"Nanozeolite synthesis was carried out through seeding method, in which the seed was Y zeolite (member of faujasite, FAU, family) using tetraethyl orto silicate (TEOS) as silica source, and aluminium isopropoxide Al[(CH3)2CHO)]3 as aluminum source, and tetramethylammoniumhydroxide (TMAOH) as template, under hydrothermal condition. The seeds then were grown on glassy carbon (GC) sheet, that prior being used was modified, using layer by layer (LbL) technique, with three layers of polyelectrolytes: Poly(diallyldimethylammoniumchloride), PDDA; Poly-4-sodium-styrenesulfonate, PSS; and PDDA again. The seeded GC sheet then was immersed into colloidal suspension with molar composition as follow: 14Na2O: Al2O3: 10SiO2: 798H2O: 3Na2SO4 and the pH of the suspension was kept at 9,0 before was treated hydrothermally for 20 hours at 100oC. The variation on number of seed layers on GC (1, 2 and 3 layers), observed by SEM, showed that homogenous structure and crystal size was obtained with 1 layer of seeds applied on the surface of glassy carbon. When more layers of seeds applied, the agregation and intergrowth of zeolite crystals in the thin film of zeolite became more visible. XRD pattern of the as-prepared thin film zeolite indicates that the zeolite has nanoparticle structure. Furthermore, the pattern of glassy carbon predominated the XRD pattern and covered the pattern of Y-zeolite. On the other hand, XRD of as prepared bulk Y-zeolite shows structure of FAU framework."

"ZnO nanopartikel dengan berbagai variasi konsentrasi dopan Co2+ (3, 6, 15 dan 17 at.%) disintesis dengan metode ko-presipitasi. Karakerisasi yang dilakukan meliputi pengukuran EDX, XRD dan UV-VIS untuk mengamati struktur dan sifat optis dari ZnO didop Co nanopartikel. Komposisi Co dalam sample dikatahui dari karakterisasi EDX,. Hasil difraksi sinar X (XRD) menunjukkan bahwa sampel memiliki fase wurtzite dan tidak ditemaknnya fase sekunder. Hasil tersebut membuktikan bahwa ion Co2+ telah berhasil mensubtitusi Zn2+ dalam matrix ZnO. Analisis pelebaran puncak sinar X dilakukan untuk menilai crystalline size dan lattice strain dengan menggunakan metode analisis Williamson-Hall (W-H). Seluruh parameter terkait seperti strain, stress dan nilai energy density turut ditentukan nilainya dengan menggunakan berbagai model dari analisis W-H, yakni uniform deformation model (UDM), uniform stress deformation model (USDM) dan uniform deformation energy density model (UDEDM). Ketiga model analisis tersebut akan menghasilkan nilai strain yang berbeda diakibatkan pendekatan-pendekatan yang dilakukan. Sifat optis seperti celah pita energy dikarakterisasi dengan spektroskopi UV-VIS menunjukan penurunan seiring dengan bertambahnya konsentrasi dopan yang diberikan.

---

ZnO nanoparticles with different Co2+ doping concentrations (3,6,15 and 17 at.%) were synthesized by co-precipitation method. Characterization technique of EDX, XRD and UV-Visible spectra measurement were done to investigate the effects of the doping concentration on the structural and optical properties of Co doped ZnO nanoparticles (NP). The compositional analysis was carried out by Energy Dispersive X-Ray (EDX) measurement. X-Ray diffraction analysis reveals that the Co doped ZnO NP crystallize in wurzite structure without any impurity phase and Co2+ ion were successfully incorporated into the lattice position of Zn2+ ions in ZnO matrix. The wurzite structure (lattice constant) is decreasing with increasing Co doping concentration, it show their crystallization decrease with the increase of Co2+ doping Concentration. The crystalline development in the Co doped ZnO NP was investigated by X-Ray peak broadening. The Williamson-Hall (WH) analysis was used to study the individual contribution of crystallize size and lattice strain on the peak broadening. All other relevant physical parameter such as strain, stress and energy density values were also calculated using W-H plot analysis with different model, viz, uniform deformation model, uniform stress deformation model and uniform deformation energy density model, the three models yield different strain values, it may be due to anisotropic nature or the material. The optical studies show that the band gap of Co doped ZnO NP decreases with increase doping concentration."

