by Mitutoyo SJ201 surface roughness tester. Result: Surface roughness was significantly increased after one time gel application, and decreased significantly after twice gel application. (p<0,05)Conclusion: APF gel decreased resin sealant surface roughness after second application.

Abstrak :
ABSTRAK
Penelitian ini bertujuan untuk menganalisis pengaruh pasta gigi nano kalsium karbonat dan siwak terhadap kekasaran permukaan email yang mengalami demineralisasi. Spesimen gigi manusia yang telah didemineralisasi dengan asam sitrat disikat setara 6 minggu dengan pasta gigi nano kalsium karbonat dan siwak. Kekasaran permukaan email diukur dengan Surface Roughness Tester, dan diamati melalui SEM, serta analisis unsur dengan EDS sebagai penunjang. Hasil menunjukkan bahwa terdapat penurunan kekasaran permukaan email yang terdemineralisasi setelah penyikatan setara 6 minggu dengan pasta gigi nano kalsium karbonat dan siwak (p<0,05). Penyikatan pasta gigi nano kalsium karbonat dan siwak dapat menurunkan kekasaran permukaan email gigi yang terdemineralisasi.

---

ABSTRACT
The aim of this study was to analyze the effect of nano calcium carbonate and siwak toothpaste to demineralized enamel surface roughness. Human tooth specimen which has been immersed in citric acid were brushed with nano calcium carbonate and siwak toothpaste for 6 weeks. Enamel surface roughness was tested with Surface Roughness Tester with supporting test SEM and EDS was taken. The application of nano calcium carbonate and siwak toothpaste for 6 weeks can decrease surface roughness of demineralized enamel (p<0,05). Brushing with nano calcium carbonate and siwak toothpaste can decrease surface roughness of demineralized enamel.

Abstrak :
PENDAHULUAN : Pit dan fissure sealant merupakan bahan restorasi yang sering digunakan untuk perawatan pencegahan khususnya pada permukaan oklusal gigi anak. Semua bahan restorasi yang berkontak dengan air akan mengalami 2 mekanisme: penyerapan air, yang menyebabkan pembengkakan matriks serta meningkatnya massa dan kelarutan air, terlepasnya komponen dari monomer yang tidak bereaksi dan menyebabkan berkurangnya massa. TUJUAN: Mengetahui pengaruh peningkatan waktu perendaman resin PFS terhadap penyerapan air dan kelarutan resin PFS di dalam air. ALAT & METODE: Sesuai spesifikasi ISO 4049 (2000). Delapan belas spesimen dibuat dari cetakkan (15x1mm) yang dimanipulasi sesuai petunjuk pabrik. Spesimen dimasukkan ke dalam desikator selama 1 hari (T 37 °C; 22 jam dan 23ºC ; 2 jam) ditimbang berulang kali sampai didapat massa konstan (M1). Spesimen direndam selama 1, 2 dan 7 hari di dalam akuabides kemudian dikeringkan dengan kertas penghisap dan digetarkan di udara selama 15 detik setelah itu ditimbang berulang kali sampai massa konstan didapat (M2). Kemudian spesimen dimasukkan lagi ke dalam desikator selama 2 hari (T 37 °C; 22 jam dan 23ºC ; 2 jam) x 2 dan segera ditimbang berulang kali sampai didapatkan massa konstan (M3). Nilai penyerapan air dan kelarutan bahan dari setiap spesimen dihitung menurut perubahan berat sebelum dan setelah perendaman dan pengeringan. HASIL : Dianalisis secara statistik dengan uji non-Parametrik Kruskal-Wallis dengan Post Hoc Mann-Whitney, p<0,05. Nilai penyerapan air meningkat secara signifikan seiring lamanya perendaman dan berbeda bermakna di antara setiap waktu perendaman sedangkan nilai kelarutan air meningkat tertinggi pada 1 hari perendaman dan tidak berbeda bermakna diantara setiap waktu perendaman, kecuali dengan 0 hari (kontrol). KESIMPULAN : 1) Peningkatan waktu perendaman menyebabkan peningkatan penyerapan air. 2) Peningkatan waktu perendaman berpengaruh terhadap kelarutan bahan hanya pada hari 1. ...... INTRODUCTION : Pit and fissure sealant is one of the restorative material that often used as a preventive treatment, especially at occlusal surface of child dentition. All of restorative material that contact with water will experienced 2 mechanism: water sorption, which leads to swelling and mass increase and water solubility, elution of unreacted monomer which leads to a reduction of mass. OBJECTIVE: To evaluate the effect of different time of immersion to the value of water sorption and water solubility in aquabidest. METHOD AND MATERIALS: According to ISO (4049) specification. Eighteen disks (15 x 1 mm) of each material are prepared according to the manufacturers' instructions. Specimens are first desiccated for 1 day (T 37 °C; 22 hr dan 23ºC ; 2 hr) weigh several times until a consistent mass is obtained (M1). Specimens are immersed for 1, 2 and 7 days in aquabidest, remove then dried with absorbent paper, waved in the air for 15 second then immediately weighed after this period (M2). After that the specimen is inserted in dessicator again for 2 days (T 37 °C; 22 hr and 23ºC ; 2 hr) x 2 and weighed several times until constant mass is reached (M3). The value of water sorption and solubility of each specimen were calculated according to the change in its weight as observed before and after immersion and desiccation periods. RESULTS: This result is analyzed statistically with nonparametric test Kruskal-Wallis with post hoc test Mann-Whitney p<0,05. The value of water sorption is increasing significantly along the time of immersion and different significantly from the other time of immersion while water solubility reach its maximum value in the first day and doesn?t different significantly with other time of immersion, except with control. CONCLUSIONS: 1) The longer time of immersion increases the value of water sorption 2) The longer time of immersion only affect the first day value of water solubility.

