"Teknologi fotokatalitik dengan memanfaatkan katalis TiO2 cukup menjanjikan dalam mengatasi permasalahan energi dan lingkungan. Tujuan penelitian adalah melakukan sintesis Nanotube TiO2 menggunakan proses hydrothermal untuk penyisihan methyl orange. Tahapan penelitian adalah sintesis TiO2 dengan proses non-hydrolytic sol gel (NSG) dari prekursor TiCl4 dan dilanjutkan proses hydrothermal. Pada proses hydrothermal digunakan juga prekursor TiO2 P-25.Hasil penelitian menunjukkan TiO2 dengan morfologi nanotube mempunyai luas permukaan spesifik lebih besar daripada TiO2 morfologi nanopartikel. Proses hydrothermal mengubah stuktur TiO2 dari kristalin menjadi amorf nanotube sehingga post treatment dilakukan untuk meningkatkan derajat kristalin nanotube TiO2. Dari hasil uji kinerja katalis didapatkan katalis nonotube TiO2 paling efektif menyisihan methyl orange sebesar 41, 6 % sedangkan katalis TiO2 P-25 dapat menyisihan methyl orange sebesar 93,8 % selama 90 menit.

---

Photocatalysis is currently accepted as one of the most promising technologies for overcoming problems of energy and environmental. The purpose of research is to the synthesis of nanotube TiO2 using hydrothermal method for dyes decolorization of methyl orange. The procedure of research was the synthesis of TiO2 catalyst from TiCl4 precursor using non-hydrolytic sol gel (NSG) and continued hydrothermal process.The result of research showed that Nonotube TiO2 has specific surface area bigger than nanoparticle TiO2. Hydrothermal process can change TiO2 from crystalline becomes nanotube amorf. The result of photocatalytic process showed that nonotube TiO2 catalystis was the most effectively of methyl orange decolorization about 41, 6 % whereas nanoparticle TiO2 P-25 catalyst about 93,8 % for methyl orange decolorization during 90 minutes. "

"Dye-Sensitized Solar Cell (DSSC) merupakan sumber energi alternatif yang sangat menjanjikan. Salah satu komponen penting DSSC adalah fotoanoda yaitu berupa bahan TiO2 yang disensitasi dengan zat warna. Pada penelitian kali ini, TiO2 Nanorod telah berhasil disintesis dengan menggunakan metode hidrotermal menggunakan Ti(OBu)4 sebagai prekursor Ti dan dilanjutkan dengan perlakuan panas (kalsinasi) pada variasi suhu (tanpa kalsinasi, 500ºC, 700ºC, 800ºC, dan 950ºC). Berdasarkan hasil karakterisasi SEM-EDX, bentuk morfologi nanorod belum nampak pada sampel TiO2 (tanpa kalsinasi), untuk sampel TiO2 (dengan suhu kalsinasi 700ºC) sudah mulai nampak terbentuk morfologi nanorod tetapi belum sempurna dan untuk sampel TiO2 (dengan suhu kalsinasi 950ºC) sudah terbentuk morfologi nanorod secara jelas dengan diameter lubang rod yang bervariasi yaitu sebesar 223.8 nm, 277.8 nm, 322.0 nm, dan 326.3 nm. Hasil analisis FTIR menunjukkan bahwa pada suhu kalsinasi semakin tinggi maka puncak serapan pada daerah yang khas untuk gugus fungsi hidroksil semakin rendah nilai serapannya, mengindikasikan semakin berkurangnya keberadaan residu gugus OH bebas. Sedangkan, hasil dari analisis XRD didapatkan hasil bahwa sampel tanpa kalsinasi menunjukkan keberadaan fasa anatase dan rutile dengan ukuran kristalit sebesar 11.34 nm. Sampel TiO2 Nanorod dengan perlakuan panas pada suhu kalsinasi 500ºdidominasi oleh keberadaan fasa kristal rutile, memiliki ukuran kristalit sebesar 20.98 nm. Semakin besar suhu kalsinasi diamati semakin didominasi oleh fasa rutile, dan ukuran kristalitnya menjadi semakin besar, berturut-turut sampel TiO2 Nanorod (dengan suhu kalsinasi 700º, 800ºC dan 950ºC) sebesar 22.14 nm, 39.45 nm, 46.76 nm. Hasil karakterisasi dengan menggunakan Spektrofotometri UV-DRS didapatkan hasil semakin besar suhu kalsinasi maka nilai energi band gap semakin kecil. Nilai band gap yang dihasilkan berada pada rentang anatase dan rutile. TiO2 Nanorod (tanpa kalsinasi) memiliki nilai band gap sebesar 3.06 eV, sedangkan untuk TiO2 Nanorod (dengan suhu kalsinasi 500ºC, 700ºC, 800ºC dan 950ºC sebesar 3.05 eV, 3.04 eV, 3.03 eV, dan 3.03 eV.