"Pada penelitian ini, nanopartikel Li₃PO₄, Fe₃(PO₄)₂, LiFePO₄ sampel A telah berhasil disintesis menggunakan ekstrak daun delima (Punica granatum L) dengan metode green synthesis dan nanopartikel LiFePO₄ sampel B telah berhasil disintesis dengan metode kimia (sol-gel). Ekstrak daun delima (EDD) yang dihasilkan mengandung senyawa metabolit sekunder yang berfungsi sebagai sumber basa dan capping agent dalam menstabilkan ukuran nanopartikel dan mencegah terjadinya proses aglomerasi. Hasil karakterisasi FTIR menunjukkan bahwa LiFePO₄ sampel A dan B membentuk serapan vibrasi (v₂-v₄) PO₄^3- pada bilangan gelombang 586 cm^-1 - 461 cm^-1 (v₄ & v₂) dan 1038/1035 cm^-1 (v₃). Pada hasil XRD menunjukkan nanopartikel LiFePO₄ sampel A dan B memiliki sistem kristal orthorombik. Hasil SEM menunjukkan morfologi LiFePO₄ memiliki bentuk yang heterogen. Nanopartikel LiFePO₄ yang telah disintesis kemudian dijadikan sebagai lembaran katoda dan disusun menjadi baterai ion litium kemudian dilakukan karakterisasi elektrokimia menggunakan EIS, CV dan GCD. Hasil uji GCD menunjukkan bahwa sampel A memiliki kapasitas discharge sebesar 0,35 mAH/gram sedangkan sampel B memiliki kapasitas discharge sebesar 0,93 mAH/gram.

---

In this research, Li₃PO₄, Fe₃(PO₄)₂, LiFePO₄ nanoparticles sample A have been successfully synthesized using pomegranate leaf extract (Punica granatum L) with green synthesis method and LiFePO₄ nanoparticle sample B have also been successfully synthesized by chemical method (sol-gel). Pomegranate leaf extract (EDD) produced contains secondary metabolite compounds that function as a source of base and capping agent in stabilizing the size of nanoparticles and preventing agglomeration. The results of FTIR characterization shows that the LiFePO₄ nanoparticles of samples A and B forms vibrational absorption (v₂-v₄) PO₄^3- at wavenumbers 586-461 cm^-1 (v₄ & v₂) and 1038/1035 cm^-1 (v₃). The XRD results show that the LiFePO₄ nanoparticles of samples A and B have an orthorhombic crystal system. SEM results show that the morphology of LiFePO₄ has a heterogeneous shape. The LiFePO₄ nanoparticles that were formed were successfully used as cathode sheets and arranged into lithium ion batteries then electrochemical characterization was carried out using EIS, CV and GCD. The GCD test results show that sample A has a discharge capacity of 0,35 mAH/gram while sample B has a discharge capacity of 0,93 mAH/gram."

"Sintesis material ferroelektrik SrTiO3 (STO) dan material magnet SrFe12O19 (SHF) melalui teknik pemaduan mekanik dilanjutkan perlakuan sintering pada temperatur 1100°C selama 3 jam. Kedua material sudah berfasa tunggal berdasarkan hasil identifikasi puncak-puncak difraksi sinar-x pada masing-masing pola difraksi. Ukuran partikel material STO dan SHF masing-masing adalah 1116 nm dan 1230 nm. Destruksi partikel secara ultrasonik selama 7 jam, memperkecil ukuran rata-rata partikel dari kedua senyawa menjadi 522 nm dan 70 nm. Teknik destruksi secara mekanik dan ultrasonik dapat digunakan untuk pembentukan nanopartikel.

---

Synthesis of ferroelectric material SrTiO3 (STO) and magnetic material SrFe12O19 (SHF) with mechanical alloying method and sintering with temperature at 1100°C for 3 hours. Both of the material have been a single phase based on the identification result of the peaks in each diffraction pattern. The particle size of material STO and SHF is 1116 nm and 1230 nm. Ultrasonic destruction for 7 hours reduced the mean particle size for both material to 522 nm and 70 nm. Particle destruction with mechanical and ultrasonic method can be used to synthesis of nanoparticle."

