Hasil Pencarian  ::  Simpan CSV :: Kembali

Abstrak :
Pengelasan memiliki peran penting dalam industri konstruksi, manufaktur, serta oil and gas. Salah satu penerapan teknologi pengelasan dalam industri adalah pengelasan pada pipa. Dalam penelitian ini, pengelasan pipa orbital dilakukan dengan Gas Tungsten Arc Welding (GTAW) tanpa filler metal (autogenous) pada pipa baja tahan karat tipe SS316L. Dimensi material uji adalah diameter luar 114 mm dan ketebalan 3 mm. Pengujian pengelasan dilakukan untuk mengetahui kualitas pengelasan (lebar manik) dan kekuatan tarik. Parameter pengelasan yang digunakan adalah arus terpulsasi, kecepatan pengelasan sebesar 0,150 mm/s, 0,154 mm/s, dan 0,161 mm/s, serta 4 posisi sudut pipa saat pengelasan yaitu 0°, 90°, 180°, dan 270°. Tahapan pengujian yang dilakukan meliputi persiapan alat dan benda uji, pengelasan bahan uji, dan pengujian kekuatan tarik dan mikrokekerasan. Alat pengelasan yang digunakan adalah alat pengelasan pipa orbital prototipe dengan metode 5G. Selanjutnya, untuk material SS316L, setelah dilakukan pengelasan, dilakukan pembentukan benda uji kekuatan tarik dengan bentuk standar bahan uji menggunakan standar ASTM E-8M. Hasil pengukuran lebar manik paling lebar terjadi pada kecepatan pengelasan 0,154 mm/s dengan lebar manik 12,14 mm pada posisi 90°. Hasil pengujian kekuatan tarik tertinggi terjadi pada kecepatan pengelasan 0,150 mm/d dengan kekuatan tarik maksimum sebesar 571,07 MPa pada posisi 180° dengan arus sebesar 100A.  ......Welding plays a significant role in the construction, manufacturing, and oil and gas industries. One application of welding technology in these industries is pipe welding. In this study, orbital pipe welding was conducted using Gas Tungsten Arc Welding (GTAW) without filler metal (autogenous) on SS316L stainless steel pipes. The test material had an outer diameter of 114 mm and a thickness of 3 mm. Welding testing was performed to assess the weld quality (bead width) and tensile strength. The welding parameters used were pulsed current, welding speed of 0.150 mm/s, 0.154 mm/s, and 0.161 mm/s, and four pipe corner positions during welding: 0°, 90°, 180°, and 270°. The testing stages included tool and sample preparation, welding of the test material, and tensile strength and microhardness testing. A prototype orbital pipe welding tool using the 5G method was employed. Additionally, for SS316L material, after welding, test specimens for tensile strength were formed using the standard shape of the test material following ASTM E-8M. The widest bead width measurement was obtained at a welding speed of 0.154 mm/s with a bead width of 12.14 mm at the 90° position. The highest tensile strength test results occurred at a welding speed of 0.150 mm/s with a maximum tensile strength of 571.07 MPa at the 180° position with a current of 100A.