---

Dye-sensitized solar cell (DSSC) is a very promising source of alternative energy. One of the key components of the DSSC is photoanoda, which is associated with the TiO2 content. In this research, nanorod TiO2 has been successfully synthesized using the hydrothermal method, by using Ti(OBu)4 as a precursor of Ti, and followed by thermal treatment (calcination) at various temperature (without calcination, 500ºC, 700ºC, 800ºC, and 950ºC). Based on SEM-EDX characterization, TiO2 samples the sample (without calcination) showed no clear formation of nanorod morphology. In the other hand, the TiO2 sample which was heated at 700ºC, started showing the nanorod morphology and a clear nanorod morphology was observed in the TiO2 sample which has heated at 950ºC. The diameter of the rood produced was 223.8 nm, 277.8 nm, 322.0 nm, and 326.3 nm, respectively. The FTIR analysis showed that the peak absorption attributed to the OH group decreased when with more high temperature treatment exposed to the TiO2 samples. The XRD analysis of uncalcinated sample indicated the formation of slightly anatase and more predominantly by rutile, which has a crystallite size of 11.34 nm. It was observed that with more higher temperatures, TiO2 Nanorod samples were predominated by rutile crystal phase. In addition the higher calcination temperatures resulted bigger crystallite size these are the calcination temperature of 500ºC, 700ºC, 800ºC, and 950oC resulted crystallite size of 20.98 nm, 22.14 nm, 39.45 nm, and 46.76 nm, respectively. The characterization results using UV-DRS spectrophotometry showed that the greater the calcination temperature, the smaller the band gap energy value. The resulting band gap values are in the anatase and rutile ranges. TiO2 Nanorod (without calcination) has a band gap value of 3.06 eV, while for TiO2 Nanorod (with calcination temperatures of 500ºC, 700ºC, 800ºC and 950ºC of 3.05 eV, 3.04 eV, 3.03 eV and 3.03 eV."

"Fabrikasi Dye-Sensitized Solar Cell (DSSC)menggunakan klorofil dan rhodamin B telah berhasil dilakukan.Bahan semikonduktor sebagai elektroda kerja dalam DSSC yang digunakan adalah TiO2nanotube yang ditumbuhkan pada plat titanium dengan teknik anodisasi, dilanjutkan dengan kalsinasi pada 500⁰C untuk membentuk fasa kristal TiO2. Karakterisasi terhadap Ti/TiO2-NT meliputi Field Emission Scanning Electron Microscope(FE-SEM), UV-VisDiffuse Reflectance Spectrometry (DRS), X-ray Diffraction (XRD), Fourier Transform Infra Red (FTIR), dan Linear Sweep Voltametry (LSV). Gambar FE-SEM menunjukkan bahwa TiO2 bermorfologi tube dengan diameter 88.99nm. Pola XRD menunjukkan puncak TiO2 anatase pada sudut 2θ: 25, 37,48,54, dan 55 derajat. Karakterisasi UV-Vis menunjukkan nilai bandgap TiO2 sebesar 3.24 eV. Spektrum FTIR menunjukkan keberadaan vibrasi ikatan ~Ti-O-Ti~. Kurva LSV menunjukkan bahwa TiO2 aktif pada daerah UV. Plat Ti/TiO2 dilapisi oleh zat warna melalui teknik elektroforesis dengan variasi waktu 8,10,12, dan 14 menit. Spektrum UV-Vis DRS dari TiO2 yang terlapisi zat warna menghasilkan puncak khas dari masing-masing zat warna, menunjukkan bahwa zat warna telah menempel pada TiO2. Pengujian terhadap performa DSSC menunjukkan nilai efiensi sebesar 0.3565% untuk Ti/TiO2-NT/Klorofil; 0.4351% untuk Ti/TiO2-NT/Rhodamin B; dan 0.3963% untuk Ti/TiO2-NT/Klorofil-Rhodamin B.Indonesia