Abstrak :
Pemutihan gigi kini menjadi pilihan untuk mengembalikan warna gigi yang mengalami diskolorasi. Salah satu teknik pemutihan gigi yang menjadi pilihan adalah teknik pemutihan gigi in-office yang dilakukan oleh dokter gigi. Namun pada praktiknya, aplikasi bahan pemutih gigi tidak hanya mengenai jaringan gigi yang sehat tapi juga jaringan gigi yang mengalami tumpatan, contohnya tumpatan sewarna gigi resin komposit. Untuk memaksimalkan kegunaan dari resin komposit, bahan ini haruslah halus, karena permukaan yang kasar dapat menjadi tempat retensi plak, mengiritasi gingiva dan juga mengurangi kenyamanan pasien. Tujuan : Mengetahui adanya pengaruh aplikasi bahan pemutih gigi hidrogen peroksida 38% terhadap kekasaran resin komposit hibrid. Material dan Metode :20 spesimen resin komposit berdiameter 6mm dan tebal 3mm dibuat secara inkremental dan dipolimerasi menggunakan sinar halogen selama 30 detik. Spesimen dibagi menjadi 2 kelompok, yaitu kelompok aplikasi sebanyak 10 spesimen yang diberi aplikasi bahan pemutih gigi hidrogen peroksida 38% selama 30 menit dan dilanjutkan sampai 60 menit. Sedangkan kelompok kontrol hanya direndam dalam aquabides selama 30 menit dan dilanjutkan sampai 60 menit. Hasil : Terjadi peningkatan nilai kekasaran permukaan resin komposit hidrid setelah aplikasi bahan pemutih gigi hidrogen peroksida 38% baik selama 30 menit maupun 60 menit. Kesimpulan : Bahan pemutih gigi hidrogen peroksida 38% dapat meningkatkan nilai kekasaran permukaan resin komposit hibrid. Peningkatan kekasaran ini dapat menyebabkan berkurangnya nilai estetika resin komposit hibrid. ...... Bleaching is one of the technique that used to get back the colour of the discolour tooth. One of the bleaching technique than can be use is in-office bleaching that should be applied by the dentist. But, in the fact, bleaching agent not only applied on the healthy tooth but also in a tooth that has been restorated,by resin composite. To optimize the benefit of resin composite, it has to be smooth, because the rough surface of resin composite can increase the plaque retention, irritate the gingiva, and also make the patient uncomfortable. Objective : To evaluate the effect of 38% hydrogen peroxide ? containing at in-office bleaching agent apllication to the surface roughness of hybrid composite resin. Material and Method: Twenty specimen of hybrid composite resin (6mm diameter & 3mm in thick) were incrementally polimerized by halogen light for 20 seconds. All spesimens were devided into two groups as follow: 10 spesimens were applied with 38% hydrogen peroxide for 30 minutes and continue to 60 minutes. The other group was soak into the aquabidest for 30 minutes and continue to 60 minutes. Result: The surface roughness (Ra) of hybrid composite resin is increased significantly before and after application of 38% hidrogen peroxide for 30 minutes or 60 minutes. Conclusions : The in ? office bleaching agent 38% hydrogen peroxide could increase the surface roughness of hybrid composite resin and may be reduce the estetic of hybrid composite resin.