"Saat ini, metode pengujian kandungan 3- Monochloropropanediol (3-MCPD) yang merupakan zat kontaminan pada minyak kelapa sawit dilakukan menggunakan instrumen GC-MS. Metode tersebut memerlukan prosedur yang lama dan rumit. Pengembangan nanopartikel emas dengan pengkaping Cysteine berpeluang menjadi solusi untuk mendeteksi 3-MCPD dalam waktu cepat berbasis analisis kolorimetri. Tujuan dari penelitian ini adalah untuk mengetahui kondisi optimal sintesis, ukuran, dan sensitivitas nanopartikel dalam mendeteksi 3-MCPD. Penelitian dilakukan dengan memvariasikan konsentrasi dan volume Cysteine. Variasi konsentrasi Cysteine yang digunakan adalah 0 hingga 0,5 mM, sedangkan variasi volume Cysteine yang dipakai adalah 0 hingga 2 ml. Pengujian 3-MCPD dilakukan dengan variasi konsentrasi 0 hingga 10 ppm. Selanjutnya, karakterisasi dilakukan dengan UV – Vis, FTIR, dan PSA. Sintesis yang optimal didapatkan ketika nanopartikel emas ditambahkan dengan 1 ml 0,025 mM Cysteine menghasilkan warna ruby red yang stabil hingga 24 jam. Ukuran nanopartikel didapatkan 27,1 nm dan terjadi pemutusan ikatan gugus fungsi tiol pada Cys-AuNPs. Nanopartikel emas ini berpotensi untuk dikembangkan lebih lanjut dalam mendeteksi 3-MCPD.

---

Currently, the assay method of 3-Monochloropropanediol (3-MCPD) which is a contaminant in palm oil is carried out by using the GC-MS instrument. This method requires a long and complicated procedure. The development of gold nanoparticles with cysteine capping has the opportunity to be a solution to detect 3-MCPD in a fast time based on colorimetric analysis. This study aims to determine the optimal conditions for synthesis, size, and sensitivity of nanoparticles in detecting 3-MCPD. The research was conducted by varying the concentration and volume of Cysteine. Cysteine concentration variations used are 0 to 0.5 mM and the volume variation of Cysteine used is 0 to 2 ml. The 3-MCPD test was carried out with a concentration variation of 0 to 10 ppm. Furthermore, characterization was carried out using UV-Vis, FTIR, and PSA. Optimal synthesis was obtained when gold nanoparticles were added with 1 ml of 0.025 mM Cysteine. The color of the nanoparticles is ruby red and stable for up to 24 hours. The nanoparticle size was 27.1 nm, and the thiol functional group bond was broken in Cys-AuNPs. These gold nanoparticles have the potential to be further developed in detecting 3-MCPD."

"Sampel nanopartikel coupled magnetite Fe3O4/ZnO dengan tiga variasi rasio molar disintesis dengan metode sol gel. Karakterisasi sampel dilakukan dengan menggunakan Field Emission Scanning Electron Microscope (FESEM), X-ray Diffraction (XRD), Electron Dispersive X-Ray (EDX), spektroskopi UV-Vis dan Vibrating Sample Magnetometer (VSM). Pengujian aktivitas fotokalitik dilakukan dengan mengamati degradasi larutan methylene blue (MB) sebagai model polutan organik di bawah penyinaran cahaya UV. Hasil analisis FESEM menunjukkan sampel nanopartikel coupled memiliki morfologi sferis. Hasil kurva XRD menunjukkan peningkatan intensitas seiring dengan meningkatnya rasio molar ZnO dalam nanopartikel coupled Fe3O4/ZnO. Keberadaan atom Fe, O dan Zn pada sampel nanopartikel coupled dikonfirmasi oleh spektrum EDX. Aktivitas fotokalitik yang paling baik ditunjukkan oleh sampel nanopartikel coupled rasio molar 1:5 dengan dosis sebanyak 20 mg/L pada kondisi pH 13. Nanopartikel Fe3O4 dan nanopartikel coupled Fe3O4/ZnO menunjukkan sifat feromagnetik yang memungkinkan sampel untuk dipisahkan secara magnetik dari dye methylene blue.