---

Fabrication of Dye-Sensitized Solar Cell (DSSC) employing chlorophyll and rhodamine B has been successfully carried out. TiO2 nanotubes which was grown on titanium plate by an anodizationtechniques, followed by calcination at 500⁰C to form a crystalline phase of TiO2, was used as working electrode in the DSSC. Characterization of the Ti/TiO2-NT included Field Emission Scanning Electron Microscope (FE-SEM), UV-Vis Diffuse Reflectance Spectrometry (DRS), X-ray Diffraction (XRD), Fourier Transform Infra Red (FTIR), and Linear Sweep Voltametry (LSV). FE-SEM images showed the tube morphologies of TiO2 with a diameter of 88,99 nm. XRD pattern showed the TiO2 anatase peak at 2θ : 25, 37, 48, 54, dan 55 degree. UV-Vis DRS characterization revealed that the bandgap of the prepared TiO2is 3.24 eV. FTIR spectrum showed the presence of ~Ti?O-Ti~ vibration. LSV curves obtained indicate that the TiO2is active in the UV region . The Ti/TiO2 plate then was being coated with the dye through electrophoresis technique with time variation of 8, 10, 12, and 14 minutes. UV-Vis DRS spectrum of the dyes coated TiO2 showed that all typical dyes realted peaks were observed, indicate that the dyes was attached to the Ti/TiO2-NT. Performance tests of the assembled DSSC showed the efficiencies of 0.3565%for the Ti/TiO2-NT/Chlorophyll; 0.4351% for the Ti/TiO2-NT/Rhodamine B; and 0.3963% for the Ti/TiO2-NT/Chlorophyll/Rhodamine B respectively."