Abstrak :
Skripsi ini memberikan informasi mengenai ketersediaan bahan restorasi gigi plastis di Puskesmas dan Rumah Sakit di lingkungan kabupaten Bireuen propinsi Nanggroe Aceh Darussalam (NAD) selama Agustus 2007 sampai dengan Agustus 2008. Penelitian ini adalah penelitian kuantitatif dengan desain deskriptif. Hasil penelitian menunjukkan bahwa Amalgam adalah bahan restorasi plastis yang paling banyak tersedia di rumah sakit dan puskesmas di Kabupaten Bireuen. Perlu menjadi perhatian bagi rumah sakit dan puskesmas yang ada di Kabupaten Bireuen adalah penyeragaman harga penambalan pada pasien dengan jenis bahan restorasi yang sama serta merek yang sama. Perlu juga diperhatikan pengadaan ketiga jenis bahan restorasi plastis antara lain amalgam, GIC dan resin komposit oleh Dinkes setempat. Hal ini diperlukan agar tersedianya ketiga jenis bahan restorasi tersebut di setiap rumah sakit dan puskesmas yang ada di Kabupaten Bireuen sehingga memudahkan masyarakat dalam memperoleh perawatan restorasi gigi karena tidak harus dirujuk ke rumah sakit atau puskesmas yang jauh dari tempat tinggalnya.

---

This survey give the information about availability of dental restorative materials used at hospitals and public health centers at Nanggroe Aceh Darussalam (NAD), especially at Bireuen Regency during August 2007 until August 2008. This research is quantitative descriptive interpretive. Based on the results of the survey, it is identified that the restorative materials used by hospitals and public hospitals at Bireuen Regency, the most preferred one is the Amalgam. It is necessary for hospital and public health centers at Bireuen regency to charge the same prices for the tooth patch with the same type and materials. In addition, local health office is expected to have more attention on the procurement of the three dental restorative materials. It is necessary in order that the materials are always available at the hospitals and public health centers at Bireuen Regency so it will facilitate the local people to obtain tooth patch service. Accordingly, local people will not have to be referred to other hospital and public health centers located far from their houses.

Abstrak :
Rosela mengandung zat warna berupa antosianin. Untuk mengetahui pengaruh lama perendaman terhadap perubahan warna email, digunakan 10 buah spesimen gigi sapi yang direndam dalam larutan ekstrak kelopak bunga rosela selama 15 menit, 30 menit, 45 menit, dan 60 menit. Nilai perubahan warna diperoleh dengan menggunakan VITA Easyshade dan rumus CIEL*a*b*. Hasil uji Repeated ANOVA menunjukkan nilai ?L*, ?a*, ?b*, dan perubahan warna (?E) yang bermakna antara perendaman 15 menit, 30 menit, 45 menit, dan 60 menit (p<0,05). Larutan ekstrak kelopak bunga rosela dapat menyebabkan perubahan warna email. ......Roselle contains anthocyanins, a group of color pigment . This research was conducted to determine the effect of tooth immersion duration in roselle extract solution on enamel discoloration using 10 bovine teeth for 15 minutes, 30 minutes, 45 minutes, and 60 minutes of exposure. Color was measured using VITA Easyshade and CIEL*a*b* color scale. Differences in ?L*, ?a*, ?b*, and ?E were analyzed using repeated ANOVA. There were significant differences between control and treatment groups (p<0,05). Roselle extract solution could cause discoloration of enamel.