---

Nanoparticle coupled magnetite Fe3O4/ZnO with various molar ratio has been syntesized using sol gel method. Characterization using Field Emission Scannig Electron Microscope (FESEM), X-Ray Diffraction (XRD), Electron Dispersive X-ray (EDX), UV-Vis Diffuse Reflectance and Vibrating Sampel Magnetometer (VSM) were conducted to identify morphology, structure, composition, optical and magnetic properties of nanoparticle coupled Fe3O4/ZnO. Photocatalytic activity studied by observing methylene blue (MB) degradation under UV light irradiation. FESEM shows Fe3O4/ZnO has spherical shape. XRD result shows ZnO phase intensity in nanoparticle coupled increase as ZnO molar ratio increase. The peaks corresponding to Fe, O and Zn atom were observed using EDX spectra. Maximum degradation of methylene blue was showed by 20 mg/L nanoparticle coupled with molar ratio 1:5 at pH 13. VSM result shows Fe3O4 and nanoparticle coupled samples exhibit ferromagnetic behavior. Therefore, samples can easily seperate from methylene blue using external magnetic."

"Sel surya perovskit (PSC) efisiensi tinggi biasanya didasarkan pada ETL TiO₂. Namun, sistem berbasis TiO₂ memerlukan proses di atas 450℃. Metode suhu rendah sangat penting untuk komersialisasi PSC yang fleksibel. Oleh karena itu, SnO₂ datang sebagai kandidat yang menjanjikan yang dapat menggantikan TiO₂ sebagai ETL karena SnO₂ dapat diproses menggunakan metode suhu rendah. Sintesis dilakukan dengan metode yang simple pada suhu yang relatif rendah, dan dilanjutkan dengan proses deposisi ETL dengan variasi temperatur 90℃, 120℃, 150℃, 190℃, dan 220℃. Sampel dilakukan karakterisasi menggunakan XRD, SEM, dan UV-Vis. Untuk sampel hasil sintesis didapatkan Ukuran kristal sebesar 7,82 nm dan diameter nanopartikel sebesar 0,21 μm. serta memiliki Nilai energi celah pita (Eg) sebesar 5,21 eV. Akan tetapi setelah dilakukan anil untuk proses deposisi, Nanopartikel mengalami pertumbuhan ukuran diameter. Hasilnya dengan variasi anil 90℃, 120℃, 150℃, 190℃, dan 220℃ adalah 0.21; 0.20; 0.20; 0.22 and 0.23 μm secara berturut-turut. Dan untuk hasil dari kurva absorbansi setelah dilakukan proses anil, hasilnya menunjukkan kelima sampel tidak memiliki nilai absorbansi. Terbukti dengan dilakukannya pengujian efisiensi pada kelima variasi anil, hasilnya menunjukkan kelima sampel memiliki nilai efisiensi yang sangat kecil dengan nilai PCE paling besar sebesar 0,01% pada variasi suhu 190℃. Kemudian, dilakukan uji efisiensi dengan menggunakan sampel sel surya perovskit baru dengan lapisan ETL yang tidak dianil selama proses fabrikasi. Hasil penelitian menunjukkan nilai efisiensi yang lebih besar dibandingkan sampel yang dianil, dengan nilai PCE sebesar 1,3936%.

---

High efficiency perovskite solar cell (PSC) usually based on a TiO₂ electron transport layer (ETL). However, TiO₂-based systems require treatment at typically above 450℃. Low temperature method is critical for flexible PSC commercialization. Hence, SnO₂ comes as promising candidate that can substitute TiO₂ as ETL because SnO₂ can be processed using low temperature method. The synthesis was carried out using a simple method at a relatively low temperature, and continued with the ETL deposition process with temperature variations of 90℃, 120℃, 150℃, 190℃, and 220℃. The samples were characterized using XRD, SEM, and UV-Vis. The synthesis produces crystallite size of 7.82 nm with nanoparticle diameter of 0.21 μm and a band gap energy (Eg) of 5.21 eV. However, after the annealing for the deposition process, the nanoparticles grew in diameter. The results with annealing variations of 90℃, 120℃, 150℃, 190℃, and 220℃ are 0.21; 0.20; 0.20; 0.22 and 0.23 μm respectively. For the results of the absorbance curve after the annealing process, the results showed that the five samples did not have any absorbance values. It is proven by testing the efficiency on the five annealing variations that the five samples have very small efficiency values with the largest PCE value of 0.01% at a temperature variation of 190℃. In addition, an efficiency test was carried out using a new sample of perovskite solar cells with the ETL layer not annealed during the fabrication process. The results show a greater efficiency value than the annealed sample, with a PCE value of 1.3936%."