"ABSTRAKNama : Najmawati SulaimanProgram Studi : S2 Ilmu KimiaJudul : Sintesis Nanomaterial La2O3-NiO Menggunakan Ekstrak Daun Ciplukan dan Aktivitas Fotokatalitiknya terhadap Methyl OrangePembimbing : Dr. Yoki Yulizar, M.Sc. Pendekatan konvensional telah dilakukan untuk mensintesis dan meningkatkan kinerja La2O3. Akan tetapi, sintesis nanopartikel La2O3 masih menggunakan metode konvensional yang melibatkan bahan kimia yang berbahaya dan tidak ramah lingkungan. Untuk itu, diperlukan pendekatan green synthesis menggunakan ekstrak tanaman yang ramah lingkungan, aman, tidak berbahaya dan terjangkau. Aktivitas fotokatalitik NPs La2O3 dapat ditingkatkan dengan cara memodifikasi NPs La2O3 dengan NPs NiO secara in-situ membentuk nanomaterial La2O3-NiO. Ekstrak daun ciplukan Physalis Angulata mengandung alkaloid yang berperan sebagai sumber basa, flavonoid, saponin, polifenol yang berfungsi sebagai pengstabil dalam sintesis nanopartikel La2O3 dan La2O3-NiO. NPs NiO juga disintesis sebagai variabel kontrol. Penelitian ini bertujuan untuk mensintesis dan mengkarakterisasi NPs La2O3 dan La2O3-NiO menggunakan ekstrak daun ciplukan serta mengamati aktivitas fotokatalitiknya terhadap Methyl Orange.Hasil sintesis NPs La2O3 dan La2O3-NiO dianalisis dengan spektroskopi FTIR, spektroskopi raman, XRD, spektroskopi UV-Vis-DRS, PSA, SEM-EDX dan TEM-SAED. Adanya vibrasi logam dengan oksigen M-O pada bilangan gelombang 400 cm-1 mengindikasikan pembentukan NPs La2O3 sedangkan pada 418 dan 514 cm-1 dari spektra FTIR menunjukkan terbentuknya nanomaterial La2O3-NiO. Empat pita pada 454, 405, 340 dan 284 cm-1 merupakan mode vibrasi raman untuk La2O3. Pergeseran raman pada 380 dan 96,7 cm-1 menegaskan munculnya mode vibrasi spesifik untuk nanomaterial La2O3-NiO. Pola XRD menunjukkan La2O3 berstruktur kubik dengan space group Ia-3 dan La2O3-NiO diasumsikan berbentuk ortorombik dengan space group Pncb. Nilai band gap NPs La2O3 dan La2O3-NiO berturut-turut sebesar 5,390 dan 3,410 eV dengan distribusi ukuran partikel untuk La2O3 sekitar 87,38 nm dan untuk La2O3-NiO sekitar 100,2 nm. Morfologi SEM NPs La2O3 berbentuk nano-chip dengan ukuran berdasarkan TEM yaitu 30-40 nm sedang La2O3-NiO berbentuk bulatan dengan ukuran berdasarkan TEM sekitar 25-35 nm.Aktivitas fotokatalitik NPs La2O3 dan nanomaterial La2O3-NiO terhadap MO dilakukan baik dibawah penyinaran cahaya UV maupun pada keadaan gelap sebagai perbandingan dan menunjukkan bahwa 92,01 MO terdegradasi di bawah sinar UV dan 64,64 MO teradsorpsi pada kondisi gelap selama 180 menit. Dapat disimpulkan bahwa nanomaterial La2O3-NiO memiliki potensi sebagai fotokatalis yang efisien dalam mendegradasi zat warna, MO. Kata Kunci :Green synthesis, nanopartikel La2O3, nanomaterial La2O3-NiO, Physalis angulata, fotokatalitik, Methyl Orangexvi 68 hlm : 46 gambar, 9 tabel, 10 lampiranBibliografi : 43 1972-2018