Abstrak :
Pada penelitian ini dilakukan pengelasan pipa orbital dengan pengelasan Tungsten Inert Gas (TIG) tanpa logam pengisi (autogenous) pada pipa baja tahan karat tipe 316L. Dimensi dari material uji adalah diameter luar 114.3 mm dan ketebalan 3 mm. Tujuan dari penelitian ini untuk mengetahui pengaruh arus pengelasan dan sequence terhadap karakteristik geometri las, distorsi, sifat mekanik dan struktur makro. Variasi parameter dalam penelitian ini yaitu arus 100, 110, 120 ampere dan variasi sequence, yaitu 1 sequence (360˚), 2 sequence (180˚), 3 sequence (120˚), 4 sequence (90˚). Kecepatan pengelasan yang digunakan adalah 1,4 mm/detik. Hasil menunjukkan bahwa meningkatkan arus las dapat menaikkan rata-rata lebar manik luar dan variasi sequence pada pengelasan dapat membatasi temperatur kerja. Pada distorsi pengelasan, menaikan sequence dapat menurunkan kekuatan distorsi dan menambah nilai arus dapat menaikkan kekuatan distorsi. Untuk hasil uji tarik, menambahkan nilai arus dapat meningkatkan nilai UTS dan menambah sequence pengelasan akan membuat nilai UTS nya semakin rendah. Pada pengamatan makro, meningkatkan nilai arus pengelasan akan membuat hasil penetrasi las semakin baik. Namun pada perbedaan sequence tidak terlalu signifikan hasilnya, hanya dilihat dari penambahan jumlah sequence akan membuat trend penetrasi nya menurun. ...... Orbital pipe welding was carried out in this research by current Tungsten Inert Gas (TIG) welding without metal filler (autogenous) of 316L stainless steel pipes. The dimensions of the specimens were 114.3 mm outside diameter and the thickness of 3 mm. The purpose of this study was to determine the effect of current parameters and welding sequence on the characteristics of weld geometry, distortion, mechanical properties and macrostructure. Variation of welding current in this research were (100,110,120) ampere and sequence welding variation were 1 sequence (360˚), 2 sequence (180˚), 3 sequence (120˚), 4 sequence (90)˚.The welding speed used was 1,4 mm/s. Results indicated that the average outer bead width increases with increase in current value and sequence variations limit the working temperatur. Upon welding distortion, increasing the amount of sequence decreases the distortion strength, while adding current value increases the distortion strength. Tension test results indicated that with the increase in welding current the UTS will increase until an optimum value, while increase in welding sequence decreased the UTS value. Macro observation data shows that welding current is of primary importance to penetration where weld penetration increases as welding current increases. Variations of welding sequence results in no significant changes, whereas increasing the number of sequence will reduce welding penetration.

Abstrak :
Pada penelitian ini dilakukan pengelasan pipa orbital dengan pengelasan Tungsten Inert Gas (TIG) arus pulsa tanpa logam pengisi (autogenous) pada pipa baja tahan karat tipe 304. Dimensi dari material uji adalah diameter luar 114 mm dan ketebalan 3 mm. Tujuan dari penelitian ini untuk mengetahui pengaruh parameter arus pulsa, posisi las dan siklus kerja terhadap karakteristik geometri las, sifat mekanik dan struktur mikro. Variasi parameter dalam penelitian ini yaitu arus konstan, arus pulsa dan siklus kerja. Arus rata-rata dari setiap parameter dibuat sama yaitu 100 ampere, namun pada arus pulsa terdapat variasi arus puncak, arus dasar, waktu arus puncak dan waktu arus dasar. Kecepatan pengelasan yang digunakan adalah 1,4 mm/detik. Hasil penelitian ini menunjukkan bahwa pada pengelasan dengan variasi arus pulsa menghasilkan lebar manik las yang lebih besar dari pada pengelasan dengan arus konstan. Hasil lebar manik las berbanding lurus dengan peningkatan arus pulsa. Terjadi penurunan kekuatan tarik sebesar 23,95 % pada parameter 65-B posisi las 0⁰ dan kenaikan kekuatan tarik sebesar 16,09 % pada parameter 65-A posisi las 180⁰ terhadap kekuatan tarik logam dasar. Pada kekerasan mikro dengan metode vickers, terjadi penurunan kekerasan terbesar pada daerah HAZ dan daerah las sebesar 20,50 % dan 7,22 % pada parameter 50-C.  ...... Orbital pipe welding was carried out in this research by pulse current Tungsten Inert Gas (TIG) welding without metal filler (autogenous) of 304 stainless steel pipes. The dimensions of the specimens were 114 mm outside diameter and the thickness of 3 mm. The purpose of this study was to determine the effect of pulse current parameters, weld position and duty cycle on the characteristics of weld geometry, mechanical properties and microstructure. Variation of parameters in this study were constant current, pulse current and duty cycle. The average current of each parameter was the same 100 ampere, but in the pulse current there were variations in peak current, base current, peak current time and base current time. The welding speed used was 1.4 mm/second. The results of this study indicate that in the welding with variations in pulse currents it produces a larger weld bead width than the welding with a constant current. The width of the weld bead was directly proportional to the increase in pulse current. There was a decrease in tensile strength of 23.95% in the parameter 65-B weld position 0⁰ and an increase in tensile strength of 16.09% in parameter 65-A weld position 180⁰ against the tensile strength of the base metal. In the micro hardness with vickers method, the greatest hardness occurred in the HAZ region and the weld area by 20.50% and 7.22% in the 50-C parameter.