"Nanopartikel TiO2 didop Cu telah berhasil disintesis dengan metode kopresipitasi dengan reagen TiO2 sebagai material dasar dan CuSO4.5H2O sebagai pemberi dopant. Karakterisasi komposisi, struktur, optik, dan spesies paramagnetic dilakukan dengan spektroskopi Energy Dispersive X-ray, X-ray Diffraction, Fourier Transform Infrared, Diffuse Reflectance UV-Visible, dan Electron Spin Resonance. Nanopartikel yang terbentuk memiliki struktur kristal tetragonal anatase dengan ukuran grain antara 52 nm hingga 54 nm. Munculnya fase CuO pada sampel dengan konsentrasi 6% dan 12% menunjukkan adanya batas kelarutan Cu pada TiO2 yang juga memengaruhi parameter kisi TiO2. Penambahan unsur Cu pada TiO2 memberikan efek penyempitan celah pita energi (energy gap) dengan adanya redshift pada spektrum reflektansi UV-vis. Pensubstitusian unsur Ti dengan Cu mengakibatkan munculnya spesies paramagnetik yang terdeteksi pada spektroskopi ESR.

---

Cu-doped TiO2 nanoparticles have been synthesized by coprecipitation method using chemical TiO2 as base material and CuSO4.5H2O as a dopant precursor. Several characterization was used to obtain compositional, structural, optical, and paramagnetic properties using Energy Dispersive X-ray spectroscopy, X-ray Diffraction, Fourier Transform Infrared, Diffuse Reflectance UV-Visible and Electron Spin Resonance. The sample possessed tetragonal anatase structure with grain size between 52 to 54 nm. Secondary CuO phase on 6% and 12% sample showed solubility limit of Cu in TiO2 lattice that also influence the lattice parameters. Bandgap narrowing has occurred as concentration of Cu dopant was increased, showed by redshift on band edge of reflectance. Substitution Ti with Cu atoms led to detection of paramagnetic species by ESR spectroscopy."

"Satu seri nanopartikel TiO2 didop Ni dengan variasi konsentrasi Ni dibuat dengan metode kopresipitasi. Komposisi elemen, sifat strukFtur, dan optik dikarakterisasi menggunakan X-Ray Diffraction, Electron Dispersive X-Ray dan UV-VIS diffuse reflectance spectroscopy. Identifikasi spesies paramagnetik dilakukan menggunakan Electron Spin Resonance. Berdasarkan pola difraksi XRD, hanya fase tunggal anatase yang muncul karena radius ionik Ni2+ dan Ti4+ yang hampir sama sehingga dapat menggantikan ion-ion Ti4+ pada kristal TiO2. Ukuran kristal rata-rata menurun seiring dengan peningkatan konsentrasi Ni.Fenomena ini kemungkinan terjadi akibat kehadiran ion-ion Ni2+ yang menghambat pertumbuhan kristal. Spektrum reflektansi difus UV-VIS menunjukkan bahwa penyerapan UV bergeser ke arah panjang gelombang sinar merah dan celah pita energi menurun. Hal ini disebabkan oleh atom-atom Ni yang membentuk levellevel energi localized dibawah pita konduksi pada kristal TiO2. Studi ESR pada nanopartikel TiO2 didop Ni menunjukkan adanya kehadiran Ni+, Ti3+, dan defek oksigen pada semua sampel.