---

ABSTRACTName Najmawati Sulaiman Study Program Magister of ChemistryTitle Synthesis of La2O3 NiO Nanomaterial Using Physalis Angulata Leaf Extract and Its Photocatalitic Activity on Methyl OrangeSupervisor Dr. Yoki Yulizar, M.Sc. A conventional approach has always been applied to synthesize and improve La2O3 performance. However, La2O3 nanoparticles synthesis still uses conventional methods involving harmful and non environmentally friendly chemicals. Therefore, it needs a green synthesis approach using plant extracts that are environmentally friendly, safe, harmless and affordable. The photocatalytic performance of La2O3 NPs can be enhanced by modifying the La2O3 NPs with NiO NPs in situ to obtain La2O3 NiO nanomaterials. Ciplukan leaf extract Physalis angulata contains alkaloids that can perform as a base source and the flavonoids, saponins, polyphenols can act as stabilizers for the formation of La2O3 and La2O3 NiO nanomaterials. NiO NPs are also synthesized as control variables. This study aimed to synthesize and characterize NPs La2O3 and La2O3 NiO using ciplukan leaf extract and observed its photocatalytic activity toward methyl orange.The synthesis products of La2O3 and La2O3 NiO NPs were analyzed by FTIR spectroscopy, raman spectroscopy, XRD, UV Vis DRS spectroscopy, PSA, SEM and TEM SAED. The presence of metal vibrations with oxygen M O at 400 cm 1 indicates the formation of La2O3 NPs while at 418 and 514 cm 1 of the FTIR spectra showed the formation of La2O3 NiO nanomaterial. Four bands at 454, 405, 340 and 284 cm 1 are the raman vibration modes for La2O3. Raman shifts at 380 and 96.7 cm 1 confirmed the result of specific vibration modes for La2O3 NiO NPs. The XRD pattern showed La2O3 in cubic structure with the Ia 3 and La2O3 NiO was assumed as orthorhombic structure with Pncb space groups. The band gap values of NPs La2O3 and La2O3 NiO were 5.39 and 3.410 eV respectively with the particle size distribution for La2O3 of about 87.38 nm and for La2O3 NiO of about 100.2 nm. The morphology of La2O3 NPs was nanochip shaped with a TEM based size of 30 40 nm while La2O3 NiO is spherical with a TEM based size of about 25 35 nm.The photocatalytic activity of NPs La2O3 and La2O3 NiO on MO was performed either under UV light irradiation or in the dark as a comparison and showed that 92.01 of MO was degraded under UV light and in the dark 64.64 of MO was adsorbed for 180 min. It can be concluded that La2O3 NiO nanomaterials has potential as an efficient photocatalyst in degrading MO. Keywords Green synthesis, La2O3 nanoparticles, La2O3 NiO nanomaterial, Physalis angulata, photocatalitic, Methyl Orange xvi 68 pages 46 figures, 9 tables, 10 attachmentsBibliography 43 1972 2018 "

"Nanokomposit selulosa/Ag₃PO₄/ZnO untuk fotokatalisis degradasi metil jingga telah disintesis dan dikarakterisasi menggunakan FTIR, XRD, UV-DRS dan SEM. Penambahan Ag₃PO₄ pada ZnO dapat menurunkan energi band gap ZnO dari 3.21 eV menjadi 3.19 eV. Pada penelitian ini, ZnO akan bertindak sebagai sisi aktif katalis, Ag₃PO₄ bertindak sebagai sensitizer yang dapat meningkatkan kemampuan katalis untuk menyerap sinar visible, sedangkan selulosa bertindak sebagai support katalis. Proses fotokatalisis degradasi metil jingga dilakukan di bawah sinar UV dan visible selama 1 jam. Kondisi optimum yang diperolah adalah ketika proses fotokatalisis dilakukan pada pH 6, menggunakan jumah katalis 45 mg, dengan rasio komposit pada ZnO/Ag₃PO₄ 1:2, dan rasio selulosa pada nanokomposit selulosa/Ag₃PO₄/ZnO 1:2:1.  Nilai efisiensi fotodegradasi metil jingga yang paling tinggi adalah sebesar 81.05%. Reaksi ini mengikuti kinetika pseudo orde satu dan proses adsorpsi yang terjadi mengikuti model isoterm adsorpsi Langmuir.

---

Cellulose/Ag₃PO₄/ZnO nanocomposite for photocatalytic degradation of methyl orange have been synthesized and characterized by FTIR, XRD, UV-DRS, and SEM. The addition of Ag₃PO₄ to ZnO can reduce the band gap energy from 3.21 eV to 3.19 eV. In this work, ZnO acts as an active site, Ag₃PO₄ acts as sensitizer that can increase the ability of catalyst to absorb visible light, and cellulose acts as a catalyst support. The photocatalysis degradation of methyl orange was observe under UV and light illumination for an hour. The optimum condition obtained was when the photocatalyst was conducted at pH 6 using 45 mg catalyst with composite ratio ZnO/Ag₃PO₄ 1:2, and cellulose ratio on cellulose/Ag₃PO4/ZnO nano composite 1:2:1. The highest photodegradation efficiency of methyl orange is 81.05%. This reaction fits well to the pseudo-first order kinetics and Langmuir adsorption isotherm model."

"Methyl orange (MO) adalah salah satu bahan pewarna yang banyak digunakan di industri tekstil. MO memiliki sifat karsinogen dan berbahaya yang dapat mencemari air dan sangat beracun jika dikonsumsi oleh manusia, sehingga perlu dilakukan fotodegradasi yang efektif. Pada penelitian ini dilakukan sintesis Ag-ZnO/GO untuk fotodegradasi methyl orange. Ag-ZnO/GO memiliki aktivitas fotodegradasi yang baik terhadap methyl orange yang dibuktikan dengan menggunakan UV–Vis diffuse reflectance spectroscopy (UV-DRS) dengan perbandingan nilai band gap yang menurun dari 3,40 eV untuk ZnO menjadi 2,43 eV untuk Ag-ZnO/GO, lalu terdapat peningkatan persentase degradasi sebesar 92 % pada ZnO menjadi 99,6% pada Ag-ZnO/GO dan nilai Kt pada ZnO sebesar 2,21 x 10-2 menit-1 menjadi 2,47 x 10-2 menit-1 pada Ag- ZnO/GO. Katalis juga dikarakterisasi menggunakan Fourier Transform Infra Red (FTIR), Raman Spectrophotometer, X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM) Surface Area Analyzer (SAA-BET), dan persentase degradasi methyl orange diukur dengan UV-VIS Spectrophotometry.

---

Methyl orange (MO) is a dye that is widely used in the textile industry. MO has carcinogenic and dangerous properties that can pollute water and is very toxic if consumed by humans, so it is necessary to carry out effective photodegradation. In this research, Ag-ZnO/GO was synthesized for photodegradation of methyl orange. Ag- ZnO/GO has good photodegradation activity against methyl orange as proved by using UV-Vis diffuse reflectance spectroscopy (UV-DRS) with a ratio of band gap values that decreased from 3.40 eV for ZnO to 2.43 eV for Ag- ZnO/GO, then there is an increase in the percentage of degradation by 92% in ZnO to 99.6% in Ag-ZnO/GO and the Kt value in ZnO by 2.21 x 10-2 minutes-1 to 2.47 x 10-2 minutes-1 in Ag-ZnO/GO. The catalyst was also characterized using Fourier Transform Infra Red (FTIR), Raman Spectrophotometer, X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), Surface Area Analyzer (SAA-BET), and the percentage of methyl orange degradation was measured by UV-VIS Spectrophotometry."

"Pewarna limbah telah merusak lingkungan ekologi sebagai zat pencemar, fotokatalisis merupakan metode yang tepat untuk mengontrol zat polutan. Molybdenum disulfide (MoS2) termasuk kedalam Group6-Transition metal dichalcogenides (G6-TMDs) memiliki struktur yang unik dan melimpah di alam. Pada penelitian ini MoS2 telah berhasil disintesis dengan variasi waktu sintesis 16, 20 jam dan 24 jam dan pelarut dionized water dan etilen glikol menggunakan metode hidrotermal. Morfologi MoS2 mengahasilkan bentuk microspehere dan pola difraksi menunjukkan campuran fasa 2H MoS2, 1T MoS2 dan MoO3 dengan jumlah fasa 1T yang lebih tinggi pada sampel MoS2 16 jam. Hasil efek fotokatalis degradasi methyl orange dibawah pengaruh sinar cahaya tampak tidak menunjukkan adanya degradasi warna. Sedangkan dibawah pengaruh sinar ultraviolet fasa 1T yang dominan pada MoS2 16 jam berhasil mendapatkan laju degradasi tertinggi mencapai 68% dalam waktu 160 menit. Hal ini disebabkan oleh paling tingginya fasa 1T berdasarkan hasil XRD yang terbentuk dan band gap paling rendah yaitu 3,48 eV serta hasil uji raman menunjukkan fasa 1T MoS2.