---

A series Ni doped TiO2 nanoparticles with different Ni dopant concentration were facricated by coprecipitation method. The element composition, structural, and optical properties were characterized using X-Ray Diffraction, Electron Dispersive X-Ray and UV-VIS diffuse reflectance spectroscopy. Identification of paramagnetic species are conducted using Electron Spin Resonance. Based on XRD pattern, only single phase of anatase were appeared because the almost similar ionic radius of Ni2+ to that of Ti4+ which was found to replace some portion of Ti4+ ions in TiO2 lattice. The crystallite size decreases with increasing Ni content.

This phenomena probably arisen from introducing of Ni2+ ions which decrease crystalline growth. The UV-VIS diffuse reflectance spectra showed that the UV absorption moved to a longer wavelength (red shift) and the band gap energy was decreased. It caused the doped Ni atoms formed a localized energy states below conduction band of TiO2 lattice. ESR studies of Ni doped TiO2 nanoparticles revealed the presence of Ni+, Ti3+, and oxygen defects in all samples."

"Elekroda Boron-Doped Diamond BDD termodifikasi nanopartikel emas AuNP telah berhasil dipreparasi dengan metode perendaman. Sintesis AuNP dilakukan menggunakan capping agent alil amina dan poli alil amina dan menghasilkan AuNP dengan ukuran partikel rata-rata 93.197 39.228 nm. Karakterisasi BDD termodifikasi AuNP menggunakan XPS dan spektrofotometer SEM-EDS menunjukan adanya keberadaan Au pada permukaan BDD. Namun karakterisasi dengan cyclic voltammetry untuk BDD-AuNP hanya mendeteksi adanya puncak oksidasi dan reduksi Au pada BDD-AuNP dengan dengan capping agent alil amina, dan tidak mendeteksi kedua puncak tersebut pada BDD-AuNP dengan capping agent poli alil amina. BDD-AuNP hasil preparasi kemudian diaplikasikan sebagai sensor oksigen dan sensor Biochemical Oxygen Demand BOD dengan mengukur jumlah oksigen yang dibutuhkan oleh mikroorganisme Rhodoturula mucilaginosa UICC Y-181 dalam larutan untuk mengoksidasi senyawa organik. Glukosa digunakan sebagai sebagai model senyawa organik. Kadar oksigen sisa dalam larutan diukur dengan teknik Multi Pulse Amperometry melalui reaksi reduksi oksigen pada -500mV vs Ag/AgCl. Kurva kalibrasi linier diperoleh dari selisih arus reduksi oksigen sebelum dan setelah waktu kontak 20 menit mikroorganisme dengan larutan glukosa - ?I= I0-I20. Larutan glukosa yang digunakan divariasikan dengan rentang konsentrasi 0,1 ndash; 0,5 mM. Hasil pengukuran menunjukan bahwa BDDN-AuNP yang dipreparasi memiliki sensitifitas dan stabilitas yang baik digunakan sebagai elektroda dalam biosensor BOD.

---

Boron Doped Diamond BDD modified gold nanoparticles AuNP electrode were successfully prepared by immersion method. The synthesis performed by using allylamine and poly allylamine as the capping agent produced AuNP with an average particle size of 93.197 39.228 nm. Characterization of AuNP modified BDD using XPS and SEM EDS spectrophotometers indicates the presence of Au on BDD surfaces. However, characterization with cyclic voltammetry observed the oxidation reduction couple peaks only at BDD AuNP with allylamine as the capping agent. On the contrary, the peaks were not observed at BDD AuNP with poly allylamine as the capping agent. Then, BDD AuNP electrode was applied as oxygen sensor and biochemical oxygen demand BOD sensors by measuring the amount of oxygen required by the Rhodoturula mucilaginosa UICC Y 181 to oxidize the organic compound in solution. Glucose has been used as a model of organic compounds. The residual oxygen content in solution was measured by Multy Pulse Amperometry technique through oxygen reduction reaction at 500mV vs Ag AgCl. The calibration curve with a concentration range of 0.1 0.5 mM glucose was obtained from the difference of the oxygen reduction current before and after 20 min contact time of microorganism with glucose solution I I0 I20. The measurement results show that the prepared BDD AuNP electrode has good sensitivity and stability for application in BOD biosensor. "