---

As a pollutant, waste dye has harmed the environment; photocatalysis is an effective way to reduce polluting compounds. Group 6-Transition metal dichalcogenides (G6-TMDs) include Molybdenum disulfide (MoS2), which has a distinctive structure and is abundant in nature. The hydrothermal approach was used to successfully synthesize MoS2 with different synthesis times of 16, 20, and 24 hours, as well as dionized water and ethylene glycol solvents. The morphology of MoS2 provides a microsphere form, and the diffraction pattern indicates a mixture of 2H MoS2, 1T MoS2, and MoO3 phases in 16 hours MoS3 samples with a higher number of 1T phases. There was no color degradation in the photocatalyst effect of methyl orange degradation under the impact of visible light. Meanwhile, under the impact of ultraviolet radiation, the dominating 1T phase of 16 hours MoS2 achieved the maximum degradation rate of 68% within 160 minutes. This is due to the greatest 1T phase developed based on XRD data, as well as the lowest band gap of 3.48 eV and Raman test results indicating the 1T MoS2 phase.

"

"Studi adsorpsi methyl orange (MO) menggunakan adsorben karbon aktif dan lumpur alum telah dilakukan untuk mengetahui efektivitas adsorben serta mengetahui faktor-faktor yang mempengaruhi eksperimen pada tingkat penyisihan MO. Beberapa faktor pengaruh yang diamati pada proses adsorpsi ini adalah efek konsentrasi adsorben, konsentrasi polutan, pH, temperatur, kecepatan pengadukan, volume reaksi serta penggunaan kembali adsorben (reuse). Studi dilakukan karena MO merupakan salah satu zat pewarna yang berbahaya dalam industri tekstil yang memiliki dampak terhadap manusia dan lingkungan. Berdasarkan eksperimen parametrik yang dilakukan pada adsorben karbon aktif diketahui bahwa seiring dengan naiknya konsentrasi adsorben, efisien penyisihan polutan MO juga meningkat sebesar 99,87% pada 1 g/L karbon aktif. Sedangkan pada efek konsentrasi polutan MO berbanding terbalik dimana semakin besar konsentrasi polutan yang diberikan, tingkat penyisihan pada adsorben semakin menurun, yaitu dari 95,89% menjadi 16,8%. Dan untuk adsorben lumpur alum, efisiensi penghilangan polutan MO sangat kecil hanya 5% dengan aktivasi KOH. Dari kedua perbandingan adsorben yang telah dilakukan, karbon aktif merupakan adsorben yang efektif digunakan untuk menghilangkan polutan methyl orange di air dengan persentase removal hampir 100% pada konsentrasi adsorben 0.5 g/L. Karbon aktif juga dapat diregenerasi dengan efisiensi penyisihan mencapai 80%."

"Peningkatan kebutuhan terhadap energi dan kesadaran akan ancaman polusi lingkungan, medorong kebutuhan akan adanya solusi terhadap energi yang bersih dan berkelanjutan. Material semikonduktor TiO2 merupakan material yang diharapkan dapat memainkan peran penting untuk membantu menyelesaikan masalah krisis energi melalui pemanfaatan energi matahari berbasis perangkat fotovoltaik. Dye sensitized Solar Cells (DSSC) merupakan sel surya alternatif yang lebih murah dibandingkan dengan sel fotovoltaik berbasis silikon. Pada penelitian ini dilaporkan proses fabrikasi DSSC menggunakan TiO2 nanotube serbuk yang diperoleh dari anodisasi plat Ti dengan teknik Rapid Breakdown Anodization (RBA) dalam elektrolit HClO4 0,15 M. Beberapa variasi potensial yang diberikan, yaitu 10, 13, 14, 15 dan 20 V dengan tujuan untuk memperoleh area permukaan yang lebih luas dengan waktu sintesis yang cepat, sehingga menghasilkan DSSC dengan efisiensi yang lebih tinggi. Berdasarkan waktu sintesis yang diamati, TiO2 nanotube dapat dihasilkan dalam waktu yang relatif cepat adalah yang diperoleh dari hasil sintesis pada potensial 15 V dan 20 V, yaitu kurang dari 3 jam. Dari hasil karakterisasi TiO2 nanotube serbuk yang diperoleh tersebut diketahui TiO2 hasil sintesis dengan teknik RBA pada potensial 15 V pada suhu kalsinasi 500oC memiliki area permukaan yang lebih luas, yaitu 69,723 m2/g dibandingkan dengan potensial 20 V pada suhu kalsinasi 500oC, yaitu 63,824 m2/g. TiO2 nanotube-serbuk tersebut kemudian diaplikasikan sebagai perangkat DSSC untuk mengetahui pengaruhnya pada konversi energi surya ke energi listrik. Pada aplikasinya sebagai DSSC, elektroda pendukung yang digunakan dibuat dari deposisi larutan 5 mM H2PtCl6 sebagai partikel Pt pada substrat kaca fluorine-doped tin oxide (FTO) yang memiliki hambatan < 11 Ω/cm2. TiO2/FTO pada sistem DSSC dikarakterisasi gdengan menggunakan FESEM, diperoleh ketebalan film TiO2 sekitar 1,6-1,7 μm dan Spektrofotometer UV-Vis. Sedangkan pengujian nilai efisiensinya diukur dengan metoda Linier Sweep Voltametry menggunakan potensiostat. Iluminasi pada bagian depan (Frontside Illumination) kemudian dibandingkan dengan iluminasi pada bagian belakang pada system DSSC (Backside Illumination). Nilai efisiensi tertinggi yang diperoleh adalah 2,63% dibawah sumber cahaya lampu halogen 150 watt pada kondisi Frontside Illumination. Nilai tersebut diperoleh dari DSSC berbasis TiO2 yang disintesis dengan potensial 15 V dengan menggunakan zat warna Alizarin Red S. Kondisi yang sama untuk untuk DSSC dengan TiO2 dari proses sintesis pada 20 V menghasilkan efisiensi hanya 0,006%.

---

An increasing energy demand and environmental pollution concern, lead to a pressing need for a clean and sustainable energy solutions. TiO2 semiconductor material is expected to play an important role in helping solve the energy crisis through effective utilization of solar energy based on photovoltaic devices. Dye-sensitized solar cells (DSSCs) are potentially lower cost alternative to inorganic silicon-based photovoltaic cells. In this study, we report on the fabrication of DSSCs, which was constructed by TiO2 nanotubes powder, produced by rapid breakdown anodization (RBA) of Ti foil. The RBA was conducted in 0.15 M HClO4 electrolyte with variations voltage, namely 10, 13 14, 15 and 20 V to obtain better surface area in order to increase efficiency of DSSC in a quickly synthesize.

Based on the observation during anodizing process, nanotube TiO2 powder can be obtained in rapid condition, less than 3 hours by anodization potential applied at 15 and 20 V. Characterization of morphology and surface area of these nanotube titania powder showed the best TiO2 nanotube was obtained by the RBA technique with applied potential 15 V, 69,723 m2/g, meanwhile for potential 20 V is 63,824 m2/g in the same calcination temperature. These Titania will be utilized as DSSC to compare its performance. The counter electrode was made by electrodeposition of Pt from an aqueous solution of 5 mM H2PtCl6 onto fluorine doped tin oxide (FTO) glass substrate. The TiO2/FTO were characterized by FESEM which is obtained thin film of TiO2 is around 1,6-1,7 μm and Spectrofotometer DRS UV-Vis, while efficiency was measured by Linier Sweep Voltametry method using potensiostat.

The frontside of illuminated DSSCs were compared with the backside one. The highest cell efficiency was 2,63% under 150 W using halogen as light source at frontside illumination which is obtained from TiO2 which is synthesized on 15 V and using Alizarin Red S as sensitizer. That efficiency is higher than TiO2 on 20 V in the same condition (0,006%)."